Single-mode and high power waveguide lasers fabricated by ion-exchange

G. Della Valle, A. Festa, G. Sorbello, K. Ennser, C. Cassagnetes, D. Barbier, and S. Taccheo  »View Author Affiliations


Optics Express, Vol. 16, Issue 16, pp. 12334-12341 (2008)
http://dx.doi.org/10.1364/OE.16.012334


View Full Text Article

Acrobat PDF (822 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

We report on a single-end diode-pumped waveguide laser providing output power in excess of 20 mW with 17% slope efficiency in robust single longitudinal and transverse mode operation at 1533.5 nm. The active medium was an Er:Yb-doped waveguide only 9-mm long fabricated by Ag-Na ion-exchange in a phosphate glass. The overall cavity length including butt-coupled fiber-Bragg-grating mirrors was <60 mm. We also report on high power waveguide lasers providing more than 160 mW output power and 46% slope efficiency in multimode operation. Feasibility of high power single mode waveguide lasers based on ion-exchange technology in phosphate glasses is also experimentally investigated by using a 50-mm long active waveguide specially designed for efficient single-end pumping.

© 2008 Optical Society of America

1. Introduction

Among the growing request of new high performance laser sources one of the key issue is to develop compact single-mode lasers at 1.5 μm. In fact, several applications like free space optical communications [1

1. H. Willebrand and B. S. Ghuman, Free-Space Optics: Enabling Optical Connectivity in Today’s Networks (Sams Publishing, Indianapolis, In., 2002).

], laser radar and satellite based remote sensing [2

2. C. J. Karlsson, F. A. Olsson, D. Letalick, and M. Harris, “All-Fiber Multifunction Continuous-Wave Coherent Laser Radar at 1.55 μm for Range, Speed, Vibration, and Wind Measurements,” Appl. Opt. 39, 3716–3726 (2000). [CrossRef]

], distribute fiberoptic sensors [3

3. F. T. S. Yu and S. Yin, Fiber Optic Sensors (Marcel Dekker Inc., New York – Basel, 2002). [CrossRef]

], and frequency domain reflectometry [4

4. J. Geng, C. Spiegelberg, and S. Jiang, “Narrow linewidth fiber laser for 100-km optical frequency domain reflectometry,” Photon. Technol. Lett. 17, 1827–1829 (2005). [CrossRef]

], are becoming more and more demanding in terms of power, compactness, insensitivity to environmental disturbance and high temporal coherence. The most exploited solution, which is represented by bulk lasers able to provide high output powers in view of large mode volume, actually suffers from several limitations in terms of compactness and robustness of the cavity. Recently, short fiber lasers [5

5. C. Spiegelberg, J. Geng, Y. Hu, Y. Kaneda, S. Jiang, and N. Peyghambarian, “Low-noise narrow-linewidth fiber laser at 1550 nm (June 2003),” J. Lightwave Technol. 22, 57–62 (2004). [CrossRef]

] have demonstrated the potential to satisfy all the requirements previously outlined in view of an intrinsic compactness and robustness provided by a monolithic cavity structure. Furthermore, with the development of heavily-doped glasses and specially designed fibers, such as large-mode area or micro-structured fibers, fiber lasers demonstrated mode volumes even larger than several bulk lasers and the first watt-level single mode fiber laser at 1.5 μm has been already reported [6

6. A. Schülzgen, L. Li, V. L. Temyanko, S. Suzuki, J. V. Moloney, and N. Peyghambarian, “Single-frequency fiber oscillator with watt-level output power using photonic crystal phosphate glass fiber,” Opt. Express 14, 7087–7092 (2006). [CrossRef] [PubMed]

]. However, still the cavity was not so rigid as it can be in a waveguide device where all components can be realized, in principle, on the same substrate. Therefore waveguide laser cavities are expected to provide even better performance in terms of robustness and insensitivity to environmental noise, though demonstration of high output power, especially in single-mode operation, is still a challenging task. This limit stems from the difficulty in fabricating high quality active waveguides in heavily-doped glasses and in optimizing doping concentration for efficient pumping over short lengths. In fact a highly-doped material is required to meet the demand of high-power together with a compact laser cavity (around few cm long) allowing single longitudinal mode operation. This requirement makes glass-on-silicon technology unsuitable because erbium concentration is limited by quenching effects in silica [7

7. E. Snoeks, G. N. van den Hoven, A. Polman, B. Hendriksen, M. B. J. Diemeer, and F. Priolo, “Cooperative upconversion in erbium-implanted soda-lime silicate glass optical waveguides,” J. Opt. Soc. Am. B 12, 1468–1474 (1995).

]. On the contrary, other glasses offer better solubility of erbium. In particular, phosphate glass offers a far better solubility with respect to silica and also makes codoping with Yb ions more beneficial for pumping in view of higher phonon energies in the phosphate, resulting in efficient energy transfer from Yb to Er. The use of Yb is also the key solution for high pump absorption over short lengths.

We recently demonstrated 50 mW single-mode operation in a diode-pumped waveguide laser based on a 22-mm long active waveguide fabricated by femtosecond laser writing in an Er:Yb-doped phosphate glass [8

8. G. Della Valle, S. Taccheo, R. Osellame, A. Festa, G. Cerullo, and P. Laporta, “1.5 μm single longitudinal mode waveguide laser fabricated by femtosecond laser writing,” Opt. Express 15, 3190–3194 (2007). [CrossRef] [PubMed]

]. Another method to fabricate high quality active waveguides in a phosphate glass base is the ion-exchange (see [9

9. R. V. Ramaswamy and R. Srivastava, “Ion-exchanged glass waveguides: a review,” J. Lightwave Technol. 6, 984–1002 (1988). [CrossRef]

] and references therein), which offers the advantage of being a well developed technique, providing high reliability and mass production. Furthermore, channel waveguides fabricated by ion-exchange technology are close enough to the glass surface to allow mode-field interaction with materials placed at the surface or with a micro-structured surface. This allows an integration of cavity mirrors into ion-exchanged waveguides by means of surface patterning with mask lithography [10

10. S. Blaize, L. Bastard, C. Cassagnétes, and J. E. Broquin “Multiwavelengths DFB waveguide laser arrays in Yb-Er codoped phosphate glass substrate,” IEEE Photon. Technol. Lett. 15, 516–518 (2003). [CrossRef]

] or laser irradiation [11

11. S. Yliniemi, J. Albert, Q. Wang, and S. Honkanen “UV-exposed Bragg gratings for laser applications in silver-sodium ion-exchanged phosphate glass waveguides,” Opt. Express 14, 2898–2903 (2006). [CrossRef] [PubMed]

]. For these reasons, ion-exchanged waveguide lasers have attracted much interest, but only few mW output power have been demonstrated up to now [10

10. S. Blaize, L. Bastard, C. Cassagnétes, and J. E. Broquin “Multiwavelengths DFB waveguide laser arrays in Yb-Er codoped phosphate glass substrate,” IEEE Photon. Technol. Lett. 15, 516–518 (2003). [CrossRef]

,11

11. S. Yliniemi, J. Albert, Q. Wang, and S. Honkanen “UV-exposed Bragg gratings for laser applications in silver-sodium ion-exchanged phosphate glass waveguides,” Opt. Express 14, 2898–2903 (2006). [CrossRef] [PubMed]

,12

12. G. Sorbello, S. Taccheo, P. Laporta, O. Svelto, E. Cianci, V. Foglietti, S. Jiang, and N. Peyghambarian, “Singlemode Er-Yb waveguide laser array at 1.5 μm,” Electron. Lett. 37, 1014–1015 (2001). [CrossRef]

], except from a Ti:Sapphire-pumped large mode area waveguide laser providing few tens of mW [13

13. D. L. Veasey, D. S. Funk, P. M. Peters, N. A. Sanford, G. E. Obarski, N. Fontaine, M. Young, A. P. Peskin, W.-C. Liu, S. N. Houde-Walter, and J. S. Hayden, “Yb/Er-codoped and Yb-doped waveguide lasers in phosphate glass,” J. Non-Cryst. Solids 263&264, 369–381 (2000). [CrossRef]

].

In this paper we report on the development of a single-mode and single-end diode-pumped waveguide laser based on a 9-mm long Er-Yb-doped waveguide fabricated by Ag-Na ion exchange in a heavily doped phosphate glass. Furthermore, we report on preliminar experiments on high power waveguide lasers based on longer waveguides fabricated in the same phosphate base. An experimental investigation of power scaling feasibility towards 100 mW power level in single mode operation was also carried out by using a commercial 50-mm long active waveguide optimized for efficient single-end pumping.

2. Waveguide fabrication and laser set-up

2.1 Waveguide fabrication

The ion-exchange method is a very reliable, rugged and low cost technique for waveguide fabrication, and was already demonstrated for several exchanging ions, including K-Na [10

10. S. Blaize, L. Bastard, C. Cassagnétes, and J. E. Broquin “Multiwavelengths DFB waveguide laser arrays in Yb-Er codoped phosphate glass substrate,” IEEE Photon. Technol. Lett. 15, 516–518 (2003). [CrossRef]

,13

13. D. L. Veasey, D. S. Funk, P. M. Peters, N. A. Sanford, G. E. Obarski, N. Fontaine, M. Young, A. P. Peskin, W.-C. Liu, S. N. Houde-Walter, and J. S. Hayden, “Yb/Er-codoped and Yb-doped waveguide lasers in phosphate glass,” J. Non-Cryst. Solids 263&264, 369–381 (2000). [CrossRef]

] and Ag-Na [11

11. S. Yliniemi, J. Albert, Q. Wang, and S. Honkanen “UV-exposed Bragg gratings for laser applications in silver-sodium ion-exchanged phosphate glass waveguides,” Opt. Express 14, 2898–2903 (2006). [CrossRef] [PubMed]

,12

12. G. Sorbello, S. Taccheo, P. Laporta, O. Svelto, E. Cianci, V. Foglietti, S. Jiang, and N. Peyghambarian, “Singlemode Er-Yb waveguide laser array at 1.5 μm,” Electron. Lett. 37, 1014–1015 (2001). [CrossRef]

]. In order to address compactness of the waveguide laser cavity, a heavily doped glass substrate allowing high gain per unit length is required. Phosphate glasses are good candidates, allowing for much higher doping levels Er and Yb with respect to silicate glasses. Among commercially available phosphates we selected Schott IOG-1, which already demonstrated high optical quality and, in view of a high content of sodium (20%wt of Na2O), allows both K-Na and Ag-Na ion exchange fabrication. Doping concentration was 3.43x1020 ions/cm3 of Er3+ and 2.49×1020 ions/cm3 of Yb3+. A two-step Ag-Na ion-exchange process was adopted for waveguide fabrication. In the first step the glass substrate was immersed for 8 minutes in a ternary mixture of molten salts (8%wt AgNO3, 5.25%wt NaNO3, 86.75%wt KNO3) at 330°C (see [14

14. G. Jose, G. Sorbello, S. Taccheo, G. Della Valle, E. Cianci, V. Foglietti, and P. Laporta “Ag-Na ion-exchange from dilute melt: guidelines for planar waveguide fabrication on a commercial phosphate glass,” Opt. Mater. 23, 559–567 (2003). [CrossRef]

]). A titanium mask with 6-μm wide linear apertures was previously deposited onto the glass substrate thus allowing fabrication of linear channel waveguides at the surface. A second burial step was performed by applying a transversal driving electric field to the substrate in order to reduce waveguide propagation losses and coupling losses to single-mode fibers (see [15

15. G. Della Valle, S. Taccheo, G. Sorbello, E. Cianci, V. Foglietti, and P. Laporta, “Compact high gain erbium-ytterbium doped waveguide amplifier fabricated by Ag-Na ion exchange,” Electron. Lett. 42, 632–633 (2006). [CrossRef]

] for fabrication details). After fabrication, the waveguide end-facets have been polished and the resulting waveguide length was 9 mm. In total we fabricated a linear array consisting of sixteen 250-μm spaced buried channel active waveguides.

Fig. 1. (a). Typical waveguide refractive index profiles. (b) Typical near-field mode profiles of the waveguide compared to near-field mode profiles of standard SMF-28 fiber at 1550 nm.

Figure 1(a) shows typical refractive index profiles of the waveguides fabricated by this double-step process, measured according to standard refracted-near-field technique by means of a commercial refractive index profilometer (Rinck Elektronik). A maximum refractive index change of 0.0112 was measured and the waveguide resulted to be about 4 μm buried in the glass substrate. The waveguides exhibited a single transverse mode at 1550 nm, and by using an infrared camera the mode-field profiles were recorded and compared to mode-field profiles of SMF-28 telecom fiber [see Fig. 1(b)]. We obtained a quite circularly symmetric waveguide mode, resulting to be fully compatible with standard SMF-28 telecom fiber, which is an essential requirement to minimize laser intracavity losses, especially in an ultra-short active medium. From the overlap between waveguide and fiber near-field profiles we estimated coupling losses to standard single-mode fiber as low as 0.2 dB/facet. Overall insertion losses (namely coupling losses plus propagation losses) of the 9 mm long waveguide were measured to be about 0.8 dB.

2.2 Laser cavity setup

Figure 2 shows the laser cavity set-up based on the 9-mm long active waveguide. Two fiber-Bragg-gratings (FBGs) were butt-coupled to the waveguide by using a suitable index matching fluid (allowing high pump intensity). The high-reflectivity (HR) FBG has a 99.8% reflectivity centered at 1533.5 nm with 125-GHz bandwidth (FWHM). To enhance erbium inversion along the 9-mm long waveguide we adopted a laser diode emitting at 976 nm, thus matching the Yb absorption peak and maximizing pump absorption over such a short length. The diode provides a maximum incident pump power of 250 mW. Note that the employment of an ultra-compact active waveguide allows a linear laser cavity as short as few cm, resulting in a free-spectral-range as large as few GHz.

Fig. 2. (a). Schematic of waveguide laser set-up. (b) Picture of the 9-mm waveguide laser.

3. Single-mode laser experiment

To evaluate the optimum output coupling we performed a first set of laser experiments employing several FBGs of different reflectivity as output couplers.

Fig. 3. (a). Slope efficiency (triangles) and pump power threshold (squares) vs. output coupling. (b) Maximum output power vs. output coupling.

Figure 3 shows the slope efficiency, pump power threshold and output power for five FBG output couplers with peak reflectivity centered at 1533.5 nm and 30 GHz bandwidth (FWHM).

During the test the cavity length was of the order of 1 m and the laser was therefore not operating in single-mode. However the laser bandwidth was of few GHz only, as defined by FBG reflection bandwidth, and only few modes were oscillating within a bandwidth of about 1.5 GHz. From Fig. 3 the FBG with 46% output coupling is found to provide the best laser performance. However to ensure single-mode operation we preferred the 52% output-coupling FBG, because of a narrower bandwidth, of about 80 pm (10 GHz) against 100 pm (12.5 GHz) of the 46% output-coupler. After selection of the proper output coupler the cavity was shortened by cutting FBG fiber. We estimated an overall cavity length of about 55 mm. The active waveguide was also displaced from the center of the cavity in order to reduce spatial hole burning effect and thus longitudinal mode competition.

Fig. 4. (a). Single mode laser output power as a function of pump power. Inset shows RIN spectrum at 22 mW output power. (b). Fabry-Perot spectrum of the single mode laser. The frequency offset shows drift without mode-hopping.

Figure 4(a) shows the output power characteristic of the 55 mm long laser cavity. The pump power threshold was 135 mW and we measured a maximum output power of 22 mW with 17% slope efficiency with respect to the incident pump power. We noticed a remarkably stable single-mode operation at all pump power levels, even in the absence of thermal stabilization. Figure 4(b) shows the laser spectrum recorded by means of a high-finesse Fabry-Perot interferometer (Burleigh Mod. SA201), ascertaining single mode operation (the interferometer has a fixed free spectral range of 8 GHz, a finesse of 100, and the signal to noise ratio on the photodiode was about 26 dB). Inset in Fig. 4(a) shows the relative intensity noise (RIN) spectrum of the laser when operating at maximum output power. The relatively high peak value is due to the structure of the cavity, still discrete in nature because of the butt-coupling between the waveguide and FBG fibers. We believe that a RIN peak reduction is achievable once FBG fibers are bonded to the waveguide, thus providing a monolithic waveguide structure. Note also that, in view of the high doping level of the glass substrate, no saturation behavior of the laser output power was observed, as ascertained by the fairly linear input-output characteristic of Fig. 4(a). Therefore, the maximum output power of 22 mW was only limited by the pump power available.

4. Power scaling towards single-mode high power waveguide lasers

Fig. 5. Laser cavity setup for high power waveguide laser experiments. PC: polarization controller. Picture shows a 45 mm long active waveguide butt-coupled to FBG fibers under double-end pumping.

From the single mode experiment we also found that a linear cavity as short as 60-mm with an output coupler providing 80-pm reflectivity bandwidth is able to ensure stable single-mode operation. This means that a 40-mm to 50-mm long waveguide could be suitable for high-power single-mode operation.

To address this aim, we first tested the feasibility of high-power lasers based on active waveguides fabricated in a 50 mm long IOG-1 substrate under the same ion-exchange parameters as reported above. The refractive index profiles as well as the near-field mode profiles resulted to be almost the same as the ones reported in section 2. After polishing of the end facets the waveguide length was 45 mm.

Considering the quasi-three level nature of Er systems, a lower doping concentration of erbium is required, for a given pump power, to achieve high average inversion in this much longer waveguide [16

16. P. C. Becker, N. A. Olsson, and J. R. Simpson, Erbium-Doped Fiber Amplifiers (Academic Press, 1998).

]. According to preliminary numerical simulations (based on a rate-equation model similar to the one reported in [17

17. C. E. Chryssou, F. Di Pasquale, and C. W. Pitt, “Improved Gain Performance In Yb3+-Sensitized Er3+-Doped Alumina (Al2O3) Channel Optical Waveguide Amplifiers,” J. Lightwave Technol. 19, 345–349 (2001). [CrossRef]

]), we selected, among commercially available concentrations, an erbium doping level of 1.88×1020 ions/cm3. Considering the available pump power we also adopted a double-end pumping scheme with a second pump diode at 980 nm because the pump diode at 976 nm was already significantly absorbed after about half of the waveguide. To avoid feedback and interplays between the two pumps we used a polarization controller and a pump isolator. The test laser cavity set-up is shown in Fig. 5. The cavity was as long as 1 m and the total maximum available pump power was 500 mW. Fig. 5 also shows a picture of the 45-mm long waveguide under double-end pumping. Note that the green light emission (due to fluorescence from erbium energy levels populated by up-conversion processes) is almost uniform along the waveguide, indicating that a high inversion of Er is achieved all along the waveguide.

Before starting laser experiments we measured the small-signal gain and the insertion loss of the 45-mm long waveguide. Results are reported in the inset of Fig. 6(a), showing a peak internal gain of 19 dB at 1534 nm, and insertion loss as low as 2.4 dB, resulting in a peak net gain exceeding 16 dB. This ascertains the high optical quality and efficiency of the 45-mm long ion-exchanged waveguide amplifier and suggests feasibility of high power waveguide lasers by exploiting this longer active medium and a laser cavity with high output coupling. For the laser experiment we tested several output couplers and the best result was obtained with the lowest reflectivity available, indicating the possibility of even better performance providing higher output coupling. In Fig. 6(b) the output power versus pump power is reported for three different output couplers. With the 21.5% reflectivity FBG we obtained 164 mW fiber-coupled output power with 500 mW incident pump power. The slope efficiency (with respect to the incident pump power) was 46% and represents, to our knowledge, the highest value so far reported in erbium-ytterbium doped ion-exchanged waveguide lasers. Note that FOM = 36.4 mW/cm, but usually at least two main longitudinal modes were oscillating (on the same transverse mode), therefore this result refers to multi-longitudinal mode operation.

Fig. 6. (a). Laser output power (in multimode operation) vs. pump power (double-end pumping) for the 45-mm long active waveguide for three different output couplers. Inset shows the small-signal internal gain and insertion losses of the 45-mm long active waveguide under 500 mW total incident pump power (double-end pumping scheme). (b) Laser characteristics of the 60 mm long laser cavity based on a 50-mm long active waveguide specially designed to allow efficient single-end pumping at 980 nm.

5. Conclusion

We reported on a stable single-mode ion-exchanged waveguide laser providing more than 20 mW output power at 1533.5 nm under single-end diode pumping. The laser is based on an ultra-compact high gain Er-Yb-doped waveguide efficiently mode-matched to standard single mode telecom fibers. The waveguide was fabricated in a commercial (Schott IOG-1) phosphate glass by using an optimized double-step Ag-Na ion-exchange process. By exploiting the same fabrication technique we also demonstrated a high power multi-mode waveguide laser providing more than 160 mW output power and 46% slope efficiency, which represents to our knowledge the best power performance so far reported by Er-Yb-doped ion-exchanged waveguide lasers. We also evaluated the feasibility of single-mode power scaling to 100 mW output power by employing a state of the art ion-exchanged waveguide (by Teem Photonics) also fabricated in a phosphate glass. By using a 10-cm long linear laser cavity and this optimized waveguide we obtained 80 mW output power in quite single-mode operation with over 85% of the power carried by the main lasing mode under 260 mW incident pump power.

This preliminary result suggests that ion-exchange technique is a really promising solution to achieve 100-mW output power in single-mode operation out of a waveguide laser by exploiting the high erbium solubility in phosphate glass substrates.

Acknowledgments

Authors acknowledge partial support from MIUR project #2005099872.

References and links

1.

H. Willebrand and B. S. Ghuman, Free-Space Optics: Enabling Optical Connectivity in Today’s Networks (Sams Publishing, Indianapolis, In., 2002).

2.

C. J. Karlsson, F. A. Olsson, D. Letalick, and M. Harris, “All-Fiber Multifunction Continuous-Wave Coherent Laser Radar at 1.55 μm for Range, Speed, Vibration, and Wind Measurements,” Appl. Opt. 39, 3716–3726 (2000). [CrossRef]

3.

F. T. S. Yu and S. Yin, Fiber Optic Sensors (Marcel Dekker Inc., New York – Basel, 2002). [CrossRef]

4.

J. Geng, C. Spiegelberg, and S. Jiang, “Narrow linewidth fiber laser for 100-km optical frequency domain reflectometry,” Photon. Technol. Lett. 17, 1827–1829 (2005). [CrossRef]

5.

C. Spiegelberg, J. Geng, Y. Hu, Y. Kaneda, S. Jiang, and N. Peyghambarian, “Low-noise narrow-linewidth fiber laser at 1550 nm (June 2003),” J. Lightwave Technol. 22, 57–62 (2004). [CrossRef]

6.

A. Schülzgen, L. Li, V. L. Temyanko, S. Suzuki, J. V. Moloney, and N. Peyghambarian, “Single-frequency fiber oscillator with watt-level output power using photonic crystal phosphate glass fiber,” Opt. Express 14, 7087–7092 (2006). [CrossRef] [PubMed]

7.

E. Snoeks, G. N. van den Hoven, A. Polman, B. Hendriksen, M. B. J. Diemeer, and F. Priolo, “Cooperative upconversion in erbium-implanted soda-lime silicate glass optical waveguides,” J. Opt. Soc. Am. B 12, 1468–1474 (1995).

8.

G. Della Valle, S. Taccheo, R. Osellame, A. Festa, G. Cerullo, and P. Laporta, “1.5 μm single longitudinal mode waveguide laser fabricated by femtosecond laser writing,” Opt. Express 15, 3190–3194 (2007). [CrossRef] [PubMed]

9.

R. V. Ramaswamy and R. Srivastava, “Ion-exchanged glass waveguides: a review,” J. Lightwave Technol. 6, 984–1002 (1988). [CrossRef]

10.

S. Blaize, L. Bastard, C. Cassagnétes, and J. E. Broquin “Multiwavelengths DFB waveguide laser arrays in Yb-Er codoped phosphate glass substrate,” IEEE Photon. Technol. Lett. 15, 516–518 (2003). [CrossRef]

11.

S. Yliniemi, J. Albert, Q. Wang, and S. Honkanen “UV-exposed Bragg gratings for laser applications in silver-sodium ion-exchanged phosphate glass waveguides,” Opt. Express 14, 2898–2903 (2006). [CrossRef] [PubMed]

12.

G. Sorbello, S. Taccheo, P. Laporta, O. Svelto, E. Cianci, V. Foglietti, S. Jiang, and N. Peyghambarian, “Singlemode Er-Yb waveguide laser array at 1.5 μm,” Electron. Lett. 37, 1014–1015 (2001). [CrossRef]

13.

D. L. Veasey, D. S. Funk, P. M. Peters, N. A. Sanford, G. E. Obarski, N. Fontaine, M. Young, A. P. Peskin, W.-C. Liu, S. N. Houde-Walter, and J. S. Hayden, “Yb/Er-codoped and Yb-doped waveguide lasers in phosphate glass,” J. Non-Cryst. Solids 263&264, 369–381 (2000). [CrossRef]

14.

G. Jose, G. Sorbello, S. Taccheo, G. Della Valle, E. Cianci, V. Foglietti, and P. Laporta “Ag-Na ion-exchange from dilute melt: guidelines for planar waveguide fabrication on a commercial phosphate glass,” Opt. Mater. 23, 559–567 (2003). [CrossRef]

15.

G. Della Valle, S. Taccheo, G. Sorbello, E. Cianci, V. Foglietti, and P. Laporta, “Compact high gain erbium-ytterbium doped waveguide amplifier fabricated by Ag-Na ion exchange,” Electron. Lett. 42, 632–633 (2006). [CrossRef]

16.

P. C. Becker, N. A. Olsson, and J. R. Simpson, Erbium-Doped Fiber Amplifiers (Academic Press, 1998).

17.

C. E. Chryssou, F. Di Pasquale, and C. W. Pitt, “Improved Gain Performance In Yb3+-Sensitized Er3+-Doped Alumina (Al2O3) Channel Optical Waveguide Amplifiers,” J. Lightwave Technol. 19, 345–349 (2001). [CrossRef]

OCIS Codes
(140.3500) Lasers and laser optics : Lasers, erbium
(140.3570) Lasers and laser optics : Lasers, single-mode
(230.7380) Optical devices : Waveguides, channeled

ToC Category:
Lasers and Laser Optics

History
Original Manuscript: May 2, 2008
Revised Manuscript: June 8, 2008
Manuscript Accepted: June 12, 2008
Published: August 1, 2008

Citation
G. Della Valle, A. Festa, G. Sorbello, K. Ennser, C. Cassagnetes, D. Barbier, and S. Taccheo, "Single-mode and high power waveguide lasers fabricated by ion-exchange," Opt. Express 16, 12334-12341 (2008)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-16-16-12334


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. H. Willebrand and B. S. Ghuman, Free-Space Optics: Enabling Optical Connectivity in Today's Networks (Sams Publishing, Indianapolis, In., 2002).
  2. C. J. Karlsson, F. A. Olsson, D. Letalick, and M. Harris, "All-Fiber Multifunction Continuous-Wave Coherent Laser Radar at 1.55 µm for Range, Speed, Vibration, and Wind Measurements," Appl. Opt. 39, 3716-3726 (2000). [CrossRef]
  3. F. T. S. Yu and S. Yin, Fiber Optic Sensors (Marcel Dekker Inc., New York - Basel, 2002). [CrossRef]
  4. J. Geng, C. Spiegelberg and S. Jiang, "Narrow linewidth fiber laser for 100-km optical frequency domain reflectometry," Photon. Technol. Lett. 17, 1827-1829 (2005). [CrossRef]
  5. C. Spiegelberg, J. Geng, Y. Hu, Y. Kaneda, S. Jiang and N. Peyghambarian, "Low-noise narrow-linewidth fiber laser at 1550 nm (June 2003)," J. Lightwave Technol. 22, 57-62 (2004). [CrossRef]
  6. A. Schülzgen, L. Li, V. L. Temyanko, S. Suzuki, J. V. Moloney, and N. Peyghambarian, "Single-frequency fiber oscillator with watt-level output power using photonic crystal phosphate glass fiber," Opt. Express 14, 7087-7092 (2006). [CrossRef] [PubMed]
  7. E. Snoeks, G. N. van den Hoven, A. Polman, B. Hendriksen, M. B. J. Diemeer, and F. Priolo, "Cooperative upconversion in erbium-implanted soda-lime silicate glass optical waveguides," J. Opt. Soc. Am. B 12, 1468-1474 (1995).
  8. G. Della Valle, S. Taccheo, R. Osellame, A. Festa, G. Cerullo, and P. Laporta, "1.5 ?m single longitudinal mode waveguide laser fabricated by femtosecond laser writing," Opt. Express 15, 3190-3194 (2007). [CrossRef] [PubMed]
  9. R. V. Ramaswamy and R. Srivastava, "Ion-exchanged glass waveguides: a review," J. Lightwave Technol. 6, 984-1002 (1988). [CrossRef]
  10. S. Blaize, L. Bastard, C. Cassagnètes and J. E. Broquin "Multiwavelengths DFB waveguide laser arrays in Yb-Er codoped phosphate glass substrate," IEEE Photon. Technol. Lett. 15, 516-518 (2003). [CrossRef]
  11. S. Yliniemi, J. Albert, Q. Wang and S. Honkanen "UV-exposed Bragg gratings for laser applications in silver-sodium ion-exchanged phosphate glass waveguides," Opt. Express 14, 2898-2903 (2006). [CrossRef] [PubMed]
  12. G. Sorbello, S. Taccheo, P. Laporta, O. Svelto, E. Cianci, V. Foglietti, S. Jiang and N. Peyghambarian, "Singlemode Er-Yb waveguide laser array at 1.5 µm," Electron. Lett. 37, 1014-1015 (2001). [CrossRef]
  13. D. L. Veasey, D. S. Funk, P. M. Peters, N. A. Sanford, G. E. Obarski, N. Fontaine, M. Young, A. P. Peskin, W.-C. Liu, S. N. Houde-Walter, J. S. Hayden, "Yb/Er-codoped and Yb-doped waveguide lasers in phosphate glass," J. Non-Cryst. Solids 263 & 264, 369-381 (2000). [CrossRef]
  14. G. Jose, G. Sorbello, S. Taccheo, G. Della Valle, E. Cianci, V. Foglietti and P. Laporta "Ag-Na ion-exchange from dilute melt: guidelines for planar waveguide fabrication on a commercial phosphate glass," Opt. Mater. 23, 559-567 (2003). [CrossRef]
  15. G. Della Valle, S. Taccheo, G. Sorbello, E. Cianci, V. Foglietti and P. Laporta, "Compact high gain erbium-ytterbium doped waveguide amplifier fabricated by Ag-Na ion exchange," Electron. Lett. 42, 632-633 (2006). [CrossRef]
  16. P. C. Becker, N. A. Olsson, and J. R. Simpson, Erbium-Doped Fiber Amplifiers (Academic Press, 1998).
  17. C. E. Chryssou, F. Di Pasquale, and C. W. Pitt, "Improved Gain Performance In Yb3+-Sensitized Er3+-Doped Alumina (Al2O3) Channel Optical Waveguide Amplifiers," J. Lightwave Technol. 19, 345-349 (2001). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited