Abstract

Thermal stability and 2-<i>µ</i>m fluorescence of high and low Al(PO₃)₃ content of fluorophosphate glasses are investigated. Thermal stability of high Al(PO₃)₃ content of fluorophosphate glass is better than low Al(PO₃)₃ content of fluorophosphate glass. However, 2.04-<i>µ</i>m fluorescence intensity of high Al(PO₃)₃ content of fluorophosphate glass is only 48.2, lower than low Al(PO₃)₃ content of fluorophosphate glass. Raman spectroscopy is employed to investigate the difference in thermal stability and 2-<i>µ</i>m fluorescence. Moreover, fluorescence peak intensity ratios of 2.04 to 1.81 <i>µ</i>m and 2.04 to 1.57 <i>µ</i>m are calculated, which indicate that Er-Tm-Ho doped fluorophosphate glasses are suitable materials in 2-<i>µ</i>m applications.

© 2009 Chinese Optics Letters

Effect of Ba(PO₃)₂ addition on the optical properties of Tm³⁺-doped fluorophosphate glasses

Xin Sun, Jiangbo She, Xiaohui Li, Min Lu, Pengfei Wang, and Dongdong Li
Opt. Mater. Express 9(3) 1233-1245 (2019)

Physical, chemical, and optical properties of Er³⁺-doped low Al(PO₃)₃/Al(H₂PO₄)₃ modified fluoroaluminate glasses for 2.7  μm application

Feifei Huang, Weiwei Li, Lili Hu, and Danping Chen
J. Opt. Soc. Am. B 31(5) 1137-1144 (2014)

Intense 2.7 μm and broadband 2.0 μm emission from diode-pumped Er³⁺/Tm³⁺/Ho³⁺-doped fluorophosphate glass

Ying Tian, Rongrong Xu, Lili Hu, and Junjie Zhang
Opt. Lett. 36(16) 3218-3220 (2011)

Optical properties of Er³⁺-doped K-Ca-Al fluorophosphate glasses for optical amplification at 1.53 μm

K. Linganna, K. Suresh, S. Ju, W.-T. Han, C.K. Jayasankar, and V. Venkatramu
Opt. Mater. Express 5(8) 1689-1703 (2015)

Effect of chloride ion introduction on structural and 1.5 μm emission properties in Er³⁺-doped fluorophosphate glass

Ying Tian, Rongrong Xu, Lili Hu, and Junjie Zhang
J. Opt. Soc. Am. B 28(7) 1638-1644 (2011)