Abstract

DuPont E-120 high-modulus pitch-based carbon fibers were treated electrochemically in 0.5 M (NH₄)₂CO₃ solution under both potentiostatic and galvanostatic modes. X-ray photoelectron spectroscopy (XPS) was used to monitor the chemical changes on the carbon fiber surfaces. Both core-level and valence-band spectra showed that the treatment introduced both oxygen-containing and nitrogen-containing functional groups onto the fiber surfaces, and the mainly oxygen-containing functional groups produced were carbonyl (C=O) type functional groups after longer treatment time. For short treatment time, hydroxide (C-OH) type groups were the dominant functionality, and ether (C-O-C) or epoxide type groups were also formed. The O 2<i>s</i> peaks from oxygen atoms in the hydroxide functionality and the ether or epoxide groups are well separated in the valence-band spectra; the corresponding O 1<i>s</i> peaks, however, are not separated in the O 1<i>s</i> core-region spectra.

X-ray photoelectron spectroscopy study of thin TiO₂ films cosputtered with Al

Jin-Cherng Hsu, Paul W. Wang, and Cheng-Chung Lee
Appl. Opt. 45(18) 4303-4309 (2006)

Electronic properties of undoped LiBaAlF₆ single crystals: far-ultraviolet optical, luminescence, and x-ray photoelectron spectroscopy studies

Vladimir A. Pustovarov, Igor N. Ogorodnikov, Sergey I. Omelkov, Dmitry A. Spassky, and Ludmila I. Isaenko
J. Opt. Soc. Am. B 31(8) 1926-1934 (2014)

Oxidation of aluminum thin films protected by ultrathin MgF₂ layers measured using spectroscopic ellipsometry and X-ray photoelectron spectroscopy

Brian I. Johnson, Tahereh G. Avval, R. Steven Turley, Matthew R. Linford, and David D. Allred
OSA Continuum 4(3) 879-895 (2021)

Effect of the content of ammonium dichromate in dichromated gelatin on Cr 2P_3/2 x-ray photoelectron spectroscopy

Liang-wen Xiong and Bi-xian Peng
Appl. Opt. 38(2) 279-283 (1999)

Laser based soft-x-ray pulses for photoelectron spectroscopy of surfaces

G. Tsilimis, C. Benesch, J. Kutzner, and H. Zacharias
J. Opt. Soc. Am. B 20(1) 246-253 (2003)