Effect of the laser treatment on electroless Ni-P-SiC composite coatings was investigated. The microscopic structure, surface morphology, ingredient, and performance of the Ni-P-SiC composite coatings were synthetically analyzed by the use of X-ray diffraction apparatus, scanning electron microscope, energy distribution spectrometer, micro-hardness tester, wear tester and so on. It was found that the composite coatings did make crystalloblastic transformation after laser heating. Structural analysis confirmed that some new types of phase Ni2Si or Ni3Si compound would emerge in the Ni-P-SiC coatings after laser treatment. The micro-hardness measurement results showed that when the laser power was 450 W with scanning speed of 0.5 m/min, the hardness of the coating was superior to the coating obtained by the conventional furnace heating, and wear resistance of the composite coating after laser treating could also improve.
© 2006 Chinese Optics Letters
(050.5080) Diffraction and gratings : Phase shift
(120.6650) Instrumentation, measurement, and metrology : Surface measurements, figure
(140.0140) Lasers and laser optics : Lasers and laser optics
Honghong Shao, Xiaoyan Jiang, Lan Wang, and Yinqun Hua, "Study on the laser treatment of electroless Ni-P-SiC composite coatings," Chin. Opt. Lett. 4, 589-591 (2006)