Spectroscopic properties and laser performance of resonantly-pumped cryo-cooled Er3+:GdVO4

N. Ter-Gabrielyan, V. Fromzel, W. Ryba-Romanowski, T. Lukasiewicz, and M. Dubinskii  »View Author Affiliations


Optics Express, Vol. 20, Issue 6, pp. 6080-6084 (2012)
http://dx.doi.org/10.1364/OE.20.006080


View Full Text Article

Acrobat PDF (1889 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

We report a highly efficient cryo-cooled eye-safe laser operation of a resonantly-pumped (in-band) Er3+:GdVO4 single crystal. The maximum continuous wave (CW) power of 10.3 W with 84% slope efficiency was achieved at 1598.7 with pumping at 1538.6 nm by a spectrally-narrowed Er-fiber laser. Under the 1529 nm resonant pumping by a commercially available diode bar stack operating in a quasi-CW (QCW) mode, the laser delivered 37 W of output power with 68% slope efficiency. This is believed to be the first reported cryo-cooled Er3+:GdVO4 laser, resonantly-pumped into the 4I15/24I13/2 transition.

© 2012 OSA

1. Introduction

Er-doped laser materials have been established as one of the best choices in designing resonantly-pumped, highly scalable eye-safe lasers operating in the 1.6 micrometer (μm) wavelength range. Cryogenically-cooled, Er-doped lasers such as Er:YAG, Er:YVO4, Er:Sc2O3 and Er:NaY(WO4)2, have demonstrated very efficient low quantum defect (QD) operation [1

1. S. D. Setzler, M. J. Shaw, M. J. Kukla, J. R. Unternahrer, K. M. Dinndorf, J. A. Beattie, and E. P. Chicklis, “A 400 W cryogenic Er:YAG slab laser at 1645 nm,” Proc. SPIE 7686, 76860C, C7 (2010). [CrossRef]

5

5. N. Ter-Gabrielyan, V. Fromzel, T. Lukasiewicz, W. Ryba-Romanowski, and M. Dubinskii, “Nearly quantum-defect-limited efficiency, resonantly pumped, Er3+:YVO₄ laser at 1593.5 nm,” Opt. Lett. 36(7), 1218–1220 (2011). [CrossRef] [PubMed]

]. Cryogenic cooling is known to improve thermo-mechanical, thermo-optical, and spectroscopic properties for the majority of laser hosts. While absorption and emission cross-sections become stronger with cooling, the absorption lines also become much narrower and require narrow-linewidth pump sources – the issue which can hinder pumping efficiency [6

6. N. Ter-Gabrielyan, V. Fromzel, L. D. Merkle, and M. Dubinskii, “Resonant in-band pumping of cryo-cooled Er3+:YAG laser at 1532, 1534 and 1546 nm: a comparative study,” Opt. Mater. Express 1(2), 223–233 (2011). [CrossRef]

]. Disordered laser hosts, such as Er:NaY(WO4)2, even at cryogenic temperatures exhibit very broad absorption transitions convenient for resonant pumping, but their thermal conductivity is usually low, which limits power scaling [3

3. M. Dubinskii, V. Fromzel, N. Ter-Gabrielyan, M. D. Serrano, D. E. Lahera, C. Cascales, and C. Zaldo, “Spectroscopic characterization and laser performance of resonantly diode-pumped Er(3+)-doped disordered NaY(WO4)2.,” Opt. Lett. 36(16), 3263–3265 (2011). [CrossRef] [PubMed]

]. Uniaxial Erbium-doped yttrium vanadate material (Er:YVO4) offers a compromise: it exhibits large absorption and emission cross-sections while its absorption lines remain relatively broad. This feature helps in achieving efficient laser operation with InP diode-based pump sources [4

4. N. Ter-Gabrielyan, V. Fromzel, T. Lukasiewicz, W. Ryba-Romanowski, and M. Dubinskii, “High power resonantly diode-pumped σ-configuration Er3+:YVO4 laser at 1593.5 nm,” Laser Phys. Lett. 8(7), 529–534 (2011). [CrossRef]

]. Similarly high efficiency can potentially be expected for Er:GdVO4 laser (which is a close analog to Er:YVO4).

Rare earth-doped gadolinium vanadate (GdVO4) was introduced in 1992 [7

7. A. I. Zagumenny, V. G. Ostroumov, I. A. Shcherbakov, T. Jensen, J.-P. Meyn, and G. Huber, “The Nd:GdVO4 crystal: a new material for diode-pumped laser,” Sov. J. Quantum Electron. 22(12), 1071–1072 (1992). [CrossRef]

] as a close analog to commercially available YVO4. Additional interest to GdVO4 is also driven by contradictory literature data on its thermal conductivity relative to that of YAG and especially of YVO4 [8

8. A. I. Zagumenny, P. A. Popov, F. Zerouk, Yu. D. Zavartsev, S. A. Kutovoi, and I. A. Scherbakov, “Heat conduction of laser vanadate crystals,” Quantum Electron. 38(3), 227–232 (2008). [CrossRef]

10

10. J. Didierjean, E. Herault, F. Balembois, and P. Georges, “Thermal conductivity measurements of laser crystals by infrared thermography. Application to Nd:doped crystals,” Opt. Express 16(12), 8995–9010 (2008). [CrossRef] [PubMed]

]. Most of the latest reported data indicates that the thermal conductivity of GdVO4 along its crystallographic c-axis is higher than that of YAG and at least similar to that of YVO4. While efficient resonantly-pumped cryogenic and room temperature Er:YVO4 lasers have been reported earlier [4

4. N. Ter-Gabrielyan, V. Fromzel, T. Lukasiewicz, W. Ryba-Romanowski, and M. Dubinskii, “High power resonantly diode-pumped σ-configuration Er3+:YVO4 laser at 1593.5 nm,” Laser Phys. Lett. 8(7), 529–534 (2011). [CrossRef]

, 5

5. N. Ter-Gabrielyan, V. Fromzel, T. Lukasiewicz, W. Ryba-Romanowski, and M. Dubinskii, “Nearly quantum-defect-limited efficiency, resonantly pumped, Er3+:YVO₄ laser at 1593.5 nm,” Opt. Lett. 36(7), 1218–1220 (2011). [CrossRef] [PubMed]

, 11

11. J. Sulc, H. Jelinkova, W. Ryba-Romanowski, and T. Lukasiewicz, “1.6 um microchip laser,” Laser Phys. Lett. 6(3), 207–211 (2009). [CrossRef]

, 12

12. C. Brandt, V. Matrosov, K. Petermann, and G. Huber, “In-band fiber-laser-pumped Er:YVO₄ laser emitting around 1.6 μm,” Opt. Lett. 36(7), 1188–1190 (2011). [CrossRef] [PubMed]

], the laser potential of the similarly pumped Er3+:GdVO4, to the best of our knowledge, has only been evaluated at room temperature [13

13. N. Ter-Gabrielyan, V. Fromzel, W. Ryba-Romanowski, T. Lukasiewicz, and M. Dubinskii, “Efficient, Resonantly Pumped, Room Temperature Er3+:GdVO4 Laser,” Opt. Lett.: posted 01/27/2012; Doc. ID 160739

]. The maximum CW output power of 3.5 W with slope efficiency of 56% was achieved with resonant pumping by an Er-fiber laser at 1538.6 nm. With pumping by a commercial diode laser bar stack, a quasi-CW (QCW) output of 7.7 W and a maximum slope efficiency of ~53% with respect to the absorbed pump power were obtained [13

13. N. Ter-Gabrielyan, V. Fromzel, W. Ryba-Romanowski, T. Lukasiewicz, and M. Dubinskii, “Efficient, Resonantly Pumped, Room Temperature Er3+:GdVO4 Laser,” Opt. Lett.: posted 01/27/2012; Doc. ID 160739

].

In this paper, we present spectroscopic characteristics of Er3+:GdVO4 in the 1450–1650 nm wavelength range defined by the 4I13/24I15/2 transitions and report the laser performance of a cryo-cooled Er3+:GdVO4 crystal under the resonant pumping by two different pump sources: spectrally-narrow Er-fiber laser and commercial InGaAsP/InP diode bar stack. The maximum CW power of 10.3 W with 84% slope efficiency was achieved at 1598.7 nm with pumping at 1538.6 nm by a fiber laser. Under the 1529 nm resonant pumping by a diode bar stack operating in a QCW mode, the laser delivered 37 W of output power with 68% slope efficiency. To the best of our knowledge, this is the first resonantly-pumped cryo-cooled laser based on 4I13/24I15/2 transitions of Er3+ in GdVO4.

2. Spectroscopy

For spectroscopic characterization, we used an Er3+:GdVO4 crystal grown by the Czochralski technique with a doping concentration of 0.5% (NEr = 6.05∙1019 cm−3). The measurements were focused on the 4I13/24I15/2 transitions within the 1450–1650 nm wavelength range.

The polarization-resolved absorption spectra of the Er3+:GdVO4 crystal, cryogenically-cooled to 77 K, were measured using Cary 6000i spectrophotometer, operating in the fixed-slit-width mode with the 0.1 nm resolution. The cross-sections of Er3+:GdVO4, derived from the measured absorbance, are presented in Fig. 1(a)
Fig. 1 Polarization resolved absorption (a) and emission (b) cross-sections of the 4I15/24I13/2 transitions in Er3+:GdVO4.
. The absorption bands are generally stronger for σ-polarization, with the exception of a broad and strong transition at ~1502 nm (cross-section σabs ~2.2∙10−19 cm2). The zero-zero absorption line at 1529.3 nm, which corresponds to the transition from the lowest Stark components of the 4I15/2 and the 4I13/2 manifolds, also exhibits a large cross-section of ~1.5-1.6∙10−19 cm2. This transition has approximately equal strength for both polarizations with the linewidth of ~1.3 nm full width half maximum (FWHM) and, thus, is suitable for pumping by an unpolarized source.

The emission spectra of Er3+:GdVO4 sample were obtained by exciting the 4I13/24I15/2 fluorescence with a 970 nm diode laser (via 4I15/24I11/2 transition). Luminescence was collected and processed by an optical spectrum analyzer (Yokogawa, model AQ6370C) with spectral resolution set to 0.02 nm. A polarization beam splitter was inserted into collecting optics to separate the σ- and π-polarized signals. Cross-sections (σemi) of the 4I13/24I15/2 transitions in both polarizations, calculated using the standard Fuchtbauer-Landenburg method [14

14. W. Fowler and D. Dexter, “Relation between absorption and emission probabilities in luminescent centers in ionic solids,” Phys. Rev. 128(5), 2154–2165 (1962). [CrossRef]

], are shown in Fig. 1(b).

The π-polarized emission exhibits a major peak around 1599 nm (σemi ~2∙10−20 cm2), formed by the two overlapping transitions centered at ~1598.7 (Y1 →Z7) and at ~1599 nm (Y2→Z8). In the σ-polarized spectrum, there is an attractive peak around 1588 nm with σemi ~1.3∙10−20 cm2. This peak is also formed by two almost indistinguishable (wavelength-wise) transitions: Y1 →Z6 and Y3 →Z7.

The fluorescence lifetime of the 4I13/2 level was measured on a 0.5%-doped Er3+:GdVO4 crystal sample, which was pulverized in order to minimize effects of reabsorption and radiation trapping on experimental results. The sample was excited by 100 μsec pulses of an InP diode laser tuned to the 1529 nm absorption line. The fluorescence signal was detected with a Germanium photodiode and the sampled kinetic was processed by a digital oscilloscope (Tektronix, model TDS 2022B). A room temperature lifetime was measured to be ~3.06 ms and versus ~3.5 ms measured at 77 K. The results for the entire temperature range of 77-300K, presented in Fig. 2(a)
Fig. 2 (a) Temperature dependence of the 4I13/2 lifetime of Er3+ in GdVO4. (b) A simplified energy level diagram of the 4I13/2 and the 4I15/2 manifolds with Boltzmann populations at 77 K. The major pump transitions are shown with blue arrows; red arrows represent the fluorescence transitions of relevance to laser operation around 1.6 μm.
, were consistent with those measured by Bertini et al for a 1% Er:GdVO4 sample [15

15. C. Bertini, A. Toncelli, M. Tonelli, E. Cavalli, and N. Magnani, “Optical spectroscopy and laser parameters of GdVO4:Er3+,” J. Lumin. 106(3-4), 235–242 (2004). [CrossRef]

].

The simplified energy level diagram of the Er3+:GdVO4 crystal for the 4I13/2 and the 4I15/2 manifolds obtained from the analysis of the absorption and emission spectra and major transitions between their Stark sublevels are shown in Fig. 2(b). This diagram is also consistent with that reported by Bertini et al [15

15. C. Bertini, A. Toncelli, M. Tonelli, E. Cavalli, and N. Magnani, “Optical spectroscopy and laser parameters of GdVO4:Er3+,” J. Lumin. 106(3-4), 235–242 (2004). [CrossRef]

].

3. Cryogenic Laser Experiments

Laser experiments were carried out on an anti-reflection coated 10 mm long, 7 mm wide, and 3 mm thick Er3+(0.7%):GdVO4 single crystal (NEr = 8.47∙1019 cm−3). Its crystallographic c-axis was normal to the axis of the laser cavity, thus, the crystal could be longitudinally pumped in any chosen polarization. The crystal was mounted on a copper plate inside the liquid nitrogen cryostat. The setup was almost identical to that described in [4

4. N. Ter-Gabrielyan, V. Fromzel, T. Lukasiewicz, W. Ryba-Romanowski, and M. Dubinskii, “High power resonantly diode-pumped σ-configuration Er3+:YVO4 laser at 1593.5 nm,” Laser Phys. Lett. 8(7), 529–534 (2011). [CrossRef]

].

Two different pump sources spectrally matching one of the major absorption lines of Er3+:GdVO4 were used in laser experiments. One of them was a 20 W, CW, unpolarized, single mode Er-fiber laser with a ~0.3 nm FWHM emission bandwidth, which fits inside the 1538.6 nm absorption line. The motivation for using a narrow-linewidth, single mode fiber laser as a pump source was to avoid both spectral and spatial mismatches in pumping in order to achieve maximum efficiency of the Er3+:GdVO4 laser in a low QD operation.

The pump beam was focused into the crystal by the F = 100 mm spherical lens through a flat dichroic mirror (T > 98% @ 1520 −1540 nm, R > 99.5% @ 1590 −1650 nm). The pumped volume was cylindrical in shape with a diameter of ~330 μm (at 1/e2 level) along the entire crystal length, as measured by IR CCD camera (Spiricon, model LW230).

The laser cavity was formed by the flat dichroic mirror and a concave output coupler with the radius of curvature (RCC) of 100 mm and reflectivities (ROC) within the 70% - 90% range. The cavity length (Lcav) was chosen to be about 80 mm to provide the best pump-cavity mode spatial matching.

The CW performance of the cryogenic Er3+:GdVO4 laser, resonantly pumped into the 1538.6 nm absorption line by the Er-fiber laser, is shown in Fig. 3(a)
Fig. 3 Input-Output characteristics of the cryogenic Er3+:GdVO4 laser. (a) CW pumping with the Er-fiber laser; (b) Pumping with the QCW diode bar stack.
. Without any wavelength selective elements inside the cavity, the laser operated in π-polarization at 1598.7 nm with 3.9% QD. The emission bandwidth strongly depended on the pump power and its full value approached 4 nm at the maximum pump.

The fraction of the absorbed pump varied due to the saturation effect [16

16. Y. Sato and T. Taira, “Saturation factors of pump absorption in solid-state lasers,” IEEE J. Quantum Electron. 40(3), 270–280 (2004). [CrossRef]

] from ~0.85 at the threshold to ~0.65 at full 20 W of the incident pump and was predictably dependent on the output coupling. In order to avoid inconsistencies in laser efficiency measurement, we determined the absorbed pump when the laser was in the “operational” mode (above the threshold), measuring the incident pump, the transmitted pump and the laser output power simultaneously.

As seen in Fig. 3(a), the maximum achieved slope efficiency was 84% with ROC = 85%. The maximum obtained CW output power was 10.3 W for the ROC = 70%.

Figure 3(b) shows the QCW performance of the Er3+:GdVO4 laser with the laser diode stack pumping. It also operated in a π-polarization at 1598.7 nm (4.6% QD). The best slope efficiency of 68% was achieved with the ROC = 85%. The maximum obtained QCW laser output was 37.3 W. The fraction of the QCW absorbed pump varied from 0.73 - 0.83 at the threshold to 0.66-0.77 at full 96 W of the pump power (for ROC = 85% and 70% respectively). The difference in efficiencies of fiber laser- and the diode bar stack-pumped Er:GdVO4 lasers can be explained by much better pump-cavity mode matching in the former case.

4. Conclusions

We reported what is believed to be the first resonantly-pumped cryo-cooled laser based on an Er3+ doped GdVO4 single crystal. Spectroscopic characteristics and laser performance of this laser utilizing transitions between the 4I15/2 and 4I13/2 manifolds (1450-1650 nm) at cryogenic temperatures were investigated. A slope efficiency as high as 84% and a maximum CW output power of 10.3 W at 1598.7 nm have been obtained for resonant pumping into the 1538.6 nm absorption line by a narrow-linewidth Er-fiber laser. With the resonant pumping into the 1529 nm absorption band by a commercial InGaAsP/InP FAC/SAC laser diode bar stack, we achieved the maximum slope efficiency of ~68% and the maximum QCW output power of ~37 W.

References and links

1.

S. D. Setzler, M. J. Shaw, M. J. Kukla, J. R. Unternahrer, K. M. Dinndorf, J. A. Beattie, and E. P. Chicklis, “A 400 W cryogenic Er:YAG slab laser at 1645 nm,” Proc. SPIE 7686, 76860C, C7 (2010). [CrossRef]

2.

N. Ter-Gabrielyan, L. D. Merkle, A. Ikesue, and M. Dubinskii, “Ultralow quantum-defect eye-safe Er:Sc2O3 laser,” Opt. Lett. 33(13), 1524–1526 (2008). [CrossRef] [PubMed]

3.

M. Dubinskii, V. Fromzel, N. Ter-Gabrielyan, M. D. Serrano, D. E. Lahera, C. Cascales, and C. Zaldo, “Spectroscopic characterization and laser performance of resonantly diode-pumped Er(3+)-doped disordered NaY(WO4)2.,” Opt. Lett. 36(16), 3263–3265 (2011). [CrossRef] [PubMed]

4.

N. Ter-Gabrielyan, V. Fromzel, T. Lukasiewicz, W. Ryba-Romanowski, and M. Dubinskii, “High power resonantly diode-pumped σ-configuration Er3+:YVO4 laser at 1593.5 nm,” Laser Phys. Lett. 8(7), 529–534 (2011). [CrossRef]

5.

N. Ter-Gabrielyan, V. Fromzel, T. Lukasiewicz, W. Ryba-Romanowski, and M. Dubinskii, “Nearly quantum-defect-limited efficiency, resonantly pumped, Er3+:YVO₄ laser at 1593.5 nm,” Opt. Lett. 36(7), 1218–1220 (2011). [CrossRef] [PubMed]

6.

N. Ter-Gabrielyan, V. Fromzel, L. D. Merkle, and M. Dubinskii, “Resonant in-band pumping of cryo-cooled Er3+:YAG laser at 1532, 1534 and 1546 nm: a comparative study,” Opt. Mater. Express 1(2), 223–233 (2011). [CrossRef]

7.

A. I. Zagumenny, V. G. Ostroumov, I. A. Shcherbakov, T. Jensen, J.-P. Meyn, and G. Huber, “The Nd:GdVO4 crystal: a new material for diode-pumped laser,” Sov. J. Quantum Electron. 22(12), 1071–1072 (1992). [CrossRef]

8.

A. I. Zagumenny, P. A. Popov, F. Zerouk, Yu. D. Zavartsev, S. A. Kutovoi, and I. A. Scherbakov, “Heat conduction of laser vanadate crystals,” Quantum Electron. 38(3), 227–232 (2008). [CrossRef]

9.

Y. Sato and T. Taira, “The studies of thermal conductivity in GdVO4, YVO4, and Y3Al5O12 measured by quasi-one-dimensional flash method,” Opt. Express 14(22), 10528–10536 (2006). [CrossRef] [PubMed]

10.

J. Didierjean, E. Herault, F. Balembois, and P. Georges, “Thermal conductivity measurements of laser crystals by infrared thermography. Application to Nd:doped crystals,” Opt. Express 16(12), 8995–9010 (2008). [CrossRef] [PubMed]

11.

J. Sulc, H. Jelinkova, W. Ryba-Romanowski, and T. Lukasiewicz, “1.6 um microchip laser,” Laser Phys. Lett. 6(3), 207–211 (2009). [CrossRef]

12.

C. Brandt, V. Matrosov, K. Petermann, and G. Huber, “In-band fiber-laser-pumped Er:YVO₄ laser emitting around 1.6 μm,” Opt. Lett. 36(7), 1188–1190 (2011). [CrossRef] [PubMed]

13.

N. Ter-Gabrielyan, V. Fromzel, W. Ryba-Romanowski, T. Lukasiewicz, and M. Dubinskii, “Efficient, Resonantly Pumped, Room Temperature Er3+:GdVO4 Laser,” Opt. Lett.: posted 01/27/2012; Doc. ID 160739

14.

W. Fowler and D. Dexter, “Relation between absorption and emission probabilities in luminescent centers in ionic solids,” Phys. Rev. 128(5), 2154–2165 (1962). [CrossRef]

15.

C. Bertini, A. Toncelli, M. Tonelli, E. Cavalli, and N. Magnani, “Optical spectroscopy and laser parameters of GdVO4:Er3+,” J. Lumin. 106(3-4), 235–242 (2004). [CrossRef]

16.

Y. Sato and T. Taira, “Saturation factors of pump absorption in solid-state lasers,” IEEE J. Quantum Electron. 40(3), 270–280 (2004). [CrossRef]

OCIS Codes
(140.3480) Lasers and laser optics : Lasers, diode-pumped
(140.3500) Lasers and laser optics : Lasers, erbium
(140.3580) Lasers and laser optics : Lasers, solid-state

ToC Category:
Lasers and Laser Optics

History
Original Manuscript: December 9, 2011
Revised Manuscript: February 16, 2012
Manuscript Accepted: February 21, 2012
Published: February 29, 2012

Citation
N. Ter-Gabrielyan, V. Fromzel, W. Ryba-Romanowski, T. Lukasiewicz, and M. Dubinskii, "Spectroscopic properties and laser performance of resonantly-pumped cryo-cooled Er3+:GdVO4," Opt. Express 20, 6080-6084 (2012)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-20-6-6080


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. S. D. Setzler, M. J. Shaw, M. J. Kukla, J. R. Unternahrer, K. M. Dinndorf, J. A. Beattie, and E. P. Chicklis, “A 400 W cryogenic Er:YAG slab laser at 1645 nm,” Proc. SPIE7686, 76860C, C7 (2010). [CrossRef]
  2. N. Ter-Gabrielyan, L. D. Merkle, A. Ikesue, and M. Dubinskii, “Ultralow quantum-defect eye-safe Er:Sc2O3 laser,” Opt. Lett.33(13), 1524–1526 (2008). [CrossRef] [PubMed]
  3. M. Dubinskii, V. Fromzel, N. Ter-Gabrielyan, M. D. Serrano, D. E. Lahera, C. Cascales, and C. Zaldo, “Spectroscopic characterization and laser performance of resonantly diode-pumped Er(3+)-doped disordered NaY(WO4)2.,” Opt. Lett.36(16), 3263–3265 (2011). [CrossRef] [PubMed]
  4. N. Ter-Gabrielyan, V. Fromzel, T. Lukasiewicz, W. Ryba-Romanowski, and M. Dubinskii, “High power resonantly diode-pumped σ-configuration Er3+:YVO4 laser at 1593.5 nm,” Laser Phys. Lett.8(7), 529–534 (2011). [CrossRef]
  5. N. Ter-Gabrielyan, V. Fromzel, T. Lukasiewicz, W. Ryba-Romanowski, and M. Dubinskii, “Nearly quantum-defect-limited efficiency, resonantly pumped, Er3+:YVO₄ laser at 1593.5 nm,” Opt. Lett.36(7), 1218–1220 (2011). [CrossRef] [PubMed]
  6. N. Ter-Gabrielyan, V. Fromzel, L. D. Merkle, and M. Dubinskii, “Resonant in-band pumping of cryo-cooled Er3+:YAG laser at 1532, 1534 and 1546 nm: a comparative study,” Opt. Mater. Express1(2), 223–233 (2011). [CrossRef]
  7. A. I. Zagumenny, V. G. Ostroumov, I. A. Shcherbakov, T. Jensen, J.-P. Meyn, and G. Huber, “The Nd:GdVO4 crystal: a new material for diode-pumped laser,” Sov. J. Quantum Electron.22(12), 1071–1072 (1992). [CrossRef]
  8. A. I. Zagumenny, P. A. Popov, F. Zerouk, Yu. D. Zavartsev, S. A. Kutovoi, and I. A. Scherbakov, “Heat conduction of laser vanadate crystals,” Quantum Electron.38(3), 227–232 (2008). [CrossRef]
  9. Y. Sato and T. Taira, “The studies of thermal conductivity in GdVO4, YVO4, and Y3Al5O12 measured by quasi-one-dimensional flash method,” Opt. Express14(22), 10528–10536 (2006). [CrossRef] [PubMed]
  10. J. Didierjean, E. Herault, F. Balembois, and P. Georges, “Thermal conductivity measurements of laser crystals by infrared thermography. Application to Nd:doped crystals,” Opt. Express16(12), 8995–9010 (2008). [CrossRef] [PubMed]
  11. J. Sulc, H. Jelinkova, W. Ryba-Romanowski, and T. Lukasiewicz, “1.6 um microchip laser,” Laser Phys. Lett.6(3), 207–211 (2009). [CrossRef]
  12. C. Brandt, V. Matrosov, K. Petermann, and G. Huber, “In-band fiber-laser-pumped Er:YVO₄ laser emitting around 1.6 μm,” Opt. Lett.36(7), 1188–1190 (2011). [CrossRef] [PubMed]
  13. N. Ter-Gabrielyan, V. Fromzel, W. Ryba-Romanowski, T. Lukasiewicz, and M. Dubinskii, “Efficient, Resonantly Pumped, Room Temperature Er3+:GdVO4 Laser,” Opt. Lett.: posted 01/27/2012; Doc. ID 160739
  14. W. Fowler and D. Dexter, “Relation between absorption and emission probabilities in luminescent centers in ionic solids,” Phys. Rev.128(5), 2154–2165 (1962). [CrossRef]
  15. C. Bertini, A. Toncelli, M. Tonelli, E. Cavalli, and N. Magnani, “Optical spectroscopy and laser parameters of GdVO4:Er3+,” J. Lumin.106(3-4), 235–242 (2004). [CrossRef]
  16. Y. Sato and T. Taira, “Saturation factors of pump absorption in solid-state lasers,” IEEE J. Quantum Electron.40(3), 270–280 (2004). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.

Figures

Fig. 1 Fig. 2 Fig. 3
 

« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited