Fabrication of large diffractive optical elements in thick film on a concave lens surface

Yongjun Xie, Zhenwu Lu, and Fengyou Li  »View Author Affiliations


Optics Express, Vol. 11, Issue 9, pp. 992-995 (2003)
http://dx.doi.org/10.1364/OE.11.000992


View Full Text Article

Acrobat PDF (120 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

We demonstrate experimentally the technique of fabricating large diffractive optical elements (DOEs) in thick film on a concave lens surface (mirrors) with precise alignment by using the strategy of double exposure. We adopt the method of double exposure to overcome the difficulty of processing thick photoresist on a large curved substrate. A uniform thick film with arbitrary thickness on a concave lens can be obtained with this technique. We fabricate a large concentric circular grating with a 10-µm period on a concave lens surface in film with a thickness of 2.0 µm after development. It is believed that this technique can also be used to fabricate larger DOEs in thicker film on the concave or convex lens surface with precise alignment. There are other potential applications of this technique, such as fabrication of micro-optoelectromechanical systems (MOEMS) or microelectromechanical systems (MEMS) and fabrication of microlens arrays on a large concave lens surface or convex lens surface with precise alignment.

© 2003 Optical Society of America

1. Introduction

There are many applications for fabricating large computer-generated diffractive optical elements (DOEs) on curved surfaces such as convex and concave lenses (mirrors) for use in the measurement of convex secondary mirrors [1

1. J. H. Burge, D. S. Anderson, T. D. Milster, and C. L. Vernold, “Measurement of a convex secondary mirror using a holographic test plat,” in Advanced Technology Optical Telescopes V, L. M. Stepp, ed., Proc. SPIE2199, 193–198 (1994). [CrossRef]

] and ultraviolet spectroscopic instruments [2

2. T. Harada, S. Moriyama, and T. Kita, “Mechanically ruled stigmatic concave gratings,” Jpn. J. Appl. Phys. 14, 175–179 (1974).

]. At present, approaches to the fabrication of DOEs with continuous surface relief include diamond milling, soft lithography, and direct writing [2

2. T. Harada, S. Moriyama, and T. Kita, “Mechanically ruled stigmatic concave gratings,” Jpn. J. Appl. Phys. 14, 175–179 (1974).

5

5. C. L. Vernold and T. D. Milster, “Non-photolithographic fabrication of large computer-generated diffractive optical elements,” in Current Developments in Optical Design and Optical Engineering IV, R. E. Fischer and W. J. Smith, eds., Proc. SPIE2263, 125–133 (1994). [CrossRef]

]. Limited resolution restricts applications of diamond milling to relatively smooth, slowly varying relief structures [3

3. M. T. Gale, M. Rossi, J. Pedersen, and H. Schutz, “Fabrication of continuous-relief micro-optical elements by direct laser writing in photoresists,” Opt. Eng. 33, 3556–3566 (1994). [CrossRef]

].

Digitization of the desired surface figure, or binary optics as it has been called, would not work well for the fabrication of DOEs on a curved surface because it is generated by integrated-circuit microfabrication technology. Soft lithography technology would not work well when the pattern needs precise alignment with a curved substrate. Direct writing by a focused laser beam, in which accurate control of the process parameters enables a complex continuous-relief microstructure to be fabricated in a single-exposure scan and development step, has significant advantages (writing area and scanning speed) over the electron-beam direct-writing technology for the fabrication of large DOEs on a curved surface with precise alignment. To overcome the difficulty of processing photoresist on a large curved substrate, one can use the nonlithography technique that was developed at the University of Arizona Optical Sciences Center [5

5. C. L. Vernold and T. D. Milster, “Non-photolithographic fabrication of large computer-generated diffractive optical elements,” in Current Developments in Optical Design and Optical Engineering IV, R. E. Fischer and W. J. Smith, eds., Proc. SPIE2263, 125–133 (1994). [CrossRef]

]. The technique involves thermally selective oxidization to transfer a large DOE pattern onto a metallic film on a curved substrate. However, the linear profile produced with this nonlithography technique is of inferior quality in comparison with that produced by use of lithography.

Recently, Xie et al. have experimentally demonstrated the lithography technique for fabricating a large computer-generated DOE pattern on a concave lens surface with precise alignment by using a laser direct writer [6

6. Y. Xie, Z. Lu, F. Li, J. Zhao, and Z. Weng, “Lithographic fabrication of large diffractive optical elements on a concave lens surface,” Opt. Express 10, 1043–1047 (2002), http://www.opticsexpress.org/abstract.cfm?URI=OPEX-10-20-1043. [CrossRef] [PubMed]

]. In this paper, we extend lithographic fabrication of large DOEs on the concave lens surface to the photoresist film with arbitrary thickness from the thin film. It will be possible to fabricate DOEs with continuous surface relief by this extension. [3

3. M. T. Gale, M. Rossi, J. Pedersen, and H. Schutz, “Fabrication of continuous-relief micro-optical elements by direct laser writing in photoresists,” Opt. Eng. 33, 3556–3566 (1994). [CrossRef]

] To our knowledge this is the first time that a laser direct writer has been used to transfer with precise alignment a large DOE pattern onto a concave lens surface in thick photoresist film by means of lithography.

2. Fabrication and characterization

Fabrication begins with spin coating a photoresist onto the concave substrate surface. The substrate is 110 mm in diameter and has a radius of curvature of 504 mm. We can learn by experiment that the thickness of the photoresist in the radial direction will increase significantly by spin coating with thick film. There may be other approaches to coating uniform thick film on the lens surface. However, the surface quality of the photoresist film may be not suitable for the laser direct writer. There is also the additional investment.

In our experiment we adopt the method of double exposure to overcome the difficulty of processing thick photoresist film on a large curved substrate. The preexposure setup is shown in Fig. 1. An object lens is used to obtain the focused laser beam from the laser. A special spherical diaphragm with a designed pattern is introduced in the setup to modulate the exposure area on the photoresist film. In this exposure process the substrate needs to be rotated at constant angular velocity.

Fig. 1. Schematic of the setup for preexposure.

For our experiment we used the Shipley S1813 Microposit photoresist, which we diluted with Shipley Type P Microposit thinner in a volume ratio of 1:0.5 ml (photoresist:thinner). The photoresist was dispensed in liquid form onto a concave substrate with a 504-mm radius of curvature. The spin rate was controlled to reach 1000 rpm within 15 s. A thick substrate was obtained after it was subjected to a spin rate of 1000 rpm for 30 s. The photoresist film was approximately 2.3 µm thick. Before the first exposure, we prebaked the sample in a 90°C oven for 30 min to remove the excess solvent and to improve the adhesion of film to substrate. Then the substrate was exposed by the setup shown in Fig. 1. After the first exposure, we developed the substrate in the Microposit developer for 20 s and then baked the sample in a 90°C oven for 15 min to remove the excess solvent and to again improve the adhesion of film to substrate. The thickness of the photoresist will be in the range of 100 nm in the radial direction after the first exposure process. It should be noted that these operations should be performed in a clean room.

Fig. 2. Schematic of our laser direct writer.

A schematic diagram of our laser direct-writing system is shown in Fig. 2. It should be noted that we used a 150-mW He-Cd laser at a wavelength of 442 nm. Stage (or focal spot) movement was controlled to a precision of 0.1 µm in three Cartesian axes by use of feedback from distance measurements with linear encoders from Heidenhain GmbH. The concave substrate coated by photoresist film is aligned with the air-bearing spindle by means of a high-precision alignment apparatus. [7

7. Z. Lu and Z. Weng, “Lens centering by using binary phase grating,” in Current Developments in Lens Design and Optical Systems Engineering, R. E. Fischer, R. B. Johnson, W. J. Smith, and W. H. Swantner, eds., Proc. SPIE.4093, 176–180 (2000). [CrossRef]

] We aligned the axis of the optical head assembly with the air-bearing spindle’s center of rotation by means of spinning a diffraction grating [8

8. T. D. Milster and C. L. Vernold, “Technique for aligning optical and mechanical axes based on a rotating linear grating,” Opt. Eng. 34, 2840–2844 (1995). [CrossRef]

].

Fig. 3. Three-dimensional plot of the grating profile.

Using an atomic-force microscope, we evaluated the linear profiles of the grating with a 10-µm period produced by this technique. The film thickness is ~2.0 µm after development, and the thickness variation in the radial coordinate direction is ~0.093 µm.

3. Conclusions

We have fabricated a concentric circular grating in photoresist film with thickness of 2.0 µm on a concave lens surface with precise alignment by using the strategy of double exposure. It is believed that this technique can also be used to fabricate larger DOEs in thicker film on a concave or convex lens surface (mirrors) with precise alignment. For our laser direct-writing system, the DOEs can be fabricated at a maximum diameter of ϕ400 mm and at a maximum area of 200 mm×200 mm. It should be possible to fabricate DOEs with continuous surface relief by use of this technique, and there are other potential applications, such as fabrication of MOEMS or MEMS on a large concave lens surface and fabrication of microlens arrays on a large concave lens surface.

Acknowledgments

This study is supported in part by the National Natural Science Foundation (60078006), the innovation fund of the Chinese Academy of Science (2002LQ4), and the State Key Laboratory of Applied Optics of the Chinese Academy of Science.

References and links

1.

J. H. Burge, D. S. Anderson, T. D. Milster, and C. L. Vernold, “Measurement of a convex secondary mirror using a holographic test plat,” in Advanced Technology Optical Telescopes V, L. M. Stepp, ed., Proc. SPIE2199, 193–198 (1994). [CrossRef]

2.

T. Harada, S. Moriyama, and T. Kita, “Mechanically ruled stigmatic concave gratings,” Jpn. J. Appl. Phys. 14, 175–179 (1974).

3.

M. T. Gale, M. Rossi, J. Pedersen, and H. Schutz, “Fabrication of continuous-relief micro-optical elements by direct laser writing in photoresists,” Opt. Eng. 33, 3556–3566 (1994). [CrossRef]

4.

R. J. Jackman, S. T. Brittain, A. Adams, M. G. Prentiss, and G. M. Whitesides, “Design and fabrication of topologically complex, three-dimensional microstructures,” Science 280, 2091–2098 (1998). [CrossRef]

5.

C. L. Vernold and T. D. Milster, “Non-photolithographic fabrication of large computer-generated diffractive optical elements,” in Current Developments in Optical Design and Optical Engineering IV, R. E. Fischer and W. J. Smith, eds., Proc. SPIE2263, 125–133 (1994). [CrossRef]

6.

Y. Xie, Z. Lu, F. Li, J. Zhao, and Z. Weng, “Lithographic fabrication of large diffractive optical elements on a concave lens surface,” Opt. Express 10, 1043–1047 (2002), http://www.opticsexpress.org/abstract.cfm?URI=OPEX-10-20-1043. [CrossRef] [PubMed]

7.

Z. Lu and Z. Weng, “Lens centering by using binary phase grating,” in Current Developments in Lens Design and Optical Systems Engineering, R. E. Fischer, R. B. Johnson, W. J. Smith, and W. H. Swantner, eds., Proc. SPIE.4093, 176–180 (2000). [CrossRef]

8.

T. D. Milster and C. L. Vernold, “Technique for aligning optical and mechanical axes based on a rotating linear grating,” Opt. Eng. 34, 2840–2844 (1995). [CrossRef]

OCIS Codes
(050.1970) Diffraction and gratings : Diffractive optics
(220.3740) Optical design and fabrication : Lithography

ToC Category:
Research Papers

History
Original Manuscript: March 6, 2003
Revised Manuscript: April 14, 2003
Published: May 5, 2003

Citation
Yongjun Xie, Zhenwu Lu, and Fengyou Li, "Fabrication of large diffractive optical elements in thick film on a concave lens surface," Opt. Express 11, 992-995 (2003)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-11-9-992


Sort:  Journal  |  Reset  

References

  1. J. H. Burge, D. S. Anderson, T. D. Milster, and C. L. Vernold, �??Measurement of a convex secondary mirrorusing a holographic test plat,�?? in Advanced Technology Optical Telescopes V, L. M. Stepp, ed., Proc. SPIE 2199, 193-198 (1994). [CrossRef]
  2. T. Harada, S. Moriyama, and T. Kita, �??Mechanically ruled stigmatic concave gratings,�?? Jpn. J. Appl. Phys. 14, 175-179 (1974)
  3. R. J. Jackman, S. T. Brittain, A. Adams, M. G. Prentiss, and G. M. Whitesides, �??Design and fabrication of topologically complex, three-dimensional microstructures,�?? Science 280, 2091-2098 (1998). [CrossRef]
  4. C. L. Vernold and T. D. Milster, �??Non-photolithographic fabrication of large computer-generated diffractive optical elements,�?? in Current Developments in Optical Design and Optical Engineering IV, R. E. Fischer and W. J. Smith, eds., Proc. SPIE 2263, 125-133 (1994). [CrossRef]
  5. Y. Xie, Z. Lu, F. Li, J. Zhao, and Z. Weng, �??Lithographic fabrication of large diffractive optical elements on a concave lens surface,�?? Opt. Express 10, 1043-1047 (2002), <a href="http://www.opticsexpress.org/abstract.cfm?URI=OPEX-10-20-1043">http://www.opticsexpress.org/abstract.cfm?URI=OPEX-10-20-1043</a> . [CrossRef] [PubMed]
  6. Z. Lu and Z. Weng, �??Lens centering by using binary phase grating,�?? in Current Developments in Lens Design and Optical Systems Engineering, R. E. Fischer, R. B. Johnson, W. J. Smith, and W. H. Swantner, eds., Proc. SPIE. 4093, 176-180 (2000). [CrossRef]
  7. T. D. Milster and C. L. Vernold, �??Technique for aligning optical and mechanical axes based on a rotating linear grating,�?? Opt. Eng. 34, 2840-2844 (1995). [CrossRef]
  8. M. T. Gale, M. Rossi, J. Pedersen, and H. Schutz, �??Fabrication of continuous-relief micro-optical elements by direct laser writing in photoresists,�?? Opt. Eng. 33, 3556-3566 (1994)

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.

Figures

Fig. 1. Fig. 2. Fig. 3.
 

« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited