Near infrared broadband emission of bismuth-doped aluminophosphate glass

Xian-geng Meng, Jian-rong Qiu, Ming-ying Peng, Dan-ping Chen, Quan-zhong Zhao, Xiong-wei Jiang, and Cong-shan Zhu  »View Author Affiliations


Optics Express, Vol. 13, Issue 5, pp. 1628-1634 (2005)
http://dx.doi.org/10.1364/OPEX.13.001628


View Full Text Article

Acrobat PDF (136 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

Near infrared broadband emission characteristics of bismuth-doped aluminophosphate glass have been investigated. Broad infrared emissions peaking at 1210nm, 1173nm and 1300nm were observed when the glass was pumped by 405nm laser diode (LD), 514nm Ar+ laser and 808nm LD, respectively. The full widths at half maximum (FWHMs) are 235nm, 207nm and 300nm for the emissions at 1210nm, 1173nm and 1300nm, respectively. Based on the energy matching conditions, it is suggested that the infrared emission may be ascribed to 3P13P0 transition of Bi+. The broadband infrared luminescent characteristics of the glasses indicate that they are promising for broadband optical fiber amplifiers and tunable lasers.

© 2005 Optical Society of America

1. Introduction

Recently, Fujimoto discovered a new infrared broadband emission from bismuth-doped silica glasses and realized 1.3µm optical amplification with 0.8µm excitation [3

3. Y. Fujimoto and M. Nakatsuka, “Infrared luminescence from bismuth-doped silica glass,” Jpn. J. App. Phys. 40, L279–L281 (2001) [CrossRef]

,4

4. Y. Fujimoto and M. Nakatsuka, “Optical amplification in bismuth-doped silica glass,” App. Phys. Lett. 82, 3325–3326 (2003) [CrossRef]

], which provided a promising candidate for 1.3µm broadband optical fiber amplifiers and tunable lasers. Subsequently, bismuth-doped germanate glasses have also been developed and investigated [5

5. M. Peng, J. Qiu, D. Chen, X. Meng, L. Yang, X. Jiang, and C. Zhu, “Bismuth- and aluminum co-doped germanium oxide glasses for super-broadband optical amplification,” Opt. Lett. 29, 1998–2000 (2004) [CrossRef] [PubMed]

].

It is well known that phosphate glasses are very attractive hosts for rare-earth ions, and have significant applications in optoelectronic fields. To the best of our knowledge, infrared emission of bismuth-doped aluminophosphate glasses hasn’t been investigated up to now. In this letter, we synthesized bismuth-doped aluminophosphate glasses and observed infrared broadband emission centered at 1300nm with FWHM of 300nm under 808nm LD excitation. The lifetime is as long as 500µs, comparable to those of other transition metal ions (e.g. Ni2+, Cr4+) [6

6. T. Sazuki and Y. Ohishi, “Broadband 1400nm emission from Ni2+ in zink-alumino-silicate glass,” Appl. Phys. Lett. 84, 3804–3806 (2004) [CrossRef]

,7

7. I. T. Sorokina, S. Naumov, E. Sorokin, E. Wintner, and A. V. Shestakov, “Directly diode-pumped tunable continuous-wave room-temperature Cr4+: YAG laser,” Opt. Lett. 24, 1578–1580 (1999) [CrossRef]

].

2. Experimental

A glass with the composition of 82P2O5-17Al2O3-1Bi2O3 (PAB) in molar percentage was prepared by a conventional melting method. Analytical pure reagents of NH4H2PO4, Al(OH)3 and Bi2O3 were used as raw materials. The batch was melt in a corundum crucible in air at 1550°C for 1h. The melts were poured onto a stainless steel plate. For comparison, a germanate glass with the composition of 96GeO2-3Al2O3-1Bi2O3 (GAB) was also prepared by melting the corresponding batch at 1550°C for 1h. The obtained glass samples were transparent and bubble-free and were polished to 10mm×10mm×1mm size before optical measurements. Optical absorption spectra of the samples were measured on JASCO V-570 spectrophotometer. The infrared luminescence spectra were obtained on ZOLIX SBP300 spectrophotometer with InGaAs as detector in 850–1800nm with excitation of a 405nm LD, 514nm Ar+ laser and 808nm LD. And the lifetime was obtained by exciting the sample with a modulated 808nm LD with a maximum power of 2W. The signals detected by an InGaAs photodetector were recorded by a storage digital oscilloscope (Tektronix TDS3052). All the measurements were taken at room temperature.

3. Results and discussion

Fig. 1. Transmission spectra of PAB and GAB glasses

Figure 2 shows the luminescence specta of PAB glass under various pumping sources. Infrared emissions peaking at 1210nm, 1173nm, 1300nm and 1194nm were observed when the glass sample was excited by 405nm LD, 514nm Ar+ laser, 808nm LD and 980nm LD, respectively. The corresponding FWHMs of 1210nm, 1173nm and 1300nm emissions are 235nm, 207nm and 300nm, respectively.

Fig. 2. Normalized emission spectra of PAB, when excited by 405nm LD, 514nm Ar+ laser, 808nm LD and 980nm LD, respectively.

The luminescent spectra of PAB and GAB glasses are shown in Fig. 3 when excited by 808nm LD. It could be observed that the infrared luminescent properties (emission peak, FWHM) of PAB glass are comparable to those of GAB glasses. We note that in aluminophosphate or germanate hosts the photoluminescence peak red-shifted about 50nm with respect to the silica hosts.

Fig. 3. Emission spectra of PAB and GAB glasses, when excited by 808nm LD.

It is not clear that which valent bismuth ion contributes to the infrared emission up to now. Not only the positions of both absorption and emission peaks of bismuth-doped aluminophosphate glass differ from those of previously reported Bi3+ or Bi2+ doped materials [9

9. G. Blasse and A. Bril, “Investigations on Bi3+-activated phosphors,” J. Chem. Phys. 48, 217–222 (1968) [CrossRef]

13

13. A. M. Strivastava, “Luminescence of divalent bismuth in M2+BPO5 (M2+=Ba2+, Sr2+ and Ca2+),” J. Lumin. 78, 239–243 (1998) [CrossRef]

], but also the lifetime is almost two orders of those of Bi3+ or Bi2+ [10

10. M. J. Weber and R. R. Monchamp, “Luminescence of Bi4Ge3O12 : spectral and decay properties,” J. Appl. Phys. 44, 5495–5499 (1973) [CrossRef]

, 13

13. A. M. Strivastava, “Luminescence of divalent bismuth in M2+BPO5 (M2+=Ba2+, Sr2+ and Ca2+),” J. Lumin. 78, 239–243 (1998) [CrossRef]

]. Such large differences indicate that the infrared emission might not be originated from those valent bismuth ions. Fujimoto et al ascribed the absorption and emission bands of bismuth-doped silica glasses to the Bi5+ transitions between the ground state of 1S0 and the excited states of 3D3,2,1 and 1D2. As Al3+ ions are doped in host and substitute for Si4+ sites, negative defect of AlSi’ will be formed and might be electrically compensated by the BiSi· defect as Bi5+ in Si4+ site of the glass network. However, the weak acidic vitreous GeO2 [14

14. M. B. Volf, Chemical approach to glass, Vol. 7 of Glass Science and Technology Series (Elsevier, New York, 1984) 406–410, 465–469

] as well as emission quenching with increasing alkaline earth metal oxide in borate glasses [15

15. X. Meng, Photon Craft Project, Shanghai Institute of Optics and Fine Mechanics, Graduate School of Chinese Academy of Sciences and Japan Science and Technology Agency, Shanghai 201800, China, and M. Peng, J. Qiu, D. Chen, X. Jiang and C. Zhu are preparing a manuscript to be called “Infrared broadband emission of bismuth-doped barium-aluminum-borate glasses.”

] seems that the upper oxidation state of dopant is not preferable based on the optical basicity theory proposed by J. A. Duffy [16

16. J. A. Duffy, “Redox equilibria of glass,” J. Non-Cryst. Solids 196, 45–50 (1996) [CrossRef]

]. Furthermore, at higher temperature, dissociation of Bi2O3 would occur. Bi2O3 may convert into the suboxide BiO or bismuth metal [14

14. M. B. Volf, Chemical approach to glass, Vol. 7 of Glass Science and Technology Series (Elsevier, New York, 1984) 406–410, 465–469

]. We did not observe apparent visible luminescence due to transitions of Bi3+ in the PAB glass when excited by ultraviolet light. Therefore, we suggest there are few Bi ions existing as Bi3+ and Bi5+ states in the glass though more detailed experiments should be carried out. We think that bismuth may exist as low valence state (Bi+ or bismuth cluster) in the glasses investigated herein.

Based on energy matching conditions, we suggest tentatively that the infrared emission derives from monovalent bismuth ions. The simplified energy levels of Bi+ are presented in Fig. 4. The ground configuration of Bi+ (6s26p2) is split by spin-orbit coupling interaction into the ground state 3P0 and the excited states 1S0, 1D2 and 3P2,1. Although only two absorption bands at 460nm and 700nm occur in bismuth-doped aluminophosphate glass, additional 800nm absorption band in bismuth-doped silica glass and 800nm, 1000nm absorption bands in bismuth-doped germanate glass have also been reported. The above absorption bands centered at: 460, 700nm, 800nm and 1000nm could be ascribed to the transitions between the ground state 3P0 and the excited states 1S0, 1D2 and 3P2,1. It should also be mentioned that infrared emissions peaking differently can be observed in bismuth-doped silica glasses under 500nm, 700nm and 800nm pumping. Bismuth-doped aluminophosphate, silica and germanate glass systems show the near infrared emission due to 3P13P0 transition under the above pumping sources excitation. After absorption the system reaches high vibrational levels of the excited states. Subsequently it relaxes non-radiatively to the lowest vibrational level of 3P1 where emission 3P13P0 occurs as a broad band.

Fig.4. . nergy level diagram for Bi+, which is proposed based on energy matching conditions (NIR: near infrared emission).

Another possibility for the infrared emission has come into consideration: 1S01D2. In this case, a two-photon absorption process should be involved based on energy matching conditions when excited by 808nm and 980nm. However, the log-log dependence of the infrared emission intensity on excitation power shown in Fig. 5 is roughly linear, showing that one incident photon is involved in this infrared emission. Since there is no confirmed evidence to prove the existence of Bi+, spectrum might be an effective way to assume the mechanism of the unusual infrared emission from bismuth ions. More experiments should be carried out to clarify the mechanism of the infrared emission.

Fig. 5. Log-log plots of infrared emission intensity as a function of pump power at 808nm and 980nm

It is attractive that infrared emissions from PAB glass are acceptable with multiple wavelengths excitation and the emissions all cover the second telecommunication window. The broadband emission of 1300nm with FWHM of 300nm is of much more interest because it is the working wavelength of the second telecommunication window. Furthermore, the 1300nm broadband emission of bismuth ions covers the O, E, S, C and L bands (1260–1625nm), which shows that this material is also promising for ultrabroadband amplification. The 808nm-pumping scheme has offered a potential advantage of high power semiconductor lasers, which are most widely utilized in optical telecommunications and commercially available.

The fluorescence decay curve at 1300nm with 808nm LD excitation is shown in Fig. 6. The decay curve shows a good consistence with the first order exponential decay with the lifetime as long as 500µs.

Fig.6. . he emission decay curve of PAB, the monitoring wavelength is 1300nm under 808nm LD excitation.

The stimulated emission cross section σ as a function of wavelength to a first approximation coincides with the spontaneous emission spectrum, which is expressed by the following formula:

σ(λ)=λ2g(λ)8πn2τ
(1)

where λ is wavelength, g(λ)is the normalized spontaneous emission shape function, n is the host refractive index, and τ is the emission lifetime. By assuming a Gaussian-shaped emission band, the stimulated emission cross section σ at the band center can be estimated by the following formula:

σ=λ024πn2τ21Δν(ln2π)12
(2)

where λ 0 is the band center wavelength and Δν is the FWHM of the emission. We can obtain σ=1.0×10-20cm2, with λ 0=1300nm, n=1.53, τ=500µs, and Δν=1800cm-1 for the PAB glass, and σ=1.68×10-20cm2, with λ 0=1300nm, n=1.60, τ=254.5µs, and Δν=1922cm-1 for GAB glass. The product of the stimulated emission cross section and the lifetime, στ, is an important parameter to characterize laser materials, because the laser threshold is proportional to (στ)-1. The στ products of the bismuth ions in the PAB glass and the GAB glass are 5.0×10-24cm2s and 4.28×10-24cm2s, respectively. The στ product of the glasses is about three times larger than that of Ti:Al2O3 (στ=1.4×10-24cm2s). It indicates that both bismuth-doped aluminophosphate glass and germanate glass are promising materials for optical amplification.

4. Conclusion

In summary, we have observed near infrared broadband emissions in bismuth-doped aluminophosphate glasses. This material possesses long lifetime even at room temperature and large product of the stimulated emission cross section and the lifetime. We ascribed the infrared emissions to 3P13P0 transition of Bi+ based on the observed absorption and luminescent spectra. Together with the possibility of multiple wavelengths excitation, the scheme of using 808nm LD as a pumping source suggests that this material might be a promising candidate for broadband fiber amplifiers and tunable lasers.

Acknowledgments

The authors would like to acknowledge the financial support provided by the National Natural Science Foundation of China under the number of 50125258 and Shanghai Science and Technology under the number of 04XD14018.

References and links

1.

A. Mori, Y. Ohishi, and S. Sudo, “Erbium-doped tellurite glass fibre laser and amplifier,” Electron. Lett. 33, 863–864 (1997) [CrossRef]

2.

G. P. Agrawal, Nonlinear Fiber Optics, 2nd edition (Academic, San Diego, 1995)

3.

Y. Fujimoto and M. Nakatsuka, “Infrared luminescence from bismuth-doped silica glass,” Jpn. J. App. Phys. 40, L279–L281 (2001) [CrossRef]

4.

Y. Fujimoto and M. Nakatsuka, “Optical amplification in bismuth-doped silica glass,” App. Phys. Lett. 82, 3325–3326 (2003) [CrossRef]

5.

M. Peng, J. Qiu, D. Chen, X. Meng, L. Yang, X. Jiang, and C. Zhu, “Bismuth- and aluminum co-doped germanium oxide glasses for super-broadband optical amplification,” Opt. Lett. 29, 1998–2000 (2004) [CrossRef] [PubMed]

6.

T. Sazuki and Y. Ohishi, “Broadband 1400nm emission from Ni2+ in zink-alumino-silicate glass,” Appl. Phys. Lett. 84, 3804–3806 (2004) [CrossRef]

7.

I. T. Sorokina, S. Naumov, E. Sorokin, E. Wintner, and A. V. Shestakov, “Directly diode-pumped tunable continuous-wave room-temperature Cr4+: YAG laser,” Opt. Lett. 24, 1578–1580 (1999) [CrossRef]

8.

N. Sugimoto, H. Kanbara, S. Fujiwara, K. Tanaka, and K. Hirao, “Ultrafast response of third-order optical nonlinearity in glasses containing Bi2O3,” Opt. Lett. 21, 1637–1639 (1996) [CrossRef] [PubMed]

9.

G. Blasse and A. Bril, “Investigations on Bi3+-activated phosphors,” J. Chem. Phys. 48, 217–222 (1968) [CrossRef]

10.

M. J. Weber and R. R. Monchamp, “Luminescence of Bi4Ge3O12 : spectral and decay properties,” J. Appl. Phys. 44, 5495–5499 (1973) [CrossRef]

11.

R. B. Lauer, “Photoluminescence in Bi12SiO20 and Bi12GeO20,” Appl. Phys. Lett. 17, 178–179 (1970) [CrossRef]

12.

G. Blasse, “Unusual bismuth luminescence in strontium tetraborate (SrB4O7: Bi),” J. Phys. Chem. Solids 55, 171–174 (1994) [CrossRef]

13.

A. M. Strivastava, “Luminescence of divalent bismuth in M2+BPO5 (M2+=Ba2+, Sr2+ and Ca2+),” J. Lumin. 78, 239–243 (1998) [CrossRef]

14.

M. B. Volf, Chemical approach to glass, Vol. 7 of Glass Science and Technology Series (Elsevier, New York, 1984) 406–410, 465–469

15.

X. Meng, Photon Craft Project, Shanghai Institute of Optics and Fine Mechanics, Graduate School of Chinese Academy of Sciences and Japan Science and Technology Agency, Shanghai 201800, China, and M. Peng, J. Qiu, D. Chen, X. Jiang and C. Zhu are preparing a manuscript to be called “Infrared broadband emission of bismuth-doped barium-aluminum-borate glasses.”

16.

J. A. Duffy, “Redox equilibria of glass,” J. Non-Cryst. Solids 196, 45–50 (1996) [CrossRef]

OCIS Codes
(160.2750) Materials : Glass and other amorphous materials
(300.2140) Spectroscopy : Emission

ToC Category:
Research Papers

History
Original Manuscript: January 13, 2005
Revised Manuscript: February 21, 2005
Published: March 7, 2005

Citation
Xian-geng Meng, Jian-rong Qiu, Ming-ying Peng, Dan-ping Chen, Quan-zhong Zhao, Xiong-wei Jiang, and Cong-shan Zhu, "Near infrared broadband emission of bismuth-doped aluminophosphate glass," Opt. Express 13, 1628-1634 (2005)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-13-5-1628


Sort:  Journal  |  Reset  

References

  1. A. Mori, Y. Ohishi and S. Sudo, �??Erbium-doped tellurite glass fibre laser and amplifier,�?? Electron. Lett. 33, 863-864 (1997) [CrossRef]
  2. G. P. Agrawal, Nonlinear Fiber Optics, 2nd edition (Academic, San Diego, 1995)
  3. Y. Fujimoto and M. Nakatsuka, �??Infrared luminescence from bismuth-doped silica glass,�?? Jpn. J. App. Phys. 40, L279-L281 (2001) [CrossRef]
  4. Y. Fujimoto and M. Nakatsuka, �??Optical amplification in bismuth-doped silica glass,�?? App. Phys. Lett. 82, 3325-3326 (2003) [CrossRef]
  5. M. Peng, J. Qiu, D. Chen, X. Meng, L. Yang, X. Jiang and C. Zhu, �??Bismuth- and aluminum co-doped germanium oxide glasses for super-broadband optical amplification,�?? Opt. Lett. 29, 1998-2000 (2004) [CrossRef] [PubMed]
  6. T. Sazuki and Y. Ohishi, �??Broadband 1400nm emission from Ni2+ in zink-alumino-silicate glass,�?? Appl. Phys. Lett. 84, 3804-3806 (2004) [CrossRef]
  7. I. T. Sorokina, S. Naumov, E. Sorokin, E. Wintner and A. V. Shestakov, �??Directly diode-pumped tunable continuous-wave room-temperature Cr4+: YAG laser,�?? Opt. Lett. 24, 1578-1580 (1999) [CrossRef]
  8. N. Sugimoto, H. Kanbara, S. Fujiwara, K. Tanaka and K. Hirao, �??Ultrafast response of third-order optical nonlinearity in glasses containing Bi2O3,�?? Opt. Lett. 21, 1637-1639 (1996) [CrossRef] [PubMed]
  9. G. Blasse and A. Bril, �??Investigations on Bi3+-activated phosphors,�?? J. Chem. Phys. 48, 217-222 (1968) [CrossRef]
  10. M. J. Weber and R. R. Monchamp, �??Luminescence of Bi4Ge3O12 : spectral and decay properties,�?? J. Appl. Phys. 44, 5495-5499 (1973) [CrossRef]
  11. R. B. Lauer, �??Photoluminescence in Bi12SiO20 and Bi12GeO20,�?? Appl. Phys. Lett. 17, 178-179 (1970) [CrossRef]
  12. G. Blasse, �??Unusual bismuth luminescence in strontium tetraborate (SrB4O7: Bi),�?? J. Phys. Chem. Solids 55, 171-174 (1994) [CrossRef]
  13. A. M. Strivastava, �??Luminescence of divalent bismuth in M2+BPO5 (M2+=Ba2+, Sr2+ and Ca2+),�?? J. Lumin. 78, 239-243 (1998) [CrossRef]
  14. M. B. Volf, Chemical approach to glass, Vol. 7 of Glass Science and Technology Series (Elsevier, New York, 1984) 406-410, 465�?? 469
  15. X. Meng, Photon Craft Project, Shanghai Institute of Optics and Fine Mechanics, Graduate School of Chinese Academy of Sciences and Japan Science and Technology Agency, Shanghai 201800, China, and M. Peng, J. Qiu, D. Chen, X. Jiang and C. Zhu are preparing a manuscript to be called �??Infrared broadband emission of bismuth-doped barium-aluminum-borate glasses.�??
  16. J. A. Duffy, �??Redox equilibria of glass,�?? J. Non-Cryst. Solids 196, 45-50 (1996) [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited