Abstract
Efficient dual-wavelength laser performance of Yb:YAG crystal grown by temperature gradient technique was achieved at room temperature. Slope efficiencies of 57%, 68% at 1049 nm and 1030 nm were achieved for 10 at.% Yb:YAG sample.
© 2006 Optical Society of America