Abstract
We prepared a back-contact dye-sensitized solar cell and investigated effect of the sputter deposited thin TiO2 film on the back-contact ITO electrode on photovoltaic property. The nanocrystalline TiO2 layer with thickness of about 11 μm formed on a plain glass substrate in the back-contact structure showed higher optical transmittance than that formed on an ITO-coated glass substrate, which led to an improved photocurrent density by about 6.3%. However, photovoltage was found to decrease from 817 mV to 773 mV. The photovoltage recovered after deposition of a 35 nm-thick thin TiO2 film on the surface of the back-contact ITO electrode. Little difference in time constant for electron transport was found for the back-contact ITO electrodes with and without the sputter deposited thin TiO2 film. Whereas, time constant for charge recombination increased after introduction of the thin TiO2 film, indicating that such a thin TiO2 film protected back electron transfer, associated with the recovery of photovoltage. As the result of the improved photocurrent density without deterioration of photovoltage, the back-contact dye-sensitized solar cell exhibited 13.6% higher efficiency than the ITO-coated glass substrate-based dye-sensitized solar cell.
©2010 Optical Society of America
Full Article | PDF ArticleMore Like This
Yongbeom Kwon, Jaeyoung Seo, Yoonmook Kang, Donghwan Kim, and Jihyun Kim
Opt. Express 26(2) A30-A38 (2018)
Dorota M. Bacal, Niraj N. Lal, Askhat N. Jumabekov, Qicheng Hou, Yinghong Hu, Jianfeng Lu, Anthony S. R. Chesman, and Udo Bach
Opt. Express 28(9) 12650-12660 (2020)
Seungkeun Choi, William J. Potscavage, and Bernard Kippelen
Opt. Express 18(S3) A458-A466 (2010)