Vertical InGaN light-emitting diodes with a sapphire-face-up structure

Y.C. Yang, Jinn-Kong Sheu, Ming-Lun Lee, Shang-Ju Tu, Feng-Wen Huang, Wei-Chih Lai, Schang Jing Hon, and Tsun Kai Ko  »View Author Affiliations


Optics Express, Vol. 20, Issue S1, pp. A119-A124 (2012)
http://dx.doi.org/10.1364/OE.20.00A119


View Full Text Article

Acrobat PDF (1459 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

Vertical GaN-based light-emitting diodes (LEDs) were fabricated with a Si substrate using the wafer-bonding technique. Lapping and dry-etching processes were performed for thinning the sapphire substrate instead of removing this substrate using the laser lift-off technique and the thinning process associated with the wafer-bonding technique to feature LEDs with a sapphire-face-up structure and vertical conduction property. Compared with conventional lateral GaN/sapphire-based LEDs, GaN/Si-based vertical LEDs exhibit higher light output power and less power degradation at a high driving current, which could be attributed to the fact that vertical LEDs behave in a manner similar to flip-chip GaN/sapphire LEDs with excellent heat conduction. In addition, with an injection current of 350 mA, the output power (or forward voltage) of fabricated vertical LEDs can be enhanced (or reduced) by a magnitude of 60% (or 5%) compared with conventional GaN/sapphire-based LEDs.

© 2011 OSA

1. Introduction

High-power GaN-based light-emitting diodes (LEDs) have been recognized as a promising next-generation general lighting source [1

1. E. F. Schubert, Light-Emitting Diode, 2nd ed. (Cambridge University Press, 2006), pp. 150–160.

]. Recently, the vertical thin-GaN LED have been identified as the most promising structure for improving the efficiency of high-power LEDs over other traditional LED structures with sapphire substrates [2

2. W. S. Wong, M. Kneissl, P. Mei, D. W. Treat, M. Teepe, and N. M. Johnson, “Continuous-wave InGaN multiple-quantum-well laser diodes on copper substrates,” Appl. Phys. Lett. 78(9), 1198–1200 (2001) (and references therein). [CrossRef]

4

4. D. S. Wuu, S. C. Hsu, S. H. Huang, C. C. Wu, C. E. Lee, and R. H. Horng, “GaN/mirror/Si light-emitting diodes for vertical current injection by laser lift-off and wafer bonding techniques,” Jpn. J. Appl. Phys. 43(8A), 5239–5242 (2004) (and references therein). [CrossRef]

]. Unlike conventional LED structures, a conductive substrate and a metal reflector are implanted into thin-GaN LEDs to improve light-extraction efficiency (LEE) and to reduce thermal resistance [2

2. W. S. Wong, M. Kneissl, P. Mei, D. W. Treat, M. Teepe, and N. M. Johnson, “Continuous-wave InGaN multiple-quantum-well laser diodes on copper substrates,” Appl. Phys. Lett. 78(9), 1198–1200 (2001) (and references therein). [CrossRef]

4

4. D. S. Wuu, S. C. Hsu, S. H. Huang, C. C. Wu, C. E. Lee, and R. H. Horng, “GaN/mirror/Si light-emitting diodes for vertical current injection by laser lift-off and wafer bonding techniques,” Jpn. J. Appl. Phys. 43(8A), 5239–5242 (2004) (and references therein). [CrossRef]

]. To achieve this goal, the well-known techniques of laser lift-off and wafer bonding processes are used to remove the epitaxial substrates (i.e., sapphires) and to support the thin-GaN films through an electrical and thermal conductive carrier substrate (such as a Si substrate), respectively. To separate GaN thin films from the sapphire substrate, laser pulses are directed through the transparent sapphire substrate and are absorbed throughout the sapphire/GaN interface, thereby resulting in the decomposition of the GaN layer, and hence, the peeling of epitaxial layers from the sapphire substrate [2

2. W. S. Wong, M. Kneissl, P. Mei, D. W. Treat, M. Teepe, and N. M. Johnson, “Continuous-wave InGaN multiple-quantum-well laser diodes on copper substrates,” Appl. Phys. Lett. 78(9), 1198–1200 (2001) (and references therein). [CrossRef]

]. However, the transfer of GaN films to receptor substrates results in a considerable release in stresses, which originate from the large lattice and thermal mismatch between the GaN-based layers and sapphire substrate. The released stresses may result in structure defects and even cracks in the epitaxial layers that degrade device performance [3

3. S. C. Hsu, B. J. Pong, W. H. Li, T. E. Beechem, S. Graham, and C. Y. Liu, “Stress relaxation in GaN by transfer bonding on Si substrates,” Appl. Phys. Lett. 91(25), 251114 (2007) (and references therein). [CrossRef]

]. In addition to the inherent mismatch, laser-induced damage also results in residual stresses after the laser lift-off (LLO) process, thereby degrading the electrical and optical properties of LEDs [5

5. Y. S. Wu, J. H. Cheng, W. C. Peng, and H. Ouyang, “Effects of laser sources on the reverse-bias leakages of laser lift-off GaN-based light-emitting diodes,” Appl. Phys. Lett. 90(25), 251110 (2007).

]. In the present study, a vertical-type GaN-based LED (VLED) without the removal of the sapphire substrate is demonstrated. That is, thinning and etching were performed on sapphire substrate instead of the LLO process to expose the n-GaN layer for the fabrication of VLEDs. The detailed process and the properties of VLEDs are presented in the present paper.

2. Experiments

3. Results and discussions

Figure 1(c) shows the typical cross-sectional view scanning electron microscopy (SEM) image of LED-II, which was taken to inspect the etching profile of sapphire and the bonding interface between the Si substrate and GaN layer. The void-free bonding interface is displayed in the typical SEM images, indicating that the bonding interface was reasonably good. Vertical thin-GaN LEDs with a smooth bonding interface facilitates heat dissipation, mechanical support, and current conduction. The presence of voids around the bonding interface reduces the reliability and performance of the LEDs [7

7. H. Y. Kuo, S. J. Wang, P. R. Wang, K. M. Uang, T. M. Chen, S. L. Chen, W. C. Lee, H. K. Hsu, J. C. Chou, and C. H. Wu, “Use of elastic conductive adhesive as the bonding agent for the fabrication of vertical structure GaN-based LEDs on flexible metal substrate,” IEEE Photon. Technol. Lett. 20(7), 523–525 (2008). [CrossRef]

]. Figure 2(a)
Fig. 2 (a) Typical forward I-V and light-output power-current (L-I) characteristics of the experimental LEDs (b) reverse I-V characteristics of the experimental LEDs.
shows the typical forward I-V characteristics of LED-I and LED-II. The forward voltages at a driving current of 350 mA (Vf) were 3.45 and 3.28 V for LED-I and LED-II, respectively. The slightly higher Vf observed in LED-I can be attributed to the relatively its higher series resistance (Rs) compared with LED-II. In fact, the Rs extracted from the I-V characteristics were approximately 1.6 and 1.1 Ω for LED-I and LED-II, respectively. As shown in Fig. 1(b), the current path between the anode and cathode electrodes in LED-I could be expected to be longer than those in LED-II. Although LED-II consists of a greater number of metal/semiconductor interfaces and an additional Si substrate, these factors in the vertical LEDs with adequate bonding and ohmic contact layers contribute limited magnitude in Rs. Therefore, the higher Rs of LED-I was attributed to the relatively larger distance between anode and cathode electrodes. In other words, the low Rs in the vertical LEDs can be attributed to a relatively better current-spreading effect compared with that of the lateral LEDs. In addition to the superior forward I-V characteristics, typical reverse leakage current (Ir) of the proposed vertical LEDs (LED-II) was comparable with the conventional lateral LEDs (LED-I) but markedly lower than the conventional vertical LEDs, as shown in Fig. 2(b). The relative higher Ir could be attributed to the fact that strain release and laser-induced damage on the GaN-based epitaxial layers led to the degradation of electrical properties of the conventional vertical LEDs. Figure 2(a) also shows the typical L-I characteristics of LED-I and LED-II. With an injection current of 350 mA, the light output powers were 205 and 243 mW for LED-I and LED-II, respectively. This significant improvement in the output power of LED-II was attributable to the increase in its LEE compared with that of LED-I. That is, LED-II behaved in a manner similar to flip-chip LEDs [8

8. O. B. Shchekin, J. E. Epler, T. A. Trottier, T. Margalith, D. A. Steigerwald, M. O. Holcomb, P. S. Martin, and M. R. Krames, “High performance thin-film flip-chip InGaN–GaN light-emitting diodes,” Appl. Phys. Lett. 89(7), 071109 (2006). [CrossRef]

]. For LED-II, photons were emitted through sapphire with a relatively lower refractive index compared with that of LEDs with a GaN-emitting surface. Compared with the LED-I with emitting surface, the indium tin oxide (ITO) layer possesses a relatively lower critical angle for light escaping into the air because the refractive index of ITO is larger than that of sapphire. In addition, the remaining top sapphire layer with a thickness of 7 μm was significantly thicker than that of the ITO layer. Therefore, the top sapphire layer served as a window layer to facilitate light extraction. Also, LED-II possesses the nature of thin-GaN LEDs [2

2. W. S. Wong, M. Kneissl, P. Mei, D. W. Treat, M. Teepe, and N. M. Johnson, “Continuous-wave InGaN multiple-quantum-well laser diodes on copper substrates,” Appl. Phys. Lett. 78(9), 1198–1200 (2001) (and references therein). [CrossRef]

4

4. D. S. Wuu, S. C. Hsu, S. H. Huang, C. C. Wu, C. E. Lee, and R. H. Horng, “GaN/mirror/Si light-emitting diodes for vertical current injection by laser lift-off and wafer bonding techniques,” Jpn. J. Appl. Phys. 43(8A), 5239–5242 (2004) (and references therein). [CrossRef]

], that is, downward-propagating light is reflected up by a metal reflector sandwiched between the p-GaN layer and Si substrate. On the other hand, the light-shadowing effect by opaque electrodes in LED-II is weaker than that in LED-I, as shown in the insets of Fig. 1 (a) and (b).

Another benefit of the design scheme of LED-II is that the heat generated in LED flows directly from the p-n junction to the Si substrate. However, heat extraction through the thermally resistive sapphire substrate is inevitable for conventional GaN-based LEDs, i.e., LED-I. The degradation of light output power and redshift of emission wavelength of LED-I attributable to junction heating are expected when the LEDs are operated under a high driving current because of the low thermal conductivity of sapphire. As shown in Fig. 2, LED-II can clearly operate up to 1.0 A without significant power degradation. However, LED-I exhibits substantial power degradation when the injection current exceeds 600 mA. Furthermore, the heating effect on the redshift of the emission wavelength was also observed. Figure 3
Fig. 3 Emission wavelength against injection current for the LED-I and LED-II.
shows the typical curves of emission wavelengths against injection current for LED-I and LED-II. At a low injection current, the quantum-confined Stark effect (QCSE) attributable to the polarization field in the QWs reflects on the blueshift of the emission wavelengths [9

9. T. Mukai, M. Yamada, and S. Nakamura, “Current and temperature dependences of electroluminescence of InGaN-based UV/blue/green light-emitting diodes,” Jpn. J. Appl. Phys. 37(11B), L1358–L1361 (1998). [CrossRef]

]. The redshift of the emission wavelength resulting from band-gap shrinkage at a high injection current is attributed to the junction heating effect. LED-II exhibited low Rs and excellent heat conduction, resulting in low junction heating. As shown in Fig. 3, the redshift of the emission wavelength was not observed in LED-II even when the injection current reached 1000 mA. In contrast, LED-I exhibited a significant redshift as the injection current exceeded 200 mA. The redshift occurring in the relatively lower current levels revealed that junction temperature increased rapidly with increasing injection current and that the heat extraction rate of LED-I through sapphire was lower than the heat generation rate. Thus, the band-gap shrinkage rate resulting from junction heating versus injection current was higher than that of the band-gap widening rate.

To further enhance the light output power, surface texturing was attempted to be performed on the sapphire surface of LED-II. The texturing process was conducted after the thinning of sapphire and before exposure of the n+-GaN layer. In this process, the Ag layer with a thickness of 100 nm was initially deposited on the sapphire surface and was then thermally annealed at 350 °C for 10 min under nitrogen ambient produced self-assembled Ag metal islands to serve as etching nanomask. Next, plasma etching using chlorine-based gas sources was performed on the wafers with the Ag masked sapphire surface. Figure 4
Fig. 4 Typical AFM images taken from the sapphire surfaces of (a) LED-II and (b) LED-III.
shows the typical atomic force microscopy images of the sapphire surface. After the etching process, the textured sapphire surface had a root-mean-square (RMS) roughness of approximately 84 nm. The RMS roughness of sapphire without texture was approximately 6 nm. The fabricated vertical LEDs with textured sapphire were labeled LED-III. Figure 2 also shows that the I-V characteristics of LED-III are almost identical to those of LED-II. In addition, a significant improvement in light output power was achieved. With an injection current of 350 mA, LED-III exhibited output power of approximately 330 mW, corresponding to enhancements of 60% and 35% compared with LED-I and the LED-II, respectively. These results indicated that the texturing process performed on the wafers could significantly enhance the LEE of LEDs and did not alter their electrical properties.

4. Conclusions

Acknowledgments

Financial support from the Bureau of Energy, Ministry of Economic Affairs of Taiwan, ROC, through grant No.100-D0204-6 and the LED Lighting Research Center of NCKU are appreciated. The authors would also like to acknowledge the National Science Council for the financial support of the research Grant Nos. NSC 98-2221-E-218-005-MY3, 100-2112-M-006-011-MY3 and 100-3113-E-006-015.

References and links

1.

E. F. Schubert, Light-Emitting Diode, 2nd ed. (Cambridge University Press, 2006), pp. 150–160.

2.

W. S. Wong, M. Kneissl, P. Mei, D. W. Treat, M. Teepe, and N. M. Johnson, “Continuous-wave InGaN multiple-quantum-well laser diodes on copper substrates,” Appl. Phys. Lett. 78(9), 1198–1200 (2001) (and references therein). [CrossRef]

3.

S. C. Hsu, B. J. Pong, W. H. Li, T. E. Beechem, S. Graham, and C. Y. Liu, “Stress relaxation in GaN by transfer bonding on Si substrates,” Appl. Phys. Lett. 91(25), 251114 (2007) (and references therein). [CrossRef]

4.

D. S. Wuu, S. C. Hsu, S. H. Huang, C. C. Wu, C. E. Lee, and R. H. Horng, “GaN/mirror/Si light-emitting diodes for vertical current injection by laser lift-off and wafer bonding techniques,” Jpn. J. Appl. Phys. 43(8A), 5239–5242 (2004) (and references therein). [CrossRef]

5.

Y. S. Wu, J. H. Cheng, W. C. Peng, and H. Ouyang, “Effects of laser sources on the reverse-bias leakages of laser lift-off GaN-based light-emitting diodes,” Appl. Phys. Lett. 90(25), 251110 (2007).

6.

C. M. Tsai, J. K. Sheu, W. C. Lai, M. L. Lee, S. J. Chang, C. S. Chang, T. K. Ko, and C. F. Shen, “GaN-based LEDs output power improved by textured GaN/sapphire interface using in situ SiH4 treatment process during epitaxial growth,” IEEE J. Sel. Top. Quantum Electron. 15(4), 1275–1280 (2009). [CrossRef]

7.

H. Y. Kuo, S. J. Wang, P. R. Wang, K. M. Uang, T. M. Chen, S. L. Chen, W. C. Lee, H. K. Hsu, J. C. Chou, and C. H. Wu, “Use of elastic conductive adhesive as the bonding agent for the fabrication of vertical structure GaN-based LEDs on flexible metal substrate,” IEEE Photon. Technol. Lett. 20(7), 523–525 (2008). [CrossRef]

8.

O. B. Shchekin, J. E. Epler, T. A. Trottier, T. Margalith, D. A. Steigerwald, M. O. Holcomb, P. S. Martin, and M. R. Krames, “High performance thin-film flip-chip InGaN–GaN light-emitting diodes,” Appl. Phys. Lett. 89(7), 071109 (2006). [CrossRef]

9.

T. Mukai, M. Yamada, and S. Nakamura, “Current and temperature dependences of electroluminescence of InGaN-based UV/blue/green light-emitting diodes,” Jpn. J. Appl. Phys. 37(11B), L1358–L1361 (1998). [CrossRef]

OCIS Codes
(230.0250) Optical devices : Optoelectronics
(230.3670) Optical devices : Light-emitting diodes
(230.5590) Optical devices : Quantum-well, -wire and -dot devices

ToC Category:
Light-Emitting Diodes

History
Original Manuscript: October 10, 2011
Revised Manuscript: December 8, 2011
Manuscript Accepted: December 13, 2011
Published: December 22, 2011

Citation
Y.C. Yang, Jinn-Kong Sheu, Ming-Lun Lee, Shang-Ju Tu, Feng-Wen Huang, Wei-Chih Lai, Schang Jing Hon, and Tsun Kai Ko, "Vertical InGaN light-emitting diodes with a sapphire-face-up structure," Opt. Express 20, A119-A124 (2012)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-20-S1-A119


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. E. F. Schubert, Light-Emitting Diode, 2nd ed. (Cambridge University Press, 2006), pp. 150–160.
  2. W. S. Wong, M. Kneissl, P. Mei, D. W. Treat, M. Teepe, and N. M. Johnson, “Continuous-wave InGaN multiple-quantum-well laser diodes on copper substrates,” Appl. Phys. Lett.78(9), 1198–1200 (2001) (and references therein). [CrossRef]
  3. S. C. Hsu, B. J. Pong, W. H. Li, T. E. Beechem, S. Graham, and C. Y. Liu, “Stress relaxation in GaN by transfer bonding on Si substrates,” Appl. Phys. Lett.91(25), 251114 (2007) (and references therein). [CrossRef]
  4. D. S. Wuu, S. C. Hsu, S. H. Huang, C. C. Wu, C. E. Lee, and R. H. Horng, “GaN/mirror/Si light-emitting diodes for vertical current injection by laser lift-off and wafer bonding techniques,” Jpn. J. Appl. Phys.43(8A), 5239–5242 (2004) (and references therein). [CrossRef]
  5. Y. S. Wu, J. H. Cheng, W. C. Peng, and H. Ouyang, “Effects of laser sources on the reverse-bias leakages of laser lift-off GaN-based light-emitting diodes,” Appl. Phys. Lett.90(25), 251110 (2007).
  6. C. M. Tsai, J. K. Sheu, W. C. Lai, M. L. Lee, S. J. Chang, C. S. Chang, T. K. Ko, and C. F. Shen, “GaN-based LEDs output power improved by textured GaN/sapphire interface using in situ SiH4 treatment process during epitaxial growth,” IEEE J. Sel. Top. Quantum Electron.15(4), 1275–1280 (2009). [CrossRef]
  7. H. Y. Kuo, S. J. Wang, P. R. Wang, K. M. Uang, T. M. Chen, S. L. Chen, W. C. Lee, H. K. Hsu, J. C. Chou, and C. H. Wu, “Use of elastic conductive adhesive as the bonding agent for the fabrication of vertical structure GaN-based LEDs on flexible metal substrate,” IEEE Photon. Technol. Lett.20(7), 523–525 (2008). [CrossRef]
  8. O. B. Shchekin, J. E. Epler, T. A. Trottier, T. Margalith, D. A. Steigerwald, M. O. Holcomb, P. S. Martin, and M. R. Krames, “High performance thin-film flip-chip InGaN–GaN light-emitting diodes,” Appl. Phys. Lett.89(7), 071109 (2006). [CrossRef]
  9. T. Mukai, M. Yamada, and S. Nakamura, “Current and temperature dependences of electroluminescence of InGaN-based UV/blue/green light-emitting diodes,” Jpn. J. Appl. Phys.37(11B), L1358–L1361 (1998). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.

Figures

Fig. 1 Fig. 2 Fig. 3
 
Fig. 4
 

« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited