Sparse-exposure technique in holographic two-photon polymerization

Hidetomo Takahashi, Satoshi Hasegawa, Akihiro Takita, and Yoshio Hayasaki  »View Author Affiliations


Optics Express, Vol. 16, Issue 21, pp. 16592-16599 (2008)
http://dx.doi.org/10.1364/OE.16.016592


View Full Text Article

Acrobat PDF (1888 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

Holographic two-photon polymerization is based on a high-speed, low-loss parallel laser irradiation technique inside photosensitive materials using a computer-generated hologram displayed on a liquid crystal spatial light modulator. We demonstrated a sparse exposure technique combining parallel exposure and scanning exposure to improve the fabrication throughput and to achieve simultaneous fabrication of linear structures with different widths. We also demonstrated fabrication of space-variant structures by changing a CGH, as well as parallel fabrication of voxel structures with single femtosecond laser pulse irradiation.

© 2008 Optical Society of America

1. Introduction

Two-photon polymerization based on scanning irradiation of femtosecond laser pulses is an interesting tool for fabrication of microstructures [1

1. S. Maruo, O. Nakamura, and S. Kawata, “Three-dimensional microfabrication with two-photon-absorbed photopolymerization,” Opt. Lett. 22, 132–134 (1997). [CrossRef] [PubMed]

6

6. V. Mizeikis, K. K. Seet, S. Juodkazis, and H. Misawa, “Three-dimensional woodpile photonic crystal templates for the infrared spectral range,” Opt. Lett. 29, 2061–2063 (2004). [CrossRef] [PubMed]

]. The technique has been applied to three-dimensional (3D) microstructures [2

2. H. -B. Sun, S. Matsuo, and H. Misawa, “Three-dimensional photonic crystal structures achieved with two-photon-absorption photopolymerization of resin,” Appl. Phys. Lett. 74, 786–788 (1999). [CrossRef]

,3

3. H. -B. Sun, T. Tanaka, and S. Kawata, “Three-dimensional focal spots related to two-photon excitation,” Appl. Phys. Lett. 80, 3673–3675 (2002). [CrossRef]

,5

5. J. Serbin, A. Egbert, A. Ostendorf, B. N. Chickov, R. Houbertz, G. Domann, J. Schulz, C. Cronauer, L. Fröhlich, and M. Popall, “Femtosecond laser-induced two-photon polymerization of inorganic-organic hybrid materials for applications in photonics,” Opt. Lett. 28, 301–303 (2003). [CrossRef] [PubMed]

,6

6. V. Mizeikis, K. K. Seet, S. Juodkazis, and H. Misawa, “Three-dimensional woodpile photonic crystal templates for the infrared spectral range,” Opt. Lett. 29, 2061–2063 (2004). [CrossRef] [PubMed]

]. Recently, sub-wavelength writing has been demonstrated by some groups [7

7. S. H. Park, T. W. Lim, D. -Y. Yang, N. C. Cho, and K. -S. Lee, “Fabrication of a bunch of sub-30-nm nanofibers inside microchannels using photopolymerization via a long exposure technique,” Appl. Phys. Lett. 89, 173133 (2006). [CrossRef]

9

9. J. -F. Xing, X. -Z. Dong, W. -Q. Chen, X. -M. Duan, N. Takeyasu, T. Tanaka, and S. Kawata, “Improving spatial resolution of two-photon microfabrication by using photoinitiator with high initiating efficiency,” Appl. Phys. Lett. 90, 131106 (2007). [CrossRef]

]. Because such 3D microstructures have numerous irradiation points with a sub-wavelength unit size, a femtosecond laser irradiation system with high throughput and high energy utilization efficiency will be required to fabricate devices with a practically effective size. Parallel femtosecond laser irradiation techniques can satisfy these demands [10

10. Y. Kuroiwa, N. Takeshima, Y. Narita, S. Tanaka, and K. Hirao, “Arbitrary micropatterning method in femtosecond laser microprocessing using diffractive optical elements,” Opt. Exp. 12, 1908–1915 (2004). [CrossRef]

12

12. J. Kato, N. Takeyasu, Y. Adachi, H. -B. Sun, and S. Kawata, “Multiple-spot parallel processing for laser micronanofabrication,” Appl. Phys. Lett. , 86, 044102 (2005). [CrossRef]

]. Additionally, parallel femtosecond laser irradiation using a computer-generated hologram (CGH) displayed on a spatial light modulator (SLM) is a powerful technique, because a CGH can generate a desired arbitrarily variable beam, such as a beam with a prescribed spatial shape, a split beam, a focused beam, or a wavefront corrected beam, with low loss of light [13

13. Y. Hayasaki, T. Sugimoto, A. Takita, and N. Nishida, “Variable holographic femtosecond laser processing by use of a spatial light modulator,” Appl. Phys. Lett. 87, 031101 (2005). [CrossRef]

15

15. S. Hasegawa and Y. Hayasaki, “Holographic femtosecond laser processing with multiplexed phase fresnel lenses displayed on a liquid crystal spatial light modulator,” Opt. Rev. 14, 208–213 (2007). [CrossRef]

]. This technique, which is called holographic femtosecond laser processing, can also be directly applied to two-photon polymerization with the above advantages. Recently, parallel two-photon polymerization with a hologram has been demonstrated [16

16. L. Kelemen, S. Valkai, and P. Ormos, “Parallel photopolymerisation with complex light patterns generated by diffractive optical elements,” Opt. Express 15, 14488–14497 (2007). [CrossRef] [PubMed]

].

In the study described in this paper, we demonstrated a sparse exposure technique combining parallel exposure and scanning exposure. This technique improved the fabrication throughput and enabled simultaneous fabrication of linear structures with different widths. We also demonstrated the fabrication of space-variant structures by changing a CGH, as well as parallel fabrication of voxel structures with single femtosecond laser pulse irradiation.

2. Experimental setup

Figure 1 shows the experimental setup we used for holographic two-photon polymerization. The system mainly consisted of an amplified femtosecond laser system, a liquid-crystal spatial light modulator (LCSLM; Hamamatsu Photonics, PPM) [17

17. Y. Igasaki, F. Li, N. Yoshida, H. Toyoda, T. Inoue, N, Mukohzaka, Y. Kobayashi, and T. Hara, “High efficiency electrically-addressable phase-only spatial light modulator,” Opt. Rev. 6, 339–344 (1999). [CrossRef]

], and relay optics. The amplified femtosecond laser system consisted of a mode-locked Ti:sapphire laser (Spectra Physics, Tsunami) pumped by a diode-pumped, solid-state continuous-wave green laser (Spectra Physics, Millenia), and a pulsed Ti:sapphire regenerative amplifier (Spectra Physics, Spitfire) pumped by a diode-pumped, Q-switched Nd:YLF laser (Spectra Physics, Merlin). The femtosecond laser system generated pulses with a peak wavelength of λp=800 nm and a width of ~150 fs. The laser pulse, collimated by a beam expander, was diffracted by a CGH displayed on the LCSLM to form a fabrication pattern at the Fourier plane P of Lens 3. The 0-th order beam was obstructed at the plane P. The fabrication pattern was applied to the sample by reduction optics composed of Lens 4 and a 100× microscope objective lens (OL) with a numerical aperture (NA) of 1.25. The irradiation energy at the sample was given by the product of the energy measured before introducing the laser pulse into the OL in each experiment and the OL’s transmittance of 0.5 that was measured in advance. The axial and lateral processing positions of the sample were controlled by a three-dimensional motorized stage. A halogen lamp (HL) and a charge-coupled device (CCD) image sensor were used to observe the processing.

Fig. 1. Experimental setup.

The size of a pixel on the sample plane in the experimental setup, corresponding to that in the computer, was calculated. The CGH with 512×512 pixels was designed with the optimum rotation angle (ORA) method [18

18. J. Bengtsson, “Kinoform design with an optimal-rotation-angle method,” Appl. Opt. 33, 6879–6884 (1994). [CrossRef] [PubMed]

], with compensation for the spatial frequency response of the LCSLM [19

19. H. Takahashi, S. Hasegawa, and Y. Hayasaki, “Holographic femtosecond laser processing using optimalrotation-angle method with compensation of spatial frequency response of liquid crystal spatial light modulator,” Appl. Opt. 46, 5917–5923 (2007). [CrossRef] [PubMed]

,20

20. K. Chaen, H. Takahashi, S. Hasegawa, and Y. Hayasaki, “Display method with compensation of the spatial frequency response of a liquid crystal spatial light modulator for holographic femtosecond laser processing,” Opt. Commun. , 280, 165–172 (2007). [CrossRef]

], and was displayed on a W 2=13×13 mm2 area on the LCSLM. The focal length of the first Fourier transform lens L3 was F 3=600 mm, the position x of the diffraction beam from the grating with the maximum spatial frequency ν max of 19.2 line pairs/mm (lp/mm) was 9.22 mm, as calculated from xp F 3 ν max. Therefore, the size of a pixel on the plane P was 36 µm. Because the focal lengths of Lens 4 and OL were F 4=200 mm and F OL=1.9 mm, respectively, the pixel size on the sample plane was geometrically corresponding to p s=342 nm. The pixel size was an important system parameter because it decided the position resolution of fabricated structures. The beam radius at the pupil of the OL was 2.17 mm (=W/2×F 4/F 3), and the effective NA calculated from this beam radius was NAeff=1.14.

The sample was spin-coated negative photoresist (SU-8 3000, Microchem) with a film thickness of 7 µm. A scanning electron microscope (SEM; Hitachi, S4700) was used to observe the structures.

3. Experimental results

Figure 2 shows the experimental result of simultaneous microfabrication of line structures with different widths using the sparse-exposure technique. Figure 2(a) shows a CGH with 10 diffraction peaks. The minimum and maximum spatial frequencies were 1.59 and 2.99 lp/mm, respectively. Figure 2(b) shows its optical reconstruction observed on the plane P. The peak at the left in the picture is the 0th-order beam, which was obstructed when exposure was performed. Figure 2(c) shows an SEM image of the fabricated linear structure when the sample was exposed using the CGH, with lateral translation of the sample stage in the direction indicated by the arrow. The repetition of the laser pulses was 1kHz and the irradiation energy was 40 nJ/pulse. The scanning speed of the stage was 100 µm/s. The widths of the fabricated linear structures were 1.9 µm, 0.78 µm, and 3.6 µm from the top of the picture, respectively.

In this demonstration, the important technique was that the diffraction peaks were positioned sparsely to avoid interference between them. The distance between the diffraction beams should be sufficiently longer than the beam diameter. The pixel size on the sample plane was p s=342 nm, and the beam diameter was d Airy=856 nm, in terms of the Airy disk size calculated from NAeff and λp. In order to avoid overlapping of the central Airy disk, it is required that the adjacent diffraction peaks be spaced by more than 2.5 pixels (=d Airy/p s). The distance between the nearest peaks of the diffraction shown in Fig. 2(b) was 6 pixels; therefore, the diffraction peaks did not interfere. The number of pixels in the vertical direction of the sample motion, indicated by x, was 2. Because 2p s<d Airy, the linear structures exposed by the diffraction peaks joined the thick linear structures. The sparse exposure technique thus enabled simultaneous fabrication of linear structures with different widths.

Fig. 2. Sparse exposure technique. (a) CGH, (b) its optical reconstruction of the CGH, and (c) SEM image of three linear structures with different widths.

The width of the linear structure depends on the scanning speed and the energy of the diffraction peaks. The dependency was examined by using the CGH with ten diffraction peaks shown in Fig. 3(a). The minimum and maximum spatial frequencies of the diffraction peaks were 1.59 lp/mm and 4.96 lp/mm, respectively. Figure 3(b) shows the computer reconstruction and its intensity profile, and Fig. 3(c) shows the optical reconstruction and its intensity profile on the plane P. In the computer reconstruction, the uniformity U was 99.86%, and the diffraction efficiency η was 69.2%. In the optical reconstruction, U was 91% and η was 61%. Here, the uniformity is defined as U=I min/I max, where I min and I max are the minimum and the maximum peak intensities, respectively. The diffraction efficiency η is defined as the ratio of the 1st-order diffracted light intensity to the 0th-order light intensity when the LCSLM does not display a CGH. The degradation of U from the computer to the experimental reconstructions was caused by the incompleteness of the compensation for the spatial frequency response of the LCSLM in the computer [19

19. H. Takahashi, S. Hasegawa, and Y. Hayasaki, “Holographic femtosecond laser processing using optimalrotation-angle method with compensation of spatial frequency response of liquid crystal spatial light modulator,” Appl. Opt. 46, 5917–5923 (2007). [CrossRef] [PubMed]

,20

20. K. Chaen, H. Takahashi, S. Hasegawa, and Y. Hayasaki, “Display method with compensation of the spatial frequency response of a liquid crystal spatial light modulator for holographic femtosecond laser processing,” Opt. Commun. , 280, 165–172 (2007). [CrossRef]

].

Figures 4 show the optical reconstruction of a CGH used for fabricating supports on the plane P. The supports were applied to measure the size of the linear structures fabricated by the CGH by detaching them from a glass substrate. The use of the supports prevented to lose the fabricated structures during development. This technique was first demonstrated by Seet et al. [21

21. K. K. Seet, V. Mizeikis, S. Juodkazis, and H. Misawa, “Three-dimensional horizontal circular spiral photonic crystals with stop gaps below 1µm,” Appl. Phys. Lett. 88, 221101 (2006). [CrossRef]

]. For easy understanding, the center peak of the 0th-order beam was not obstructed when the picture in Fig. 4 was taken. Each of the thick supports was fabricated by the sparse exposure technique with scanning of the three diffraction beams.

Fig. 3. (a). CGH for generating ten beams, (b) its computer reconstruction, and (c) its optical reconstruction.
Fig. 4. Optical reconstruction of the CGH for fabrication of supports. The center peak is the 0-th order beam.

Figure 5 shows an SEM image of the ten linear structures with the four thick linear supports fabricated by the holographic two-photon polymerization. The ten linear structures were fabricated with a pulse repetition of 1kHz, an irradiation energy of 40 nJ/pulse, and a scanning speed of 100 µm/s. The supports were fabricated with an irradiation energy of 110 nJ/pulse and a scanning speed of 25 µm/s. They were separated from the glass substrate and supported with four thick linear structures so as not to be lost during development. The adjacent linear structures were contacted with the outsides of the supports in a drying process after the development [22

22. H. Segawa, S. Yamaguchi, Y. Yamazaki, T. Yano, S. Shibata, and H. Misawa, “Top-gathering pillar array of hybrid organic-inorganic material by means of self-organization,” Appl. Phys. A 83, 447–451 (2006). [CrossRef]

].

Figure 5(c) shows the width of the linear structure for an average irradiation energy of ten diffraction peaks. The filled circles, the filled triangles, and the rectangles indicate the widths of the linear structures fabricated when the stage speeds were 6.24 µm/s, 25 µm/s, and 100 µm/s, respectively. The solid curves were calculated by the equation d=w[ln(E/E th)]1/2, where w (=d Airy) is the beam diameter, E is the irradiation energy, and E th is the threshold energy for fabrication [21

21. K. K. Seet, V. Mizeikis, S. Juodkazis, and H. Misawa, “Three-dimensional horizontal circular spiral photonic crystals with stop gaps below 1µm,” Appl. Phys. Lett. 88, 221101 (2006). [CrossRef]

]. The values of E th were estimated as 0.8, 1.3, and 2.0 nJ/pulse, respectively. The minimum linear structure was 230 nm under an average irradiation energy of 1.0 nJ/pulse and a scanning speed of 6.24 µm/s, in our present experimental setup. When the scanning speed was low and the irradiation energy was high, the dependency of the width on the irradiation energy was larger than the value expected by the equation because of a micro explosion induced by the laser pulse. At the scanning speed of 6.24 µm/s, when the average irradiation energy was more than 3.0 nJ/pulse, a distorted complex structure was fabricated, and its width could not be measured.

Fig. 5. SEM images of ten linear structures with four thick linear supports fabricated by holographic two-photon polymerization. (a) Top and (b) oblique views. (c) The width of the linear structures for the average irradiation energy of ten diffraction peaks. The scanning speeds of the sample stage were 6.24 µm/s (circles), 25 µm/s (triangles), and 100 µm/s (squares), respectively.
Fig. 6. SEM images of two-dimensional structure formed by switching the 15 CGHs. (a) Top view and (b) oblique view.

Figure 6 is a demonstration of the holographic two-photon polymerization. Fifteen CGHs calculated in advance were switched at 2 Hz with a stage speed of 6.24 µm/s. When the CGH with 20 diffraction peaks, which was the maximum number in this experiment, was used, the pulse repetition was 1kHz and the irradiation energy was 70 nJ/pulse. When the number of diffraction peaks was small, the CGH was designed to ensure that the irradiation energy was 3.5 nJ/pulse per linear structure. The width of each structure was about 700 nm.

Figure 7 show the first demonstration of a voxel structure fabricated with single femtosecond laser pulse irradiation. The CGH generated ten diffraction peaks. The total irradiation energy was 150 nJ. The structures were fabricated while changing the axial focus position in the glass substrate. Figure 7(a) shows an oblique SEM image of the fabricated structures. When the focus was far from the substrate, the contact area between the fabricated voxel structure and the glass substrate became small, consequently, the fabricated voxel structure was pushed down and was washed out during development. On the other hand, when the focus was toward the inside of the glass substrate, the fabricated structure became small and eventually disappeared. Figure 7(b) shows 10 voxels with a diameter of ~400 nm, indicated by the arrow in Fig. 7(a). Figure 7(c) shows the voxel diameter for the average irradiation energy of ten diffraction peaks. Figure 7(d) shows the fabricated voxel when the irradiation energy was 10 nJ. The diameter was measured as shown in the figure. When the irradiation energy was more than 25 nJ, the fabricated structures were distorted by formation of a micro bubble, as shown in Fig. 7(e). The range of the irradiation energy for the fabrication of voxels was narrow, at only 10 to 25 nJ. As indicated by the solid curve, E th was estimated to be 8.0 nJ.

4. Conclusion

We demonstrated holographic two-photon polymerization using a sparse exposure technique based on a combination of parallel exposure and scanning exposure. The sparse exposure technique enabled the simultaneous fabrication of linear structures with different widths. The technique is expected to improve the throughput in large-scale fabrication. We also demonstrated fabrication of space-variant structures by changing a CGH, which is a major advantage of holographic two-photon polymerization. We further demonstrated parallel fabrication of voxel structures with single femtosecond laser pulse irradiation.

Fig. 7. (a). SEM image of ten voxels fabricated by a single laser pulse. (b). Close-up view of the region indicated by the arrow in (a). (c). The voxel diameter for the average irradiation energy of ten diffraction peaks. Close-up views of the voxels when E=10 nJ and 25 nJ, respectively.

Acknowledgments

This work was supported by The Murata Science Foundation, and The Asahi Glass Foundation, Amada Foundation for Metal Work Technology, and by a grant for Research for Promoting Technological Seeds from the Japan Science and Technology Agency, and Grant-in-Aid for Scientific Research (B) from the Ministry of Education, Culture, Sports, Science and Technology.

References and links

1.

S. Maruo, O. Nakamura, and S. Kawata, “Three-dimensional microfabrication with two-photon-absorbed photopolymerization,” Opt. Lett. 22, 132–134 (1997). [CrossRef] [PubMed]

2.

H. -B. Sun, S. Matsuo, and H. Misawa, “Three-dimensional photonic crystal structures achieved with two-photon-absorption photopolymerization of resin,” Appl. Phys. Lett. 74, 786–788 (1999). [CrossRef]

3.

H. -B. Sun, T. Tanaka, and S. Kawata, “Three-dimensional focal spots related to two-photon excitation,” Appl. Phys. Lett. 80, 3673–3675 (2002). [CrossRef]

4.

H. -B. Sun, M. Maeda, K. Takada, J. W. M. Chon, M. Gu, and S. Kawata, “Experimental investigation of single voxels for laser nanofabrication via two-photon photopolymerization,” Appl. Phys. Lett. 83, 819–821 (2003). [CrossRef]

5.

J. Serbin, A. Egbert, A. Ostendorf, B. N. Chickov, R. Houbertz, G. Domann, J. Schulz, C. Cronauer, L. Fröhlich, and M. Popall, “Femtosecond laser-induced two-photon polymerization of inorganic-organic hybrid materials for applications in photonics,” Opt. Lett. 28, 301–303 (2003). [CrossRef] [PubMed]

6.

V. Mizeikis, K. K. Seet, S. Juodkazis, and H. Misawa, “Three-dimensional woodpile photonic crystal templates for the infrared spectral range,” Opt. Lett. 29, 2061–2063 (2004). [CrossRef] [PubMed]

7.

S. H. Park, T. W. Lim, D. -Y. Yang, N. C. Cho, and K. -S. Lee, “Fabrication of a bunch of sub-30-nm nanofibers inside microchannels using photopolymerization via a long exposure technique,” Appl. Phys. Lett. 89, 173133 (2006). [CrossRef]

8.

D. Tan, Y. Li, F. Qi, H. Yang, Q. Gong, X. Dong, and X. Duan, “Reduction in feature size of two-photon polymerization using SCR500,” Appl. Phys. Lett. 90, 071106 (2007). [CrossRef]

9.

J. -F. Xing, X. -Z. Dong, W. -Q. Chen, X. -M. Duan, N. Takeyasu, T. Tanaka, and S. Kawata, “Improving spatial resolution of two-photon microfabrication by using photoinitiator with high initiating efficiency,” Appl. Phys. Lett. 90, 131106 (2007). [CrossRef]

10.

Y. Kuroiwa, N. Takeshima, Y. Narita, S. Tanaka, and K. Hirao, “Arbitrary micropatterning method in femtosecond laser microprocessing using diffractive optical elements,” Opt. Exp. 12, 1908–1915 (2004). [CrossRef]

11.

S. Matsuo, S. Juodkazis, and H. Misawa, “Femtosecond laser microfabrication of periodic structures using a microlens array,” Appl. Phys. A 80, 683–685 (2005). [CrossRef]

12.

J. Kato, N. Takeyasu, Y. Adachi, H. -B. Sun, and S. Kawata, “Multiple-spot parallel processing for laser micronanofabrication,” Appl. Phys. Lett. , 86, 044102 (2005). [CrossRef]

13.

Y. Hayasaki, T. Sugimoto, A. Takita, and N. Nishida, “Variable holographic femtosecond laser processing by use of a spatial light modulator,” Appl. Phys. Lett. 87, 031101 (2005). [CrossRef]

14.

S. Hasegawa, Y. Hayasaki, and N. Nishida, “Holographic femtosecond laser processing with multiplexed phase Fresnel lenses,” Opt. Lett. 31, 1705–1707 (2006). [CrossRef] [PubMed]

15.

S. Hasegawa and Y. Hayasaki, “Holographic femtosecond laser processing with multiplexed phase fresnel lenses displayed on a liquid crystal spatial light modulator,” Opt. Rev. 14, 208–213 (2007). [CrossRef]

16.

L. Kelemen, S. Valkai, and P. Ormos, “Parallel photopolymerisation with complex light patterns generated by diffractive optical elements,” Opt. Express 15, 14488–14497 (2007). [CrossRef] [PubMed]

17.

Y. Igasaki, F. Li, N. Yoshida, H. Toyoda, T. Inoue, N, Mukohzaka, Y. Kobayashi, and T. Hara, “High efficiency electrically-addressable phase-only spatial light modulator,” Opt. Rev. 6, 339–344 (1999). [CrossRef]

18.

J. Bengtsson, “Kinoform design with an optimal-rotation-angle method,” Appl. Opt. 33, 6879–6884 (1994). [CrossRef] [PubMed]

19.

H. Takahashi, S. Hasegawa, and Y. Hayasaki, “Holographic femtosecond laser processing using optimalrotation-angle method with compensation of spatial frequency response of liquid crystal spatial light modulator,” Appl. Opt. 46, 5917–5923 (2007). [CrossRef] [PubMed]

20.

K. Chaen, H. Takahashi, S. Hasegawa, and Y. Hayasaki, “Display method with compensation of the spatial frequency response of a liquid crystal spatial light modulator for holographic femtosecond laser processing,” Opt. Commun. , 280, 165–172 (2007). [CrossRef]

21.

K. K. Seet, V. Mizeikis, S. Juodkazis, and H. Misawa, “Three-dimensional horizontal circular spiral photonic crystals with stop gaps below 1µm,” Appl. Phys. Lett. 88, 221101 (2006). [CrossRef]

22.

H. Segawa, S. Yamaguchi, Y. Yamazaki, T. Yano, S. Shibata, and H. Misawa, “Top-gathering pillar array of hybrid organic-inorganic material by means of self-organization,” Appl. Phys. A 83, 447–451 (2006). [CrossRef]

OCIS Codes
(090.1760) Holography : Computer holography
(090.2890) Holography : Holographic optical elements
(140.7090) Lasers and laser optics : Ultrafast lasers
(220.4000) Optical design and fabrication : Microstructure fabrication
(230.6120) Optical devices : Spatial light modulators
(220.4241) Optical design and fabrication : Nanostructure fabrication

ToC Category:
Holography

History
Original Manuscript: August 1, 2008
Revised Manuscript: September 16, 2008
Manuscript Accepted: September 22, 2008
Published: October 2, 2008

Citation
Hidetomo Takahashi, Satoshi Hasegawa, Akihiro Takita, and Yoshio Hayasaki, "Sparse-exposure technique in holographic two-photon polymerization," Opt. Express 16, 16592-16599 (2008)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-16-21-16592


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. S. Maruo, O. Nakamura, and S. Kawata, "Three-dimensional microfabrication with two-photon-absorbed photopolymerization," Opt. Lett. 22, 132-134 (1997). [CrossRef] [PubMed]
  2. H. -B. Sun, S. Matsuo, and H. Misawa, "Three-dimensional photonic crystal structures achieved with two-photon-absorption photopolymerization of resin," Appl. Phys. Lett. 74, 786-788 (1999). [CrossRef]
  3. H. -B. Sun, T. Tanaka, and S. Kawata, "Three-dimensional focal spots related to two-photon excitation," Appl. Phys. Lett. 80, 3673-3675 (2002). [CrossRef]
  4. H. -B. Sun, M. Maeda, K. Takada, J. W. M. Chon, M. Gu, and S. Kawata, "Experimental investigation of single voxels for laser nanofabrication via two-photon photopolymerization," Appl. Phys. Lett. 83, 819-821 (2003). [CrossRef]
  5. J. Serbin, A. Egbert, A. Ostendorf, B. N. Chickov, R. Houbertz, G. Domann, J. Schulz, C. Cronauer, L. Fröhlich, and M. Popall, "Femtosecond laser-induced two-photon polymerization of inorganic-organic hybrid materials for applications in photonics," Opt. Lett. 28, 301-303 (2003). [CrossRef] [PubMed]
  6. V. Mizeikis, K. K. Seet, S. Juodkazis, and H. Misawa, "Three-dimensional woodpile photonic crystal templates for the infrared spectral range," Opt. Lett. 29, 2061-2063 (2004). [CrossRef] [PubMed]
  7. S. H. Park, T. W. Lim, D. -Y. Yang, N. C. Cho, and K. -S. Lee, "Fabrication of a bunch of sub-30-nm nanofibers inside microchannels using photopolymerization via a long exposure technique," Appl. Phys. Lett. 89, 173133 (2006). [CrossRef]
  8. D. Tan, Y. Li, F. Qi, H. Yang, Q. Gong, X. Dong, and X. Duan, "Reduction in feature size of two-photon polymerization using SCR500," Appl. Phys. Lett. 90, 071106 (2007). [CrossRef]
  9. J. -F. Xing, X. -Z. Dong, W. -Q. Chen, X. -M. Duan, N. Takeyasu, T. Tanaka, and S. Kawata, "Improving spatial resolution of two-photon microfabrication by using photoinitiator with high initiating efficiency," Appl. Phys. Lett. 90, 131106 (2007). [CrossRef]
  10. Y. Kuroiwa, N. Takeshima, Y. Narita, S. Tanaka, and K. Hirao, "Arbitrary micropatterning method in femtosecond laser microprocessing using diffractive optical elements," Opt. Express 12, 1908-1915 (2004). [CrossRef]
  11. S. Matsuo, S. Juodkazis, and H. Misawa, "Femtosecond laser microfabrication of periodic structures using a microlens array," Appl. Phys. A 80, 683-685 (2005). [CrossRef]
  12. J. Kato, N. Takeyasu, Y. Adachi, H. -B. Sun, and S. Kawata, "Multiple-spot parallel processing for laser micronanofabrication," Appl. Phys. Lett. 86, 044102 (2005). [CrossRef]
  13. Y. Hayasaki, T. Sugimoto, A. Takita, and N. Nishida, "Variable holographic femtosecond laser processing by use of a spatial light modulator," Appl. Phys. Lett. 87, 031101 (2005). [CrossRef]
  14. S. Hasegawa, Y. Hayasaki, and N. Nishida, "Holographic femtosecond laser processing with multiplexed phase Fresnel lenses," Opt. Lett. 31, 1705-1707 (2006). [CrossRef] [PubMed]
  15. S. Hasegawa and Y. Hayasaki, "Holographic femtosecond laser processing with multiplexed phase fresnel lenses displayed on a liquid crystal spatial light modulator," Opt. Rev. 14, 208-213 (2007). [CrossRef]
  16. L. Kelemen, S. Valkai, and P. Ormos, "Parallel photopolymerisation with complex light patterns generated by diffractive optical elements," Opt. Express 15, 14488-14497 (2007). [CrossRef] [PubMed]
  17. Y. Igasaki, F. Li, N. Yoshida, H. Toyoda, T. Inoue, N, Mukohzaka, Y. Kobayashi, and T. Hara, "High efficiency electrically-addressable phase-only spatial light modulator," Opt. Rev. 6, 339-344 (1999). [CrossRef]
  18. J. Bengtsson, "Kinoform design with an optimal-rotation-angle method," Appl. Opt. 33, 6879-6884 (1994). [CrossRef] [PubMed]
  19. H. Takahashi, S. Hasegawa, and Y. Hayasaki, "Holographic femtosecond laser processing using optimal-rotation-angle method with compensation of spatial frequency response of liquid crystal spatial light modulator," Appl. Opt. 46, 5917-5923 (2007). [CrossRef] [PubMed]
  20. K. Chaen, H. Takahashi, S. Hasegawa, and Y. Hayasaki, "Display method with compensation of the spatial frequency response of a liquid crystal spatial light modulator for holographic femtosecond laser processing," Opt. Commun. 280, 165-172 (2007). [CrossRef]
  21. K. K. Seet, V. Mizeikis, S. Juodkazis, and H. Misawa, "Three-dimensional horizontal circular spiral photonic crystals with stop gaps below 1μm," Appl. Phys. Lett. 88, 221101 (2006). [CrossRef]
  22. H. Segawa, S. Yamaguchi, Y. Yamazaki, T. Yano, S. Shibata, and H. Misawa, "Top-gathering pillar array of hybrid organic-inorganic material by means of self-organization," Appl. Phys. A 83, 447-451 (2006). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.