Statistical studies of photonic heterostructure nanocavities with an average Q factor of three million

Yuki Taguchi, Yasushi Takahashi, Yoshiya Sato, Takashi Asano, and Susumu Noda  »View Author Affiliations


Optics Express, Vol. 19, Issue 12, pp. 11916-11921 (2011)
http://dx.doi.org/10.1364/OE.19.011916


View Full Text Article

Acrobat PDF (884 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

We have measured the quality (Q) factors and resonant wavelengths for 80 photonic crystal nanocavities with the same heterostructure. In this statistical evaluation, the Q factors varied according to a normal distribution centered at 3 million and ranging between 2.3 million and 3.9 million. The resonant wavelengths also fluctuated but with a standard deviation of only 0.33 nm. Such a high average Q factor and highly controlled resonant wavelength will be important for the development of advanced applications of photonic crystal nanocavities. Comparing the experimental values with calculated values suggests that factors other than structural variations of air holes, which decrease the Q factor, are indeed present in the fabricated nanocavities.

© 2011 OSA

1. Introduction

We have previously presented an important design rule for increasing the theoretical Q factors (Q ideal) of nanocavities [1

1. Y. Akahane, T. Asano, B. S. Song, and S. Noda, “High-Q photonic nanocavity in a two-dimensional photonic crystal,” Nature 425(6961), 944–947 (2003). [CrossRef] [PubMed]

] and we have proposed photonic heterostructure nanocavities with Q ideal of more than ten million [2

2. B. S. Song, S. Noda, T. Asano, and Y. Akahane, “Ultra-high-Q photonic double-heterostructure nanocavity,” Nat. Mater. 4(3), 207–210 (2005). [CrossRef]

,3

3. Y. Takahashi, Y. Tanaka, H. Hagino, T. Sugiya, Y. Sato, T. Asano, and S. Noda, “Design and demonstration of high-Q photonic heterostructure nanocavities suitable for integration,” Opt. Express 17(20), 18093–18102 (2009). [CrossRef] [PubMed]

]. However, to date the highest experimentally measured Q factor (Q exp) is approximately 2.5 million [2

2. B. S. Song, S. Noda, T. Asano, and Y. Akahane, “Ultra-high-Q photonic double-heterostructure nanocavity,” Nat. Mater. 4(3), 207–210 (2005). [CrossRef]

,18

18. Y. Takahashi, H. Hagino, Y. Tanaka, B. S. Song, T. Asano, and S. Noda, “High-Q nanocavity with a 2-ns photon lifetime,” Opt. Express 15(25), 17206–17213 (2007). [CrossRef] [PubMed]

]; the values of Q exp for different nanocavities with the same structure varied between 2.0 million and 2.5 million. Furthermore, λ fluctuated by several nanometers between different cavities. This discrepancy between Q ideal and Q exp and the partially-defined λ can mainly be attributed to nanometer-scale random variations in the radii and positions of the air holes that form the 2D PC [19

19. T. Asano, B. S. Song, and S. Noda, “Analysis of the experimental Q factors (~ 1 million) of photonic crystal nanocavities,” Opt. Express 14(5), 1996–2002 (2006). [CrossRef] [PubMed]

]. We have recently performed a numerical investigation of the influence of these structural variations on a heterostructure nanocavity by imposing random fluctuation patterns in which the air holes are shifted and the radii are varied. Our calculations revealed that Q ideal is reduced from 1.5 × 107 to approximately one million even when the standard deviation of the structural variations is as small as 1 nm [20

20. H. Hagino, Y. Takahashi, Y. Tanaka, T. Asano, and S. Noda, “Effects of fluctuation in air hole radii and positions on optical characteristics in photonic crystal heterostructure nanocavities,” Phys. Rev. B 79(8), 085112 (2009). [CrossRef]

]. Furthermore, the value of λ randomly fluctuated on the subnanometer scale. Knowledge of the magnitude of these fluctuations is important for future applications of nanocavities, but no quantitative experimental investigation has yet been carried out. Therefore, no statistical comparison of measured and predicted values of Q and λ has been performed.

In this paper, we report on experimental evaluations of the fluctuations of Q and λ for the type of high-Q heterostructure nanocavity that we previously studied theoretically [20

20. H. Hagino, Y. Takahashi, Y. Tanaka, T. Asano, and S. Noda, “Effects of fluctuation in air hole radii and positions on optical characteristics in photonic crystal heterostructure nanocavities,” Phys. Rev. B 79(8), 085112 (2009). [CrossRef]

]. We measured Q exp and λ for 80 fabricated nanocavities with the same heterostructure, all of which were integrated on the same silicon (Si) chip. The values of Q exp varied between 2.3 million and 3.9 million according to a normal distribution; the average value was 3.0 million. The value of λ also fluctuated but with a standard deviation of only 0.33 nm. By comparing with calculated values of Q and λ, we conclude that the standard deviation of the air hole positions and radii in the fabricated nanocavities is less than 0.58 nm.

2. Sample structure

Figure 1(b) shows the entire structure of a measured sample. Ten nanocavities and an extended line-defect waveguide to excite the nanocavities were fabricated in parallel, separated by 5 rows of air holes. All 10 cavities had the structure shown in Fig. 1(a). The length of the waveguide is 300 μm with a separation of 20 μm between cavities. In order to ensure that any field distortion influencing the accuracy of the electron beam (EB) lithography was steady for all 10 cavities, the pattern for each cavity was drawn at the same position within the EB field by instead displacing the EB stage (Conversely, this method may produce slight changes in the height of the EB stage from cavity to cavity). We performed optical microscopy measurements to determine the values of Q exp and λ. Input light from a tunable-wavelength laser was coupled into a facet of the excitation waveguide and dropped light emitted from the nanocavities to free space was measured. The probability that the spectral resonant peaks of the 10 nanocavities overlap is small because the linewidths of the peaks (<1 pm) are much smaller than the random fluctuation of λ, as shown in Fig. 3
Fig. 3 (a) Calculated Q factors and (b) resonant wavelengths of the nanocavity shown in Fig. 1(a) for 30 structural fluctuation patterns with σ hole = 1 nm. The x-axis indicates the identification numbers of the patterns. The solid and dashed lines indicate the average value of λ and its standard deviation.
. We fabricated 8 such samples on the same Si chip by a process described previously [2

2. B. S. Song, S. Noda, T. Asano, and Y. Akahane, “Ultra-high-Q photonic double-heterostructure nanocavity,” Nat. Mater. 4(3), 207–210 (2005). [CrossRef]

,18

18. Y. Takahashi, H. Hagino, Y. Tanaka, B. S. Song, T. Asano, and S. Noda, “High-Q nanocavity with a 2-ns photon lifetime,” Opt. Express 15(25), 17206–17213 (2007). [CrossRef] [PubMed]

] and thus efficiently measured 80 nanocavities with the same structure.

3. Experimental results

Figure 2(b) shows the variation of λ for the 80 nanocavities, determined using spectral-domain measurements. During measurements the surrounding temperature fluctuated about by 1 degree corresponding to a λ shift of 0.08 nm. The inset shows that, in similar fashion to Q exp, λ randomly fluctuates according to a normal distribution; the average value is 1574.37 nm and the standard deviation is only 0.33 nm. Such a highly controlled λ is very useful not only for the passive devices as wavelength filters [5

5. H. Takano, B. S. Song, T. Asano, and S. Noda, “Highly efficient multi-channel drop filter in a two-dimensional hetero photonic crystal,” Opt. Express 14(8), 3491–3496 (2006). [CrossRef] [PubMed]

,6

6. B. S. Song, T. Nagashima, T. Asano, and S. Noda, “Resonant-wavelength control of nanocavities by nanometer-scaled adjustment of two-dimensional photonic crystal slab structures,” IEEE Photon. Technol. Lett. 20(7), 532–534 (2008). [CrossRef]

] and environmental sensors [10

10. M. R. Lee and P. M. Fauchet, “Two-dimensional silicon photonic crystal based biosensing platform for protein detection,” Opt. Express 15(8), 4530–4535 (2007). [CrossRef] [PubMed]

,11

11. S. Kita, K. Nozaki, and T. Baba, “Refractive index sensing utilizing a cw photonic crystal nanolaser and its array configuration,” Opt. Express 16(11), 8174–8180 (2008). [CrossRef] [PubMed]

], but also for active devices as nanolasers [12

12. M. Nomura, S. Iwamoto, K. Watanabe, N. Kumagai, Y. Nakata, S. Ishida, and Y. Arakawa, “Room temperature continuous-wave lasing in photonic crystal nanocavity,” Opt. Express 14(13), 6308–6315 (2006). [CrossRef] [PubMed]

]. The difference between the highest and lowest values of λ among the 80 nanocavities is 1.90 nm. This precision might be sufficient for coarse wavelength division devices. It should be emphasized that the yield rate of the high-Q nanocavities was 100% in this study. Similar statistical results in Q and λ were obtained in different chips. We believe that these developments have been brought about both by improvements in the fabrication process and by tuning the PC structural parameters as described above.

4. Comparison with simulation results

Finally, we estimate the standard deviation (σ hole) associated with remaining variations in the radii and positions of the air holes in the measured nanocavities. Although it is difficult to specify the reasons for any remaining variations, it is important to make such an estimation in order to further improve the fabrication process and to design nanocavity devices. Because σ hole is expected to be less than 1 nm, corresponding to structural deviations that are barely visible using conventional observation apparatus, we adopted a method to compare our experimental results with 3D FDTD simulations that take these structural variations into account. We have presented such a comparison in [18

18. Y. Takahashi, H. Hagino, Y. Tanaka, B. S. Song, T. Asano, and S. Noda, “High-Q nanocavity with a 2-ns photon lifetime,” Opt. Express 15(25), 17206–17213 (2007). [CrossRef] [PubMed]

], although statistical experimental data was not included. Here, our calculations used the structural parameters shown in Fig. 1(a), and random variations in the air hole positions and radii were added using 30 different fluctuation patterns, according to a normal distribution with σ hole = 1 nm. Details of these calculations are given in [20

20. H. Hagino, Y. Takahashi, Y. Tanaka, T. Asano, and S. Noda, “Effects of fluctuation in air hole radii and positions on optical characteristics in photonic crystal heterostructure nanocavities,” Phys. Rev. B 79(8), 085112 (2009). [CrossRef]

].

Figures 3(a) and 3(b) show the calculated values of Q and λ for the 30 fluctuation patterns. The calculated Q factors in Fig. 3(a), which we denote as Q fluc, are significantly smaller than the Q ideal of 1.4 × 107 and are randomly distributed between 6.0 × 105 and 2.8 × 106. In Fig. 3(b), the average calculated value of λ is 1579.32 nm with a standard deviation of 0.48 nm. Because the lowest value of Q exp is 2.3 × 106 and the standard deviation of the experimentally determined λ is 0.33 nm, we can be certain that σ hole in our fabricated samples is below 1 nm.

An estimation of σ hole is also possible using the standard deviation of λ, which is known to be proportional to σ hole when the fluctuation pattern is fixed. This coefficient is evaluated from Fig. 3(b) as
S .D .(λ)=0 .48×σhole.
(6)
By substituting the experimental standard deviation of 0.33 nm, we obtain σ hole = 0.69 nm, which is larger than from the analysis based on 1/Q loss_fluc.

It is noted that estimated values from Avg.(1/Q loss_fluc) and S.D.(1/Q loss_fluc) are clearly different. The corresponding Q loss_fluc for σ hole of 0.36 nm is 9.98 × 106 from Eq. (4), which is different by 6.27 × 106 from the value for Avg.(1/Q loss_fluc). Here, it should be noted that our estimations based on 1/Q loss_fluc only take into account Q loss factors due to structural variations of the air holes. If other factors in the fabricated cavities contribute, the evaluation of σ hole from Avg.(1/Q loss_fluc) might be overestimated. If one assumes that S.D.(1/Q loss_fluc) is unaffected by any additional factors, the smaller σ hole estimated from S.D.(1/Q loss_fluc) is likely to be closer to the actual value, which suggests that other constant Q loss factors of 6.27 × 106 are indeed present in the fabricated nanocavities, such as absorption at the Si surface [21

21. M. Borselli, T. J. Johnson, and O. Painter, “Measuring the role of surface chemistry in silicon microphotonics,” Appl. Phys. Lett. 88(13), 131114 (2006). [CrossRef]

]. In other words, we can still increase Q exp factor by decreasing the constant Q loss factors. The larger value of σ hole estimated from S.D.(λ) is probably due either to the fluctuation of the measurement temperature or to tiny fluctuations in the height of the EB stage occurring during EB lithography, which would only increase the fluctuation of λ. The standard error arising from the finite number of fluctuation patterns is also a probable cause. Although unknown factors remain, we conclude that the value of σ hole in our nanocavities is less than 0.58 nm.

5. Summary

In summary, we have measured the Q exp factors and resonant wavelengths λ for 80 high-Q nanocavities with the same heterostructure. The values of Q exp follow a normal distribution between 2.3 million and 3.9 million, with an average Q exp of three million. The value of λ also fluctuates but with a standard deviation of only 0.33 nm. Such a high average Q exp and stable λ will be important for expanding the area of nanocavity applications. Furthermore, we have used a statistical comparison of our experimental results and FDTD calculations to estimate that the standard deviation of the structural variations of our air holes is less than 0.58 nm and that Q loss factors other than Q loss_fluc due to the air hole variations might be present. This method will be an important tool for further developing high-Q nanocavities .

Acknowledgments

This work was partly supported by the Special Coordination Funds for Promoting Science and Technology commissioned by MEXT, by the CREST and PRESTO programs of the JST, by the Global COE Program, and by KAKENHI (No. 23104721).

References and links

1.

Y. Akahane, T. Asano, B. S. Song, and S. Noda, “High-Q photonic nanocavity in a two-dimensional photonic crystal,” Nature 425(6961), 944–947 (2003). [CrossRef] [PubMed]

2.

B. S. Song, S. Noda, T. Asano, and Y. Akahane, “Ultra-high-Q photonic double-heterostructure nanocavity,” Nat. Mater. 4(3), 207–210 (2005). [CrossRef]

3.

Y. Takahashi, Y. Tanaka, H. Hagino, T. Sugiya, Y. Sato, T. Asano, and S. Noda, “Design and demonstration of high-Q photonic heterostructure nanocavities suitable for integration,” Opt. Express 17(20), 18093–18102 (2009). [CrossRef] [PubMed]

4.

S. Noda, A. Chutinan, and M. Imada, “Trapping and emission of photons by a single defect in a photonic bandgap structure,” Nature 407(6804), 608–610 (2000). [CrossRef] [PubMed]

5.

H. Takano, B. S. Song, T. Asano, and S. Noda, “Highly efficient multi-channel drop filter in a two-dimensional hetero photonic crystal,” Opt. Express 14(8), 3491–3496 (2006). [CrossRef] [PubMed]

6.

B. S. Song, T. Nagashima, T. Asano, and S. Noda, “Resonant-wavelength control of nanocavities by nanometer-scaled adjustment of two-dimensional photonic crystal slab structures,” IEEE Photon. Technol. Lett. 20(7), 532–534 (2008). [CrossRef]

7.

Y. Tanaka, J. Upham, T. Nagashima, T. Sugiya, T. Asano, and S. Noda, “Dynamic control of the Q factor in a photonic crystal nanocavity,” Nat. Mater. 6(11), 862–865 (2007). [CrossRef] [PubMed]

8.

J. Upham, Y. Tanaka, T. Asano, and S. Noda, “Dynamic increase and decrease of photonic crystal nanocavity Q factors for optical pulse control,” Opt. Express 16(26), 21721–21730 (2008). [CrossRef] [PubMed]

9.

M. Notomi, E. Kuramochi, and T. Tanabe, “Large-scale arrays of ultrahigh-Q coupled nanocavities,” Nat. Photonics 2(12), 741–747 (2008). [CrossRef]

10.

M. R. Lee and P. M. Fauchet, “Two-dimensional silicon photonic crystal based biosensing platform for protein detection,” Opt. Express 15(8), 4530–4535 (2007). [CrossRef] [PubMed]

11.

S. Kita, K. Nozaki, and T. Baba, “Refractive index sensing utilizing a cw photonic crystal nanolaser and its array configuration,” Opt. Express 16(11), 8174–8180 (2008). [CrossRef] [PubMed]

12.

M. Nomura, S. Iwamoto, K. Watanabe, N. Kumagai, Y. Nakata, S. Ishida, and Y. Arakawa, “Room temperature continuous-wave lasing in photonic crystal nanocavity,” Opt. Express 14(13), 6308–6315 (2006). [CrossRef] [PubMed]

13.

S. Noda, M. Fujita, and T. Asano, “Spontaneous-emission control by photonic crystals and nanocavities,” Nat. Photonics 1(8), 449–458 (2007). [CrossRef]

14.

S. Iwamoto, Y. Arakawa, and A. Gomyo, “Observation of enhanced photoluminescence from silicon photonic crystal nanocavity at room temperature,” Appl. Phys. Lett. 91(21), 211104 (2007). [CrossRef]

15.

X. Yang and C. W. Wong, “Coupled-mode theory for stimulated Raman scattering in high-Q/V(m) silicon photonic band gap defect cavity lasers,” Opt. Express 15(8), 4763–4780 (2007). [CrossRef] [PubMed]

16.

T. Yoshie, A. Scherer, J. Hendrickson, G. Khitrova, H. M. Gibbs, G. Rupper, C. Ell, O. B. Shchekin, and D. G. Deppe, “Vacuum Rabi splitting with a single quantum dot in a photonic crystal nanocavity,” Nature 432(7014), 200–203 (2004). [CrossRef] [PubMed]

17.

K. Hennessy, A. Badolato, M. Winger, D. Gerace, M. Atatüre, S. Gulde, S. Fält, E. L. Hu, and A. Imamoğlu, “Quantum nature of a strongly coupled single quantum dot-cavity system,” Nature 445(7130), 896–899 (2007). [CrossRef] [PubMed]

18.

Y. Takahashi, H. Hagino, Y. Tanaka, B. S. Song, T. Asano, and S. Noda, “High-Q nanocavity with a 2-ns photon lifetime,” Opt. Express 15(25), 17206–17213 (2007). [CrossRef] [PubMed]

19.

T. Asano, B. S. Song, and S. Noda, “Analysis of the experimental Q factors (~ 1 million) of photonic crystal nanocavities,” Opt. Express 14(5), 1996–2002 (2006). [CrossRef] [PubMed]

20.

H. Hagino, Y. Takahashi, Y. Tanaka, T. Asano, and S. Noda, “Effects of fluctuation in air hole radii and positions on optical characteristics in photonic crystal heterostructure nanocavities,” Phys. Rev. B 79(8), 085112 (2009). [CrossRef]

21.

M. Borselli, T. J. Johnson, and O. Painter, “Measuring the role of surface chemistry in silicon microphotonics,” Appl. Phys. Lett. 88(13), 131114 (2006). [CrossRef]

OCIS Codes
(350.4238) Other areas of optics : Nanophotonics and photonic crystals
(230.5298) Optical devices : Photonic crystals

ToC Category:
Photonic Crystals

History
Original Manuscript: April 21, 2011
Revised Manuscript: May 21, 2011
Manuscript Accepted: May 27, 2011
Published: June 3, 2011

Citation
Yuki Taguchi, Yasushi Takahashi, Yoshiya Sato, Takashi Asano, and Susumu Noda, "Statistical studies of photonic heterostructure nanocavities with an average Q factor of three million," Opt. Express 19, 11916-11921 (2011)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-19-12-11916


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. Y. Akahane, T. Asano, B. S. Song, and S. Noda, “High-Q photonic nanocavity in a two-dimensional photonic crystal,” Nature 425(6961), 944–947 (2003). [CrossRef] [PubMed]
  2. B. S. Song, S. Noda, T. Asano, and Y. Akahane, “Ultra-high-Q photonic double-heterostructure nanocavity,” Nat. Mater. 4(3), 207–210 (2005). [CrossRef]
  3. Y. Takahashi, Y. Tanaka, H. Hagino, T. Sugiya, Y. Sato, T. Asano, and S. Noda, “Design and demonstration of high-Q photonic heterostructure nanocavities suitable for integration,” Opt. Express 17(20), 18093–18102 (2009). [CrossRef] [PubMed]
  4. S. Noda, A. Chutinan, and M. Imada, “Trapping and emission of photons by a single defect in a photonic bandgap structure,” Nature 407(6804), 608–610 (2000). [CrossRef] [PubMed]
  5. H. Takano, B. S. Song, T. Asano, and S. Noda, “Highly efficient multi-channel drop filter in a two-dimensional hetero photonic crystal,” Opt. Express 14(8), 3491–3496 (2006). [CrossRef] [PubMed]
  6. B. S. Song, T. Nagashima, T. Asano, and S. Noda, “Resonant-wavelength control of nanocavities by nanometer-scaled adjustment of two-dimensional photonic crystal slab structures,” IEEE Photon. Technol. Lett. 20(7), 532–534 (2008). [CrossRef]
  7. Y. Tanaka, J. Upham, T. Nagashima, T. Sugiya, T. Asano, and S. Noda, “Dynamic control of the Q factor in a photonic crystal nanocavity,” Nat. Mater. 6(11), 862–865 (2007). [CrossRef] [PubMed]
  8. J. Upham, Y. Tanaka, T. Asano, and S. Noda, “Dynamic increase and decrease of photonic crystal nanocavity Q factors for optical pulse control,” Opt. Express 16(26), 21721–21730 (2008). [CrossRef] [PubMed]
  9. M. Notomi, E. Kuramochi, and T. Tanabe, “Large-scale arrays of ultrahigh-Q coupled nanocavities,” Nat. Photonics 2(12), 741–747 (2008). [CrossRef]
  10. M. R. Lee and P. M. Fauchet, “Two-dimensional silicon photonic crystal based biosensing platform for protein detection,” Opt. Express 15(8), 4530–4535 (2007). [CrossRef] [PubMed]
  11. S. Kita, K. Nozaki, and T. Baba, “Refractive index sensing utilizing a cw photonic crystal nanolaser and its array configuration,” Opt. Express 16(11), 8174–8180 (2008). [CrossRef] [PubMed]
  12. M. Nomura, S. Iwamoto, K. Watanabe, N. Kumagai, Y. Nakata, S. Ishida, and Y. Arakawa, “Room temperature continuous-wave lasing in photonic crystal nanocavity,” Opt. Express 14(13), 6308–6315 (2006). [CrossRef] [PubMed]
  13. S. Noda, M. Fujita, and T. Asano, “Spontaneous-emission control by photonic crystals and nanocavities,” Nat. Photonics 1(8), 449–458 (2007). [CrossRef]
  14. S. Iwamoto, Y. Arakawa, and A. Gomyo, “Observation of enhanced photoluminescence from silicon photonic crystal nanocavity at room temperature,” Appl. Phys. Lett. 91(21), 211104 (2007). [CrossRef]
  15. X. Yang and C. W. Wong, “Coupled-mode theory for stimulated Raman scattering in high-Q/V(m) silicon photonic band gap defect cavity lasers,” Opt. Express 15(8), 4763–4780 (2007). [CrossRef] [PubMed]
  16. T. Yoshie, A. Scherer, J. Hendrickson, G. Khitrova, H. M. Gibbs, G. Rupper, C. Ell, O. B. Shchekin, and D. G. Deppe, “Vacuum Rabi splitting with a single quantum dot in a photonic crystal nanocavity,” Nature 432(7014), 200–203 (2004). [CrossRef] [PubMed]
  17. K. Hennessy, A. Badolato, M. Winger, D. Gerace, M. Atatüre, S. Gulde, S. Fält, E. L. Hu, and A. Imamoğlu, “Quantum nature of a strongly coupled single quantum dot-cavity system,” Nature 445(7130), 896–899 (2007). [CrossRef] [PubMed]
  18. Y. Takahashi, H. Hagino, Y. Tanaka, B. S. Song, T. Asano, and S. Noda, “High-Q nanocavity with a 2-ns photon lifetime,” Opt. Express 15(25), 17206–17213 (2007). [CrossRef] [PubMed]
  19. T. Asano, B. S. Song, and S. Noda, “Analysis of the experimental Q factors (~ 1 million) of photonic crystal nanocavities,” Opt. Express 14(5), 1996–2002 (2006). [CrossRef] [PubMed]
  20. H. Hagino, Y. Takahashi, Y. Tanaka, T. Asano, and S. Noda, “Effects of fluctuation in air hole radii and positions on optical characteristics in photonic crystal heterostructure nanocavities,” Phys. Rev. B 79(8), 085112 (2009). [CrossRef]
  21. M. Borselli, T. J. Johnson, and O. Painter, “Measuring the role of surface chemistry in silicon microphotonics,” Appl. Phys. Lett. 88(13), 131114 (2006). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.

Figures

Fig. 1 Fig. 3 Fig. 2
 

« Previous Article

OSA is a member of CrossRef.

CrossCheck Deposited