V3+:YAG as the saturable absorber for a diode-pumped quasi-three-level dual-wavelength Nd:GGG laser

Hai-Tao Huang, Jing-Liang He, Bai-Tao Zhang, Jian-Fei Yang, Jin-Long Xu, Chun-Hua Zuo, and Xu-Tang Tao  »View Author Affiliations


Optics Express, Vol. 18, Issue 4, pp. 3352-3357 (2010)
http://dx.doi.org/10.1364/OE.18.003352


View Full Text Article

Acrobat PDF (273 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

The performance of a diode-end-pumped passively Q-switched dual-wavelength Nd:GGG laser operating at 932.9 and 936.5nm with V3+:YAG as the saturable absorber was demonstrated for the first time to the best of our knowledge. The maximum dual-wavelength average output power of 150mW was achieved with a T = 2% output coupler under the absorbed pump power of 2.55W, corresponding to the optical-to-optical conversion and slope efficiency of 5.9% and 8.0%, respectively. The minimum pulse width was 395ns with the pulse repetition frequency of 140kHz, which was attained with a T = 5% output coupler under the absorbed pump power of 2.55W.

© 2010 OSA

1. Introduction

Yttrium-Aluminum Garnet doped with three-valence vanadium (V3+:YAG) has attracted great interest due to the excellent optical, mechanical and thermal properties, which give an opportunity to design compact and reliable pulsed laser sources. The V3+ ions can occupy both tetrahedrally and octahedrally coordinated positions, which make V3+:YAG have different absorption peaks [1

1. M. J. Weber and L. A. Riseberg, “Optical Spectra of Vanadium Ions in Yttrium Aluminum Garnet,” J. Chem. Phys. 55(5), 2032–2038 (1971). [CrossRef]

,2

2. K. V. Yumashev, N. V. Kuleshov, A. M. Malyarevich, P. V. Prokoshin, V. G. Shcherbitsky, N. N. Posnov, V. P. Mikhailov, and V. A. Sandulenko, “Ultrafast dynamics of excited-state absorption in V3+:YAG crystal,” J. Appl. Phys. 80(8), 4782–4784 (1996). [CrossRef]

]. The tetrahedrally coordinated V3+ ions contribute to the peaks at 800, 1140 and 1320nm, corresponding to the 3A2-3T1 (3F), 3A2-1E (1D) and 3A2-3T2 (3F) transitions, respectively. Therefore it is this co-ordination of the ions that is important for the action of the passive Q-switching at 1.0 and 1.3μm. The peak at 425nm is assigned to the 3T1 (3F)-3T2 (3P) transition of V3+ ion in octahedral position of garnet lattice [3

3. D. Zhang, L. Su, H. Li, X. Qian, and J. Xu, “Characteristics and optical spectra of V:YAG crystal grown in reducing atmosphere,” J. Cryst. Growth 294(2), 437–441 (2006). [CrossRef]

]. Due to the extremely high ground state absorption cross-section (3.0 × 10−18cm2 at 1064nm, 7.2 × 10−18cm2 at 1342nm) and nearly negligible excite state absorption [4

4. A. M. Malyarevich, I. A. Denisov, K. V. Yumashev, V. P. Mikhailov, R. S. Conroy, and B. D. Sinclair, “V:YAG-a new passive Q-switch for diode-pumped solid-state lasers,” Appl. Phys. B 67(5), 555–558 (1998). [CrossRef]

], V3+:YAG has been successfully exploited in the efficient Q-switching of Nd3+-doped lasers emitting at 1.0 and 1.3μm [5

5. P. Tidemand-Lichtenberg, J. Janousek, R. Melich, J. L. Mortensen, and P. Buchhave, “Synchronization of 1064 and 1342 nm pulses using passive saturable absorbers,” Opt. Commun. 241(4-6), 487–492 (2004). [CrossRef]

7

7. H.-T. Huang, B.-T. Zhang, J.-L. He, J.-F. Yang, J.-L. Xu, X.-Q. Yang, C.-H. Zuo, and S. Zhao, “Diode-pumped passively Q-switched Nd:Gd0.5Y0.5VO4 laser at 1.34 microm with V3+:YAG as the saturable absorber,” Opt. Express 17(9), 6946–6951 (2009), http://www.opticsinfobase.org/abstract.cfm?URI=oe-17-9-6946. [CrossRef] [PubMed]

]. Q-switching and passive mode-locking for the solid state lasers with wavelengths at 747nm, 780nm have also been obtained with V3+:YAG saturable absorber [8

8. V. P. Mikhailov, N. V. Kuleshov, N. I. Zhavoronkov, P. V. Prokohsin, K. V. Yumashev, and V. A. Sandulenko, “Optical absorption and nonlinear transmission of tetrahedral V3+ (d2) in yttrium aluminum garnet,” Opt. Mater. 2(4), 267–272 (1993). [CrossRef]

]. However, to the best of our knowledge, there is no report on the pulsed laser at 0.9μm using V3+:YAG as the saturable absorber. According to the absorption spectrum of V3+:YAG presented in Ref [4

4. A. M. Malyarevich, I. A. Denisov, K. V. Yumashev, V. P. Mikhailov, R. S. Conroy, and B. D. Sinclair, “V:YAG-a new passive Q-switch for diode-pumped solid-state lasers,” Appl. Phys. B 67(5), 555–558 (1998). [CrossRef]

], the broad absorption band near infrared covers the water vapor absorption region ranging from 930 to 960nm [9

9. K. Cynthia, Williamson, Syed Ismail, Edward V. Browell, “Spectroscopy of water vapor in the 930nm to 960 nm spectral region,” Quantum Electronics and Laser Science Conference, 1999. QELS '99, p.249.

,10

10. D. Lisak and J. T. Hodges, “Low-uncertainty H2O line intensities for the 930-nm region,” J. Mol. Spectrosc. 249(1), 6–13 (2008). [CrossRef]

]. Therefore, the pulsed laser at 940nm region by exploiting V3+:YAG as the saturable absorber can be a promising source for the differential absorption lidar in water vapor detection.

Nd3+-doped Gadolinium gallium garnet (Nd:GGG) has many advantages suitable for the diode pumping, such as good thermal conductivity, good mechanical properties, and wide absorption band near 808nm. Due to that Nd3+ substituting Gd3+ has only weak concentration quenching; the concentration of Nd3+ in GGG can reach to 4% or even higher. Furthermore, the Nd:GGG crystal can be grown core-free in larger size with superior optical quality [11

11. K. Yoshida, H. Yoshida, and Y. Kato, “Characterization of high average power Nd:GGG slab lasers,” IEEE J. Quantum Electron. 24(6), 1188–1192 (1988). [CrossRef]

,12

12. Z. Jia, X. T. Tao, C. Dong, X. Cheng, W. Zhang, F. Xu, and M. Jiang, “Study on crystal growth of large size Nd3+:Gd3Ga5O12 (Nd3+:GGG) by Czochralski method,” J. Cryst. Growth 292(2), 386–390 (2006). [CrossRef]

]. The diode-pumped Nd:GGG lasers emitting at 1.06 and 1.33μm have been studied widely [13

13. L. J. Qin, D. Y. Tang, G. Q. Xie, H. Luo, C. M. Dong, Z. T. Jia, H. H. Yu, and X. T. Tao, “Diode-end-pumped passively mode-locked Nd:GGG laser with a semiconductor saturable mirror,” Opt. Commun. 281(18), 4762–4764 (2008). [CrossRef]

,14

14. C.-H. Zuo, B.-T. Zhang, J.-L. He, X.-L. Dong, J.-F. Yang, H.-T. Huang, J.-L. Xu, S. Zhao, C.-M. Dong, and X.-T. Tao, “CW and passive Q-switching of 1331-nm Nd:GGG laser with Co2+:LMA saturable absorber,” Appl. Phys. B 95(1), 75–80 (2009). [CrossRef]

].The quasi-three-level operation of Nd:GGG induced by the Nd3+ transition of 4F3/2-4I9/2 emits at 940nm region, overlapping the absorption peaks of water vapor. Zhang Chun-Yu et.al have reported the continuous-wave laser operation of a diode pumped 1.6 at. % Nd:GGG laser at 938nm, with 620mW output power obtained at the incident pump power of 5.0W [15

15. Z. Chun-Yu, G. Chun-Qing, Z. Ling, W. Zhi-Yi, and Z. Zhi-Guo, “Laser Performance of Nd:GGG Operating at 938 nm,” Chin. Phys. Lett. 24(2), 440–441 (2007). [CrossRef]

].

In this paper, a diode-end-pumped passively Q-switched dual-wavelength Nd:GGG laser operating at 932.9 and 936.5nm with V3+:YAG as the saturable absorber was realized in a simple linear cavity. The maximum dual-wavelength average output power of 150mW was achieved with a T = 2% output coupler under the absorbed pump power of 2.55W, corresponding to the optical-to-optical conversion and slope efficiency of 5.9% and 8.0%, respectively. The minimum pulse width was 395ns with the pulse repetition frequency of 140kHz, which was attained with a T = 5% output coupler under the absorbed pump power of 2.55W.

2. Experimental setup

3. Experimental results and analysis

In the quasi-three-level operation, a thin laser crystal could reduce the loss induced by the reabsorption of the lower laser state. However, this would inevitably lower the absorption of laser crystal at the pump radiation. For the 1.2mm long and 1.0at.% Nd:GGG exploited in our experiment, the absorption efficiency at the 808nm was measured to be about 40%, corresponding to the absorption coefficient of 4.3cm−1. To make an accurate evaluation of the performance of Nd:GGG laser, the absorbed pump power was introduced in the following discussion. The continuous-wave operation of the Nd:GGG laser was performed firstly. The dependence of output power on the absorbed pump power for different output couplers was given in Fig. 2
Fig. 2 The output power including the continuous-wave and pulsed operation versus the absorbed pump power.
. As could be seen, when the output couplers T = 2% and T = 5% were exploited, the maximum output powers of 430 and 360mW were respectively obtained under the absorbed pump power of 3.3W, with the threshold pump powers of 0.54 and 0.85W, respectively. The corresponding optical-to-optical conversion efficiency for the said two situations were estimated to be respectively 13.0% and 10.9%, with the slope efficiency estimated to be 15.6% and 14.7%, respectively. According to the measured threshold pump power under different output couplers, the Findlay–Clay analysis could be performed to deduce the intracavity passive losses in the current resonator, with the value estimated to be ~1.8%. The high quality Nd:GGG as well as optimized resonator (to enhance the overlap efficiency between the lasing mode and the pump volume) were expected to be used to improve the CW quasi-three-level laser performance.

By inserting the V3+:YAG into the cavity adopted in the continuous-wave operation, the passive Q-switching operation of the Nd:GGG laser was realized, with the relationship between the average output power and absorbed pump power also shown in Fig. 2. The best performance was obtained with the T = 2% output coupler. The maximum average output power of 150mW was achieved under the absorbed pump power of 2.55W, corresponding to optical-to-optical conversion and slope efficiency of 5.9% and 8.0%, respectively. The fluctuation at the average output power 150mW over hours-long operation was found to be less than 1.5%. For the other situation, 100mW average output power was obtained under the same pump power, with the threshold pump power of 1.24W. In our experiment, the efficient and stable passive Q-switching operation of Nd:GGG/V3+:YAG laser could be readily achieved in a short plano-concave resonator, which could be attributed to three factors: the smaller stimulated emission cross-section of Nd:GGG at 0.93μm, the relatively larger ground state absorption cross-section and nearly negligible excited state absorption cross-section of V3+:YAG. This looses control on the ratio of the effective mode area in the gain medium to that in the absorber.

A fiber-coupled spectrometer with a resolution of 0.75nm (HR4000CG-UV-NTR Ocean Optics) was used for the spectral measurements. Figure 3
Fig. 3 The laser emission spectrum of the Nd:GGG/V3+:YAG laser with the inset displaying the 2D beam spatial profile.
presented the laser emission spectrum for the pulsed Nd:GGG laser with 150mW output power. As could be seen, the laser emitted at dual-wavelength locating at 932.9 and 936.5nm. It was further found that the two modes had almost the same thresholds. Ref [15

15. Z. Chun-Yu, G. Chun-Qing, Z. Ling, W. Zhi-Yi, and Z. Zhi-Guo, “Laser Performance of Nd:GGG Operating at 938 nm,” Chin. Phys. Lett. 24(2), 440–441 (2007). [CrossRef]

] has reported that two fluorescence emission peaks at 934 and 938nm was obtained with a 1.6at.% Nd:GGG, which make the Nd:GGG have the potential to operate at dual-wavelength. However, only one wavelength at 936.5nm was observed in our continuous-wave Nd:GGG laser. Once one mode oscillated in the continuous-wave operation, the residual inversion population density would be too low to sustain the other mode reaching the threshold. The greatly increased inversion population density induced by the Q-switching operation of V3+:YAG gave the other wavelength (932.9nm) an opportunity to oscillate, which consequently result in the simultaneously dual-wavelength operation. The passively Q-switched simultaneously dual-wavelength laser should be possible to be used as a source for the generation of terahertz radiation. Considering the little difference in the spectral response of spectrometer at the two neighboring wavelengths, the output power ratio of the two wavelengths could be estimated by comparing the spectral intensity of the two wavelengths. It was found that the spectral intensity ratio of the two wavelengths was nearly unchanged with increasing the pump power. The corresponding value was 0.72:1 for 932.9:936.5nm. So the maximum output power at 932.9 and 936.5nm were estimated to be 63 and 87mW, respectively. The beam spatial profile at the average output power 150mW was also measured by using a laser beam analyzer (Spiricon), with the image displayed in the inset of Fig. 3.

The relationship between the pulse repetition frequency (PRF) and the absorbed pump power was displayed in Fig. 4(a)
Fig. 4 (a) The pulse repetition frequency versus the absorbed pump powe; (b) the pulse widths versus the absorbed pump power.
. It was found that the PRF increased with the pump powers. When T = 2% output coupler was used, the PRF presented the variations of 61-136 kHz with the pump power increasing from 1.24 to 2.55W. For the other situation, the PRF increased from 80 to 140kHz with the increase of pump power from 1.6 to 2.55W. The high PRF induced by the V3+:YAG has also been observed in the passively Q-switched lasers at 1.34μm [6

6. F. Q. Liu, J. L. He, B. T. Zhang, J. L. Xu, X. L. Dong, K. J. Yang, H. R. Xia, and H. J. Zhang, “Diode-pumped passively Q-switched Nd:LuVO4 laser at 1.34μm with a V3+:YAG saturable absorber,” Opt. Express 16, 1759–11763 (2008), http://www.opticsinfobase.org/abstract.cfm?URI=oe-16-16-11759.

,7

7. H.-T. Huang, B.-T. Zhang, J.-L. He, J.-F. Yang, J.-L. Xu, X.-Q. Yang, C.-H. Zuo, and S. Zhao, “Diode-pumped passively Q-switched Nd:Gd0.5Y0.5VO4 laser at 1.34 microm with V3+:YAG as the saturable absorber,” Opt. Express 17(9), 6946–6951 (2009), http://www.opticsinfobase.org/abstract.cfm?URI=oe-17-9-6946. [CrossRef] [PubMed]

], which should be attributed to the short absorption recovery time and low saturable energy intensity of V3+:YAG.

Figure 4(b) depicted the pulse widths versus the absorbed pump powers for the two output couplers. As could be seen, the pulse width for the T = 2% output coupler firstly decreased to 522ns with increasing the pump power to 2.23W, and then slightly increased with the pump power. For the Q-switched lasers, when the PRF achieved such a high value that the initial inversion population could not be fully consumed during the interval when the Q-switch was turned on, the rise time of a pulse would be extended, resulting in the generation of stretched pulses. So the slight increase of the pulse widths was observed in our experiment. The minimum pulse width of 395ns with the PRF of 140kHz was attained with the T = 5% output coupler under the absorbed pump power of 2.55W. The temporal pulse profiles for the above situation, along with the corresponding train of pulses, were shown in Fig. 5(a)
Fig. 5 (a) The temporal pulse profile taken at the absorbed pump power of 2.55W with T = 5% output coupler exploited; (b) the corresponding pulse train.
and 5(b), respectively. Compared with the previously published results on the passively Q-switched lasers at 0.9μm obtained with Nd,Cr:YAG, Cr4+:YAG or SESAM [16

16. K. He, C. Gao, Z. Wei, D. Li, Z. Zhang, H. J. Zhang, and J. Wang, “Diode-pumped passively Q-switched Nd:LuVO4 laser at 916nm,” Opt. Commun. 282(12), 2413–2416 (2009). [CrossRef]

18

18. Y. P. Huang, K. W. Su, A. Li, Y. F. Chen, and K. F. Huang, “High-peak-power passively Q-switched Nd:YAG laser at 946nm,” Appl. Phys. B 91(3-4), 429–432 (2008). [CrossRef]

], the 395ns pulse width was obviously large. This should be attributed to the low pump power available and over 100kHz PRF generated by the pulsed Nd:GGG/V3+:YAG laser.

4. Conclusions

In summary, a diode-pumped quasi-three-level dual-wavelength Nd:GGG laser with V3+:YAG as the saturable absorber was demonstrated in this paper. The maximum continuous-wave output power of 430mW at 936.5nm was achieved with the T = 2% output coupler under the absorbed pump power of 3.3W. As for the passive Q-switching operation, the simultaneously dual-wavelength operation at 932.9 and 936.5nm was realized. The maximum dual-wavelength average output power of 150mW was obtained with the T = 2% output coupler, corresponding to the optical-to-optical conversion and slope efficiency of 5.9% and 8.0%, respectively. The minimum pulse width was 395ns with the pulse repetition frequency of 140kHz, which was attained with a T = 5% output coupler under the absorbed pump power of 2.55W.

Acknowledgements

This work was supported by the National Natural Science Foundation of China (No: 60878012, and 50721002), the Grander Independent Innovation Project of Shandong Province Grant No: 2006GG1103047, and Program for Taishan Scholars. He Jing-Liang’s e-mail address is jlhe@sdu.edu.cn.

References and links

1.

M. J. Weber and L. A. Riseberg, “Optical Spectra of Vanadium Ions in Yttrium Aluminum Garnet,” J. Chem. Phys. 55(5), 2032–2038 (1971). [CrossRef]

2.

K. V. Yumashev, N. V. Kuleshov, A. M. Malyarevich, P. V. Prokoshin, V. G. Shcherbitsky, N. N. Posnov, V. P. Mikhailov, and V. A. Sandulenko, “Ultrafast dynamics of excited-state absorption in V3+:YAG crystal,” J. Appl. Phys. 80(8), 4782–4784 (1996). [CrossRef]

3.

D. Zhang, L. Su, H. Li, X. Qian, and J. Xu, “Characteristics and optical spectra of V:YAG crystal grown in reducing atmosphere,” J. Cryst. Growth 294(2), 437–441 (2006). [CrossRef]

4.

A. M. Malyarevich, I. A. Denisov, K. V. Yumashev, V. P. Mikhailov, R. S. Conroy, and B. D. Sinclair, “V:YAG-a new passive Q-switch for diode-pumped solid-state lasers,” Appl. Phys. B 67(5), 555–558 (1998). [CrossRef]

5.

P. Tidemand-Lichtenberg, J. Janousek, R. Melich, J. L. Mortensen, and P. Buchhave, “Synchronization of 1064 and 1342 nm pulses using passive saturable absorbers,” Opt. Commun. 241(4-6), 487–492 (2004). [CrossRef]

6.

F. Q. Liu, J. L. He, B. T. Zhang, J. L. Xu, X. L. Dong, K. J. Yang, H. R. Xia, and H. J. Zhang, “Diode-pumped passively Q-switched Nd:LuVO4 laser at 1.34μm with a V3+:YAG saturable absorber,” Opt. Express 16, 1759–11763 (2008), http://www.opticsinfobase.org/abstract.cfm?URI=oe-16-16-11759.

7.

H.-T. Huang, B.-T. Zhang, J.-L. He, J.-F. Yang, J.-L. Xu, X.-Q. Yang, C.-H. Zuo, and S. Zhao, “Diode-pumped passively Q-switched Nd:Gd0.5Y0.5VO4 laser at 1.34 microm with V3+:YAG as the saturable absorber,” Opt. Express 17(9), 6946–6951 (2009), http://www.opticsinfobase.org/abstract.cfm?URI=oe-17-9-6946. [CrossRef] [PubMed]

8.

V. P. Mikhailov, N. V. Kuleshov, N. I. Zhavoronkov, P. V. Prokohsin, K. V. Yumashev, and V. A. Sandulenko, “Optical absorption and nonlinear transmission of tetrahedral V3+ (d2) in yttrium aluminum garnet,” Opt. Mater. 2(4), 267–272 (1993). [CrossRef]

9.

K. Cynthia, Williamson, Syed Ismail, Edward V. Browell, “Spectroscopy of water vapor in the 930nm to 960 nm spectral region,” Quantum Electronics and Laser Science Conference, 1999. QELS '99, p.249.

10.

D. Lisak and J. T. Hodges, “Low-uncertainty H2O line intensities for the 930-nm region,” J. Mol. Spectrosc. 249(1), 6–13 (2008). [CrossRef]

11.

K. Yoshida, H. Yoshida, and Y. Kato, “Characterization of high average power Nd:GGG slab lasers,” IEEE J. Quantum Electron. 24(6), 1188–1192 (1988). [CrossRef]

12.

Z. Jia, X. T. Tao, C. Dong, X. Cheng, W. Zhang, F. Xu, and M. Jiang, “Study on crystal growth of large size Nd3+:Gd3Ga5O12 (Nd3+:GGG) by Czochralski method,” J. Cryst. Growth 292(2), 386–390 (2006). [CrossRef]

13.

L. J. Qin, D. Y. Tang, G. Q. Xie, H. Luo, C. M. Dong, Z. T. Jia, H. H. Yu, and X. T. Tao, “Diode-end-pumped passively mode-locked Nd:GGG laser with a semiconductor saturable mirror,” Opt. Commun. 281(18), 4762–4764 (2008). [CrossRef]

14.

C.-H. Zuo, B.-T. Zhang, J.-L. He, X.-L. Dong, J.-F. Yang, H.-T. Huang, J.-L. Xu, S. Zhao, C.-M. Dong, and X.-T. Tao, “CW and passive Q-switching of 1331-nm Nd:GGG laser with Co2+:LMA saturable absorber,” Appl. Phys. B 95(1), 75–80 (2009). [CrossRef]

15.

Z. Chun-Yu, G. Chun-Qing, Z. Ling, W. Zhi-Yi, and Z. Zhi-Guo, “Laser Performance of Nd:GGG Operating at 938 nm,” Chin. Phys. Lett. 24(2), 440–441 (2007). [CrossRef]

16.

K. He, C. Gao, Z. Wei, D. Li, Z. Zhang, H. J. Zhang, and J. Wang, “Diode-pumped passively Q-switched Nd:LuVO4 laser at 916nm,” Opt. Commun. 282(12), 2413–2416 (2009). [CrossRef]

17.

Q. Li, B. Feng, D. Zhang, Z. Zhang, H. Zhang, and J. Wang, “Q-switched 935 nm Nd:CNGG laser,” Appl. Opt. 48(10), 1898–1903 (2009), http://www.opticsinfobase.org/abstract.cfm?URI=ao-48-10-1898. [CrossRef] [PubMed]

18.

Y. P. Huang, K. W. Su, A. Li, Y. F. Chen, and K. F. Huang, “High-peak-power passively Q-switched Nd:YAG laser at 946nm,” Appl. Phys. B 91(3-4), 429–432 (2008). [CrossRef]

OCIS Codes
(140.3480) Lasers and laser optics : Lasers, diode-pumped
(140.3530) Lasers and laser optics : Lasers, neodymium
(140.3540) Lasers and laser optics : Lasers, Q-switched

ToC Category:
Lasers and Laser Optics

History
Original Manuscript: September 17, 2009
Revised Manuscript: January 19, 2010
Manuscript Accepted: January 21, 2010
Published: February 2, 2010

Citation
Hai-Tao Huang, Jing-Liang He, Bai-Tao Zhang, Jian-Fei Yang, Jin-Long Xu, Chun-Hua Zuo, and Xu-Tang Tao, "V3+:YAG as the saturable absorber for a diode-pumped quasi-three-level dual-wavelength Nd:GGG laser," Opt. Express 18, 3352-3357 (2010)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-18-4-3352


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. M. J. Weber and L. A. Riseberg, “Optical Spectra of Vanadium Ions in Yttrium Aluminum Garnet,” J. Chem. Phys. 55(5), 2032–2038 (1971). [CrossRef]
  2. K. V. Yumashev, N. V. Kuleshov, A. M. Malyarevich, P. V. Prokoshin, V. G. Shcherbitsky, N. N. Posnov, V. P. Mikhailov, and V. A. Sandulenko, “Ultrafast dynamics of excited-state absorption in V3+:YAG crystal,” J. Appl. Phys. 80(8), 4782–4784 (1996). [CrossRef]
  3. D. Zhang, L. Su, H. Li, X. Qian, and J. Xu, “Characteristics and optical spectra of V:YAG crystal grown in reducing atmosphere,” J. Cryst. Growth 294(2), 437–441 (2006). [CrossRef]
  4. A. M. Malyarevich, I. A. Denisov, K. V. Yumashev, V. P. Mikhailov, R. S. Conroy, and B. D. Sinclair, “V:YAG-a new passive Q-switch for diode-pumped solid-state lasers,” Appl. Phys. B 67(5), 555–558 (1998). [CrossRef]
  5. P. Tidemand-Lichtenberg, J. Janousek, R. Melich, J. L. Mortensen, and P. Buchhave, “Synchronization of 1064 and 1342 nm pulses using passive saturable absorbers,” Opt. Commun. 241(4-6), 487–492 (2004). [CrossRef]
  6. F. Q. Liu, J. L. He, B. T. Zhang, J. L. Xu, X. L. Dong, K. J. Yang, H. R. Xia, and H. J. Zhang, “Diode-pumped passively Q-switched Nd:LuVO4 laser at 1.34μm with a V3+:YAG saturable absorber,” Opt. Express 16, 1759–11763 (2008), http://www.opticsinfobase.org/abstract.cfm?URI=oe-16-16-11759 .
  7. H.-T. Huang, B.-T. Zhang, J.-L. He, J.-F. Yang, J.-L. Xu, X.-Q. Yang, C.-H. Zuo, and S. Zhao, “Diode-pumped passively Q-switched Nd:Gd0.5Y0.5VO4 laser at 1.34 microm with V3+:YAG as the saturable absorber,” Opt. Express 17(9), 6946–6951 (2009), http://www.opticsinfobase.org/abstract.cfm?URI=oe-17-9-6946 . [CrossRef] [PubMed]
  8. V. P. Mikhailov, N. V. Kuleshov, N. I. Zhavoronkov, P. V. Prokohsin, K. V. Yumashev, and V. A. Sandulenko, “Optical absorption and nonlinear transmission of tetrahedral V3+ (d2) in yttrium aluminum garnet,” Opt. Mater. 2(4), 267–272 (1993). [CrossRef]
  9. K. Cynthia, Williamson, Syed Ismail, Edward V. Browell, “Spectroscopy of water vapor in the 930nm to 960 nm spectral region,” Quantum Electronics and Laser Science Conference, 1999. QELS '99, p.249.
  10. D. Lisak and J. T. Hodges, “Low-uncertainty H2O line intensities for the 930-nm region,” J. Mol. Spectrosc. 249(1), 6–13 (2008). [CrossRef]
  11. K. Yoshida, H. Yoshida, and Y. Kato, “Characterization of high average power Nd:GGG slab lasers,” IEEE J. Quantum Electron. 24(6), 1188–1192 (1988). [CrossRef]
  12. Z. Jia, X. T. Tao, C. Dong, X. Cheng, W. Zhang, F. Xu, and M. Jiang, “Study on crystal growth of large size Nd3+:Gd3Ga5O12 (Nd3+:GGG) by Czochralski method,” J. Cryst. Growth 292(2), 386–390 (2006). [CrossRef]
  13. L. J. Qin, D. Y. Tang, G. Q. Xie, H. Luo, C. M. Dong, Z. T. Jia, H. H. Yu, and X. T. Tao, “Diode-end-pumped passively mode-locked Nd:GGG laser with a semiconductor saturable mirror,” Opt. Commun. 281(18), 4762–4764 (2008). [CrossRef]
  14. C.-H. Zuo, B.-T. Zhang, J.-L. He, X.-L. Dong, J.-F. Yang, H.-T. Huang, J.-L. Xu, S. Zhao, C.-M. Dong, and X.-T. Tao, “CW and passive Q-switching of 1331-nm Nd:GGG laser with Co2+:LMA saturable absorber,” Appl. Phys. B 95(1), 75–80 (2009). [CrossRef]
  15. Z. Chun-Yu, G. Chun-Qing, Z. Ling, W. Zhi-Yi, and Z. Zhi-Guo, “Laser Performance of Nd:GGG Operating at 938 nm,” Chin. Phys. Lett. 24(2), 440–441 (2007). [CrossRef]
  16. K. He, C. Gao, Z. Wei, D. Li, Z. Zhang, H. J. Zhang, and J. Wang, “Diode-pumped passively Q-switched Nd:LuVO4 laser at 916nm,” Opt. Commun. 282(12), 2413–2416 (2009). [CrossRef]
  17. Q. Li, B. Feng, D. Zhang, Z. Zhang, H. Zhang, and J. Wang, “Q-switched 935 nm Nd:CNGG laser,” Appl. Opt. 48(10), 1898–1903 (2009), http://www.opticsinfobase.org/abstract.cfm?URI=ao-48-10-1898 . [CrossRef] [PubMed]
  18. Y. P. Huang, K. W. Su, A. Li, Y. F. Chen, and K. F. Huang, “High-peak-power passively Q-switched Nd:YAG laser at 946nm,” Appl. Phys. B 91(3-4), 429–432 (2008). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.

Figures

Fig. 1 Fig. 2 Fig. 3
 
Fig. 4 Fig. 5
 

« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited