Brillouin frequency shifts in silica optical fiber with the double cladding structure

J. W. Yu, Y. Park, K. Oh, and I. B. Kwon  »View Author Affiliations


Optics Express, Vol. 10, Issue 19, pp. 996-1002 (2002)
http://dx.doi.org/10.1364/OE.10.000996


View Full Text Article

Acrobat PDF (128 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

We report theoretical and experimental analysis on Brillouin frequency shift in silica optical fibers with the double cladding structures that are comprised of GeO2-doped core, P2O5- and F-codoped inner cladding and silica outer cladding. The intrinsic Brillouin frequency shift was calculated for various fiber parameters utilizing boundary conditions for longitudinal acoustic waves. Optical fibers with different fiber parameters were fabricated and the Brillouin frequency shifts were measured in the wavelength region of 1.55μm. We confirmed that the inner cladding in an optical fiber could provide a new degree of freedom in controlling the Brillouin frequency shift.

© 2002 Optical Society of America

Stimulated Brillouin scattering (SBS) is being extensively investigated for applications in optical fiber communications and sensor systems, such as hybrid erbium/Brillouin amplifiers [1

1. S. J. Strutz and K. J. Williams, “Low-noise hybrid erbium/Brillouin amplifier,” Electron. Lett. 36, 1359–1360 (2000). [CrossRef]

], lasers [2

2. G. J. Cowle, D. Y. Stepanov, and Y. T. Chieng, “Brillouin/Erbium Fiber Lasers,” J. Lightwave Technol. 15, 1198–1204 (1997) [CrossRef]

], Brillouin/Raman multi-wavelength comb generation [3

3. B. Min, P. Kim, and N. Park, “Flat amplitude equal spacing 798-channel Rayleigh-assited Brillouin/Raman multiwavelength comb generation in dispersion compensation fiber,” IEEE Photon. Technol. Lett. 13, 1352–1354 (2001). [CrossRef]

], and the distributed measurement of strain and temperature [4

4. H. H. Kee, G. P. Lees, and T. P. Newson, “All-fiber system for simultaneous interrogation of distributed strain and temperature sensing by spontaneous Brillouin scattering,” Opt. Lett. 25, 1–3 (2000). [CrossRef]

]. In order to characterize SBS phenomena, the impacts of optical fiber materials on SBS have been reported and GeO2-doped silica was found to be an optimal glass host for the core in terms of gain and optical loss [5

5. M. Nikles, L. Thevenaz, and P. A. Robert, “Brillouin gain spectrum characterization in single-mode optical fibers,” J. Lc cightwave Technol. 15, 1842–1851 (1997). [CrossRef]

]. Brillouin gain spectrum is, however, influenced by the geometric structures of optical fibers as well as material compositions. Among geometrical parameters, the core radius of an optical fiber would be one of the highest interests because the core will determine overall wave-guiding properties as well as Brillouin responses [6

6. K. Shiraki, M. Ohashi, and M. Tateda, “Suppression of stimulated Brillouin scattering in a fiber by changing the core radius,” Electron. Lett. 31, 668–669 (1995). [CrossRef]

]. SBS is induced by parametric interaction among pump, Stokes, and acoustic waves in optical fibers [7

7. G. P. Agrawal, Nonlinear Fiber Optics (Academic Press, 1950), Chap. 9.

]. Acoustic waves in cylindrical optical fibers could be guided in definitive modes such as longitudinal, torsional, and flexural modes [8

8. P. J. Thomas, N. L. Rowell, H. M. van Driel, and G. I. Stegeman, “Normal acoustic modes and Brillouin scattering in single-mode optical fibers,” Phys. Rev. B. 19, 4986–4998 (1979). [CrossRef]

,9

9. B. A. Auld, Acoustic Fields and Waves in Solids (John Wiley-Sons, 1973).

]. Among them, the lowest longitudinal acoustic mode, L 01-mode, dominantly interacts with the input optical pump wave and gives rise to backscattered Stokes signal, which is down-shifted by the Brillouin frequency [6

6. K. Shiraki, M. Ohashi, and M. Tateda, “Suppression of stimulated Brillouin scattering in a fiber by changing the core radius,” Electron. Lett. 31, 668–669 (1995). [CrossRef]

]. Safaai-Jazi et al. analyzed the acoustic modes in optical fibers with a GeO2-doped core and pure silica cladding [10

10. A. Safaai-Jazi and R. O. Claus, “Acoustic modes in optical fiberlike waveguides,” IEEE Trans. Ultrason., Ferroelec., Freq. Contr. 35, 619–627 (1988). [CrossRef]

], where the relations between the core and cladding properties were assumed as; V L_CO < V L_CL , V S_COV S_CL, and ρCOρCL, where V L_CO ,V L_CL , V S_CO, V S_CL , ρCO and ρCL are the longitudinal velocities, the shear velocities, and densities of the core and the cladding, respectively. In the simple core and infinite cladding structure, the Brillouin frequency shift was found to monotonically decrease as a function of the core radius [6

6. K. Shiraki, M. Ohashi, and M. Tateda, “Suppression of stimulated Brillouin scattering in a fiber by changing the core radius,” Electron. Lett. 31, 668–669 (1995). [CrossRef]

], which has imposed significant restriction in optical fiber structures for SBS applications. The ability to control the Brillouin frequency shift (νB) could generate novel features in current SBS applications, especially in dense wavelength division multiplexing (DWDM) devices where precise spectral control is emphasized.

In this letter, we report, for the first time to the best knowledge of the authors, the influence of inner cladding layer of an optical fiber on the acoustic waves and the Brillouin frequency shift, νB , providing analytic understanding of non-trivial behavior of νB for various fiber parameters. The analytic relationship will endow a new degree of freedom to design novel fiber SBS devices.

Fig. 1. The schematics of refractive index profile of the optical fiber with the matched inner cladding. a , b , and c are the radii of core, inner cladding, and outer cladding, respectively.

Structure of the fiber used in the analysis is schematically shown in Fig. 1. The fiber has three layers; the core is doped with GeO2 while the inner cladding is co-doped with P2O5 and F to lower processing temperature and to match the refractive index to that of pure silica glass in the outer cladding. When the fiber is drawn at a sufficiently low speed, the density of each layer in optical fiber is dominantly affected by the thermal stress, which results from the differences in thermal expansion coefficients in the layers [11

11. Y. Park, K. Oh, U. C. Paek, D. Y. Kim, and C. R. Kurkjian, “Residual stresses in a doubly clad fiber with depressed inner cladding (DIC),” J. Lightwave Technol. 17, 1823–1833 (1999). [CrossRef]

]. The calculated thermal stress profile is shown in Fig. 2 and the corresponding density distribution is shown in Fig. 3. The thermal stress and density were calculated for the optical fiber of which the concentrations of each layer were 3.36-mol% GeO2-doped core, 2.12-mol% P2O5- and 1-mol% F-codoped inner cladding, and pure silica outer cladding. The relation between the stress and density is described in Ref. 12

12. S. P. Timoshenko and J. N. Goodier, Theory of Elasticity (McGraw Hill, 1970).

.

Fig. 2. The calculated thermal stress profile of optical fiber. σr , σθ , and σz are the radial, circumferential, and axial thermal stress, respectively. Core radius a =3 μm, outer radius of inner cladding b =6.32 μm, and outer radius of outer cladding c =62.5μm [11].
Fig. 3. Corresponding density distribution. The density in the absence of volumetric stress is 2,220kg/m3 [14].

The acoustic velocity, then, can be estimated from Eq. (1) [12

12. S. P. Timoshenko and J. N. Goodier, Theory of Elasticity (McGraw Hill, 1970).

].

VA=E(1ν)/(1+ν)(12ν)ρ
(1)

where VA is the acoustic velocity, ρ is the density, ν and E are the Poisson’s ratio and the Young’s modulus, respectively. In the range of dopant concentration in this study, ν and E are found to be nearly the same as that of pure silica. Therefore, the density of each layer plays a dominant role to alter the acoustic response such as value of VA . In double cladding fiber structure, the acoustic mode analysis, initially proposed by Safaai-Jazi et al. [10

10. A. Safaai-Jazi and R. O. Claus, “Acoustic modes in optical fiberlike waveguides,” IEEE Trans. Ultrason., Ferroelec., Freq. Contr. 35, 619–627 (1988). [CrossRef]

], has to include the inner cladding boundary as below;

Φ(0)={AnJn(u1r),forr<aBnJn(u2r)+CnYn(u2r),fora<r<bDnKn(w3r),forr>b
(2)

where Φ(0) is the zero-order solution of acoustic scalar wave equation, n is an integer, a and b denote the radii of core and inner cladding, respectively. Here indices 1, 2, and 3 denote the core, the inner cladding, and the outer cladding, respectively. u 1, u 2 and w 3 are expressed as,

ui=2πf[(1VLi)2(1V)2]1/2,i=1,2
(3)
w3=2πf[(1V)2(1VL3)2]1/2
(4)

where VLi ’s are the longitudinal velocities at individual layers. f is the acoustic frequency, that is, Brillouin frequency shift, νB . V is the phase velocity of the longitudinal acoustic mode given by [13

13. D. Cotter, “Stimulated Brillouin scattering in monomode optical fiber,” J. Opt. Commun.4, 10–19 (1983).

],

V=λ2n1f
(5)

where n 1 is the refractive index of core, and λ is the optical wavelength. For acoustic L 01 modes, νB can be obtained by solving the characteristic equation for the L 01 mode obtained from the continuity of Φ0 and ∂Φ(0) /∂r at the boundaries [10

10. A. Safaai-Jazi and R. O. Claus, “Acoustic modes in optical fiberlike waveguides,” IEEE Trans. Ultrason., Ferroelec., Freq. Contr. 35, 619–627 (1988). [CrossRef]

].

{u2J1(u2a)u1J0(u2a)}{w3J0(u1a)Y0(u2b)K1(w3b)u2J1(u1a)Y1(u2b)K0(w3b)}
{u2Y1(u2a)u1Y0(u2a)}{w3J0(u1a)J0(u2b)K1(w3b)u2J1(u1a)J1(u2b)K0(w0b)}=0
(6)

The behavior of νB is analyzed for various acoustic velocities at the inner cladding, and the results are shown Fig. 5. Here the inner cladding radius was 6.32μm, and the acoustic velocities of the core and the outer cladding were 5,691m/s and 5,759m/s, respectively. The slope in the νB increases for a higher inner cladding acoustic velocity and the sensitivity of νB with respect to the core radius change gets significantly higher.

Fig. 4. The effect of inner cladding radius, b , on Brillouin frequency shift: An optical fiber is assumed to be composed of GeO2-doped core, P2O5- and F-doped inner cladding, and pure silica outer cladding where acoustic frequencies are given by V L1 =5,691, V L2 =5,677, and V L3 =5,759m/s. Note that the acoustic velocity at the inner cladding is lower than that at the core.

In order to verify these numerical results, three types of optical fibers with the refractive index matched inner cladding were fabricated to experimentally measure the Brillouin frequency shift. All parameters of optical fibers were same except for the core radius. The core was doped with GeO2 and the inner cladding was co-doped with P2O5 and F. The inner cladding radius was 6.35 μm and the relative refractive index difference, ∆ , was 0.35%. The core radii of fabricated fibers were 4 μm, 4.7 μm, and 5.2 μm.

Fig. 5. The effect of acoustic velocity in inner cladding, V L2 , on the Brillouin frequency shift: Here we have assumed the inner cladding radius, b =6.32μm, the core acoustic velocity V L1 =5,691m/s, and outer cladding acoustic velocity V L3 =5,759m/s.

It is known that a slight strain as small as 0.0001 results in the Brillouin frequency shift change as much as 5.941MHz. Furthermore, temperature change of 1 degree induces a Brillouin frequency shift change of about 1.36MHz in a 250- μm acrylate microjacketed fiber [5

5. M. Nikles, L. Thevenaz, and P. A. Robert, “Brillouin gain spectrum characterization in single-mode optical fibers,” J. Lc cightwave Technol. 15, 1842–1851 (1997). [CrossRef]

]. In order to minimize the Brillouin frequency shift change due to applied strain and temperature, all fibers were drawn at the same conditions, such as 21 m/min low drawing speed for mechanical strain-free optical fibers. The Brillouin frequency shifts of all fibers were measured at the same room temperature of 25°C. Therefore, Brillouin frequency shift change due to strain and temperature could be neglected because uniform strain and temperature were applied to all fibers.

To measure the Brillouin frequency shift of the fabricated optical fibers, a pump and probe technique was used [5

5. M. Nikles, L. Thevenaz, and P. A. Robert, “Brillouin gain spectrum characterization in single-mode optical fibers,” J. Lc cightwave Technol. 15, 1842–1851 (1997). [CrossRef]

]. The Brillouin gain spectra (BGS) of test fibers were obtained at the wavelength of 1.55μm. The resolution of the measurement was 100kHz.

Fig. 6. Measured Brillouin frequency shifts for three different core radii. Theoretical curve assumes the estimation of the inner cladding of b =6.35μm, the core acoustic velocity of V L1 =5,694m/s, the inner cladding acoustic velocity V L2 =5,676m/s and the outer cladding velocity V L3 =5,759m/s.

Brillouin spectra of the test fibers are shown in Fig. 7. Measured BGS data were fitted with Gaussian function. Due to time-variant Rayleigh scattering from unmodulated probe signal, absolute magnitude of the Brillouin gain was not measurable and the intensity of the Stokes wave was normalized to the maximum. The Brillouin bandwidths (∆νB) were found to increase from 20.62, to 22.25, and 23.44MHz for the increasing core radii of 4.05, 4.70, and 5.18μm.

Fig. 7. The Brillouin gain spectra of test fibers. The Brillouin frequency shift (νB) and Brillouin bandwidth (∆νB) are 10.7149GHz and 20.6164MHz for 4.053μm core radius, respectively. νB =10.7168GHz, ∆νB =22.2530MHz for 4.701mm core radius and νB =10.7194GHz, ∆νB =23.4422MHz for 5.182mm core radius.

In conclusion, we analytically investigated the effect of the inner cladding on Brillouin frequency shift. Thermal stress across the double cladding structure optical fiber induced local distribution of longitudinal acoustic waves and densities, which in turn affected the behavior of Brillouin frequency shift. It was both theoretically and experimentally shown that the Brillouin frequency shift could be fine-tuned by the inner cladding adding a new degree of freedom to design SBS optical fiber devices. Brillouin gain bandwidths were also found to be affected by the fiber structures and further analysis is being undertaken by the authors.

Acknowledgments

This work was supported in part by the KOSEF through the Ultra-Fast Fiber-Optic Networks Research Center, the Korean Ministry of Education through the BK21 Program, and ITRC-CHOAN program.

References and links

1.

S. J. Strutz and K. J. Williams, “Low-noise hybrid erbium/Brillouin amplifier,” Electron. Lett. 36, 1359–1360 (2000). [CrossRef]

2.

G. J. Cowle, D. Y. Stepanov, and Y. T. Chieng, “Brillouin/Erbium Fiber Lasers,” J. Lightwave Technol. 15, 1198–1204 (1997) [CrossRef]

3.

B. Min, P. Kim, and N. Park, “Flat amplitude equal spacing 798-channel Rayleigh-assited Brillouin/Raman multiwavelength comb generation in dispersion compensation fiber,” IEEE Photon. Technol. Lett. 13, 1352–1354 (2001). [CrossRef]

4.

H. H. Kee, G. P. Lees, and T. P. Newson, “All-fiber system for simultaneous interrogation of distributed strain and temperature sensing by spontaneous Brillouin scattering,” Opt. Lett. 25, 1–3 (2000). [CrossRef]

5.

M. Nikles, L. Thevenaz, and P. A. Robert, “Brillouin gain spectrum characterization in single-mode optical fibers,” J. Lc cightwave Technol. 15, 1842–1851 (1997). [CrossRef]

6.

K. Shiraki, M. Ohashi, and M. Tateda, “Suppression of stimulated Brillouin scattering in a fiber by changing the core radius,” Electron. Lett. 31, 668–669 (1995). [CrossRef]

7.

G. P. Agrawal, Nonlinear Fiber Optics (Academic Press, 1950), Chap. 9.

8.

P. J. Thomas, N. L. Rowell, H. M. van Driel, and G. I. Stegeman, “Normal acoustic modes and Brillouin scattering in single-mode optical fibers,” Phys. Rev. B. 19, 4986–4998 (1979). [CrossRef]

9.

B. A. Auld, Acoustic Fields and Waves in Solids (John Wiley-Sons, 1973).

10.

A. Safaai-Jazi and R. O. Claus, “Acoustic modes in optical fiberlike waveguides,” IEEE Trans. Ultrason., Ferroelec., Freq. Contr. 35, 619–627 (1988). [CrossRef]

11.

Y. Park, K. Oh, U. C. Paek, D. Y. Kim, and C. R. Kurkjian, “Residual stresses in a doubly clad fiber with depressed inner cladding (DIC),” J. Lightwave Technol. 17, 1823–1833 (1999). [CrossRef]

12.

S. P. Timoshenko and J. N. Goodier, Theory of Elasticity (McGraw Hill, 1970).

13.

D. Cotter, “Stimulated Brillouin scattering in monomode optical fiber,” J. Opt. Commun.4, 10–19 (1983).

14.

G. W. McLellan and E. B. Shand, Glass Engineering Handbook (McGraw Hill, 1984).

OCIS Codes
(190.4370) Nonlinear optics : Nonlinear optics, fibers
(290.5900) Scattering : Scattering, stimulated Brillouin

ToC Category:
Research Papers

History
Original Manuscript: August 13, 2002
Revised Manuscript: September 9, 2002
Published: September 23, 2002

Citation
J. Yu, Y. Park, Kyunghwan Oh, and I. Kwon, "Brillouin frequency shifts in silica optical fiber with the double cladding structure," Opt. Express 10, 996-1002 (2002)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-10-19-996


Sort:  Journal  |  Reset  

References

  1. S. J. Strutz, and K. J. Williams, �??Low-noise hybrid erbium/Brillouin amplifier,�?? Electron. Lett. 36, 1359-1360 (2000). [CrossRef]
  2. G. J. Cowle, D. Y. Stepanov, and Y. T. Chieng, �??Brillouin/Erbium Fiber Lasers,�?? J. Lightwave Technol. 15, 1198-1204 (1997). [CrossRef]
  3. B. Min, P. Kim, and N. Park, �??Flat amplitude equal spacing 798-channel Rayleigh-assited Brillouin/Raman multiwavelength comb generation in dispersion compensation fiber,�?? IEEE Photon. Technol. Lett. 13, 1352-1354 (2001). [CrossRef]
  4. H. H. Kee, G. P. Lees, and T. P. Newson, �??All-fiber system for simultaneous interrogation of distributed strain and temperature sensing by spontaneous Brillouin scattering,�?? Opt. Lett. 25, 1-3 (2000). [CrossRef]
  5. M. Nikles, L. Thevenaz, and P. A. Robert, �??Brillouin gain spectrum characterization in single-mode optical fibers,�?? J. Lightwave Technol. 15, 1842-1851 (1997). [CrossRef]
  6. K. Shiraki, M. Ohashi, and M. Tateda, �??Suppression of stimulated Brillouin scattering in a fiber by changing the core radius,�?? Electron. Lett. 31, 668-669 (1995). [CrossRef]
  7. G. P. Agrawal, Nonlinear Fiber Optics (Academic Press, 1950), Chap. 9.
  8. P. J. Thomas, N. L. Rowell, H. M. van Driel, and G. I. Stegeman, �??Normal acoustic modes and Brillouin scattering in single-mode optical fibers,�?? Phys. Rev. B 19, 4986-4998 (1979). [CrossRef]
  9. B. A. Auld, Acoustic Fields and Waves in Solids (John Wiley-Sons, 1973).
  10. A. Safaai-Jazi, and R. O. Claus, �??Acoustic modes in optical fiberlike waveguides,�?? IEEE Trans. Ultrason., Ferroelec., Freq. Contr. 35, 619-627 (1988). [CrossRef]
  11. Y. Park, K. Oh, U. C. Paek, D. Y. Kim, and C. R. Kurkjian, �??Residual stresses in a doubly clad fiber with depressed inner cladding (DIC),�?? J. Lightwave Technol. 17, 1823-1833 (1999). [CrossRef]
  12. S. P. Timoshenko, and J. N. Goodier, Theory of Elasticity (McGraw Hill, 1970).
  13. D. Cotter, �??Stimulated Brillouin scattering in monomode optical fiber,�?? J. Opt. Commun. 4, 10-19 (1983).
  14. G. W. McLellan, and E. B. Shand, Glass Engineering Handbook (McGraw Hill, 1984).

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited