Abstract

Birefringence is caused by both orientation of polymer chains and photoelasticity. These birefringences were compensated by random copolymerization of negative birefringent methyl methacrylate and positive birefringent benzyl methacrylate, but orientational and photoelastic zero birefringences were achieved with quite different compositions of the copolymers. Note that the birefringence of the copolymer that occurred in the process of injection molding was almost completely eliminated with a composition for orientational zero birefringence. The orientational and photoelastic zero-birefringence copolymers possessed enough transparency as optical materials that the total scattering losses were 30.4 and 19.5 dB/km, respectively, competing with the transparency of homopolymers.

© 1997 Optical Society of America

Investigation of optical and thermal properties of N-(alkyl-substituted) maleimides for use in zero–zero-birefringence polymer

Shotaro Beppu, Hikaru Hotta, Houran Shafiee, Akihiro Tagaya, and Yasuhiro Koike
Appl. Opt. 54(4) 779-788 (2015)

Zero-birefringence polymer by the anisotropic molecule dope method

Akihiro Tagaya, Shuichi Iwata, Eriko Kawanami, Hisashi Tsukahara, and Yasuhiro Koike
Appl. Opt. 40(22) 3677-3683 (2001)

Gradient refractive-index optical rod prepared from methacrylate derivatives

Jui-Hsiang Liu and Hung-Tsai Liu
Opt. Lett. 22(10) 668-670 (1997)

Graded-index plastic optical fiber composed of methyl methacrylate and vinyl phenylacetate copolymers

Yasuhiro Koike, Eisuke Nihei, Norihisa Tanio, and Yasuji Ohtsuka
Appl. Opt. 29(18) 2686-2691 (1990)

All-optical induction of noncentrosymmetry in a transparent nonlinear polymer rod

Céline Fiorini, Fabrice Charra, Paul Raimond, André Lorin, and Jean-Michel Nunzi
Opt. Lett. 22(24) 1846-1848 (1997)