Fabrication of a pencil-shaped fiber probe with a nanometric protrusion from a metal film for near-field optical microscopy

Shuji Mononobe, R. Uma Maheswari, and Motoichi Ohtsu  »View Author Affiliations


Optics Express, Vol. 1, Issue 8, pp. 229-233 (1997)
http://dx.doi.org/10.1364/OE.1.000229


View Full Text Article

Acrobat PDF (80 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

We propose a method to fabricate a probe with a nanometric protrusion for near-field optical microscopy. The method involves a tapering process based on selective etching of a GeO2-doped fiber in a buffered hydrogen fluoride solution and a metallizing process by vacuum evaporation and chemical polishing. We fabricated a tapered probe which has a protrusion emerging from a metal film. The protrusion has an apex diameter less than 10nm and a foot diameter less than 20nm. Employing the probe, we succeeded in obtaining a highly resolved image of 20nm gold particles.

© Optical Society of America

Recently, super high resolution optical imaging has been performed beyond the diffraction limit by near-field optical microscopy [1–4

1. W. Pohl and D. Courjon, eds., Near field optics, Vol. 242 of NATO ASI Series E (Kluwer Academic, Dordrecht, 1993). [CrossRef]

] employing a tapered fiber probe with a nanometric apex and a small taper angle. We previously produced a probe with a taper angle of 20°, an apex diameter less than 10nm, and a nanometric protrusion emerging from a metal film [5

5. S. Mononobe, M. Naya, R. Uma Maheswari, T. Saiki, and M. Ohtsu, in The 3rd International Conference on Near Field Optics and Related Techniques (NFO-3), Brno, Czech Republic, May 1995, Vol. 8 of EOS Topical Meeting Digest, (European Optical Society, Orsay, 1995), pp. 105–106.

] by selective resin coating (SRC) [6

6. S. Mononobe, M. Naya, T. Saiki, and M. Ohtsu, “Reproducible fabrication of a fiber probe with a nanometric protrusion for near-field optics,” Appl. Opt. 36, 1496–1500 (1997). [CrossRef] [PubMed]

]. Employing the probe, we succeeded in obtaining nanometric images [7

7. M. Naya, R. Micheletto, S. Mononobe, R. Uma Maheswari, and M. Ohtsu, “Near-field optical imaging of flagellar filaments of salmonella in water with optical feedback control,” Appl. Opt. 36, 1681–1683 (1997). [CrossRef] [PubMed]

,8

8. A. Zvyagin, J. D. White, and M. Ohtsu, “Near-field optical microscope image formation: a theoretical and experimental study,” Opt. Lett. 22, 955–957 (1997). [CrossRef] [PubMed]

] of biological samples. Such a probe is found to be effective both as a scatterer (and/or a generator) of high spatial frequency evanescent components responsible for high resolution capability and as a suppresser of the low spatial frequency components and the propagating components. However, the SRC method can not be applied to a tapered probe such as a pencil-shaped probe without a flat end portion [6

6. S. Mononobe, M. Naya, T. Saiki, and M. Ohtsu, “Reproducible fabrication of a fiber probe with a nanometric protrusion for near-field optics,” Appl. Opt. 36, 1496–1500 (1997). [CrossRef] [PubMed]

]. In this letter, we propose a method to fabricate a pencil-shaped probe which has a nanometric protrusion emerging from a metal film using a commercial GeO2-doped fiber.

Fig. 1 Fabrication method of a pencil-shaped fiber probe with a protrusion from a metal film. Here, the method involves five steps; [A] tapering the cladding by meniscus etching in hydrofluoric (HF) acid with a surface layer of organic solution, [B] sharpening the core by selective etching in buffered hydrogen fluoride solution (BHF), [C] increasing the taper angle in HF-containing aqueous solution [D], coating a metal film by vacuum evaporation, and [E] removing the metal that covers the apex region by chemical polishing. α is the taper angle of the cladding. θ and θ B are the taper angles of the core. In vacuum evaporation, the fiber is tilted with the angle ϕ and rotated.
Fig. 2 (a) Scanning electron micrographs (SEM) of (a) pencil-shaped fiber with a taper angle of 20°, (b) the magnified top region. Here, the fiber is coated with gold having a thickness of 3nm. The apex diameter is less than 10nm; SEM images of (c) the top region and (d) the apex region of the metallized probe which has a protrusion from a metal film. Here, the metal is gold. The radial thickness of the gold film is 150nm. The foot diameter of the protrusion as shown by the dark portion is less than 20nm. Because the length of the protrusion is less than 10nm, nearing the limit of SEM, it is difficult to get a visualization in (d).

Figure 1 schematically explains the method involving five steps; [A] tapering the cladding, [B] sharpening the core, [C] increasing the taper angle, [D] coating a metal film, and [E] removal of metal covering the apex region. Here, the method is divided into the tapering process of steps [A]–[C] and the metallizing process of steps [D] and [E]. The symbols α, θ, and θ B are defined a s the taper angles of the pencil-shaped fiber. The notations of Oil/HF, BHF, HF are HF acid with a surface layer of an organic solution, a buffered hydrogen fluoride solution with a volume ratio of 40wt.%-NH4F aqueous solution: 50wt.%-HF acid: H2O= X:1:Y, and an aqueous solution containing HF. Throughout this letter, BHF is denoted as X:1:Y. Figures 2(a) and 2(b) show scanning electron micrographs (SEM) of the pencil-shaped fiber obtained with taper angles of θ =10° and α=20° by steps [A]–[C]. The taper angle and the apex diameter are 20° and less than 10nm, respectively. Figures 2(c) and 2(d) are, respectively, SEM images of the magnified top region of a fabricated probe with a protrusion and of the apex region. The dark portion in Fig. 2(d) shows a fabricated probe with a protrusion. The radial thickness of gold film is about 150nm. The foot diameter of silica tip protruding from the metal film is less than 20nm. In the following, we describe the method for fabricating the probe.

Next, we discuss the reproducibility of the etching process. In step [B], by denoting the etching rate of the core and cladding as R 1 and R 2, respectively, the taper angle θ B is represented by [10: Eq. (A1)]

sin(θB2)=(R1R2)sin(α2).

The right side is controlled by varying the GeO2 doping ratio and the concentrations of BHF (or X and Y). The pencil-shaped probe with taper angles of θ B=20° and α=20° is fabricated by the etching with a ratio of 1.7:1:1 where R 1/R 2=1. However, it is difficult to produce a probe with an apex diameter less than 10nm with high reproducibility. We consider that this difficulty is attributed to geometric eccentricity of the taper formed by step [A]. The taper has an eccentric radius of around 1μm between the core and the apex of the taper. To improve the reproducibility, we add steps [C]. As a result, we succeeded in obtaining the probe with a taper angle of θ =20° (±3°) and an apex diameter of less than 10nm with 80% reproducibility or more.

Futhermore, we discuss the metallizing process using vacuum evaporation. We performed step [D] with various angle ϕ in a region of 55°–90° and observed the probe by SEM. In the case of a thin coating of 120nm and a tilted angle of ϕ=50°, we evaluated a metal thickness of 30nm covering the fiber apex from the SEM photographs before and after the chemical polishing. For fabricating a probe with a protrusion, step [E] or another removal technique is required At ϕ=50°, we obtained a protrusion-type probe with a foot diameter of 20nm (± 15nm) with about 75% reproducibility or more using 12 fiber samples with apex diameters less than 10nm.

Finally, to demonstrate the imaging capability of the fabricated probe, we observed gold particles of size 20nm fixed on a glass substrate by a near-field optical microscope (NOM). The NOM is operated under illumination mode with the probe illuminating the sample substrate by an argon ion laser with a 488nm wavelength. Details of the experimental system can be found in Ref. 11

11. R. Uma Maheswari, H. Tatsumi, Y. Katayama, and M. Ohtsu, “Observation of subcellular nanostructure of single neurons with an illumination mode photon scanning tunneling microscope,” Opt. Commun. 120, 325–334 (1995). [CrossRef]

. The size of the gold particles are well calibrated by TEM to be 20nm (±1nm) and they are just suitable for the high resolution imaging capability of the probe. The obtained image is shown in Fig. 3. Here, the scan area is 200nm×200nm. The dark portions (as marked by the arrow) correspond to single gold particles. Based on power spectral analysis of the image, the estimated size of the single particles is found to be around 22nm. For details of the analysis, refer to Ref. 12

12. R. Uma Maheswari, H. Kadono, and M. Ohtsu, “Power spectral analysis for evaluating optical near-field image of 20nm gold particles,” Opt. Commun. 131, 133–142 (1996). [CrossRef]

. This closely agrees with the actual size of the particle, thus demonstrating the effective functioning is high resolution imaging of the proposed NOM probe.

Fig. 3 Near-field optical image of 20nm-gold particles illuminated by a 488nm argon ion laser. Here the scan area is 200nm×200nm. The dark portions as indicated by the arrow show single gold particles.

In conclusion, we proposed a method to fabricate a pencil-shaped fiber with a nanometric tip protruding from metal film. We obtained a probe which has a silica protrusion with an apex diameter less than 10nm and a foot diameter less than 20nm. Employing the probe, we obtained a high-resolution image of 20nm-sized gold particles.

References and links

1.

W. Pohl and D. Courjon, eds., Near field optics, Vol. 242 of NATO ASI Series E (Kluwer Academic, Dordrecht, 1993). [CrossRef]

2.

E. Betzig and J. K. Trautman, “Near-field optics: microscopy, spectroscopy, and surface modification beyond the diffraction limit,” Science 257, 189–195 (1992). [CrossRef] [PubMed]

3.

M. Ohtsu, “Progress of high-resolution photon scanning tunneling microscopy due to a nanometric fiber probe,” J. Lightwave Technol. 13, 1200–1221 (1995). [CrossRef]

4.

Special issue on NFO-3, Ultramicroscopy61 (1995), edited by M. Paesler and N. van Hulst.

5.

S. Mononobe, M. Naya, R. Uma Maheswari, T. Saiki, and M. Ohtsu, in The 3rd International Conference on Near Field Optics and Related Techniques (NFO-3), Brno, Czech Republic, May 1995, Vol. 8 of EOS Topical Meeting Digest, (European Optical Society, Orsay, 1995), pp. 105–106.

6.

S. Mononobe, M. Naya, T. Saiki, and M. Ohtsu, “Reproducible fabrication of a fiber probe with a nanometric protrusion for near-field optics,” Appl. Opt. 36, 1496–1500 (1997). [CrossRef] [PubMed]

7.

M. Naya, R. Micheletto, S. Mononobe, R. Uma Maheswari, and M. Ohtsu, “Near-field optical imaging of flagellar filaments of salmonella in water with optical feedback control,” Appl. Opt. 36, 1681–1683 (1997). [CrossRef] [PubMed]

8.

A. Zvyagin, J. D. White, and M. Ohtsu, “Near-field optical microscope image formation: a theoretical and experimental study,” Opt. Lett. 22, 955–957 (1997). [CrossRef] [PubMed]

9.

S. Mononobe and M. Ohtsu, “Fabrication of a pencil-shaped fiber probe for near-field optics by selective chemical etching,” J. Lightwave Technol. 14, 2231–2235 (1996); Erratum, J. Lightwave Technol. 15, 162 (1997). [CrossRef]

10.

S. Mononobe and M. Ohtsu, “A model based on geometrical construction in designing a pencil-shaped fiber probe for near-field optics,” J. Lightwave Technol. 15, 1051–1055 (1997). [CrossRef]

11.

R. Uma Maheswari, H. Tatsumi, Y. Katayama, and M. Ohtsu, “Observation of subcellular nanostructure of single neurons with an illumination mode photon scanning tunneling microscope,” Opt. Commun. 120, 325–334 (1995). [CrossRef]

12.

R. Uma Maheswari, H. Kadono, and M. Ohtsu, “Power spectral analysis for evaluating optical near-field image of 20nm gold particles,” Opt. Commun. 131, 133–142 (1996). [CrossRef]

OCIS Codes
(050.1220) Diffraction and gratings : Apertures
(060.2290) Fiber optics and optical communications : Fiber materials
(060.2350) Fiber optics and optical communications : Fiber optics imaging
(120.6650) Instrumentation, measurement, and metrology : Surface measurements, figure
(180.5810) Microscopy : Scanning microscopy

ToC Category:
Research Papers

History
Original Manuscript: July 29, 1997
Revised Manuscript: July 22, 1997
Published: October 13, 1997

Citation
Shuji Mononobe, R. Uma Maheswari, and Motoichi Ohtsu, "Fabrication of a pencil-shaped fiber probe with a nanometric protrusion from a metal film for near-field optical microscopy," Opt. Express 1, 229-233 (1997)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-1-8-229


Sort:  Journal  |  Reset  

References

  1. W. Pohl and D. Courjon, eds., Near field optics, Vol. 242 of NATO ASI Series E (Kluwer Academic, Dordrecht, 1993). [CrossRef]
  2. E. Betzig and J. K. Trautman, Near-field optics: microscopy, spectroscopy, and surface modification beyond the diffraction limit, Science 257, 189-195 (1992). [CrossRef] [PubMed]
  3. M. Ohtsu, Progress of high-resolution photon scanning tunneling microscopy due to a nanometric fiber probe, J. Lightwave Technol. 13, 1200-1221 (1995). [CrossRef]
  4. Special issue on NFO-3, Ultramicroscopy 61 (1995), edited by M. Paesler and N. van Hulst.
  5. S. Mononobe, M. Naya, R. Uma Maheswari, T. Saiki, and M. Ohtsu, in The 3rd International Conference on Near Field Optics and Related Techniques (NFO-3), Brno, Czech Republic, May 1995, Vol. 8 of EOS Topical Meeting Digest, (European Optical Society, Orsay, 1995), pp. 105-106.
  6. S. Mononobe, M. Naya, T. Saiki, and M. Ohtsu, Reproducible fabrication of a fiber probe with a nanometric protrusion for near-field optics, Appl. Opt. 36, 1496-1500 (1997). [CrossRef] [PubMed]
  7. M. Naya, R. Micheletto, S. Mononobe, R. Uma Maheswari, and M. Ohtsu, Near-field optical imaging of flagellar filaments of salmonella in water with optical feedback control, Appl. Opt. 36, 1681-1683 (1997). [CrossRef] [PubMed]
  8. A. Zvyagin, J. D. White, and M. Ohtsu, Near-field optical microscope image formation: a theoretical and experimental study, Opt. Lett. 22, 955-957 (1997). [CrossRef] [PubMed]
  9. S. Mononobe and M. Ohtsu, Fabrication of a pencil-shaped fiber probe for near-field optics by selective chemical etching, J. Lightwave Technol. 14, 2231-2235 (1996); Erratum, J. Lightwave Technol. 15, 162 (1997). [CrossRef]
  10. S. Mononobe and M. Ohtsu, "A model based on geometrical construction in designing a pencil-shaped fiber probe for near-field optics," J. Lightwave Technol. 15, 1051-1055 (1997). [CrossRef]
  11. R. Uma Maheswari, H. Tatsumi, Y. Katayama, and M. Ohtsu, Observation of subcellular nanostructure of single neurons with an illumination mode photon scanning tunneling microscope, Opt. Commun. 120, 325-334 (1995). [CrossRef]
  12. R. Uma Maheswari, H. Kadono, and M. Ohtsu, Power spectral analysis for evaluating optical near-field image of 20nm gold particles, Opt. Commun. 131, 133-142 (1996). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.

Figures

Fig. 1 Fig. 2 Fig. 3
 

Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited