Self Pumped Optical Phase Conjugation at 1.06 μm in Te-doped Sn2P2S6

Tobias Bach, Mojca Jazbinšek, Peter Günter, Alexander A. Grabar, Ivan M. Stoika, and Yulian M. Vysochanskii  »View Author Affiliations


Optics Express, Vol. 13, Issue 24, pp. 9890-9896 (2005)
http://dx.doi.org/10.1364/OPEX.13.009890


View Full Text Article

Acrobat PDF (235 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

We demonstrate self-pumped optical phase conjugation in Te-doped Sn2P2S6, a semiconducting ferroelectric crystal, using a 1.06 μm wavelength cw Nd:YAG laser. The photorefractive gain of this crystal has been increased to Γ = (3.9 ± 0.4)cm-1 by Te doping. We observed self-pumped optical phase conjugation in a ring cavity scheme with phase conjugate reflectivities of more than 40 percent and a very fast phase conjugate rise time below 100ms at a light intensity of 20 W/cm2. This is more than two orders of magnitude faster than in any other photorefractive crystal, as e.g. in Rh-doped BaTiO3.

© 2005 Optical Society of America

1. Introduction

For many years photorefractive materials have been investigated extensively because of their promise for various applications in photonics [1

1 . P. Günter and J.-P. Huignard , Photorefractive Materials and Their Applications I ( Springer-Verlag, Berlin , 1988 ). [CrossRef]

]. One of these applications is e.g. the spatial and spectral laser beam clean-up. Photorefractive materials with infrared response seem to be key elements for such applications using laser diodes. With photorefractive two-wave mixing it is possible to transfer energy from a high-power laser beam with a poor spatial profile to a diffraction limited beam with Gaussian shape [2

2 . A. E. Chiou and P. Yeh , “ Laser-beam cleanup using photorefractive two-wave mixing and optical phase conjugation ,” Opt. Lett. 11 , 461 – 463 ( 1986 ). [CrossRef] [PubMed]

, 3

3 . A. Brignon , J. P. Huignard , M. H. Garrett , and I. Mnushkina , “ Spatial beam cleanup of a Nd:YAG laser operating at 1.06 μ m with two-wave mixing in Rh:BaTiO 3 ,” Appl. Opt. 36 , 7788 – 7793 ( 1997 ). [CrossRef]

, 4

4 . L. Lombard , A. Brignon , J. P. Huignard , E. Lallier , G. Lucas-Leclin , P. Pauliat , and G. Roosen , “ Diffraction-limited polarized emission from a multimode ytterbium fiber amplifier after a nonlinear beam converter ,” Opt. Lett. 29 , 989 – 991 ( 2004 ). [CrossRef] [PubMed]

]. Placing a photorefractive crystal into the laser cavity [5

5 . G. Roosen , A. Godard , S. Maerten , V. Reboud , N. Dubreuil , and G. Pauliat , “ Self-organization of laser cavities using dynamic holograms ,” Opt. Mater. 23 , 289 – 293 ( 2003 ). [CrossRef]

] or into an external cavity of a laser system [6

6 . K. Tei , F. Matsuoka , M. Kato , Y. Maruyama , and T. Arisawa , “ Nd:YAG oscillator-amplifier system with a passive ring self-pumped phase-conjugate mirror ,” Opt. Lett. 25 , 481 – 483 ( 2000 ). [CrossRef]

] one can force the laser to oscillate in a single longitudinal mode. With optical phase conjugation it is possible to injection lock high-power broad-area laser diodes and laser diode arrays to obtain single mode output [7

7 . S. MacCormack and J. Feinberg , “ High-brightness output from a laser-diode array coupled to a phase-conjugating mirror ,” Opt. Lett. 18 , 211 – 213 ( 1993 ). [CrossRef] [PubMed]

]. In the last few years a remarkable effort was done to improve the photorefractive sensitivity of photorefractive materials in the near-infrared wavelength range due to widely available and powerful near-IR laser sources. One can distinguish two main groups of photorefractive inorganic materials. Semiconductors are relatively fast but have a small nonlinearity and require high external fields. From ferroelectrics oxides the most promising for near-infrared are Rh-doped KNbO3 [8

8 . M. Ewart , R. Ryf , C. Medrano , H. Wüest , M. Zgonik , and P. Günter , “ High photorefractive sensitivity at 860 nm in reduced rhodium-doped KNbO 3 ,” Opt. Lett. 22 , 781 – 783 ( 1997 ). [CrossRef] [PubMed]

] and Rh-doped BaTiO3 [9

9 . G. W. Ross , P. Hribek , R. W. Eason , M. H. Garrett , and D. Rytz , “ Impurity enhanced self-pumped phase conjugation in the near infrared in ‘blue’ BaTiO 3 ,” Opt. Commun. 101 , 60 – 64 ( 1993 ). [CrossRef]

]. Up to now the material of choice for near infrared photorefractive applications was Rh-doped BaTiO3 and it was implemented in most of the aforementioned beam cleanup schemes [3

3 . A. Brignon , J. P. Huignard , M. H. Garrett , and I. Mnushkina , “ Spatial beam cleanup of a Nd:YAG laser operating at 1.06 μ m with two-wave mixing in Rh:BaTiO 3 ,” Appl. Opt. 36 , 7788 – 7793 ( 1997 ). [CrossRef]

, 4

4 . L. Lombard , A. Brignon , J. P. Huignard , E. Lallier , G. Lucas-Leclin , P. Pauliat , and G. Roosen , “ Diffraction-limited polarized emission from a multimode ytterbium fiber amplifier after a nonlinear beam converter ,” Opt. Lett. 29 , 989 – 991 ( 2004 ). [CrossRef] [PubMed]

, 6

6 . K. Tei , F. Matsuoka , M. Kato , Y. Maruyama , and T. Arisawa , “ Nd:YAG oscillator-amplifier system with a passive ring self-pumped phase-conjugate mirror ,” Opt. Lett. 25 , 481 – 483 ( 2000 ). [CrossRef]

]. It shows a photorefractive response up to 1064nm with phase conjugate rise times in the order of 10 s at 5 W / cm2 [10

10 . N. Huot , J. M. C. Jonathan , and G. Roosen , “ Characterization and optimization of a ring self-pumped phase-conjugate mirror at 1.06 μ m with BaTiO 3 :Rh ,” J. Opt. Soc. Am. B 15 , 1992 – 1999 ( 1998 ). [CrossRef]

]. However, it often suffers of domain formation at this wavelength [11

11 . R. S. Cudney and M. Kaczmarek , “ Optical poling in Rh:BaTiO 3 ” in Trends in Optics and Photonics , Vol. 62 , pp. 485 – 489 ( 2001 ).

] and, in addition, has a phase transition at ~ 125°C and close to room temperature at ~ 9 °C [12

12 . M. B. Klein , “ Photorefractive Properties of BaTiO 3 ” in [1] pp. 195 – 236 .

], which most often leads to fatal damage of the crystal and its photorefractive characteristics. Therefore new infrared sensitive photorefractive materials are required for these applications [13

13 . G. Roosen , S. Bernhardt , and P. Delaye , “ Ba 0.77 Ca 0.23 TiO 3 : a new photorefractive material to replace BaTiO 3 in applications ,” Opt. Mater. 23 , 243 – 251 ( 2003 ). [CrossRef]

].

Tin hypothiodiphosphate (Sn2P2S6) is a photorefractive crystal with high gain coefficients and short response times in the red and near-infrared spectral range [14

14 . M. Jazbinšek , G. Montemezzani , P. Günter , A. A. Grabar , I. M. Stoika , and Y. M. Vysochanskii , “ Fast near-infrared self-pumped phase conjugation with photorefractive Sn 2 P 2 S 6 ,” J. Opt. Soc. Am. B 20 , 1241 – 1246 ( 2003 ). [CrossRef]

, 15

15 . M. Jazbinšek , D. Haertle , G. Montemezzani , P. Günter , A. A. Grabar , I. M. Stoika , and Y. M. Vysochanskii , “ Wave-length dependence of visible and near infrared photorefraction and phase conjugation in Sn 2 P 2 S 6 ,” J. Opt. Soc. Am. B 22 , 2459 – 2467 ( 2005 ). [CrossRef]

]. Photorefraction in Sn2P2S6 was first reported in the 1991, however the interest for Sn2P2S6 increased substantially when Odoulov et al. demonstrated photorefraction at 1.06 μm in 1996 [16

16 . S. G. Odoulov , A. N. Shumelyuk , U. Hellwig , R. A. Rupp , and A. A. Grabar , “ Photorefractive beam coupling in tin hypothiodiphosphate in the near infrared ,” Opt. Lett. 21 , 752 – 754 ( 1996 ). [CrossRef] [PubMed]

] using pure crystals with pre-illumination. Conventional nominally pure Sn2P2S6 crystals are grown by vapor-transport technique [17

17 . C. D. Carpentier and R. Nitsche , “ Vapor growth and crystal data of thio(seleno)hypodiphosphates Sn 2 P 2 S 6 , Sn 2 P 2 Se 6 , Pb 2 P 2 S 6 , Pb 2 P 2 Se 6 and their mixed crystals ,” Mat. Res. Bull. 9 , 401 – 410 ( 1974 ). [CrossRef]

], are of yellow color, and the photorefractive sensitivity substantially depends on pre-illumination. The grating formation shows a strong electron-hole competition leading to a decrease of the steady-state gain coefficients. By changing the growth parameters in the vapor-transport growth technique, modified brown Sn2P2S6 crystals were obtained [18

18 . A. A. Grabar , I. V. Kedyk , M. I. Gurzan , I. M. Stoika , A. A. Molnar , and Yu. M. Vysochanskii , “ Enhanced photore-fractive properties of modified Sn 2 P 2 S 6 ,” Opt. Commun. 188 , 187 – 194 ( 2001 ). [CrossRef]

]. These brown crystals are not sensitive to pre-illumination, have no pronounced electron-hole competition as well as they have a much higher two-wave mixing gain and faster response compared to yellow Sn2P2S6 [14

14 . M. Jazbinšek , G. Montemezzani , P. Günter , A. A. Grabar , I. M. Stoika , and Y. M. Vysochanskii , “ Fast near-infrared self-pumped phase conjugation with photorefractive Sn 2 P 2 S 6 ,” J. Opt. Soc. Am. B 20 , 1241 – 1246 ( 2003 ). [CrossRef]

, 18

18 . A. A. Grabar , I. V. Kedyk , M. I. Gurzan , I. M. Stoika , A. A. Molnar , and Yu. M. Vysochanskii , “ Enhanced photore-fractive properties of modified Sn 2 P 2 S 6 ,” Opt. Commun. 188 , 187 – 194 ( 2001 ). [CrossRef]

]. Brown crystals presumably contain more intrinsic (non-stoichiometric) defects, which are difficult to control in the vapor-transport growth, and up to now only small samples could be grown. Since for the self-pumped optical phase conjugation the theoretical threshold for the product of the two-wave mixing gain coefficient Γ and the length of the crystal L should exceed two [19

19 . M. Cronin-Golomb , B. Fischer , J. O. White , and A. Yariv , “ Theory and applications of four-wave mixing in photore-fractive media ,” IEEE J. Quantum Electron. QE-20 , 12 – 30 ( 1984 ). [CrossRef]

], self-pumped optical phase conjugation in brown Sn2P2S6 could only be demonstrated up to a wavelength of 980nm [15

15 . M. Jazbinšek , D. Haertle , G. Montemezzani , P. Günter , A. A. Grabar , I. M. Stoika , and Y. M. Vysochanskii , “ Wave-length dependence of visible and near infrared photorefraction and phase conjugation in Sn 2 P 2 S 6 ,” J. Opt. Soc. Am. B 22 , 2459 – 2467 ( 2005 ). [CrossRef]

].

In this paper we present phase conjugation with a new kind of Sn2P2S6 crystals obtained by doping the initial growth compound with Tellurium. Optical quality doped crystals with large dimensions and high gain coefficients could be grown. Using new Te-doped Sn2P2S6 crystals we demonstrate optical phase conjugation at the technologically important wavelength of 1.06 μm with rise times down to 85 ms.

2. Experiment

The Tellurium doped Sn2P2S6 crystal used in our experiment had the dimensions of x×y×z = 10mm × 6mm × 7.44mm along the main x, y, z axes defined as in Ref. [15

15 . M. Jazbinšek , D. Haertle , G. Montemezzani , P. Günter , A. A. Grabar , I. M. Stoika , and Y. M. Vysochanskii , “ Wave-length dependence of visible and near infrared photorefraction and phase conjugation in Sn 2 P 2 S 6 ,” J. Opt. Soc. Am. B 22 , 2459 – 2467 ( 2005 ). [CrossRef]

]. It was grown by the vapor transport growth technique [17

17 . C. D. Carpentier and R. Nitsche , “ Vapor growth and crystal data of thio(seleno)hypodiphosphates Sn 2 P 2 S 6 , Sn 2 P 2 Se 6 , Pb 2 P 2 S 6 , Pb 2 P 2 Se 6 and their mixed crystals ,” Mat. Res. Bull. 9 , 401 – 410 ( 1974 ). [CrossRef]

] with 1 % Tellurium in the initial compound. The crystal is of homogeneous light brown color. Compared to yellow Sn2P2S6 crystals the absorption edge in Te-doped crystals is shifted from λ ≈ 530nm to higher wavelengths up to λ ≈ 570nm [20

20 . A. A. Grabar , I. V. Kedyk , I. M. Stoika , Yu. M. Vysochanskii , M. Jazbinsek , G. Montemezzani , and P. Günter “ En-hanced photorefractive properties of Te-doped Sn 2 P 2 S 6 ,” in Trends in Optics and Photonics , Vol. 87 , pp. 10 – 14 ( 2003 ).

]. In all Sn2P2S6 crystals the absorption constant is rather low in the near infrared; in our Sn2P2S6:Te 1 % the absorption constant reaches α = 0.1cm-1 for the light polarized along the x-axis at 1.06 μm.

Fig. 1. Experimental setup for optical self-pumped phase conjugation in a ring cavity scheme using a Te-doped Sn2P2S6 crystal. Additional neutral density filters ND-I and ND-II were used to vary the input beam intensity and the transmission of the loop respectively. The transmission grating in the crystal is written by beam 3 with its self-diffracted beam 4 and by beams 1 and 2 counterpropagating in the loop.

The experimental setup for ring-cavity self-pumped phase conjugation is shown in Fig. 1. We used a cw Nd:YAG laser with a maximal output power of 400mW(Lightwave Electronics). The light beams were polarized in the plane of the ring-cavity loop and were almost parallel to the x-axis in the crystal and the external angle 2θ was adjusted to 30°. This configuration corresponds to the maximum two-wave mixing gain of the material [15

15 . M. Jazbinšek , D. Haertle , G. Montemezzani , P. Günter , A. A. Grabar , I. M. Stoika , and Y. M. Vysochanskii , “ Wave-length dependence of visible and near infrared photorefraction and phase conjugation in Sn 2 P 2 S 6 ,” J. Opt. Soc. Am. B 22 , 2459 – 2467 ( 2005 ). [CrossRef]

]. To reduce Fresnel losses the crystal was coated with a 190 nm thick Al2O3 layer, which gives the lowest reflectivity for an incidence angle β ~ 60° with respect to the sample normal and leads to a single reflection loss of approximately 6 %. An f = 1000-mm lens was placed into the path of the input beam to focus slightly the light into the crystal and decrease beam divergence. The beam had a Gaussian shape with a diameter of approximately 2 mm in the crystal. The used multi-layer dielectric mirrors are optimized for 1064nm and have a reflectivity of more than 99 %. To avoid parasitic reflection gratings one of the mirrors in the cavity was vibrated to ensure incoherency of the beams 1 and 3. The generated phase-conjugated signal is then a result of the coupling via the transmission grating formed by incident beam 3 and its self-diffracted beam 4 as well as by their feedback beams 1 and 2 [19

19 . M. Cronin-Golomb , B. Fischer , J. O. White , and A. Yariv , “ Theory and applications of four-wave mixing in photore-fractive media ,” IEEE J. Quantum Electron. QE-20 , 12 – 30 ( 1984 ). [CrossRef]

]. The intensity of the phase-conjugated wave 2 is observed by a photodiode placed behind a glass plate used as a beam splitter. The phase-conjugate reflectivity R is defined as the ratio between the measured intensity of the phase-conjugated wave 2 and the input wave 3. The phase conjugate rise time τ 0 is defined as τ 0 = τ 90% - τ 10%, where τ 90% and τ 10% are the times needed to reach 90% and 10% of the maximal reflectivity respectively.

3. Results

The temporal evolution of the phase conjugated beam after switching on the pump beam 3 is shown in Fig. 2. For an intensity of 20W/cm2 and the above presented configuration we obtained a maximal saturated phase conjugated reflectivity of 42 percent and a rise time of 85 ms. As seen in Fig. 2, after the phase conjugated beam reaches its saturated value it stays stable showing no self-oscillation effects as previously observed in yellow Sn2P2S crystals with a strong electron-hole competition [16

16 . S. G. Odoulov , A. N. Shumelyuk , U. Hellwig , R. A. Rupp , and A. A. Grabar , “ Photorefractive beam coupling in tin hypothiodiphosphate in the near infrared ,” Opt. Lett. 21 , 752 – 754 ( 1996 ). [CrossRef] [PubMed]

].

Fig. 2. Temporal evolution of the phase conjugated reflectivity R after switching on the pump beam 3 at t = 0. A different time scale between 0.3 s and 2 s is showing the stable phase conjugated reflection.

To investigate the transmission losses in the ring cavity different neutral density filters ND-II were introduced in the cavity (see Fig. 1). The measured steady-state phase conjugate reflectivity as a function of the loop transmission is shown in Fig. 3. The curves in Fig. 3 were calculated on the base of the four coupled-wave theory described in [19

19 . M. Cronin-Golomb , B. Fischer , J. O. White , and A. Yariv , “ Theory and applications of four-wave mixing in photore-fractive media ,” IEEE J. Quantum Electron. QE-20 , 12 – 30 ( 1984 ). [CrossRef]

] giving the solution in the form:

t02tanhκLs+σtanhκL=sI0tanhκL(σI0s2)tanhκL+(I0σ)s
(1)

where

s=[σ2+(I0σ)2ρ2]1/2,σ=I0t021t02+1,
(2)
κ=sΓ*4I0.
(3)

Here I 0 is the total incoming beam intensity, Γ the photorefractive gain coefficient, L the length of the crystal and |ρ|2 is the theoretical phase conjugate reflectivity. The parameter t 0 accounts for the changes in beam amplitudes and phases after being reflected by the mirrors in the cavity and transmitted through the crystal surface which is on the side of the cavity. As the loop transmission we define T = |t 0|2. The measured reflectivity is equal to R = |ρ|2|tL|4 where tL includes the changes in amplitudes and phases after being transmitted through the sample surface which is on the side of the input beam. By inserting Eqs. (2) and (3) into Eq. (1) one gets the transcendental equation for the theoretical reflectivity |ρ|2 which depends on the coupling strength ΓL and on the loop transmission T = |t 0|2.

Fig. 3. Measured saturated phase conjugate reflectivity R as a function of the loop transmission T. The curves represent calculations for ΓL = 2.9 (solid curve) being in best conformance with the measurement and for ΓL = 2.6 (dashed curve), ΓL = 3.2 (dotted curve) for comparison.

Following the procedure described in Ref. [14

14 . M. Jazbinšek , G. Montemezzani , P. Günter , A. A. Grabar , I. M. Stoika , and Y. M. Vysochanskii , “ Fast near-infrared self-pumped phase conjugation with photorefractive Sn 2 P 2 S 6 ,” J. Opt. Soc. Am. B 20 , 1241 – 1246 ( 2003 ). [CrossRef]

], we first estimated the parameter T|tL|4 by assuming that in first approximation the measured reflectivity is proportional to the transmission of the filter ND-II. From this we obtain T|tL|4 = (0.71±0.05). A direct estimation of T|tL|4 that accounts for absorption and reflection losses is (1 - R 1)3(1 - R 2)(1 - A)2. For the single reflection losses at the crystal surface for the angles 60 ° and 30° we get R 1 = 0.06 and R 2 = 0.1 respectively. A = 0.07 is the absorption loss of the Te-doped Sn2P2S6 crystal at 1064 nm. Therefore T|tL|4 ≈ 0.70, in good agreement with the experimental value. For the loop transmission we get T|tL|4/(1 - R 1)2 ≈ 0.71/(0.94)2 = 0.80. This value corresponds to the loop transmission without an additional ND-II filter in the ring cavity, as also taken into account when plotting our data in Fig. 3.

To obtain the coupling strength ΓL from the measurements we calculated the phase conjugated reflectivity as a function of the cavity transmission for different values of ΓL. As one can see in Fig. 3 the measured values agree best for a coupling strength of ΓL = (2.9±0.3), leading to a photorefractive gain of Γ = (3.9±0.4)cm-1.

Theoretical calculations for the reflectivity R as a function of the coupling strength ΓL for T|tL|4 = 0.71 (no neutral density filter) and T|tL|4 = 0.42 (with a 75% neutral density filter) are presented in Fig. 4. From these calculations one can see that the phase conjugate reflectivity could be increased to R ≈ 70 percent for a crystal thickness of L > 1.2cm.

The phase-conjugate reflectivity will depend also on the input beam intensity due to competing thermal effects (dark generation) and eventual background illumination. This can be modeled by introducing an uniform background intensity Iβ which will lead to a change of the parameter κ from (Eq. 3) as [14

14 . M. Jazbinšek , G. Montemezzani , P. Günter , A. A. Grabar , I. M. Stoika , and Y. M. Vysochanskii , “ Fast near-infrared self-pumped phase conjugation with photorefractive Sn 2 P 2 S 6 ,” J. Opt. Soc. Am. B 20 , 1241 – 1246 ( 2003 ). [CrossRef]

] :

κ=sΓ*4(I0+Iβ).
(4)
Fig. 4. Dependences of the reflectivity R as a function of the coupling strength ΓL for T|tL|4 = 0.71 (solid curve) and T|tL|4 = 0.42 (dashed curve). The corresponding highest experimental point of Fig. 3 and the point for a loop transmission of 0.6 are included.
Fig. 5. Saturated phase conjugate reflectivity R as a function of the input intensity. The theoretical curve was calculated with T|tL|4 = 0.71, ΓL = 2.9 and considered an effective background intensity of Iβ = 0.9 W/cm2.

To determine Iβ we were changing the intensity of the input beam by placing neutral density filters ND-I in the path and measure the phase conjugate reflectivity. The results are shown in Fig. 5. The theoretical intensity dependence with Iβ =0.9 W/cm2 and the previously obtained parameters T|tL|4 = 0.71 and ΓL = 2.9 is also shown in Fig. 5.

The response rate 1/τ 0 as a function of the incoming laser intensity I 0 is presented in Fig. 6 and shows a linear dependence as expected from the simplest one-center charge transport model. For the maximal intensity of I = 20 W/cm2 the response rate is 12 s-1 corresponding to a rise time of about 85 ms. Note that for an intensity of I = 5 W/cm2 the rise time is about 300 ms which is more than 30 times faster than reported before in Rh-doped BaTiO3 at the same wavelength and intensity [10

10 . N. Huot , J. M. C. Jonathan , and G. Roosen , “ Characterization and optimization of a ring self-pumped phase-conjugate mirror at 1.06 μ m with BaTiO 3 :Rh ,” J. Opt. Soc. Am. B 15 , 1992 – 1999 ( 1998 ). [CrossRef]

]. As seen in Fig. 6, the response rate in Sn2P2S6:Te is still expected to increase by increasing the intensity above I = 20W/cm2.

Fig. 6. Response rate 1/τ 0 versus the incident intensity with a linear curve that corresponds the measurements.

4. Conclusion

We have demonstrated low-power self-pumped phase conjugation in a ring cavity scheme at a wavelength of 1064nm using Sn2P2S6 crystals doped with Tellurium. Phase conjugate response times as low as τ = 85ms have been measured which is more than 100 times faster than any previously reported value, e.g. τ = 10s in Rh-doped BaTiO3, without forming any domains, as often seen in BaTiO3. The experimentally measured phase conjugated reflectivity is 42 percent for a 0.74cm thick crystal. Our estimation shows that the reflectivity can reach about 70 percent for a crystal with a thickness exceeding 1.2cm. Therefore, Te-doped Sn2P2S6 can be considered as one of the most promising material for photorefractive applications at near-infrared wavelengths.

Acknowledgments

This research has been supported by the Swiss National Science Foundation (NF 2-777416-04)

References and links

1 .

P. Günter and J.-P. Huignard , Photorefractive Materials and Their Applications I ( Springer-Verlag, Berlin , 1988 ). [CrossRef]

2 .

A. E. Chiou and P. Yeh , “ Laser-beam cleanup using photorefractive two-wave mixing and optical phase conjugation ,” Opt. Lett. 11 , 461 – 463 ( 1986 ). [CrossRef] [PubMed]

3 .

A. Brignon , J. P. Huignard , M. H. Garrett , and I. Mnushkina , “ Spatial beam cleanup of a Nd:YAG laser operating at 1.06 μ m with two-wave mixing in Rh:BaTiO 3 ,” Appl. Opt. 36 , 7788 – 7793 ( 1997 ). [CrossRef]

4 .

L. Lombard , A. Brignon , J. P. Huignard , E. Lallier , G. Lucas-Leclin , P. Pauliat , and G. Roosen , “ Diffraction-limited polarized emission from a multimode ytterbium fiber amplifier after a nonlinear beam converter ,” Opt. Lett. 29 , 989 – 991 ( 2004 ). [CrossRef] [PubMed]

5 .

G. Roosen , A. Godard , S. Maerten , V. Reboud , N. Dubreuil , and G. Pauliat , “ Self-organization of laser cavities using dynamic holograms ,” Opt. Mater. 23 , 289 – 293 ( 2003 ). [CrossRef]

6 .

K. Tei , F. Matsuoka , M. Kato , Y. Maruyama , and T. Arisawa , “ Nd:YAG oscillator-amplifier system with a passive ring self-pumped phase-conjugate mirror ,” Opt. Lett. 25 , 481 – 483 ( 2000 ). [CrossRef]

7 .

S. MacCormack and J. Feinberg , “ High-brightness output from a laser-diode array coupled to a phase-conjugating mirror ,” Opt. Lett. 18 , 211 – 213 ( 1993 ). [CrossRef] [PubMed]

8 .

M. Ewart , R. Ryf , C. Medrano , H. Wüest , M. Zgonik , and P. Günter , “ High photorefractive sensitivity at 860 nm in reduced rhodium-doped KNbO 3 ,” Opt. Lett. 22 , 781 – 783 ( 1997 ). [CrossRef] [PubMed]

9 .

G. W. Ross , P. Hribek , R. W. Eason , M. H. Garrett , and D. Rytz , “ Impurity enhanced self-pumped phase conjugation in the near infrared in ‘blue’ BaTiO 3 ,” Opt. Commun. 101 , 60 – 64 ( 1993 ). [CrossRef]

10 .

N. Huot , J. M. C. Jonathan , and G. Roosen , “ Characterization and optimization of a ring self-pumped phase-conjugate mirror at 1.06 μ m with BaTiO 3 :Rh ,” J. Opt. Soc. Am. B 15 , 1992 – 1999 ( 1998 ). [CrossRef]

11 .

R. S. Cudney and M. Kaczmarek , “ Optical poling in Rh:BaTiO 3 ” in Trends in Optics and Photonics , Vol. 62 , pp. 485 – 489 ( 2001 ).

12 .

M. B. Klein , “ Photorefractive Properties of BaTiO 3 ” in [1] pp. 195 – 236 .

13 .

G. Roosen , S. Bernhardt , and P. Delaye , “ Ba 0.77 Ca 0.23 TiO 3 : a new photorefractive material to replace BaTiO 3 in applications ,” Opt. Mater. 23 , 243 – 251 ( 2003 ). [CrossRef]

14 .

M. Jazbinšek , G. Montemezzani , P. Günter , A. A. Grabar , I. M. Stoika , and Y. M. Vysochanskii , “ Fast near-infrared self-pumped phase conjugation with photorefractive Sn 2 P 2 S 6 ,” J. Opt. Soc. Am. B 20 , 1241 – 1246 ( 2003 ). [CrossRef]

15 .

M. Jazbinšek , D. Haertle , G. Montemezzani , P. Günter , A. A. Grabar , I. M. Stoika , and Y. M. Vysochanskii , “ Wave-length dependence of visible and near infrared photorefraction and phase conjugation in Sn 2 P 2 S 6 ,” J. Opt. Soc. Am. B 22 , 2459 – 2467 ( 2005 ). [CrossRef]

16 .

S. G. Odoulov , A. N. Shumelyuk , U. Hellwig , R. A. Rupp , and A. A. Grabar , “ Photorefractive beam coupling in tin hypothiodiphosphate in the near infrared ,” Opt. Lett. 21 , 752 – 754 ( 1996 ). [CrossRef] [PubMed]

17 .

C. D. Carpentier and R. Nitsche , “ Vapor growth and crystal data of thio(seleno)hypodiphosphates Sn 2 P 2 S 6 , Sn 2 P 2 Se 6 , Pb 2 P 2 S 6 , Pb 2 P 2 Se 6 and their mixed crystals ,” Mat. Res. Bull. 9 , 401 – 410 ( 1974 ). [CrossRef]

18 .

A. A. Grabar , I. V. Kedyk , M. I. Gurzan , I. M. Stoika , A. A. Molnar , and Yu. M. Vysochanskii , “ Enhanced photore-fractive properties of modified Sn 2 P 2 S 6 ,” Opt. Commun. 188 , 187 – 194 ( 2001 ). [CrossRef]

19 .

M. Cronin-Golomb , B. Fischer , J. O. White , and A. Yariv , “ Theory and applications of four-wave mixing in photore-fractive media ,” IEEE J. Quantum Electron. QE-20 , 12 – 30 ( 1984 ). [CrossRef]

20 .

A. A. Grabar , I. V. Kedyk , I. M. Stoika , Yu. M. Vysochanskii , M. Jazbinsek , G. Montemezzani , and P. Günter “ En-hanced photorefractive properties of Te-doped Sn 2 P 2 S 6 ,” in Trends in Optics and Photonics , Vol. 87 , pp. 10 – 14 ( 2003 ).

OCIS Codes
(160.5320) Materials : Photorefractive materials
(190.5040) Nonlinear optics : Phase conjugation
(190.5330) Nonlinear optics : Photorefractive optics

ToC Category:
Research Papers

History
Original Manuscript: October 11, 2005
Revised Manuscript: October 11, 2005
Published: November 28, 2005

Citation
Tobias Bach, Mojca Jazbinšek, Peter Günter, Alexander Grabar, Ivan Stoika, and Yulian Vysochanskii, "Self Pumped Optical Phase Conjugation at 1.06 µm in Te-doped Sn2P2S6," Opt. Express 13, 9890-9896 (2005)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-13-24-9890


Sort:  Journal  |  Reset  

References

  1. P. Günter, J.-P. Huignard, Photorefractive Materials and Their Applications I (Springer-Verlag, Berlin, 1988). [CrossRef]
  2. A. E. Chiou, P. Yeh, ”Laser-beam cleanup using photorefractive two-wave mixing and optical phase conjugation,” Opt. Lett. 11, 461-463 (1986). [CrossRef] [PubMed]
  3. A. Brignon, J. P. Huignard, M. H. Garrett, I. Mnushkina, ”Spatial beam cleanup of a Nd:YAG laser operating at 1.06 µm with two-wave mixing in Rh:BaTiO3,” Appl. Opt. 36, 7788-7793 (1997). [CrossRef]
  4. L. Lombard, A. Brignon, J. P. Huignard, E. Lallier, G. Lucas-Leclin, P. Pauliat, G. Roosen, ”Diffraction-limited polarized emission from a multimode ytterbium fiber amplifier after a nonlinear beam converter,” Opt. Lett. 29, 989-991 (2004). [CrossRef] [PubMed]
  5. G. Roosen, A. Godard, S. Maerten, V. Reboud, N. Dubreuil, G. Pauliat, ”Self-organization of laser cavities using dynamic holograms,” Opt. Mater. 23, 289-293 (2003). [CrossRef]
  6. K. Tei, F. Matsuoka, M. Kato, Y. Maruyama, T. Arisawa, ”Nd:YAG oscillator-amplifier system with a passive ring self-pumped phase-conjugate mirror,” Opt. Lett. 25, 481-483 (2000). [CrossRef]
  7. S. MacCormack, J. Feinberg, ”High-brightness output from a laser-diode array coupled to a phase-conjugating mirror,” Opt. Lett. 18, 211-213 (1993). [CrossRef] [PubMed]
  8. M. Ewart, R. Ryf, C. Medrano, H. Wüest, M. Zgonik, P. Günter, ”High photorefractive sensitivity at 860 nm in reduced rhodium-doped KNbO3,” Opt. Lett. 22, 781-783 (1997). [CrossRef] [PubMed]
  9. G.W. Ross, P. Hribek, R. W. Eason, M. H. Garrett, D. Rytz, ”Impurity enhanced self-pumped phase conjugation in the near infrared in ’blue’ BaTiO3,” Opt. Commun. 101, 60-64 (1993). [CrossRef]
  10. N. Huot, J. M. C. Jonathan, G. Roosen, ”Characterization and optimization of a ring self-pumped phase-conjugate mirror at 1.06 µm with BaTiO3:Rh,” J. Opt. Soc. Am. B 15, 1992-1999 (1998). [CrossRef]
  11. R. S. Cudney, M. Kaczmarek, ”Optical poling in Rh:BaTiO3” in Trends in Optics and Photonics, Vol. 62, pp. 485-489 (2001).
  12. M. B. Klein, ”Photorefractive Properties of BaTiO3” in [1] pp.195-236.
  13. G. Roosen, S. Bernhardt, P. Delaye, ”Ba0.77Ca0.23TiO3: a new photorefractive material to replace BaTiO3 in applications,” Opt. Mater. 23, 243-251 (2003). [CrossRef]
  14. M. Jazbinšek, G. Montemezzani, P. Günter, A. A. Grabar, I. M. Stoika, Y. M. Vysochanskii, ”Fast near-infrared self-pumped phase conjugation with photorefractive Sn2P2S6,” J. Opt. Soc. Am. B 20, 1241-1246 (2003). [CrossRef]
  15. M. Jazbinšek, D. Haertle, G. Montemezzani, P. Günter, A. A. Grabar, I. M. Stoika, Y. M. Vysochanskii, ”Wavelength dependence of visible and near infrared photorefraction and phase conjugation in Sn2P2S6,” J. Opt. Soc. Am. B 22, 2459-2467 (2005). [CrossRef]
  16. S. G. Odoulov, A. N. Shumelyuk, U. Hellwig, R. A. Rupp, A. A. Grabar, ”Photorefractive beam coupling in tin hypothiodiphosphate in the near infrared,” Opt. Lett. 21, 752-754 (1996). [CrossRef] [PubMed]
  17. C. D. Carpentier, R. Nitsche, ”Vapor growth and crystal data of thio(seleno)hypodiphosphates Sn2P2S6, Sn2P2Se6, Pb2P2S6, Pb2P2Se6 and their mixed crystals,” Mat. Res. Bull. 9, 401-410 (1974). [CrossRef]
  18. A. A. Grabar, I. V. Kedyk, M. I. Gurzan, I. M. Stoika, A. A. Molnar, Yu. M. Vysochanskii, ”Enhanced photorefractive properties of modified Sn2P2S6,” Opt. Commun. 188, 187-194 (2001). [CrossRef]
  19. M. Cronin-Golomb, B. Fischer, J. O. White, A. Yariv, ”Theory and applications of four-wave mixing in photorefractive media,” IEEE J. Quantum Electron. QE-20, 12-30 (1984). [CrossRef]
  20. A. A. Grabar, I. V. Kedyk, I. M. Stoika, Yu. M. Vysochanskii, M. Jazbinsek, G. Montemezzani, P. Günter ”Enhanced photorefractive properties of Te-doped Sn2P2S6,” in Trends in Optics and Photonics, Vol. 87, pp. 10-14 (2003).

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited