Abstract
The optical damage threshold of indentation-induced flaws on fused silica surfaces was explored. Mechanical flaws were characterized by laser damage testing, as well as by optical, secondary electron, and photoluminescence microscopy. Localized polishing, chemical leaching, and the control of indentation morphology were used to isolate the structural features that limit optical damage. A thin defect layer on fracture surfaces, including those smaller than the wavelength of visible light, was found to be the dominant source of laser damage initiation during illumination with , laser pulses. Little evidence was found that either displaced or densified material or fluence intensification plays a significant role in optical damage at fluences . Elimination of the defect layer was shown to increase the overall damage performance of fused silica optics.
© 2010 Optical Society of America
Full Article | PDF ArticleMore Like This
Feng Shi, Yaoyu Zhong, Yifan Dai, Xiaoqiang Peng, Mingjin Xu, and Tingting Sui
Opt. Express 24(18) 20842-20854 (2016)
Yaoyu Zhong, Feng Shi, Ye Tian, Yifan Dai, Ci Song, Wanli Zhang, and Zhifan Lin
Opt. Express 27(8) 10826-10838 (2019)
J. Bude, P. Miller, S. Baxamusa, N. Shen, T. Laurence, W. Steele, T. Suratwala, L. Wong, W. Carr, D. Cross, and M. Monticelli
Opt. Express 22(5) 5839-5851 (2014)