Ultrafast laser inscription of an integrated photonic lantern

R. R. Thomson, T. A. Birks, S. G. Leon-Saval, A. K. Kar, and J. Bland-Hawthorn  »View Author Affiliations


Optics Express, Vol. 19, Issue 6, pp. 5698-5705 (2011)
http://dx.doi.org/10.1364/OE.19.005698


View Full Text Article

Acrobat PDF (970 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

We used ultrafast laser inscription to fabricate three-dimensional integrated optical transitions that efficiently couple light from a multimode waveguide to a two-dimensional array of single mode waveguides and back. Although the entire device has an average insertion loss of 5.7 dB at 1539 nm, only ≈0.7 dB is due to mode coupling losses. Based on an analysis which is presented in the paper, we expect that our device should convert a multimode input into an array of single modes with a loss of ≈2.0 dB, assuming the input coupling losses are zero. Such devices have applications in astrophotonics and remote sensing.

© 2011 OSA

1. Introduction

Astrophotonics is the application of photonic principles to astronomical instrumentation [1

1. J. Bland-Hawthorn and P. Kern, “Astrophotonics: a new era for astronomical instruments,” Opt. Express 17(3), 1880–1884 (2009). [CrossRef] [PubMed]

]. The aim of this burgeoning field is to reduce the cost, size, weight and complexity of instruments while increasing their performance. Examples of astrophotonic devices developed so far include optical waveguide circuits for beam combination in long baseline interferometry [2

2. P. Kern, E. Le Coärer, and P. Benech, “On-chip spectro-detection for fully integrated coherent beam combiners,” Opt. Express 17(3), 1976–1987 (2009). [CrossRef] [PubMed]

] and complex fibre Bragg gratings for suppressing the fluorescence lines generated by the earth’s atmosphere [3

3. J. Bland-Hawthorn, M. Englund, and G. Edvell, “New approach to atmospheric OH suppression using an aperiodic fibre Bragg grating,” Opt. Express 12(24), 5902–5909 (2004). [CrossRef] [PubMed]

].

The “photonic lantern” (PL) [4

4. S. G. Leon-Saval, T. A. Birks, J. Bland-Hawthorn, and M. Englund, “Multimode fiber devices with single-mode performance,” Opt. Lett. 30(19), 2545–2547 (2005). [CrossRef] [PubMed]

8

8. T. A. Birks, A. Diez, J. L. Cruz, S. G. Leon-Saval, and D. F. Murphy, “Fibers are looking up: optical fiber transition structures in astrophotonics,” in Frontiers in Optics, OSA Technical Digest (CD) (Optical Society of America, 2010), paper FTuU1. http://www.opticsinfobase.org/abstract.cfm?URI=FiO-2010-FTuU1.

] is a remarkable astrophotonic device that efficiently couples light between a multimode (MM) optical fibre and a set of degenerate single mode (SM) cores in several SM fibres [4

4. S. G. Leon-Saval, T. A. Birks, J. Bland-Hawthorn, and M. Englund, “Multimode fiber devices with single-mode performance,” Opt. Lett. 30(19), 2545–2547 (2005). [CrossRef] [PubMed]

7

7. S. G. Leon-Saval, A. Argyros, and J. Bland-Hawthorn, “Photonic lanterns: a study of light propagation in multimode to single-mode converters,” Opt. Express 18(8), 8430–8439 (2010). [CrossRef] [PubMed]

] or a single multicore fibre (MCF) [4

4. S. G. Leon-Saval, T. A. Birks, J. Bland-Hawthorn, and M. Englund, “Multimode fiber devices with single-mode performance,” Opt. Lett. 30(19), 2545–2547 (2005). [CrossRef] [PubMed]

,7

7. S. G. Leon-Saval, A. Argyros, and J. Bland-Hawthorn, “Photonic lanterns: a study of light propagation in multimode to single-mode converters,” Opt. Express 18(8), 8430–8439 (2010). [CrossRef] [PubMed]

9

9. R. R. Thomson, G. Brown, A. K. Kar, T. A. Birks, and J. Bland-Hawthorn, “An integrated fan-out device for astrophotonics,” in Frontiers in Optics, OSA Technical Digest (CD) (Optical Society of America, 2010), paper PDPA3. http://www.opticsinfobase.org/abstract.cfm?URI=FiO-2010-PDPA3.

]. If the SM cores are arranged into a linear array [9

9. R. R. Thomson, G. Brown, A. K. Kar, T. A. Birks, and J. Bland-Hawthorn, “An integrated fan-out device for astrophotonics,” in Frontiers in Optics, OSA Technical Digest (CD) (Optical Society of America, 2010), paper PDPA3. http://www.opticsinfobase.org/abstract.cfm?URI=FiO-2010-PDPA3.

], the PL can enable the collection of light from a telescope using a MM fibre and the low-loss reformatting of this light into a near diffraction limited input (in one axis) for a bulk optic spectrograph, minimising spectrometer size for a given resolution. Similarly it also facilitates the use of mass-producible photonic spectrographs based on Arrayed Waveguide Gratings (AWGs) [10

10. N. Cvetojevic, J. S. Lawrence, S. C. Ellis, J. Bland-Hawthorn, R. Haynes, and A. Horton, “Characterization and on-sky demonstration of an integrated photonic spectrograph for astronomy,” Opt. Express 17(21), 18643–18650 (2009). [CrossRef]

], Stationary-Wave Integrated Fourier-Transform Spectrometry (SWIFT) [11

11. E. le Coarer, S. Blaize, P. Benech, I. Stefanon, A. Morand, G. Lérondel, G. Leblond, P. Kern, J. M. Fedeli, and P. Royer, “Wavelength-scale stationary-wave integrated Fourier-transform spectrometry,” Nat. Photonics 1(8), 473–478 (2007). [CrossRef]

] or Leaky Loop Integrated Fourier Transform Spectrometers (LLIFTS) [12

12. B. Martin, A. Morand, P. Benech, G. Grosa, P. Kern, L. Jocou, and E. Le Coarer, “Realization of the compact static Fourier transform spectrometer LLIFTS in glass integrated optics,” Opt. Lett. 34(15), 2291–2293 (2009). [CrossRef] [PubMed]

]. Recently, for example, the PIMMS instrument concept has been proposed [13

13. J. Bland-Hawthorn, J. Lawrence, G. Robertson, S. Campbell, B. Pope, C. Betters, S. Leon-Saval, T. Birks, R. Haynes, N. Cvetojevic, and N. Jovanovic, “PIMMS: photonic integrated multimode microspectrograph,” Proc. SPIE 7735, 77350N (2010). [CrossRef]

] which suggests that a single AWG can be used to process all the single modes produced at the output of a PL. This could be important in diverse field spectroscopy - a group of techniques which enable astronomers and space scientists to select regions of a telescope image for spectroscopic analysis.

Currently, PLs are made in two ways based on optical fibres. In the first [4

4. S. G. Leon-Saval, T. A. Birks, J. Bland-Hawthorn, and M. Englund, “Multimode fiber devices with single-mode performance,” Opt. Lett. 30(19), 2545–2547 (2005). [CrossRef] [PubMed]

6

6. D. Noordegraaf, P. M. W. Skovgaard, M. D. Maack, J. Bland-Hawthorn, R. Haynes, and J. Laegsgaard, “Multi-mode to single-mode conversion in a 61 port Photonic Lantern,” Opt. Express 18(5), 4673–4678 (2010). [CrossRef] [PubMed]

], multiple SM fibres are stacked inside a low-index capillary. This fibre-filled capillary is then tapered down until the SM cores are too small to properly guide light. At this point the amalgamated claddings of the SM fibres become a single MM core, with the capillary acting as the cladding. If the taper is sufficiently gradual, it forms a low-loss adiabatic transition between this MM core and the SM fibres. A low-loss device has been made which efficiently couples the output of a MM fibre into a set of 61 SM cores and back [6

6. D. Noordegraaf, P. M. W. Skovgaard, M. D. Maack, J. Bland-Hawthorn, R. Haynes, and J. Laegsgaard, “Multi-mode to single-mode conversion in a 61 port Photonic Lantern,” Opt. Express 18(5), 4673–4678 (2010). [CrossRef] [PubMed]

]. However, this method is highly labour intensive and prohibitively expensive for mass-production. To overcome this drawback, PLs can instead be made using MCFs [8

8. T. A. Birks, A. Diez, J. L. Cruz, S. G. Leon-Saval, and D. F. Murphy, “Fibers are looking up: optical fiber transition structures in astrophotonics,” in Frontiers in Optics, OSA Technical Digest (CD) (Optical Society of America, 2010), paper FTuU1. http://www.opticsinfobase.org/abstract.cfm?URI=FiO-2010-FTuU1.

]. A single MCF with over 100 individual SM cores is placed inside the low-index capillary instead of the stacked SM fibres, and this construction is tapered down to achieve the required gradual transition. Since the MCF can be drawn in km lengths and only a few metres are required for each PL, this route is potentially low cost and suitable for mass-production.

Despite the success of these fibre tapering techniques, significant benefits of cost, size, robustness and suitability for mass-production arise if PLs could be realised using integrated optical waveguides. However, because the input to the PL is MM in both orthogonal axes, integrated PLs inherently require a three-dimensional (3D) waveguide fabrication technology. Recently we proposed [14

14. R. R. Thomson, A. K. Kar, and J. Allington-Smith, “Ultrafast laser inscription: an enabling technology for astrophotonics,” Opt. Express 17(3), 1963–1969 (2009). [CrossRef] [PubMed]

], and here now demonstrate, that ultrafast laser inscription can be used to fabricate integrated PLs. This 3D technique uses focused ultrashort laser pulses to locally modify the structure of a dielectric material, and hence its refractive index [15

15. K. M. Davis, K. Miura, N. Sugimoto, and K. Hirao, “Writing waveguides in glass with a femtosecond laser,” Opt. Lett. 21(21), 1729–1731 (1996). [CrossRef] [PubMed]

]. If this modification is appropriately controlled, it can be used to directly write, or inscribe, optical waveguides by translating the material in 3D through the laser focus. This unique capability facilitates the fabrication of 3D couplers [16

16. R. R. Thomson, H. T. Bookey, N. D. Psaila, A. Fender, S. Campbell, W. N. Macpherson, J. S. Barton, D. T. Reid, and A. K. Kar, “Ultrafast-laser inscription of a three dimensional fan-out device for multicore fiber coupling applications,” Opt. Express 15(18), 11691–11697 (2007). [CrossRef] [PubMed]

] and two-dimensional arrays of coupled waveguides [17

17. T. Pertsch, U. Peschel, F. Lederer, J. Burghoff, M. Will, S. Nolte, and A. Tünnermann, “Discrete diffraction in two-dimensional arrays of coupled waveguides in silica,” Opt. Lett. 29(5), 468–470 (2004). [CrossRef] [PubMed]

,18

18. C. Mauclair, G. Cheng, N. Huot, E. Audouard, A. Rosenfeld, I. V. Hertel, and R. Stoian, “Dynamic ultrafast laser spatial tailoring for parallel micromachining of photonic devices in transparent materials,” Opt. Express 17(5), 3531–3542 (2009). [CrossRef] [PubMed]

].

2. Integrated photonic lantern fabrication

An integrated PL was fabricated using ultrafast laser inscription to produce the structure shown conceptually in Fig. 1(a)
Fig. 1 Sketches of (a) a MM-to-SM integrated PL transition and (b) a MM-to-SM-to-MM transition created by inscribing two of the PLs shown in (a) back-to-back.
. At one end, the PL consisted of 16 SM waveguides arranged in a two-dimensional 4 × 4 array, with an inter-waveguide spacing of 50 µm. At the opposite end these waveguides were brought together in 3D to form a single MM waveguide.

The substrate material was a borosilicate glass (Corning Eagle 2000) with a refractive index n ≈1.49 at 1550 nm. Structures were inscribed inside the substrate using the ultrashort pulses generated by a master-oscillator power-amplifier fibre laser supplied by IMRA. The pulse energy and pulse repetition rate were set to 165 nJ and 500 kHz respectively, and the laser polarisation was set to circular. Circularly polarized light was used in order to reduce the probability of the inscribed waveguides exhibiting guiding properties which depend on the sample translation direction [19

19. M. Ams, G. D. Marshall, and M. J. Withford, “Study of the influence of femtosecond laser polarisation on direct writing of waveguides,” Opt. Express 14(26), 13158–13163 (2006). [CrossRef] [PubMed]

]. The measured pulse duration was ≈350 fs FWHM and the central wavelength was 1047 nm. The laser light was focused below the surface of the substrate using an aspheric lens with a numerical aperture of 0.4. To translate the sample through the focus, it was mounted on computer controlled Aerotech x-y-z air-bearing stages. All structures were inscribed using a sample translation velocity of 8.0 mm.s−1. Throughout the paper we will consistently refer to the laser beam direction as the z-axis, the primary sample translation direction as the y-axis and the axis orthogonal to both as the x-axis, Fig. 1.

The induced refractive index distribution was controlled using the well established multiscan technique [20

20. A. A. Said, M. Dugan, P. Bado, Y. Bellouard, A. Scott, and J. Mabesa, “Manufacturing by laser direct-write of three-dimensional devices containing optical and microfluidic networks,” Proc. SPIE 5339, 194–204 (2004). [CrossRef]

,21

21. Y. Nasu, M. Kohtoku, and Y. Hibino, “Low-loss waveguides written with a femtosecond laser for flexible interconnection in a planar light-wave circuit,” Opt. Lett. 30(7), 723–725 (2005). [CrossRef] [PubMed]

]. Each SM waveguide was therefore formed by scanning the sample back and forth through the laser focus 20 times (10 in each direction), with individual scans separated by 0.4 μm along x. The SM-to-MM transition was formed by bringing the SM waveguides together in 3D using straight waveguide paths over a y-axis length of 25 mm. At the end of the transition (i.e. the MM waveguide) this equates to four bands of refractive index modification, each starting and finishing at the same position along x but ≈8.0 μm apart along z. Each band was formed using 80 scans (40 in each direction) of the sample separated by 0.4 μm along x. The PL structures were constructed using continuous scans of the sample along its full y-axis length, without stopping at the interfaces between each section in the device. Thus, all sections of the device were constructed simultaneously, not individually. To avoid shadowing effects, the deepest scans were performed first and the device was built upwards layer by layer progressively towards the surface.

Three separate structures were inscribed on each of two 70 mm long substrates (substrates 1 and 2). These structures were a full MM-to-SM-to-MM transition comprising two PLs back-to-back as shown in Fig. 1(b), a matching straight MM waveguide, and a matching straight SM waveguide.

3. Photonic lantern characterization

3.1. Facet images and guided light

After inscription, substrate 1 was diced in the middle to expose the waveguide array and the exposed waveguide facets of one half were polished. We will refer to the MM, PL and SM structures on this half as MM-1, PL-1 and SM-1 respectively. Transmission mode optical micrographs of the SM array end of PL-1 and MM-1 are presented in Figs. 2(a)
Fig. 2 White light transmission micrographs of (a) the 4 × 4 SM array end of PL-1 and (b) one end of MM-1. (c) Single frame from a near field video recording (Media 1) of the SM array end of PL-1 while adjusting the injection of 1539 nm light into the MM end. (d) Single frame from a near field video recording (Media 2) of MM-1 while adjusting the injection of 1539 nm light into the opposite end. The field of view is 200 μm × 200 μm for (a) and (c), and 100 μm × 100 μm for (b) and (d). In all cases, the inscription laser entered the sample from below.
and 2(b) respectively.

We used 1539 nm laser light to investigate the inscribed structures. First, we coupled this light into SM-1 by direct butt-coupling from a SM fibre, while imaging the output onto a phosphor coated CCD camera. Only the TEM00 mode could be excited while adjusting the input coupling, indicating that the waveguide supported only a single mode. The light was then similarly coupled into the MM end of PL-1, and it was observed that the injected light did indeed couple to the SM array at the output, Fig. 2(c). Furthermore, as shown in Fig. 2(c) (Media 1), the intensity distribution across the SM array changed as the coupling was adjusted, confirming qualitatively that more than one of the modes of the MM end is coupled into the array.

The modes of MM-1 were similarly investigated, confirming that MM-1 was multimode and that the modes extended fully across the waveguide cross-section. Different transverse modes were excited as the input coupling was adjusted, Fig. 2(d) (Media 2). These observations confirm that our method of combining 16 SM waveguides into a single MM waveguide was successful.

3.2. Refractive index profile measurements

The refractive index profiles (RIPs) of MM-1 and one of the SM waveguides of PL-1 were measured by the refracted near field principle with 670 nm light using a Rinck-elektronik profiler. The measured RIP of the SM waveguide, Fig. 3
Fig. 3 (a) Two-dimensional refractive index profile of one of the SM waveguides of PL-1. The laser entered from the −z direction. (b) & (c) One-dimensional index profiles along z and x respectively, taken at x = 0 and z = 0 respectively in (a).
, was not measured to be a well defined top-hat profile. This could be the result of convolution with the profiler point spread function (PSF), in which case it may not measure the full magnitude of the index contrast. When the profiler laser light is optimally focused onto the sample under test, we evaluated the PSF along the z-axis to be equivalent to a Gaussian with a FWHM size of ≈1.5 μm. We presume that the PSF along the x-axis is comparable. For our sample however it was non-trivial to achieve precise focusing onto the waveguide facet due to the low Fresnel reflection from the oil-glass interface (The profiler is designed to be used with silica-on-silicon waveguides where the Fresnel reflection from the silicon substrate can be used for viewing and focusing the laser). If the laser is not correctly focused onto the waveguide facet, the PSF may be significantly larger than the optimum value reported above. Regardless of these considerations, the apparent maximum index contrast of Δ = (n coren clad)/n core ≈1.76 × 10−3 measured for the structure in Fig. 3 does at least gives an indication of the level of index change induced using the fabrication parameters described in §2.

MM-1 exhibited a high quality top-hat RIP, Fig. 4
Fig. 4 (a) Two-dimensional normalised refractive index profile of MM-1 (the structure shown in Fig. 2(b)). The laser entered from the −z direction. (b) & (c) One-dimensional normalised index profiles along z and x respectively, taken at x = 0 and z = 0 respectively in (a).
. The spatial index distribution is highly symmetric and almost 35 μm square, Fig. 4(a). However, the MM waveguide was too far below the sample surface for the profiler to measure the waveguide and the reference materials used for calibration. The profiles in Fig. 4 are therefore normalised and show only the uniformity and distribution of the index modification. Interestingly, from Fig. 4(b) it can be seen that the z-axis section through the RIP has three clear peaks where the four bands of index modification overlap. This indicates that the index modification is not fully saturated in the regions where there is no overlap between the individual bands. It should therefore be possible to further increase the refractive index contrast of the MM waveguide, either by decreasing the x-axis separation between adjacent scans or by reducing the sample translation speed. Lastly, it can be seen that both profiles shown in Fig. 3(a) and Fig. 4(a) appear to be slightly wider along the z-axis on the -x side of the profiles. For Fig. 4(a), this observation agrees with the optical micrograph of the structure shown in Fig. 2(b). This feature was observed to be repeatable across numerous MM structures written with these parameters. The multiscan process used to inscribe the structure shown in Fig. 3 started on the -x side, as did each band of modification used to fabricate the structure in Fig. 4. The narrowing of the band of modification as it is built up is therefore the result of some cumulative phenomena, the nature of which is not yet known.

3.3. Insertion loss measurements

Important considerations are the absolute loss of the integrated PL and also the coupling efficiency from the MM section into the SM array. We measured loss using MM light prepared using PL-1 as a SM-to-MM transition. 1539 nm light was coupled into each SM waveguide of PL-1 and input coupling optimized to produce different superpositions of modes at the MM end. A polarization controller after the source was used to scan all polarization states and the maximum and minimum powers at the MM end were recorded.

The MM output of PL-1 was then used as the source to characterize the losses of two structures on the 70 mm long (undiced) substrate 2: a straight MM waveguide and a full MM-to-SM-to-MM transition as shown in Fig. 1(b)). We refer to the two structures as MM-2 and PL-2 respectively (PL-2 was therefore in fact two PLs back-to-back, as shown in Fig. 1(b)). The loss was measured by directly butt-coupling the MM output of PL-1 into the structure under test and measuring the light emerging from its other end. This was repeated for light in each SM input of PL-1. We stress that the input coupling from PL-1 was not adjusted during the measurements. The average insertion loss (and polarization dependent loss) was 5.0 dB (1.1 dB) for MM-2 and 5.7 dB (1.2 dB) for PL-2. The 0.7 dB difference in average insertion loss between MM-2 and PL-2 demonstrates that mode coupling losses in the transition of PL-2 are low.

4. Discussion

The MM end of the integrated PL has dimensions of ≈35 μm × 35 μm, as expected from the inscription parameters. Although we were unable to calibrate the RIP in Fig. 4, it is reasonable to assume that the index contrast of the MM waveguide is similar to that measured for the SM waveguide in Fig. 3. Using a finite element package (Femlab), we modelled the MM end of the PL as a 35 μm square step-index waveguide with n core = 1.49263 and n cladding = 1.49 (i.e. Δ = 1.76 × 10−3) and found 13 spatial modes (26 vector modes) at 1539 nm.

Clearly the loss of our integrated PL is too high for some astrophotonic applications with their focus on deep space observations, but it is also clear that it should be possible to reduce the losses substantially. For example, neglecting the input and output coupling losses of MM-2 (since the MM output of PL-1 should be identical to MM-2) we estimate the attenuation of MM-2 to be ≈0.7 dB.cm−1. Since 2.4 cm of PL-2 was straight MM waveguide performing no useful function, we have an effective insertion loss of ≈4.0 dB for the full MM-to-SM-to-MM transition (PL-2). Furthermore, many applications require only a MM-to-SM transition, so we can expect to achieve this function with 2.0 dB loss. With careful optimization of the fabrication process it should be possible to reduce these losses to the low level required for astronomy.

5. Conclusions

We have demonstrated for the first time that ultrafast laser inscription can be used to fabricate an integrated 3D optical waveguide transition that efficiently couples the modes of a multimode waveguide to a degenerate single mode waveguide array. We also demonstrated that the multiscan technique facilitates the fabrication of large cross section multimode waveguides with top-hat refractive index profiles, and that they can be constructed by spatially combining multiple single mode waveguides.

Finally, this work opens the way to a new class of monolithic instruments for astrophotonics, remote sensing and space photonics. These instruments will operate using multimode inputs and combine functions such as dispersion, mode manipulation and detection on a single chip, removing coupling losses between components, reducing costs and increasing the instrument robustness.

Acknowledgments

This work was funded by the UK Science and Technology Facilities Council (STFC) through R. R. Thomson’s Advanced Fellowship (ST/H005595/1) and by the UK Engineering and Physical Sciences Research Council (EPSRC) (Grant EP/G030227/1). T. A. Birks thanks the Leverhulme Trust for a Research Fellowship. J. Bland-Hawthorn is supported by an Australian Research Council (ARC) Federation Fellowship and S. G. Leon-Saval is supported by an ARC Australian Postdoctoral Fellowship. R. R. Thomson sincerely thanks M. Jubber of Gemfire Europe Ltd. for providing access to the refractive index profiler.

References and links

1.

J. Bland-Hawthorn and P. Kern, “Astrophotonics: a new era for astronomical instruments,” Opt. Express 17(3), 1880–1884 (2009). [CrossRef] [PubMed]

2.

P. Kern, E. Le Coärer, and P. Benech, “On-chip spectro-detection for fully integrated coherent beam combiners,” Opt. Express 17(3), 1976–1987 (2009). [CrossRef] [PubMed]

3.

J. Bland-Hawthorn, M. Englund, and G. Edvell, “New approach to atmospheric OH suppression using an aperiodic fibre Bragg grating,” Opt. Express 12(24), 5902–5909 (2004). [CrossRef] [PubMed]

4.

S. G. Leon-Saval, T. A. Birks, J. Bland-Hawthorn, and M. Englund, “Multimode fiber devices with single-mode performance,” Opt. Lett. 30(19), 2545–2547 (2005). [CrossRef] [PubMed]

5.

D. Noordegraaf, P. M. W. Skovgaard, M. D. Nielsen, and J. Bland-Hawthorn, “Efficient multi-mode to single-mode coupling in a photonic lantern,” Opt. Express 17(3), 1988–1994 (2009). [CrossRef] [PubMed]

6.

D. Noordegraaf, P. M. W. Skovgaard, M. D. Maack, J. Bland-Hawthorn, R. Haynes, and J. Laegsgaard, “Multi-mode to single-mode conversion in a 61 port Photonic Lantern,” Opt. Express 18(5), 4673–4678 (2010). [CrossRef] [PubMed]

7.

S. G. Leon-Saval, A. Argyros, and J. Bland-Hawthorn, “Photonic lanterns: a study of light propagation in multimode to single-mode converters,” Opt. Express 18(8), 8430–8439 (2010). [CrossRef] [PubMed]

8.

T. A. Birks, A. Diez, J. L. Cruz, S. G. Leon-Saval, and D. F. Murphy, “Fibers are looking up: optical fiber transition structures in astrophotonics,” in Frontiers in Optics, OSA Technical Digest (CD) (Optical Society of America, 2010), paper FTuU1. http://www.opticsinfobase.org/abstract.cfm?URI=FiO-2010-FTuU1.

9.

R. R. Thomson, G. Brown, A. K. Kar, T. A. Birks, and J. Bland-Hawthorn, “An integrated fan-out device for astrophotonics,” in Frontiers in Optics, OSA Technical Digest (CD) (Optical Society of America, 2010), paper PDPA3. http://www.opticsinfobase.org/abstract.cfm?URI=FiO-2010-PDPA3.

10.

N. Cvetojevic, J. S. Lawrence, S. C. Ellis, J. Bland-Hawthorn, R. Haynes, and A. Horton, “Characterization and on-sky demonstration of an integrated photonic spectrograph for astronomy,” Opt. Express 17(21), 18643–18650 (2009). [CrossRef]

11.

E. le Coarer, S. Blaize, P. Benech, I. Stefanon, A. Morand, G. Lérondel, G. Leblond, P. Kern, J. M. Fedeli, and P. Royer, “Wavelength-scale stationary-wave integrated Fourier-transform spectrometry,” Nat. Photonics 1(8), 473–478 (2007). [CrossRef]

12.

B. Martin, A. Morand, P. Benech, G. Grosa, P. Kern, L. Jocou, and E. Le Coarer, “Realization of the compact static Fourier transform spectrometer LLIFTS in glass integrated optics,” Opt. Lett. 34(15), 2291–2293 (2009). [CrossRef] [PubMed]

13.

J. Bland-Hawthorn, J. Lawrence, G. Robertson, S. Campbell, B. Pope, C. Betters, S. Leon-Saval, T. Birks, R. Haynes, N. Cvetojevic, and N. Jovanovic, “PIMMS: photonic integrated multimode microspectrograph,” Proc. SPIE 7735, 77350N (2010). [CrossRef]

14.

R. R. Thomson, A. K. Kar, and J. Allington-Smith, “Ultrafast laser inscription: an enabling technology for astrophotonics,” Opt. Express 17(3), 1963–1969 (2009). [CrossRef] [PubMed]

15.

K. M. Davis, K. Miura, N. Sugimoto, and K. Hirao, “Writing waveguides in glass with a femtosecond laser,” Opt. Lett. 21(21), 1729–1731 (1996). [CrossRef] [PubMed]

16.

R. R. Thomson, H. T. Bookey, N. D. Psaila, A. Fender, S. Campbell, W. N. Macpherson, J. S. Barton, D. T. Reid, and A. K. Kar, “Ultrafast-laser inscription of a three dimensional fan-out device for multicore fiber coupling applications,” Opt. Express 15(18), 11691–11697 (2007). [CrossRef] [PubMed]

17.

T. Pertsch, U. Peschel, F. Lederer, J. Burghoff, M. Will, S. Nolte, and A. Tünnermann, “Discrete diffraction in two-dimensional arrays of coupled waveguides in silica,” Opt. Lett. 29(5), 468–470 (2004). [CrossRef] [PubMed]

18.

C. Mauclair, G. Cheng, N. Huot, E. Audouard, A. Rosenfeld, I. V. Hertel, and R. Stoian, “Dynamic ultrafast laser spatial tailoring for parallel micromachining of photonic devices in transparent materials,” Opt. Express 17(5), 3531–3542 (2009). [CrossRef] [PubMed]

19.

M. Ams, G. D. Marshall, and M. J. Withford, “Study of the influence of femtosecond laser polarisation on direct writing of waveguides,” Opt. Express 14(26), 13158–13163 (2006). [CrossRef] [PubMed]

20.

A. A. Said, M. Dugan, P. Bado, Y. Bellouard, A. Scott, and J. Mabesa, “Manufacturing by laser direct-write of three-dimensional devices containing optical and microfluidic networks,” Proc. SPIE 5339, 194–204 (2004). [CrossRef]

21.

Y. Nasu, M. Kohtoku, and Y. Hibino, “Low-loss waveguides written with a femtosecond laser for flexible interconnection in a planar light-wave circuit,” Opt. Lett. 30(7), 723–725 (2005). [CrossRef] [PubMed]

OCIS Codes
(130.3120) Integrated optics : Integrated optics devices
(140.3390) Lasers and laser optics : Laser materials processing

ToC Category:
Laser Microfabrication

History
Original Manuscript: February 10, 2011
Revised Manuscript: March 5, 2011
Manuscript Accepted: March 5, 2011
Published: March 11, 2011

Virtual Issues
April 15, 2011 Spotlight on Optics

Citation
R. R. Thomson, T. A. Birks, S. G. Leon-Saval, A. K. Kar, and J. Bland-Hawthorn, "Ultrafast laser inscription of an integrated photonic lantern," Opt. Express 19, 5698-5705 (2011)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-19-6-5698


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. J. Bland-Hawthorn and P. Kern, “Astrophotonics: a new era for astronomical instruments,” Opt. Express 17(3), 1880–1884 (2009). [CrossRef] [PubMed]
  2. P. Kern, E. Le Coärer, and P. Benech, “On-chip spectro-detection for fully integrated coherent beam combiners,” Opt. Express 17(3), 1976–1987 (2009). [CrossRef] [PubMed]
  3. J. Bland-Hawthorn, M. Englund, and G. Edvell, “New approach to atmospheric OH suppression using an aperiodic fibre Bragg grating,” Opt. Express 12(24), 5902–5909 (2004). [CrossRef] [PubMed]
  4. S. G. Leon-Saval, T. A. Birks, J. Bland-Hawthorn, and M. Englund, “Multimode fiber devices with single-mode performance,” Opt. Lett. 30(19), 2545–2547 (2005). [CrossRef] [PubMed]
  5. D. Noordegraaf, P. M. W. Skovgaard, M. D. Nielsen, and J. Bland-Hawthorn, “Efficient multi-mode to single-mode coupling in a photonic lantern,” Opt. Express 17(3), 1988–1994 (2009). [CrossRef] [PubMed]
  6. D. Noordegraaf, P. M. W. Skovgaard, M. D. Maack, J. Bland-Hawthorn, R. Haynes, and J. Laegsgaard, “Multi-mode to single-mode conversion in a 61 port Photonic Lantern,” Opt. Express 18(5), 4673–4678 (2010). [CrossRef] [PubMed]
  7. S. G. Leon-Saval, A. Argyros, and J. Bland-Hawthorn, “Photonic lanterns: a study of light propagation in multimode to single-mode converters,” Opt. Express 18(8), 8430–8439 (2010). [CrossRef] [PubMed]
  8. T. A. Birks, A. Diez, J. L. Cruz, S. G. Leon-Saval, and D. F. Murphy, “Fibers are looking up: optical fiber transition structures in astrophotonics,” in Frontiers in Optics, OSA Technical Digest (CD) (Optical Society of America, 2010), paper FTuU1. http://www.opticsinfobase.org/abstract.cfm?URI=FiO-2010-FTuU1 .
  9. R. R. Thomson, G. Brown, A. K. Kar, T. A. Birks, and J. Bland-Hawthorn, “An integrated fan-out device for astrophotonics,” in Frontiers in Optics, OSA Technical Digest (CD) (Optical Society of America, 2010), paper PDPA3. http://www.opticsinfobase.org/abstract.cfm?URI=FiO-2010-PDPA3 .
  10. N. Cvetojevic, J. S. Lawrence, S. C. Ellis, J. Bland-Hawthorn, R. Haynes, and A. Horton, “Characterization and on-sky demonstration of an integrated photonic spectrograph for astronomy,” Opt. Express 17(21), 18643–18650 (2009). [CrossRef]
  11. E. le Coarer, S. Blaize, P. Benech, I. Stefanon, A. Morand, G. Lérondel, G. Leblond, P. Kern, J. M. Fedeli, and P. Royer, “Wavelength-scale stationary-wave integrated Fourier-transform spectrometry,” Nat. Photonics 1(8), 473–478 (2007). [CrossRef]
  12. B. Martin, A. Morand, P. Benech, G. Grosa, P. Kern, L. Jocou, and E. Le Coarer, “Realization of the compact static Fourier transform spectrometer LLIFTS in glass integrated optics,” Opt. Lett. 34(15), 2291–2293 (2009). [CrossRef] [PubMed]
  13. J. Bland-Hawthorn, J. Lawrence, G. Robertson, S. Campbell, B. Pope, C. Betters, S. Leon-Saval, T. Birks, R. Haynes, N. Cvetojevic, and N. Jovanovic, “PIMMS: photonic integrated multimode microspectrograph,” Proc. SPIE 7735, 77350N (2010). [CrossRef]
  14. R. R. Thomson, A. K. Kar, and J. Allington-Smith, “Ultrafast laser inscription: an enabling technology for astrophotonics,” Opt. Express 17(3), 1963–1969 (2009). [CrossRef] [PubMed]
  15. K. M. Davis, K. Miura, N. Sugimoto, and K. Hirao, “Writing waveguides in glass with a femtosecond laser,” Opt. Lett. 21(21), 1729–1731 (1996). [CrossRef] [PubMed]
  16. R. R. Thomson, H. T. Bookey, N. D. Psaila, A. Fender, S. Campbell, W. N. Macpherson, J. S. Barton, D. T. Reid, and A. K. Kar, “Ultrafast-laser inscription of a three dimensional fan-out device for multicore fiber coupling applications,” Opt. Express 15(18), 11691–11697 (2007). [CrossRef] [PubMed]
  17. T. Pertsch, U. Peschel, F. Lederer, J. Burghoff, M. Will, S. Nolte, and A. Tünnermann, “Discrete diffraction in two-dimensional arrays of coupled waveguides in silica,” Opt. Lett. 29(5), 468–470 (2004). [CrossRef] [PubMed]
  18. C. Mauclair, G. Cheng, N. Huot, E. Audouard, A. Rosenfeld, I. V. Hertel, and R. Stoian, “Dynamic ultrafast laser spatial tailoring for parallel micromachining of photonic devices in transparent materials,” Opt. Express 17(5), 3531–3542 (2009). [CrossRef] [PubMed]
  19. M. Ams, G. D. Marshall, and M. J. Withford, “Study of the influence of femtosecond laser polarisation on direct writing of waveguides,” Opt. Express 14(26), 13158–13163 (2006). [CrossRef] [PubMed]
  20. A. A. Said, M. Dugan, P. Bado, Y. Bellouard, A. Scott, and J. Mabesa, “Manufacturing by laser direct-write of three-dimensional devices containing optical and microfluidic networks,” Proc. SPIE 5339, 194–204 (2004). [CrossRef]
  21. Y. Nasu, M. Kohtoku, and Y. Hibino, “Low-loss waveguides written with a femtosecond laser for flexible interconnection in a planar light-wave circuit,” Opt. Lett. 30(7), 723–725 (2005). [CrossRef] [PubMed]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.

Figures

Fig. 1 Fig. 2 Fig. 3
 
Fig. 4
 

Multimedia

Multimedia FilesRecommended Software
» Media 1: MOV (3701 KB)      QuickTime
» Media 2: MOV (3733 KB)      QuickTime

« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited