High-Q, low index-contrast polymeric photonic crystal nanobeam cavities

doi:10.1364/OE.19.022191

« Show journal navigation

High-Q, low index-contrast polymeric photonic crystal nanobeam cavities

Qimin Quan, Ian B. Burgess, Sindy K. Y. Tang, Daniel L. Floyd, and Marko Loncar »View Author Affiliations

Optics Express, Vol. 19, Issue 22, pp. 22191-22197 (2011)
http://dx.doi.org/10.1364/OE.19.022191

View Full Text Article

Acrobat PDF (884 KB)

Journal Search
Article Lookup

Article Tools

Citations

Alert me when this article is cited
Export Citation/Save

Full Text
Article Info
References (31)
Cited By
Figures (3)
Metrics

Abstract

We present the design, fabrication and characterization of high-Q (Q=36,000) polymeric photonic crystal nanobeam cavities made of two polymers that have an ultra-low index contrast (ratio=1.15) and observed thermo-optical bistability at hundred microwatt power level. Due to the extended evanescent field and small mode volumes, polymeric nanobeam cavities are ideal platform for ultra-sensitive biochemical sensing. We demonstrate that these sensors have figures of merit (FOM=9190) two orders of magnitude greater than surface plasmon resonance based sensors, and outperform the commercial Biacore^TM sensors. The demonstration of high-Q cavity in low-index-contrast polymers can open up versatile applications using a broad range of functional and flexible polymeric materials.

1. Introduction

The use of polymeric materials in the fabrication of micro- to nano-scale devices has rapidly increased in the past decade. Examples of successful applications can be found in broadband communications[1

H. Ma, A. K. Y. Jen, and L. R. Dalton, “Polymer-Based Optical Waveguides: Materials, Processing, and Devices,” Adv. Mater. 14, 1339–1365 (2002). [CrossRef]

], large screen and flexible displays[2

M. C. Choi, Y. Kim, and C-S. Ha, “Polymers for flexible displays: From material selection to device applications,” Prog. Polym. Sci. 33, 581–630 (2008). [CrossRef]

], solar cells[3

S-I. Na, S-S. Kim, J. Jo, and D-Y Kim, “Efficient and Flexible ITO-Free Organic Solar Cells Using Highly Conductive Polymer Anodes,” Adv. Mater. 20, 4061–4067 (2008). [CrossRef]

, 4

H-Y. Chen, J. Hou, S. Zhang, Y. Liang, G. Yang, Y. Yang, L. Yu, Y. Wu, and G. Li. “Polymer solar cells with enhanced open-circuit voltage and effciency,” Nat. Photon. 3, 649–653 (2009). [CrossRef]

] and biomedical sensors[5

D. Ghezzi, M. R. Antognazza, M. D. Maschio, E. Lanzarini, F. Benfenati, and G. Lanzani, “A hybrid bioorganic interface for neuronal photoactivation,” Nat. Commun. 2:166 (2011). [CrossRef] [PubMed]

, 6

P. Broz, (Editor) Polymer-Based Nanostructures , 1st Edition. Royal Society of Chemistry (RSC) Publishing (2010). [CrossRef]

] to name a few. However, one area where the realization of all-polymer devices has proved challenging is in the development of high quality factor (defined as

Q = ω_{0} \frac{Energy stored}{Power loss}

) nano-scale optical resonators. In particular, it has been a challenge to achieve high-Q photonic crystal (PhC) cavities made of polymeric materials due to the low index contrast between available materials. While there has been some recent demonstrations of ring resonators[7

C. Chao and L. J. Guo, “Polymer microring resonators fabricated by nanoimprint technnigue,” J. Vac. Sci. Technol. B 20, 2862 (2002). [CrossRef]

, 8

P. Rabiei, W. H. Steier, C. Zhang, and L. R. Dalton, “Polymer Micro-Ring Filters and Modulators,” J. Lightwave Technol. 20, 1968 (2002).

, 9

Y. Huang, G. T. Paloczi, J. Scheuer, and A. Yariv, “Soft lithography replication of polymeric microring optical resonators,” Opt. Express 11, 2452 (2003). [CrossRef] [PubMed]

], microtoroids[10

A. L. Martin, D. K. Armani, L. Yang, and K. J. Vahala, “Replica-molded high-Q polymer microresonators,” Opt. Lett. 29, 533 (2004). [CrossRef] [PubMed]

] and photonic crystal cavities[11

M. Khan, T. M. Babinec, M. W. McCutcheon, P.B. Deotare, and M Loncar, “Fabrication and characterization of high-quality-factor silicon nitride nanobeam cavities,” Opt. Lett. 36, 421 (2011). [CrossRef] [PubMed]

]–[16

M. M. Murshidy, A. M. Adawi, P. W. Fry, and D. G. Lidzey, “A one-dimensional photonic-crystal nanocavity incorporating a fluorescent molecular dye,” Appl. Phys. Lett. 97, 153303 (2010). [CrossRef]

] in relatively low-index-contrast platforms (n_cav/n_bg ∼ 1.5), achieving simultaneously high Q-factors and small mode volumes (defined as V = ∫ɛ|E|²dV/[ɛ|E|²]_max) in the ultra-low index-contrast regime has remained elusive. Here, we present the design, fabrication and characterization of all-polymer photonic crystal nanobeam cavities, fabricated in the electron-beam resist ZEP520 (n = 1.54) on a substrate of the spin-on fluoropolymer CYTOP (n = 1.34). Despite having an extraordinarily small index-contrast (n_cav/n_bg = 1.15) we achieved Qs as high as Q=36,000 - an order of magnitude higher than the state of the art for n_cav/n_bg = 1.46 [12

G. Gong and J. Vuckovic, “Photonic crystal cavities in silicon dioxide,” Appl. Phys. Lett. 96, 031107 (2010). [CrossRef]

]. Furthermore, nanobeam cavities have much smaller mode volumes compared to the polymeric ring resonators with the same Q-factors and made of the same materials. Due to the high Q-factors and small mode volumes we observe optical bistability in the polymeric cavities at hundred microwatt power levels. Furthermore, the greater extension of the evanescent field in our low-index-contrast platform allows polymeric nanobeam cavity-modes to display high sensitivity to the background refractive index. As such we show that polymer nanobeam cavities, as biomedical sensors, have figure of merit (FOM=9190), two orders of magnitude greater than the surface plasmon resonance (SPR) based sensors and outperform commercially avilable Biacore^TM SPR sensors. In addition, the simple fabrication process of polymeric cavities potentially eliminates the need of clean-room facilities and can be easily scaled up for mass production.

2. High-Q photonic crystal cavity in ultra-Low index-contrast polymeric materials

The nanobeam cavity geometry consists of a ridge waveguide perforated with gratings of elliptical holes (Figure 1). In our design, we considered a cavity having refractive-index n_cav = 1.54 (e.g. ZEP520) surrounded by a background index n_bg = 1.34, which is suitable for biosensing applications. The cavity was designed using the deterministic high-Q design method that we previously introduced[17

Q. Quan, P. B. Deotare, and M. Loncar, “Photonic crystal nanobeam cavity strongly coupled to the feeding waveguide,” Appl. Phys. Letts. 96, 203102 (2010). [CrossRef]

, 18

Q. Quan and M. Loncar, “Deterministic design of high Q, small mode volume photonic crystal nanobeam cavities,” Opt. Express 19, 18529–18542 (2011). [CrossRef]

]. The distances between neighboring holes are kept the same as 550nm. There are in total 100 grating sections on both sides. The first 50 grating sections are 50 ellipses whose dimensions linearly decrease from the center to both ends of the 3.2μm-wide and 500nm-thick waveguide, followed by 50 ellipses that have the same dimensions. In the linearly decreasing section, the major axes of the ellipses decrease from 1.44μm to 1.22μm, and the minor axes decrease from 165nm to 140nm. The reason for choosing elliptical shape instead of circular shape is because elliptical grating sections have larger bandgap and higher reflectivity to confine the optical mode. At current level of index contrast between the cavity and the background, a symmetric structure is essential to minimize coupling into substrate modes. A symmetric structure can be fabricated simply by adding a capping layer of CYTOP on top of the on-substrate cavity. However, we note that the refractive index of the CYTOP layer also well matches the refractive index of many common liquids (e.g. water). Thus an equivalent optical structure is formed by immersing the cavity in water instead of adding a polymer capping layer. Therefore, we used the water cladding geometry in our measurements as such a geometry is ideal for optofluidic and sensing applications. We determined the theoretical mode profile and Q of the cavity mode using the finite-difference time-domain (FDTD) method (Lumerical Solutions.). The mode profile is shown in Figure 1(a), with a simulation Q=86,000. The device was fabricated directly via electron-beam lithography in the positive-tone ZEP520 (Zeon Corp.) resist (n = 1.54) supported by a 3.2μm layer of the low-index fluoropolymer CYTOP (AGC inc.) (n = 1.34) on a silicon chip. The CYTOP layer was deposited by multiple spin-coating steps. The polymer layers were sufficiently thin that no charging effects were observed using a 100kV electron-beam (Elionix Inc.), even in the absence of an added conductive layer. Figure 1(b) shows the scanning electron microscope (SEM) image of the center region of a nanobeam cavity.

Fig. 1 (a) Energy density distribution of the cavity mode from FDTD simulation. (b) Scanning electron micrograph of the polymeric nanobeam cavity. (c) Schematics of the measurement setup. A tunable laser source is coupled to the edge of the chip through a tapered fiber (TF, Ozoptics inc.) after the fiber polarization controller (FPC), and collected from tapered fiber followed by a second FPC and an inline polarizer (Pol) to the detector. The two FPCs are to filter out unwanted TM polarization component that is not in resonance with the cavity.

A schematic of the measurement setup is shown in Figure 1(c). A tunable telecom laser source was coupled to the edge of the chip through a tapered fiber (TF, Ozoptics inc.) after a fiber polarization controller (FPC). Light was then collected from tapered fiber followed by a second FPC and an inline polarizer (Pol) to the detector. The two FPCs filter out the unwanted TM polarization component that is not in resonance with the cavity. We measured the cavities submerged in D₂O, which has negligible absorption in the telecom frequency range. Figure 2 (a) shows the full spectrum of one of the cavities. The highest Q we obtained was 36,000 in D₂O, as shown in Figure 2(b). Not only is the index ratio of our system much lower (index ratio=1.15 v.s index ratio≥1.45 in all other cases), the Q-factor is an order of magnitude higher than previously demonstrated low index PhC cavities suspended in air [12

G. Gong and J. Vuckovic, “Photonic crystal cavities in silicon dioxide,” Appl. Phys. Lett. 96, 031107 (2010). [CrossRef]

]–[16

M. M. Murshidy, A. M. Adawi, P. W. Fry, and D. G. Lidzey, “A one-dimensional photonic-crystal nanocavity incorporating a fluorescent molecular dye,” Appl. Phys. Lett. 97, 153303 (2010). [CrossRef]

Fig. 2 (a) Measured optical transmission spectrum of a high-transmission polymeric nanobeam cavity in D₂O. The cavity mode has Q=11,000 with a high on-resonance transmission 15%. (b) The experimental transmission spectrum of a different cavity with the highest measured Q, with on resonance transmission of 6%. Q of 36,000 is extracted from Lorentzian fit. (c) Comparison of theoretical Q factors and mode volumes between PhC nanobeam cavities and ring resonators with the same waveguide dimension: 3.2μm × 0.5μm, and the same material platform. Mode Volumes are normalized by (λ/n_ZEP)3. The number of tapered hole pairs in the nanobeam cavities are varied from 45 to 60, with an additional 50 hole pairs on both ends of the tapered section. The radii of the rings are varied from 25μm to 80μm. (d) Transmission spectra of the cavity mode at different input powers, showing optical bistability. The power levels indicated in the legend correspond to the powers coupled into the on-chip waveguide. The laser wavelength was swept from shorter to longer wavelengths across the cavity resonance.

3. Small mode volumes

Small mode volumes are a significant advantage of PhC nanobeam cavities over the whispering gallery mode (WGM) cavities (e.g ring resonators, microspheres etc.) since the strength of light and matter interaction scales inversely with V. A general trade off holds that higher Q-factors require larger mode volumes[18

Q. Quan and M. Loncar, “Deterministic design of high Q, small mode volume photonic crystal nanobeam cavities,” Opt. Express 19, 18529–18542 (2011). [CrossRef]

]. Maintaining high Qs in low-index contrast cavities will increase the size of the ring resonators and PhC cavities. However, we found that the mode volumes required to achieve a given Q are much larger for ring resonators than for our nanobeam PhC cavities. We illustrated this by comparing the mode volumes of nanobeam cavities with ring resonators that have the same cross sections with the nanobeam cavity waveguide (i. e. 3.2μm × 0.5μm cross section), and made of the same materials (ZEP on CYTOP immersed in D₂O). Figure 2(c) shows the relationship between Qs and mode volumes for the ring resonators with varying radii and for the nanobeam cavities with different number of tapered hole pairs (i.e. varying lengths). Notably, the ring resonators required to achieve the measured Qs of our nanobeam cavities have about 50 times larger mode volume, even theoretically.

4. Optical bistability in polymeric cavities

Due to both high Qs and the small Vs, we were able to observe optical bistability[19

H. G. Winful, J. H. Marburger, and E. Garmire, “Theory of bistability in nonlinear distributed feedback structures,” Appl. Phys. Lett. 35, 379 (1979). [CrossRef]

] in our nanobeam cavity. Optical bistability due to the thermo-optic effect (i.e. change of refractive index due to heat) has been widely observed in silicon cavities[17

Q. Quan, P. B. Deotare, and M. Loncar, “Photonic crystal nanobeam cavity strongly coupled to the feeding waveguide,” Appl. Phys. Letts. 96, 203102 (2010). [CrossRef]

, 20

V. R. Almeida and M. Lipson, “Optical bistability on a silicon chip,” Opt. Lett. 29, 2387 (2004). [CrossRef] [PubMed]

, 21

T. Uesugi, B. S. Song, T. Asano, and S. Noda, “Investigation of optical nonlinearities in an ultra-high-Q Si nanocavity in a two-dimensional photonic crystal slab,” Opt. Express 14, 377 (2006). [CrossRef] [PubMed]

, 22

L. Haret, T. Tanabe, E. Kuramochi, and M. Notomi, “Extremely low power optical bistability in silicon demonstrated using 1D photonic crystal nanocavity,” Opt. Express 17, 21108 (2009). [CrossRef] [PubMed]

], and most recently observed in polymer ring resonators by Ling et. al. [23

T. Ling, S-L Chen, and L. J. Guo, “Fabrication and Characterization of High Q Polymer Micro-ring Resonator and Its Application as a Sensitive Ultrasonic Detector,” Opt. Express 19, 861–869 (2011) [CrossRef] [PubMed]

]. In contrast to silicon case, polymer has a negative thermo-optic coefficient (dn/dT) [1

H. Ma, A. K. Y. Jen, and L. R. Dalton, “Polymer-Based Optical Waveguides: Materials, Processing, and Devices,” Adv. Mater. 14, 1339–1365 (2002). [CrossRef]

] causing the resonance of the cavity to blue-shift with increasing power (Figure 2(d)). Quantitatively, the heat (in unit of W) that is converted from optical energy (U) due to the absorption of polymer can be obtained from:

h = ω U / Q_{abs} = 2 \sqrt{T} P_{in} Q_{total} / Q_{abs}

, where ω is the cavity resonance frequency, T is the on-resonance transmission and P_in is the input optical power. Thermal equilibrium is reached through conduction and convection processes. The thermal resistance of the cavity relates the heat generated in the cavity to the temperature rise at the center of the cavity by δT = h · R_th. Therefore the resonance shift due to the thermo-optic effect can be expressed as:

δ λ = 2 \sqrt{T} Q_{total} / Q_{abs} \frac{d λ}{d n} \frac{d n}{dT} R_{th} P_{in}

(1)

The thermo-optic coefficient for ZEP 520 is expected to be

\frac{d n}{dT} \sim - 10^{- 4}

H. Ma, A. K. Y. Jen, and L. R. Dalton, “Polymer-Based Optical Waveguides: Materials, Processing, and Devices,” Adv. Mater. 14, 1339–1365 (2002). [CrossRef]

]. Using the thermal conductivity σ_th = 0.16Wm⁻¹K⁻¹[24

D. Chu, M. Touzelbaev, K. E. Goodson, S. Babin, and R. F. Pease, “Thermal conductivity measurements of thin film resist,” J. Vac. Sci. Technol. B 19, 2874 (2001). [CrossRef]

] and heat capacity C_p ∼ 1.5Jg⁻¹K⁻¹, the thermal resistance of the cavity structure was estimated to be R_th = 4.8 × 10⁴KW⁻¹ from finite-element simulation (Comsol)[22

]. Neglecting all the other heating effects, as well as higher order nonlinear effects that could change the index of the polymer, our experimentally observed resonance shift of 20pm at 170μW input power indicates Q_abs ∼ 10⁶ for linear absorption in the ZEP 520 layer, in agreement with the literature [25

O. Beyer, I. Nee, F. Havermeyer, and K. Buse, “Holographic Recording of Bragg Gratings for Wavelength Division Multiplexing in Doped and Partially Polymerized Poly(methyl methacrylate),” Appl. Opt. 42, 30 (2003). [CrossRef] [PubMed]

, 26

W. R. Folks, J. Ginn, D. Shelton, J. Tharp, and G. Boreman, “Spectroscopic ellipsometry of materials for infrared micro-device fabrication,” Phys. Stat. Sol. (c) 5, 1113 (2008). [CrossRef]

5. Ultra-sensitive glucose sensor

Due to the low index contrast, the evanescent field of the polymeric cavity is more extended into the surrounding medium than the widely used silicon based nanophotonic sensors. As a result, the resonance shift of a polymeric cavity in response to the bulk refractive index change in the surrounding media is larger. Furthermore, our cavity design is optimized for optofluidic integration, with index-matching between the substrate and the fluid layer. To illustrate the potential for such an all-polymer platform for label-free sensing[27

X. D. Fan, I. M. White, S. I. Shopova, H. Y. Zhu, J. D. Suter, and Y. Sun, “Sensitive optical biosensors for unlabeled targets: A review,” Anal. Chim. Acta 620, 8 (2008). [CrossRef] [PubMed]

], we measured the shift in the cavity resonance in response to varying glucose concentration in water. The glucose solution was delivered to the cavity via a fluidic channel that was integrated on top of the chip. The channel was made of polydimethylsiloxane (PDMS, Sylgard 184, Dow Corning) with two millimeter-diameter holes on both ends as inlet and outlet. The channel walls were painted with a CYTOP layer to maintain index-matching in the waveguide. Fluid injection was kept at a constant rate of 50μL/min. The time response to the lowest reproducibly detectable concentration (10mg/dL) is shown in Figure 3(a), along with the null response to pure DI water and the response to 20mg/dL glucose solution. The resonance shifts of glucose solutions at different concentrations are shown in Figure 3(b). Between each measurement, pure DI water was injected to the cavity and the cavity resonance shifted back to its original value. The response of the sensor to the concentration of the glucose solution exhibits excellent linearity covering the whole range of clinically relevant levels. Figure 3(b) further shows a direct comparison of our nanobeam sensor with the well-known commercial label-free biosensor: Biacore^TM instrument. Notably, nanobeam sensors demonstrated about 5 times improvement in the detection limit. As far as we know, the refractive indices of glucose solutions with different concentrations have not been measured in telecom wavelength range. Assuming the same glucose index change per concentration (0.12cm³/g) as measured in the visible wavelength range[28

A. M. Basedow, K. H. ebert, and U. Ruland, “Specific Refractive Index Increments of Dextran Fractions of Different Molecular Weights,” Makromol. Chem. 179, 1351–1353 (1978). [CrossRef]

], we obtained the wavelength shift per refractive index unit (RIU) for the nanobeam sensor is S = 386nm/RIU. This is about 4 times larger than similar PhC structures made of silicon, and is about about 2 times larger than ring resonators[29

I. M. White and X. Fan, “On the performance quantification of resonant refractive index sensors,” Opt. Express 16, 1020 (2008). [CrossRef] [PubMed]

]. The figure of merit (FOM = SQ/λ = 9190) is orders of magnitude larger than surface plasmon resonance based sensors (typically 8–23 [30

J. N. Anker, W. P. Hall, O. Lyandres, N. C. Shah, J. Zhao, and R. P. Van Duyne, “Biosensing with plasmonic nanosensors,” Nat. Mater. 7, 442 (2008). [CrossRef] [PubMed]

]) and metamaterial sensors (330 [31

A. V. Kabashin, P. Evans, S. Pastkovsky, W. Hendren, G. A. Wurtz, R. Atkinson, R. Pollard, V. A. Podolskiy, and A. V. Zayats, “Plasmonic nanorod metamaterials for biosensing,” Nat. Mater. 8, 867 (2009). [CrossRef] [PubMed]

]). Given the <1pm fluctuation in resolving the cavity resonance (Figure 3(a) DI water curve), our sensor can detect a minimum refractive index change of 2 × 10⁻⁶RIU.

Fig. 3 (a) The real-time response of the resonance shift in response to the infusion of pure DI water, and glucose solutions with concentrations of 10mg/dL and 20mg/dL. (b) Equilibrated resonance shifts in different concentrations of glucose solutions in DI water measured by the nanobeam sensor and Biacore^TM 3000 instrument respectively. The Bi-acore chip was functionalized with (11-Mercaptoundecyl)tetra(ethylene glycol) to prevent adsorption of molecules on the gold surface to insure the measured responses are due to the bulk glucose index change.

6. Conclusion

Due to high radiation losses in the low index contrast systems, the demonstration of high-Q, small-V photonic crystal cavities has been elusive. Here we experimentally demonstrated a photonic crystal cavity with Q=36,000 in polymeric materials possessing ultra-low index-contrast. These cavities have much smaller mode volumes than the previously demonstrated polymeric WGM cavities. In addition, due to the extended optical mode profile, we demonstrated high sensitivity and linearity of the polymeric nanobeam sensor in response to different glucose concentrations in water and outperformed the commercial Biacore^TM instrument. The ability to realize high-Q/V nanophotonic resonators in a non-suspended all-polymer platform makes these devices accessible to a broad range of materials as well as simple and scalable fabrication techniques such as interference lithography, imprint lithography, and replica molding. We expect our results to stimulate a new set of applications by combining functional nanostructures with new materials, such as nonlinear optics, flexible LEDs, optofluidics.

Acknowledgments

The authors acknowledge fruitful discussions with Parag B. Deotare, Yinan Zhang and Jennifer T. Choy. IBB acknowledges support from NSERC (Canada) through the PGS-D program. This work is supported in part by NSEC at Harvard and AFOSR award FA9550-09-1-0669. Fabrication of the nanobeam cavities was performed at Harvard’s Center for Nanoscale Systems.

References and links

1.	H. Ma, A. K. Y. Jen, and L. R. Dalton, “Polymer-Based Optical Waveguides: Materials, Processing, and Devices,” Adv. Mater. 14, 1339–1365 (2002). [CrossRef]
2.	M. C. Choi, Y. Kim, and C-S. Ha, “Polymers for flexible displays: From material selection to device applications,” Prog. Polym. Sci. 33, 581–630 (2008). [CrossRef]
3.	S-I. Na, S-S. Kim, J. Jo, and D-Y Kim, “Efficient and Flexible ITO-Free Organic Solar Cells Using Highly Conductive Polymer Anodes,” Adv. Mater. 20, 4061–4067 (2008). [CrossRef]
4.	H-Y. Chen, J. Hou, S. Zhang, Y. Liang, G. Yang, Y. Yang, L. Yu, Y. Wu, and G. Li. “Polymer solar cells with enhanced open-circuit voltage and effciency,” Nat. Photon. 3, 649–653 (2009). [CrossRef]
5.	D. Ghezzi, M. R. Antognazza, M. D. Maschio, E. Lanzarini, F. Benfenati, and G. Lanzani, “A hybrid bioorganic interface for neuronal photoactivation,” Nat. Commun. 2:166 (2011). [CrossRef] [PubMed]
6.	P. Broz, (Editor) Polymer-Based Nanostructures , 1st Edition. Royal Society of Chemistry (RSC) Publishing (2010). [CrossRef]
7.	C. Chao and L. J. Guo, “Polymer microring resonators fabricated by nanoimprint technnigue,” J. Vac. Sci. Technol. B 20, 2862 (2002). [CrossRef]
8.	P. Rabiei, W. H. Steier, C. Zhang, and L. R. Dalton, “Polymer Micro-Ring Filters and Modulators,” J. Lightwave Technol. 20, 1968 (2002).
9.	Y. Huang, G. T. Paloczi, J. Scheuer, and A. Yariv, “Soft lithography replication of polymeric microring optical resonators,” Opt. Express 11, 2452 (2003). [CrossRef] [PubMed]
10.	A. L. Martin, D. K. Armani, L. Yang, and K. J. Vahala, “Replica-molded high-Q polymer microresonators,” Opt. Lett. 29, 533 (2004). [CrossRef] [PubMed]
11.	M. Khan, T. M. Babinec, M. W. McCutcheon, P.B. Deotare, and M Loncar, “Fabrication and characterization of high-quality-factor silicon nitride nanobeam cavities,” Opt. Lett. 36, 421 (2011). [CrossRef] [PubMed]
12.	G. Gong and J. Vuckovic, “Photonic crystal cavities in silicon dioxide,” Appl. Phys. Lett. 96, 031107 (2010). [CrossRef]
13.	M. Kitamura, S. Iwamoto, and Y. Arakawa, “Enhanced light emission from an organic photonic crystal with a nanocavity,” Appl. Phys. Lett. 87, 151119 (2005). [CrossRef]
14.	L. Martiradonna, L. Carbone, A. Tandaechanurat, M. Kitamura, S. Iwamoto, L. Manna, M. De Vittorio, R. Cingolani, and Y. Arakawa, “Two-dimensional photonic crystal resist membrane nanocavity embedding colloidal dot-in-a-rod nanocrystals,” Nano Lett. 8, 260 (2008). [CrossRef]
15.	A. M. Adawi, M. M. Murshidy, P. W. Fry, and D. G. Lidzey, “An optical nanocavity incorporating a fluorescent organic dye having a high quality factor,” ACS Nano 4, 3039–3044 (2010). [CrossRef] [PubMed]
16.	M. M. Murshidy, A. M. Adawi, P. W. Fry, and D. G. Lidzey, “A one-dimensional photonic-crystal nanocavity incorporating a fluorescent molecular dye,” Appl. Phys. Lett. 97, 153303 (2010). [CrossRef]
17.	Q. Quan, P. B. Deotare, and M. Loncar, “Photonic crystal nanobeam cavity strongly coupled to the feeding waveguide,” Appl. Phys. Letts. 96, 203102 (2010). [CrossRef]
18.	Q. Quan and M. Loncar, “Deterministic design of high Q, small mode volume photonic crystal nanobeam cavities,” Opt. Express 19, 18529–18542 (2011). [CrossRef]
19.	H. G. Winful, J. H. Marburger, and E. Garmire, “Theory of bistability in nonlinear distributed feedback structures,” Appl. Phys. Lett. 35, 379 (1979). [CrossRef]
20.	V. R. Almeida and M. Lipson, “Optical bistability on a silicon chip,” Opt. Lett. 29, 2387 (2004). [CrossRef] [PubMed]
21.	T. Uesugi, B. S. Song, T. Asano, and S. Noda, “Investigation of optical nonlinearities in an ultra-high-Q Si nanocavity in a two-dimensional photonic crystal slab,” Opt. Express 14, 377 (2006). [CrossRef] [PubMed]
22.	L. Haret, T. Tanabe, E. Kuramochi, and M. Notomi, “Extremely low power optical bistability in silicon demonstrated using 1D photonic crystal nanocavity,” Opt. Express 17, 21108 (2009). [CrossRef] [PubMed]
23.	T. Ling, S-L Chen, and L. J. Guo, “Fabrication and Characterization of High Q Polymer Micro-ring Resonator and Its Application as a Sensitive Ultrasonic Detector,” Opt. Express 19, 861–869 (2011) [CrossRef] [PubMed]
24.	D. Chu, M. Touzelbaev, K. E. Goodson, S. Babin, and R. F. Pease, “Thermal conductivity measurements of thin film resist,” J. Vac. Sci. Technol. B 19, 2874 (2001). [CrossRef]
25.	O. Beyer, I. Nee, F. Havermeyer, and K. Buse, “Holographic Recording of Bragg Gratings for Wavelength Division Multiplexing in Doped and Partially Polymerized Poly(methyl methacrylate),” Appl. Opt. 42, 30 (2003). [CrossRef] [PubMed]
26.	W. R. Folks, J. Ginn, D. Shelton, J. Tharp, and G. Boreman, “Spectroscopic ellipsometry of materials for infrared micro-device fabrication,” Phys. Stat. Sol. (c) 5, 1113 (2008). [CrossRef]
27.	X. D. Fan, I. M. White, S. I. Shopova, H. Y. Zhu, J. D. Suter, and Y. Sun, “Sensitive optical biosensors for unlabeled targets: A review,” Anal. Chim. Acta 620, 8 (2008). [CrossRef] [PubMed]
28.	A. M. Basedow, K. H. ebert, and U. Ruland, “Specific Refractive Index Increments of Dextran Fractions of Different Molecular Weights,” Makromol. Chem. 179, 1351–1353 (1978). [CrossRef]
29.	I. M. White and X. Fan, “On the performance quantification of resonant refractive index sensors,” Opt. Express 16, 1020 (2008). [CrossRef] [PubMed]
30.	J. N. Anker, W. P. Hall, O. Lyandres, N. C. Shah, J. Zhao, and R. P. Van Duyne, “Biosensing with plasmonic nanosensors,” Nat. Mater. 7, 442 (2008). [CrossRef] [PubMed]
31.	A. V. Kabashin, P. Evans, S. Pastkovsky, W. Hendren, G. A. Wurtz, R. Atkinson, R. Pollard, V. A. Podolskiy, and A. V. Zayats, “Plasmonic nanorod metamaterials for biosensing,” Nat. Mater. 8, 867 (2009). [CrossRef] [PubMed]

OCIS Codes
(140.4780) Lasers and laser optics : Optical resonators
(160.5470) Materials : Polymers
(280.4788) Remote sensing and sensors : Optical sensing and sensors
(230.5298) Optical devices : Photonic crystals

ToC Category:
Photonic Crystals

History
Original Manuscript: August 15, 2011
Revised Manuscript: September 18, 2011
Manuscript Accepted: September 19, 2011
Published: October 24, 2011

Virtual Issues
Collective Phenomena (2011) Optics Express

Citation
Qimin Quan, Ian B. Burgess, Sindy K. Y. Tang, Daniel L. Floyd, and Marko Loncar, "High-Q, low index-contrast polymeric photonic crystal nanobeam cavities," Opt. Express 19, 22191-22197 (2011)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-19-22-22191

Sort: Author | Year | Journal | Reset

References

H. Ma, A. K. Y. Jen, and L. R. Dalton, “Polymer-Based Optical Waveguides: Materials, Processing, and Devices,” Adv. Mater.14, 1339–1365 (2002). [CrossRef]
M. C. Choi, Y. Kim, and C-S. Ha, “Polymers for flexible displays: From material selection to device applications,” Prog. Polym. Sci.33, 581–630 (2008). [CrossRef]
S-I. Na, S-S. Kim, J. Jo, and D-Y Kim, “Efficient and Flexible ITO-Free Organic Solar Cells Using Highly Conductive Polymer Anodes,” Adv. Mater.20, 4061–4067 (2008). [CrossRef]
H-Y. Chen, J. Hou, S. Zhang, Y. Liang, G. Yang, Y. Yang, L. Yu, Y. Wu, and G. Li. “Polymer solar cells with enhanced open-circuit voltage and effciency,” Nat. Photon.3, 649–653 (2009). [CrossRef]
D. Ghezzi, M. R. Antognazza, M. D. Maschio, E. Lanzarini, F. Benfenati, and G. Lanzani, “A hybrid bioorganic interface for neuronal photoactivation,” Nat. Commun.2:166 (2011). [CrossRef] [PubMed]
P. Broz, (Editor) Polymer-Based Nanostructures, 1st Edition. Royal Society of Chemistry (RSC) Publishing (2010). [CrossRef]
C. Chao and L. J. Guo, “Polymer microring resonators fabricated by nanoimprint technnigue,” J. Vac. Sci. Technol. B20, 2862 (2002). [CrossRef]
P. Rabiei, W. H. Steier, C. Zhang, and L. R. Dalton, “Polymer Micro-Ring Filters and Modulators,” J. Lightwave Technol.20, 1968 (2002).
Y. Huang, G. T. Paloczi, J. Scheuer, and A. Yariv, “Soft lithography replication of polymeric microring optical resonators,” Opt. Express11, 2452 (2003). [CrossRef] [PubMed]
A. L. Martin, D. K. Armani, L. Yang, and K. J. Vahala, “Replica-molded high-Q polymer microresonators,” Opt. Lett.29, 533 (2004). [CrossRef] [PubMed]
M. Khan, T. M. Babinec, M. W. McCutcheon, P.B. Deotare, and M Loncar, “Fabrication and characterization of high-quality-factor silicon nitride nanobeam cavities,” Opt. Lett.36, 421 (2011). [CrossRef] [PubMed]
G. Gong and J. Vuckovic, “Photonic crystal cavities in silicon dioxide,” Appl. Phys. Lett.96, 031107 (2010). [CrossRef]
M. Kitamura, S. Iwamoto, and Y. Arakawa, “Enhanced light emission from an organic photonic crystal with a nanocavity,” Appl. Phys. Lett.87, 151119 (2005). [CrossRef]
L. Martiradonna, L. Carbone, A. Tandaechanurat, M. Kitamura, S. Iwamoto, L. Manna, M. De Vittorio, R. Cingolani, and Y. Arakawa, “Two-dimensional photonic crystal resist membrane nanocavity embedding colloidal dot-in-a-rod nanocrystals,” Nano Lett.8, 260 (2008). [CrossRef]
A. M. Adawi, M. M. Murshidy, P. W. Fry, and D. G. Lidzey, “An optical nanocavity incorporating a fluorescent organic dye having a high quality factor,” ACS Nano4, 3039–3044 (2010). [CrossRef] [PubMed]
M. M. Murshidy, A. M. Adawi, P. W. Fry, and D. G. Lidzey, “A one-dimensional photonic-crystal nanocavity incorporating a fluorescent molecular dye,” Appl. Phys. Lett.97, 153303 (2010). [CrossRef]
Q. Quan, P. B. Deotare, and M. Loncar, “Photonic crystal nanobeam cavity strongly coupled to the feeding waveguide,” Appl. Phys. Letts.96, 203102 (2010). [CrossRef]
Q. Quan and M. Loncar, “Deterministic design of high Q, small mode volume photonic crystal nanobeam cavities,” Opt. Express19, 18529–18542 (2011). [CrossRef]
H. G. Winful, J. H. Marburger, and E. Garmire, “Theory of bistability in nonlinear distributed feedback structures,” Appl. Phys. Lett.35, 379 (1979). [CrossRef]
V. R. Almeida and M. Lipson, “Optical bistability on a silicon chip,” Opt. Lett.29, 2387 (2004). [CrossRef] [PubMed]
T. Uesugi, B. S. Song, T. Asano, and S. Noda, “Investigation of optical nonlinearities in an ultra-high-Q Si nanocavity in a two-dimensional photonic crystal slab,” Opt. Express14, 377 (2006). [CrossRef] [PubMed]
L. Haret, T. Tanabe, E. Kuramochi, and M. Notomi, “Extremely low power optical bistability in silicon demonstrated using 1D photonic crystal nanocavity,” Opt. Express17, 21108 (2009). [CrossRef] [PubMed]
T. Ling, S-L Chen, and L. J. Guo, “Fabrication and Characterization of High Q Polymer Micro-ring Resonator and Its Application as a Sensitive Ultrasonic Detector,” Opt. Express19, 861–869 (2011) [CrossRef] [PubMed]
D. Chu, M. Touzelbaev, K. E. Goodson, S. Babin, and R. F. Pease, “Thermal conductivity measurements of thin film resist,” J. Vac. Sci. Technol. B19, 2874 (2001). [CrossRef]
O. Beyer, I. Nee, F. Havermeyer, and K. Buse, “Holographic Recording of Bragg Gratings for Wavelength Division Multiplexing in Doped and Partially Polymerized Poly(methyl methacrylate),” Appl. Opt.42, 30 (2003). [CrossRef] [PubMed]
W. R. Folks, J. Ginn, D. Shelton, J. Tharp, and G. Boreman, “Spectroscopic ellipsometry of materials for infrared micro-device fabrication,” Phys. Stat. Sol. (c)5, 1113 (2008). [CrossRef]
X. D. Fan, I. M. White, S. I. Shopova, H. Y. Zhu, J. D. Suter, and Y. Sun, “Sensitive optical biosensors for unlabeled targets: A review,” Anal. Chim. Acta620, 8 (2008). [CrossRef] [PubMed]
A. M. Basedow, K. H. ebert, and U. Ruland, “Specific Refractive Index Increments of Dextran Fractions of Different Molecular Weights,” Makromol. Chem.179, 1351–1353 (1978). [CrossRef]
I. M. White and X. Fan, “On the performance quantification of resonant refractive index sensors,” Opt. Express16, 1020 (2008). [CrossRef] [PubMed]
J. N. Anker, W. P. Hall, O. Lyandres, N. C. Shah, J. Zhao, and R. P. Van Duyne, “Biosensing with plasmonic nanosensors,” Nat. Mater.7, 442 (2008). [CrossRef] [PubMed]
A. V. Kabashin, P. Evans, S. Pastkovsky, W. Hendren, G. A. Wurtz, R. Atkinson, R. Pollard, V. A. Podolskiy, and A. V. Zayats, “Plasmonic nanorod metamaterials for biosensing,” Nat. Mater.8, 867 (2009). [CrossRef] [PubMed]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.

Click here to see a list of articles that cite this paper

Figures


Fig. 1	Fig. 2	Fig. 3

« Previous Article | Next Article »

OSA is a member of CrossRef.

OpticsInfoBase

Optics Express

High-Q, low index-contrast polymeric photonic crystal nanobeam cavities

Article Tools

Article Navigation

Abstract

1. Introduction

2. High-Q photonic crystal cavity in ultra-Low index-contrast polymeric materials

3. Small mode volumes

4. Optical bistability in polymeric cavities

5. Ultra-sensitive glucose sensor

6. Conclusion

Acknowledgments

References and links

References

ACS Nano

Adv. Mater.

Anal. Chim. Acta

Appl. Opt.

Appl. Phys. Lett.

Appl. Phys. Letts.

J. Lightwave Technol.

J. Vac. Sci. Technol. B

Makromol. Chem.

Nano Lett.

Nat. Commun.

Nat. Mater.

Nat. Photon.

Opt. Express

Opt. Lett.

Phys. Stat. Sol. (c)

Prog. Polym. Sci.