Auger optimization in mid-infrared lasers: the importance of final-state optimization

Michael E. Flatté and C. H. Grein  »View Author Affiliations


Optics Express, Vol. 2, Issue 4, pp. 131-136 (1998)
http://dx.doi.org/10.1364/OE.2.000131


View Full Text Article

Acrobat PDF (798 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

We consider the effect of reducing the density of final hole states for Auger processes on the Auger rate at room temperature and 77K at densities near lasing thresholds. The system of interest is a strain-compensated superlattice based on the InAs/GaInSb material system with a 3.7 μm band gap. At 77K the Auger lifetime is reduced by two orders of magnitude, while the change at 300K is less than a factor of two. We conclude that final-state optimization in this particular structure, while pronounced at 77K, has little effect at 300K.

© Optical Society of America

Carrier recombination in room-temperature high-quality semiconductors with band gaps in the mid-infrared and carrier densities sufficient for lasing is typically dominated by direct Auger processes. In such a process a pair recombines and transfers its energy and momentum to another electron (electron Auger process) or another hole (hole Auger process). Strategies to reduce Auger rates through “band-structure engineering” can be placed into several categories: (1) band-edge optimization, characterized by attempts to reduce the band-edge density of states of the valence band, (2) intersubband absorption reduction, and (3) final-state optimization, characterized by attempts to eliminate final states for the carrier excited during the pair recombination process.

Band-edge optimization works because the threshold carrier density decreases when the valence band density of states decreases1

1. E. Yablonovitch and E. O. Kane, “Reduction of Lasing Threshold Current Density by the Lowering of Valence Band Effective Mass”, J. Lightwave Technol. LT-4 , 504 (1986). [CrossRef]

. Since the Auger rate per pair depends strongly on the carrier density (as n 2 for equal densities of electrons and holes in the non-degenerate regime), the reduced threshold carrier density directly translates into a reduced threshold current density. Even if the recombination rate per pair is not dominated by Auger processes, it typically increases at higher carrier densities, and so reducing the threshold carrier density has motivated the use of strained heterostructure lasers in several wavelength ranges2

2. e.gL. A. Coldren and S. W. Corzine, Diode Lasers and Photonic Integrated Circuits (Wiley, New York,1995).

. Strain lifts the heavy-light hole degeneracy at the valence band edge and thus makes the heavy-hole’s in-plane mass light, implying a lower band-edge density of states. This lower band-edge density of states induces a lower threshold carrier density, a longer carrier lifetime, and, as a final result, a lower threshold current density. In the mid-infrared several types of material systems incorporating strain have been explored3–8

3. T. C. Hasenberg, R. H. Miles, A. R. Kost, and L. West, “Recent advances in Sb-based midwave-infrared lasers”, J. Quantum Electron. QE-33, 1403 (1997). [CrossRef]

.

Strategies for intersubband absorption reduction focus on eliminating interva-lence or interconduction transitions at energies equal to the lasing energies. By reducing these loss mechanisms the threshold carrier density is reduced. Just as described above in the case of band-edge optimization, a reduced threshold carrier density implies a longer carrier lifetime and a lower threshold current density. This strategy is realized by designing a structure with gaps in the valence band states for small in-plane momentum and at energies near a lasing energy above the conduction minimum and a lasing energy below the valence maximum. This procedure has been successfully applied to systems in the mid-infrared9

9. M. E. Flatté, J. T. Olesberg, S. A. Anson, T. F. Boggess, T. C. Hasenberg, R. H. Miles, and C. H. Grein, “Theoretical Performance of Mid-Infrared Broken-Gap Multilayer Superlattice Lasers”, Appl. Phys. Lett. 70, 3212 (1997). The layer widths of the four-layer superlattice given in this reference are in error — in fact they should be the same as those of the superlattice considered here. [CrossRef]

, 10

10. M. E. Flatté, C. H. Grein, and H. Ehrenreich, “Sensitivity of optimization of mid-infrared InAs/InGaSb laser active regions to temperature and composition variations”, Appl. Phys. Lett. in press.

.

As a model system we consider a strain-compensated broken-gap superlattice9

9. M. E. Flatté, J. T. Olesberg, S. A. Anson, T. F. Boggess, T. C. Hasenberg, R. H. Miles, and C. H. Grein, “Theoretical Performance of Mid-Infrared Broken-Gap Multilayer Superlattice Lasers”, Appl. Phys. Lett. 70, 3212 (1997). The layer widths of the four-layer superlattice given in this reference are in error — in fact they should be the same as those of the superlattice considered here. [CrossRef]

with a 300K emission wavelength of 3.7 μm, 13.8Å InAs/24Å Ga0.60In0.40Sb/13.8Å InAs/40Å Al0.30Ga0.42In0.28As0.50Sb0.50. The band structure of this superlattice exhibits final-state optimization; namely, it has a gap in the growth-axis final states at certain crucial energies (so-called resonance energies). These resonance energies are located Eg below the valence maximum and Eg above the conduction minimum, where Eg is the fundamental gap. (The intersubband absorption of this structure at the lasing energy is also minimal — note that the resonance energies are also (roughly) the relevant energies for intersubband absorption9

9. M. E. Flatté, J. T. Olesberg, S. A. Anson, T. F. Boggess, T. C. Hasenberg, R. H. Miles, and C. H. Grein, “Theoretical Performance of Mid-Infrared Broken-Gap Multilayer Superlattice Lasers”, Appl. Phys. Lett. 70, 3212 (1997). The layer widths of the four-layer superlattice given in this reference are in error — in fact they should be the same as those of the superlattice considered here. [CrossRef]

.) The band structure of this superlattice is shown in Fig 1, and the resonance energies are indicated by red lines. Final states in the valence band (for hole Auger) must lie below the red line at E V - E g, while final states in the conduction band (for electron Auger) must lie above the red line at E C + E g.

Figure 1. Band structure for a 13.8Å InAs/24Å In0.40Ga0.60Sb/13.8Å InAs/40Å Al0.30In0.28Ga0.42As0.50Sb0.50 superlattice at a lattice temperature of 300K. The in-plane momentum is K while the growth-direction momentum is K . Resonance energies within the conduction band and valence band are shown by solid red lines. The subbands which contribute most to the hole Auger rate are indicated in blue. Dashed lines mark the conduction and valence edge energies. The electrons (filled magenta circles) and holes (empty magenta circles) involved in the (roughly) 500 most probable transitions at (a) 77K and n = 5 × 1016 cm-3 and (b) 300K and n = 5 × 1017 cm-3 are also shown. In (b) the single most probable transition is shown in green schematically

Calculations of the electronic structure of the superlattice considered here were performed with an envelope-function approximation and using a superlattice K·p technique similar to that used in Refs. 12

12. M. E. Flatté, C. H. Grein, H. Ehrenreich, R. H. Miles, and H. Cruz, “Theoretical performance limits of 2.1 – 4.1 μm InAs/InGaSb, HgCdTe, and InGaAsSb lasers”, J. Appl. Phys. 78, 4552 (1995). [CrossRef]

and 13

13. M. E. Flatté, P. M. Young, L.-H. Peng, and H. Ehrenreich, “Generalized superlattice K·p theory and intersubband optical transitions”, Phys. Rev. B 53, 1963 (1996). [CrossRef]

but generalized to an arbitrary number of layers in the unit cell. Parameters (with the exception of the energy gap) of the bulk materials comprising the superlattice layers are linearly interpolated from binary constituents. The valence band offsets are also largely linearly interpolated. The experimental parameters are obtained principally from Refs. 14

14. O. Madelung, in Semiconductors, Physics of Group IV Elements and III–V Compounds, edited by K.-H. Helluege and O. Madelung, Landolt-Börnstein, New Series, Group III, Vol. 17, Pt. a (Springer-Verlag, Berlin,1982).

and 15

15. O. Madelung in Intrinsic Properties of Group IV Elements and III–V, II–VI and I–VII Compounds, edited by K.-H. Helluege and O. Madelung, Landolt-Börnstein, New Series, Group III, Vol. 22, Pt. a (Springer-Verlag, Berlin,1987).

, and are tabulated in Ref. 12

12. M. E. Flatté, C. H. Grein, H. Ehrenreich, R. H. Miles, and H. Cruz, “Theoretical performance limits of 2.1 – 4.1 μm InAs/InGaSb, HgCdTe, and InGaAsSb lasers”, J. Appl. Phys. 78, 4552 (1995). [CrossRef]

. The single exception is the energy of the conduction band in the quinternary, which occurs (including strain effects) 1.045 eV above the InAs conduction band. The Auger rates are evaluated according to the formalism described in detail in Ref. 11

11. C. H. Grein, P. M. Young, M. E. Flatté, and H. Ehrenreich, “Long wavelength InAs/InGaSb infrared detectors: Optimization of carrier lifetimes”, J. Appl. Phys. 78, 7143 (1995). [CrossRef]

, with the recent addition of Umklapp processes, which contribute about half of the total direct Auger rate16

16. M. E. Flatté, C. H. Grein, T. C. Hasenberg, S. A. Anson, D.-J. Jang, J. T. Olesberg, and T. F. Boggess, “Carrier recombination rates in narrow-gap semiconductor superlattices”, unpublished.

.

In order to examine final-state optimization we focus entirely on hole Auger. Strong experimental evidence based on the density dependence of the rate indicates that the hole Auger rate dominates in this structure16

16. M. E. Flatté, C. H. Grein, T. C. Hasenberg, S. A. Anson, D.-J. Jang, J. T. Olesberg, and T. F. Boggess, “Carrier recombination rates in narrow-gap semiconductor superlattices”, unpublished.

. Calculations indicate the electron Auger rate to be more than 3 times smaller than the hole Auger rate at 300K lasing densities. This may not be the case in other mid-infrared laser active regions.

There is a substantial gap (140 meV in Fig. 1(a,b)) in the valence band around the resonance energy for momenta along the growth direction (K ). States do reside at the resonance energy, however, for finite in-plane momentum (K ). The subbands most involved as final states for hole Auger are those directly under the resonance energy line, and are shown in blue. Also shown are the (roughly) 500 most probable hole Auger transitions as a function of in-plane momentum at typical lasing threshold carrier densities at 77K (Fig. 1(a)) and 300K (Fig. 1(b)). The electrons involved in this process are indicated by filled magenta circles, while the holes are indicated by empty magenta circles. The single most probable process is shown in Fig. 1(b) schematically in green. The process whereby the equilibrium electron deep within the valence band eliminates a band-edge hole can also be understood as a band-edge hole being excited to a higher-energy state. The momentum of this final-state hole is the sum of the momenta of the initial pair and the extra band-edge hole.

The elimination of band-edge Auger processes due to final-state optimization does occur at 77K and does reduce the Auger rate. The non-equilibrium electrons in the conduction band which are involved in Auger processes (shown in Fig. 1(a)) are clearly at higher energy than the band minimum. Their energy difference is roughly 30 meV, which corresponds to ~ 4kBT. Since the occupation factors are proportional to exp(-E/kBT), this energy difference produces a reduction in the occupation factor of two orders of magnitude. Since the hole Auger rate is directly proportional to that occupation factor, the hole Auger rate is also reduced by two orders of magnitude.

The situation at 300K is shown in Fig. 1(b). Due to the marked sensitivity of the Auger rate on band gap the differences in the band structure at 77K and 300K are ignored; as a control we use the 300K band structure for both carrier temperatures. Whereas the nonequilibrium carriers were quite concentrated at the zone center at 77K, at 300K they are substantially more spread out. In addition, the non-equilibrium electrons involved in the most probable transitions are located at the conduction band minimum. Hence the contribution of final-state optimization to reducing the Auger rate at 300K seems likely to be small.

Our procedure is to take the band structure shown in Fig. 1(a,b) and manually shift the fourth, fifth and sixth valence subbands from the valence edge (shown in blue in Fig. 1(a,b)) in energy and observe the effect on the carrier lifetimes. As the bands are shifted up more states at zero in-plane momentum become accessible as final states for Auger processes. We show in Fig. 2 the 500 most probable transitions for the same situation as Fig. 1, but with the three subbands (shown in blue) shifted up by 90 meV at 77K (Fig. 2(a)) and 100 meV at 300K (Fig. 2(b)). Immediately evident in Fig. 2(a) is that the electrons (filled magenta circles) in the conduction band which were 30meV above the band edge in Fig. 1(a) are now at the band edge. Hence the final-state optimization has been removed. At 300K, in contrast, there is little difference.

Figure 2. Same as Fig. 1, but with the most important (blue) subbands shifted up in energy by (a) 90 meV and (b) 100 meV. Only the valence resonance energy is shown (red).

Fig. 3 shows the carrier lifetime as a function of the energy shift of the bands towards the band edge. The lifetime becomes long for large positive energy shifts, for the relevant bands eventually become shifted above the resonance energy, and thus cannot contribute to the Auger rate. The lifetime also becomes long for large negative energy shifts because the subbands become too far below the resonance energy to be accessible for Auger processes involving band-edge nonequilibrium electrons and holes. It is particularly the latter situation we are interested in, for it is the essence of final-state optimization.

The behavior for small shifts is markedly more pronounced at 77K than at 300K. Whereas at 77K the difference in Auger rate between the 77K band structures of Fig. 1(a) and Fig. 2(a) is over two orders of magnitude, the difference in Auger rate between the 300K band structures of Fig. 1(b) and Fig. 2(b) is less than a factor of two. In fact, the design of Fig. 1(b), which was intended to have a long Auger lifetime, has a lifetime which is near the minimum calculated. The Auger suppression of Fig. 1(a) arises because the final states of the three blue subbands are sufficiently low in energy to be difficult for band-edge electrons and holes to use as final states. At 300K a structure with a resonance energy gap 100 meV larger than Fig. 1(b) (corresponding to a -100 meV shift of the bands in Fig. 3(b)) would have a hole Auger rate suppressed by one order of magnitude simply from final-state effects.

Figure 3. Hole Auger lifetime as a function of the energy shift of the fourth, fifth and sixth valence subbands towards the band edge (a) at 77K and a density of 5 × 1016 cm-3 and (b) at 300K and a density of 5 × 1017 cm-3.

We can estimate the width of the lifetime minimum in Fig. 3(a,b) from the spread of the electron and hole distributions in the conduction and valence bands. At 77K the conduction band degeneracy is 7 meV, and added to 2kBT (one for electrons and one for holes) yields 20 meV. At 300K the conduction band degeneracy is 33 meV, which added to 2kBT yields ~ 80 meV. At both temperatures the valence band is not degenerate. These estimates of the widths of the lifetime minimum agree reasonably well with Fig. 3(a,b).

Our results indicate that increasing temperature has a profound impact on final-state optimization for Auger suppression. Future work will consider the importance of Auger suppression at temperatures intermediate between 77K and 300K. It appears from Fig. 3(b) that at 300K the final-state optimization has just ceased to be of any importance, suggesting that for this structure it may still be important at temperatures just slightly lower. We conclude by pointing out that the beneficial effects of the band structure shown in Fig. 1(b) on the loss via valence intersubband absorption9

9. M. E. Flatté, J. T. Olesberg, S. A. Anson, T. F. Boggess, T. C. Hasenberg, R. H. Miles, and C. H. Grein, “Theoretical Performance of Mid-Infrared Broken-Gap Multilayer Superlattice Lasers”, Appl. Phys. Lett. 70, 3212 (1997). The layer widths of the four-layer superlattice given in this reference are in error — in fact they should be the same as those of the superlattice considered here. [CrossRef]

remain present even though the final-state optimization is weak.

This research was supported in part by the United States Air Force, Air Force Materiel Command, Phillips Laboratory (PL), Kirtland AFB New Mexico 87117-5777 (contract F29601-97-C0041).

References

1.

E. Yablonovitch and E. O. Kane, “Reduction of Lasing Threshold Current Density by the Lowering of Valence Band Effective Mass”, J. Lightwave Technol. LT-4 , 504 (1986). [CrossRef]

2.

e.gL. A. Coldren and S. W. Corzine, Diode Lasers and Photonic Integrated Circuits (Wiley, New York,1995).

3.

T. C. Hasenberg, R. H. Miles, A. R. Kost, and L. West, “Recent advances in Sb-based midwave-infrared lasers”, J. Quantum Electron. QE-33, 1403 (1997). [CrossRef]

4.

D. H. Chow, R. H. Miles, T. C. Hasenberg, A. R. Kost, Y.-H. Zhang, H. L. Dunlap, and L. West, “Mid-wave infrared diode lasers based on GaInSb/InAs and InAs/AlSb superlattices”, Appl. Phys. Lett. 67, 3700 (1995). [CrossRef]

5.

J. R. Meyer, C. A. Hoffman, F. J. Bartoli, and L. R. Ram-Mohan, “Type II quantum-well lasers for the mid-wavelength infrared”, Appl. Phys. Lett. 67, 757 (1995). [CrossRef]

6.

H. K. Choi, G. W. Turner, and M. J. Manfra, “High CW power (>200mW/facet) at 3.4μm from InAsSb/InAlAsSb strained quantum well diode lasers”, Electron. Lett. 32, 1296 (1996). [CrossRef]

7.

H. K. Choi, G. W. Turner, M. J. Manfra, and M. K. Connors, “175K continuous wave operation of InAsSb/InAlAsSb quantum-well diode lasers emitting at 3.5μ”, Appl. Phys. Lett. 68, 2936 (1996). [CrossRef]

8.

S. R. Kurtz, R. M. Biefeld, A. A. Allerman, A. J. Howard, M. H. Crawford, and M. W. Pelczynski, “Pseudomorphic InAsSb multiple quantum well injection laser emitting at 3.5 μm”, Appl. Phys. Lett. 68, 1332 (1996). [CrossRef]

9.

M. E. Flatté, J. T. Olesberg, S. A. Anson, T. F. Boggess, T. C. Hasenberg, R. H. Miles, and C. H. Grein, “Theoretical Performance of Mid-Infrared Broken-Gap Multilayer Superlattice Lasers”, Appl. Phys. Lett. 70, 3212 (1997). The layer widths of the four-layer superlattice given in this reference are in error — in fact they should be the same as those of the superlattice considered here. [CrossRef]

10.

M. E. Flatté, C. H. Grein, and H. Ehrenreich, “Sensitivity of optimization of mid-infrared InAs/InGaSb laser active regions to temperature and composition variations”, Appl. Phys. Lett. in press.

11.

C. H. Grein, P. M. Young, M. E. Flatté, and H. Ehrenreich, “Long wavelength InAs/InGaSb infrared detectors: Optimization of carrier lifetimes”, J. Appl. Phys. 78, 7143 (1995). [CrossRef]

12.

M. E. Flatté, C. H. Grein, H. Ehrenreich, R. H. Miles, and H. Cruz, “Theoretical performance limits of 2.1 – 4.1 μm InAs/InGaSb, HgCdTe, and InGaAsSb lasers”, J. Appl. Phys. 78, 4552 (1995). [CrossRef]

13.

M. E. Flatté, P. M. Young, L.-H. Peng, and H. Ehrenreich, “Generalized superlattice K·p theory and intersubband optical transitions”, Phys. Rev. B 53, 1963 (1996). [CrossRef]

14.

O. Madelung, in Semiconductors, Physics of Group IV Elements and III–V Compounds, edited by K.-H. Helluege and O. Madelung, Landolt-Börnstein, New Series, Group III, Vol. 17, Pt. a (Springer-Verlag, Berlin,1982).

15.

O. Madelung in Intrinsic Properties of Group IV Elements and III–V, II–VI and I–VII Compounds, edited by K.-H. Helluege and O. Madelung, Landolt-Börnstein, New Series, Group III, Vol. 22, Pt. a (Springer-Verlag, Berlin,1987).

16.

M. E. Flatté, C. H. Grein, T. C. Hasenberg, S. A. Anson, D.-J. Jang, J. T. Olesberg, and T. F. Boggess, “Carrier recombination rates in narrow-gap semiconductor superlattices”, unpublished.

OCIS Codes
(140.3070) Lasers and laser optics : Infrared and far-infrared lasers
(140.5960) Lasers and laser optics : Semiconductor lasers

ToC Category:
Focus Issue: Quantum well laser design

History
Original Manuscript: October 9, 1997
Published: February 16, 1998

Citation
Michael Flatte and C. Grein, "Auger optimization in mid-infrared lasers: the importance of final-state optimization," Opt. Express 2, 131-136 (1998)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-2-4-131


Sort:  Journal  |  Reset  

References

  1. E. Yablonovitch and E. O. Kane, "Reduction of Lasing Threshold Current Density by the Lowering of Valence Band Effective Mass", J. Lightwave Technol. LT- 4, 504 (1986). [CrossRef]
  2. e.g. L. A. Coldren and S. W. Corzine, Diode Lasers and Photonic Integrated Circuits (Wiley, New York, 1995).
  3. T. C. Hasenberg, R. H. Miles, A. R. Kost, and L. West, "Recent advances in Sb-based midwaveinfrared lasers", J. Quantum Electron. QE-33, 1403 (1997). [CrossRef]
  4. D. H. Chow, R. H. Miles, T. C. Hasenberg, A. R. Kost, Y.-H. Zhang, H. L. Dunlap, and L. West, "Mid-wave infrared diode lasers based on GaInSb/InAs and InAs/AlSb superlattices", Appl. Phys. Lett. 67, 3700 (1995). [CrossRef]
  5. J. R. Meyer, C. A. Hoffman, F. J. Bartoli, and L. R. Ram-Mohan, "Type II quantum-well lasers for the mid-wavelength infrared", Appl. Phys. Lett. 67, 757 (1995). [CrossRef]
  6. H. K. Choi, G. W. Turner, and M. J. Manfra, "High CW power (>200mW/facet) at 3.4µm from InAsSb/InAlAsSb strained quantum well diode lasers", Electron. Lett. 32, 1296 (1996). [CrossRef]
  7. H. K. Choi, G. W. Turner, M. J. Manfra, and M. K. Connors, "175K continuous wave operation of InAsSb/InAlAsSb quantum-well diode lasers emitting at 3.5µm", Appl. Phys. Lett. 68, 2936 (1996). [CrossRef]
  8. S. R. Kurtz, R. M. Biefeld, A. A. Allerman, A. J. Howard, M. H. Crawford, and M. W. Pelczynski, "Pseudomorphic InAsSb multiple quantum well injection laser emitting at 3.5 µm", Appl. Phys. Lett. 68, 1332 (1996). [CrossRef]
  9. M. E. Flatte', J. T. Olesberg, S. A. Anson, T. F. Boggess, T. C. Hasenberg, R. H. Miles, and C. H. Grein, "Theoretical Performance of Mid-Infrared Broken-Gap Multilayer Superlattice Lasers", Appl. Phys. Lett. 70, 3212 (1997). The layer widths of the four-layer superlattice given in this reference are in error. In fact they should be the same as those of the superlattice considered here. [CrossRef]
  10. M. E. Flatte', C. H. Grein, and H. Ehrenreich, "Sensitivity of optimization of mid-infrared InAs/InGaSb laser active regions to temperature and composition variations", Appl. Phys. Lett. in press.
  11. C. H. Grein, P. M. Young, M. E. Flatte', and H. Ehrenreich, "Long wavelength InAs/InGaSb infrared detectors: Optimization of carrier lifetimes", J. Appl. Phys. 78, 7143 (1995). [CrossRef]
  12. M. E. Flatte', C. H. Grein, H. Ehrenreich, R. H. Miles, and H. Cruz, "Theoretical performance limits of 2:1 [CrossRef]
  13. M. E. Flatte', P. M. Young, L.-H. Peng, and H. Ehrenreich, "Generalized superlattice K p theory and intersubband optical transitions", Phys. Rev. B 53, 1963 (1996). [CrossRef]
  14. O. Madelung, in Semiconductors, Physics of Group IV Elements and III-V Compounds, edited by K.-H. Helluege and O. Madelung, Landolt-Boernstein, New Series, Group III, Vol. 17, Pt. a (Springer-Verlag, Berlin, 1982).
  15. O. Madelung in Intrinsic Properties of Group IV Elements and III-V, II-VI and I-VII Compounds, edited by K.-H. Helluege and O. Madelung, Landolt-Boernstein, New Series, Group III, Vol. 22, Pt. a (Springer-Verlag, Berlin, 1987).
  16. M. E. Flatte', C. H. Grein, T. C. Hasenberg, S. A. Anson, D.-J. Jang, J. T. Olesberg, and T. F. Boggess, "Carrier recombination rates in narrow-gap semiconductor superlattices", unpublished.

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited