SiOC thin films: an efficient light source and an ideal host matrix for Eu2+ ions

Gabriele Bellocchi, Fabio Iacona, Maria Miritello, Tiziana Cesca, and Giorgia Franzò  »View Author Affiliations


Optics Express, Vol. 21, Issue 17, pp. 20280-20290 (2013)
http://dx.doi.org/10.1364/OE.21.020280


View Full Text Article

Acrobat PDF (1477 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

The intense luminescence of SiOC layers is studied and its dependence on the parameters of the thermal annealing process elucidated. Although the emission of SiOC is bright enough to be interesting for practical applications, this material is even more promising as a host matrix for optically active Eu ions. Indeed, when incorporated in a SiOC matrix, Eu3+ ions are efficiently reduced to Eu2+, producing a very strong visible luminescence peaked at 440 nm. Eu2+ ions benefit also of the occurrence of an energy transfer mechanism involving the matrix, which increases the efficiency of photon absorption for exciting wavelengths shorter than 300 nm. We evaluate that Eu doping of SiOC produces an enhancement of the luminescence intensity at 440 nm accounting for about a factor of 15. These properties open the way to new promising perspectives for the application of Eu-doped materials in photonic and lighting technologies.

© 2013 OSA

1. Introduction

The realization of an efficient Si-based light source represents one of the most relevant issues for the scientific community currently working in the field of photonics. The main characteristics required for this source are high efficiency at room temperature, tunability in a wide wavelength range, easy integration in highly compact Si microphotonic devices. In this framework, during the last decade, the bright light emission provided by Si nanocrystals (nc) embedded in a SiO2 matrix has gathered a lot of interest [1

1. L. Pavesi, L. Dal Negro, C. Mazzoleni, G. Franzò, and F. Priolo, “Optical gain in silicon nanocrystals,” Nature 408(6811), 440–444 (2000). [CrossRef] [PubMed]

]. A leading role in the field of Si photonics is also played by rare earth (RE) ions; RE doping of insulating or semiconducting host matrices has been recognized as a powerful method to provide intense luminescence signals spanning in a wide wavelength range, opening the way to several new applications for Si-based materials in the field of photonics [2

2. G. Franzò, V. Vinciguerra, and F. Priolo, “The excitation mechanism of rare-earth ions in silicon nanocrystals,” Appl. Phys., A Mater. Sci. Process. 69(1), 3–12 (1999). [CrossRef]

]. A relevant example of this approach is represented by the very intense 1.54 µm luminescence provided by Er-doped Si nc [3

3. M. Fujii, M. Yoshida, Y. Kanzawa, S. Hayashi, and K. Yamamoto, “1.54 µm photoluminescence of Er3+ doped into SiO2 films containing Si nanocrystals: Evidence for energy transfer from Si nanocrystals to Er3+,” Appl. Phys. Lett. 71(9), 1198–1200 (1997). [CrossRef]

], which has opened new perspectives for the fabrication of Si-based optical amplifiers [4

4. J. H. Shin, J. Lee, H.-S. Han, J.-H. Jhe, J. S. Chang, S.-Y. Seo, H. Lee, and N. Park, “Si nanocluster sensitization of Er-doped silica for optical amplet using top-pumping visible LEDs,” IEEE J. Sel. Top. Quantum Electron. 12(4), 783–796 (2006). [CrossRef]

]. Among the other RE ions, a considerable attention has been devoted to Eu. Both divalent and trivalent Eu ions can act as efficient emitting centers in the visible region and their bright emission is widely employed in phosphors used in plasma display panels and in solid state lighting [5

5. X. Ye, W. Zhuang, Y. Hu, T. He, X. Huang, C. Liao, S. Zhong, Z. Xu, H. Nie, and G. Deng, “Preparation, characterization, and optical properties of nano- and submicron-sized Y2O3:Eu3+ phosphors,” J. Appl. Phys. 105(6), 064302 (2009). [CrossRef]

]. On the other hand, applications of Eu in Si photonics require the availability of Eu-containing thin films compatible with CMOS technology. Several papers have studied the optical properties of Eu-doped SiO2 films [6

6. D. Li, X. Zhang, L. Jin, and D. Yang, “Structure and luminescence evolution of annealed europium-doped silicon oxides films,” Opt. Express 18(26), 27191–27196 (2010). [CrossRef] [PubMed]

9

9. S. Prucnal, J. M. Sun, W. Skorupa, and M. Helm, “Switchable two-color electroluminescence based on a Si metal-oxide-semiconductor structure doped with Eu,” Appl. Phys. Lett. 90(18), 181121 (2007). [CrossRef]

], but the very low Eu solid solubility in silica (cluster formation occurs for Eu concentrations larger than 1018 cm−3 [10

10. N. D. Afify and G. Mountjoy, “Molecular-dynamics modeling of Eu3+-ion clustering in SiO2 glass,” Phys. Rev. B 79(2), 024202 (2009). [CrossRef]

12

12. S. Boninelli, G. Bellocchi, G. Franzò, M. Miritello, and F. Iacona, “New strategies to improve the luminescence efficiency of Eu ions embedded in Si-based matrices,” J. Appl. Phys. 113(14), 143503 (2013). [CrossRef]

]) seems to seriously limit its perspectives in photonics. As an interesting alternative approach to doping, also Eu compound thin films have received a considerable attention [13

13. J. Qi, T. Matsumoto, M. Tanaka, and Y. Masumoto, “Electroluminescence of europium silicate thin film on silicon,” Appl. Phys. Lett. 74(21), 3203–3205 (1999). [CrossRef]

16

16. G. Bellocchi, G. Franzò, F. Iacona, S. Boninelli, M. Miritello, T. Cesca, and F. Priolo, “Eu3+ reduction and efficient light emission in Eu2O3 films deposited on Si substrates,” Opt. Express 20(5), 5501–5507 (2012). [CrossRef] [PubMed]

].

In this paper we will study the optical properties of SiOC and Eu-doped SiOC thin films synthesized by rf magnetron sputtering. It will be demonstrated that the temperature and the environment of the thermal annealing process have a key role in determining the features of the PL emission in the visible region from both materials. The mechanisms of the SiOC-Eu interaction, leading to a very bright visible emission assigned to Eu2+ ions, will be also elucidated. The relevance of the above data for the realization of an efficient Si-based light source, which can be of great interest for applications in photonics as well as in solid state lighting, will be addressed.

2. Experimental section

SiOC and Eu-doped SiOC thin films have been synthesized by using an UHV rf magnetron sputtering system. The chamber base pressure was about 1 × 10−9 mbar. The deposition has been obtained by co-sputtering of 4-inches diameter, water-cooled SiO2 and SiC targets (in the case of SiOC samples), and SiO2, SiC and Eu2O3 targets (in the case of Eu-doped SiOC samples). C concentration has been fixed at about 5 at.% in both doped and undoped SiOC films, while Eu concentration was 1.5 × 1020 cm−3. The films were deposited on Si substrates kept at 400 °C in a 5 × 10−3 mbar Ar atmosphere. After deposition the films were thermally treated at temperatures ranging from 600 to 900 °C for 1 h in O2 or N2 atmosphere.

Both doped and undoped as-deposited SiOC films are about 190 nm thick, as measured by both ellipsometry and cross sectional transmission electron microscopy. The refractive index of SiOC samples was measured using an ellipsometer equipped with a He-Ne laser operating at 632.8 nm. The Eu content of the film was determined by Rutherford backscattering spectrometry measurements, performed by using a 2 MeV He+ beam, with the detector placed at an angle of 165° with respect to the incident beam.

PL measurements were performed by pumping with the 325 nm line of a He-Cd laser. The pump power was about 3 mW and the laser beam was chopped through an acousto-optic modulator at a frequency of 55 Hz. The PL signal was analyzed by a single grating monochromator and detected with a Hamamatsu visible photomultiplier. Spectra were recorded with a lock-in amplifier using the acousto-optic modulator frequency as a reference. The same experimental set-up has been maintained for PL measurements of both undoped and Eu-doped films, in order to allow the direct comparison of the intensities. PL lifetime measurements were performed by monitoring the decay of the luminescence signal at a fixed wavelength after pumping to steady state and switching off the laser beam. The overall time resolution of our system is of 200 ns.

Photoluminescence excitation (PLE) measurements in the 250-475 nm range were performed by using a FluoroMax spectrofluorometer by Horiba. All the spectra have been measured at room temperature and corrected for the system spectral response.

3. Results and discussion

The room temperature PL spectra of as-deposited and thermally annealed SiOC films, obtained by exciting with the 325 nm line of a He-Cd laser, are shown in Fig. 1
Fig. 1 Room temperature PL spectra for SiOC films as deposited and annealed in the temperature range 600 – 900 °C (a) for 1h in N2 ambient, and (b) in O2 ambient.
; Figs. 1(a) and 1(b) refer to samples annealed in N2 and O2 atmosphere, respectively, the explored temperature range is 600-900 °C and the duration of all the processes is 1 h.

It is noteworthy that all PL signals shown in the figure are visible by the naked eye. Furthermore, it is evident that the conditions of the thermal treatment strongly influence the optical properties of the films; in particular, both the intensity and the shape of the PL peaks markedly depend on the ambient and on the temperature of the thermal process. More in detail, spectra of O2-annealed samples are generally blueshifted and sharper with respect to those of samples annealed in N2 and the PL signal is maximized at 900 °C for processes performed in N2 and at 750 °C for processes performed in O2.

In order to gain deeper information about the nature of the observed PL emission, in Fig. 2
Fig. 2 Comparison between the normalized PL spectra of SiOC films as deposited and annealed at 900 °C in N2 and in O2 ambient.
we compare the PL spectrum of an as-deposited film (black line) with those measured in samples annealed in N2 (red line) or O2 (blue line) ambient at the same temperature of 900 °C. All spectra have been normalized to allow an easier comparison. The spectrum of the as-deposited sample appears quite broad, suggesting the presence of at least two different contributions originating from two different luminescent centers. The complex nature of the PL emission of SiOC films can be better understood by analyzing the PL peaks of the annealed films. Indeed, after annealing in N2 atmosphere, a peak at 510 nm becomes predominant, although it is still visible a shoulder at 400 nm. In contrast, after annealing in O2 atmosphere, the maximum of the band is found at 400 nm and the component at 510 nm is almost completely quenched.

The behavior of the two components of the PL emission of SiOC films as a function of the annealing temperature for both N2 and O2 processes can be analyzed by plotting their integrated intensity, obtained by a suitable fitting procedure employing Gaussian peaks. These data are reported in Fig. 3
Fig. 3 Integrated intensity as a function of the annealing temperature for the two components of the PL signal of SiOC films annealed (a) in N2 ambient, and (b) in O2 ambient. The red circles refer to the component at 510 nm, the blue ones to the component at 400 nm.
; for processes performed in N2 atmosphere (Fig. 3(a)) the prevalent PL band is the one at 510 nm and its intensity (plotted as red line and circles) continuously increases by increasing the annealing temperature, while the intensity of the component at 400 nm (blue line and circles) remains quite low and almost constant throughout the explored temperature range. In contrast, for samples annealed in O2 atmosphere (Fig. 3(b)), the prevalent PL band is the one at 400 nm and its intensity has a maximum at 750 °C and decreases at higher temperatures, while the component at 510 nm has a maximum at 600 °C and decreases at higher temperatures, being almost completely quenched at 900 °C.

In order to obtain more information on the nature of the two luminescent centers, we have performed PLE spectroscopy measurements on SiOC samples annealed at 900 °C. The PLE intensity shown in Fig. 4
Fig. 4 Room temperature PLE intensity obtained by integrating the PL spectra recorded as a function of the excitation wavelength in the range 250-370 nm for SiOC films annealed at 900 °C in N2 (red circles and line), and O2 (blue squares and line, multiplied by a factor of 2).
, obtained by integrating the emission spectra recorded as a function of the excitation wavelength in the range 250-370 nm, is deeply influenced by the annealing environment. In particular, for the sample annealed in N2, the integral PL intensity is almost constant between 250 and 270 nm and then steeply drops by increasing the excitation wavelength, while for the sample annealed in O2 it monotonically decreases with increasing wavelength.

On the basis of the data shown in Figs. 1-4 it is possible to reasonably conclude that the peak at 510 nm is due to the presence of Si-C bonds [17

17. S.-Y. Seo, K.-S. Cho, and J. H. Shin, “Intense blue-white luminescence from carbon-doped silicon-rich silicon oxide,” Appl. Phys. Lett. 84(5), 717–719 (2004). [CrossRef]

,20

20. A. Perez-Rodriguez, O. Gonzalez-Varona, B. Garrido, P. Pellegrino, J. R. Morante, C. Bonafos, M. Carrada, and A. Claverie, “White luminescence from Si+ and C+ ion-implanted SiO2 films,” J. Appl. Phys. 94(1), 254–262 (2003). [CrossRef]

], while the peak at 400 nm can be assigned to luminescent defects, such as oxygen vacancies [18

18. S. Gallis, V. Nikas, H. Suhag, M. Huang, and A. E. Kaloyeros, “White light emission from amorphous silicon oxycarbide (a-SiCxOy) thin films: Role of composition and postdeposition annealing,” Appl. Phys. Lett. 97(8), 081905 (2010). [CrossRef]

,21

21. Y. Ishikawa, A. V. Vasin, J. Salonen, S. Muto, V. S. Lysenko, A. N. Nazarov, N. Shibata, and V.-P. Lehto, “Color control of white photoluminescence from carbon-incorporated silicon oxide,” J. Appl. Phys. 104(8), 083522 (2008). [CrossRef]

,22

22. Y. Ding and H. Shirai, “White light emission from silicon oxycarbide films prepared by using atmospheric pressure microplasma jet,” J. Appl. Phys. 105(4), 043515 (2009). [CrossRef]

]. Indeed, when SiOC films are annealed in N2 atmosphere, a partial ordering of the film structure occurs, leading to the formation of optically active Si-C bonds; in agreement with this picture, the increase of the PL signal at 510 nm as a function of the annealing temperature for N2 processes, shown in Fig. 3(a), is due to the increment of the concentration of these bonds. The evidence that the system becomes more optically efficient at higher temperatures confirms that the PL at 510 nm cannot be assigned to defect centers, further supporting its assignment to Si-C bonds. On the other hand, by increasing the annealing temperature of O2-treated samples, Si-C bonds emission intensity decreases because the oxidation of SiOC films implies a decrease of the C concentration into the film.

As far as the component at 400 nm is concerned, the oxygen vacancies responsible of this emission are already present in the as-deposited material and their concentration is not strongly affected by annealing processes in N2. On the other hand, as expected, their concentration remarkably increases during the annealing in O2 ambient, due to the elimination of C atoms through the formation of volatile species such as CO or CO2 [28

28. C. M. Brewer, D. R. Bujalski, V. E. Parent, K. Su, and G. A. Zank, “Insights into the oxidation chemistry of SiOC ceramics derived from silsesquioxanes,” J. Sol-Gel Sci. Technol. 14(1), 49–68 (1999). [CrossRef]

], and decreases at higher annealing temperature, due to the recovery of the chemical luminescent defects of the film induced by the thermal treatment, leading to the formation of a nearly stoichiometric SiO2 layer.

A confirmation of the above picture concerning the nature of the PL emission in SiOC films has been obtained by ellipsometric measurements of the refractive index at 632.8 nm. Figure 5
Fig. 5 Refractive index, measured at 632.8 nm, as a function of the annealing temperature for SiOC films annealed in N2 (red circles and line), and O2 (blue squares and line). The refractive index of pure SiO2 is indicated by a blue dash-dotted line.
shows the evolution of the refractive index as a function of the annealing temperature for SiOC films treated in N2 or O2 ambient.

The as-deposited sample has a refractive index of about 1.57, which reflects its low C content (pure SiC refractive index is about 2.60 [29

29. T. Rajagopalan, X. Wang, B. Lahlouh, C. Ramkumar, P. Dutta, and S. Gangopadhyaya, “Low temperature deposition of nanocrystalline silicon carbide films by plasma enhanced chemical vapor deposition and their structural and optical characterization,” J. Appl. Phys. 94(8), 5252–5260 (2003). [CrossRef]

], while pure SiO2 refractive index is about 1.45 [30

30. J. Y. Kim, M. S. Hwang, Y.-H. Kim, H. J. Kim, and Y. Lee, “Origin of low dielectric constant of carbon-incorporated silicon oxide film deposited by plasma enhanced chemical vapor deposition,” J. Appl. Phys. 90(5), 2469–2473 (2001). [CrossRef]

]). For annealing in N2 atmosphere (red line and circles), the refractive index is almost constant throughout the explored temperature range (from room temperature up to 900 °C), indicating that the stoichiometry does not change during the annealing process, in agreement with the conclusions drawn on the basis of the above discussed PL data. In contrast, after annealing in O2 atmosphere (blue line and squares), the refractive index decreases with increasing the annealing temperature. This corresponds to a change in the sample stoichiometry, and in particular to a variation of the C content in the SiO2 matrix. Indeed the annealing process in oxidizing ambient induces the diffusion of oxygen inside the sample and its reaction with the C contained into the SiOC film, leading to the formation of small gaseous molecules such as CO or CO2 which can therefore escape from the sample, leaving it depleted in C and oxidized [28

28. C. M. Brewer, D. R. Bujalski, V. E. Parent, K. Su, and G. A. Zank, “Insights into the oxidation chemistry of SiOC ceramics derived from silsesquioxanes,” J. Sol-Gel Sci. Technol. 14(1), 49–68 (1999). [CrossRef]

]. With increasing temperature, oxidation rate increases too, and the final result is a deep change of the stoichiometry of SiOC samples, leading to a continuous reduction of the refractive index, towards the typical SiO2 value (1.45), indicated in Fig. 5 by a dash-dotted blue line. The variation of the refractive index of SiOC films annealed in O2 is in full agreement with the optical properties described in Figs. 1-4.

As previously reported [12

12. S. Boninelli, G. Bellocchi, G. Franzò, M. Miritello, and F. Iacona, “New strategies to improve the luminescence efficiency of Eu ions embedded in Si-based matrices,” J. Appl. Phys. 113(14), 143503 (2013). [CrossRef]

,25

25. Y. Zhang, A. Quaranta, and G. D. Soraru, “Synthesis and luminescent properties of novel Eu2+-doped silicon oxycarbide glasses,” Opt. Mater. 24(4), 601–605 (2004). [CrossRef]

], SiOC can be also a very suitable host matrix for luminescent Eu ions. Indeed, Eu precipitation, which strongly limits the optical efficiency of Eu ions embedded in the more conventional SiO2 matrix, can be almost completely suppressed in SiOC. Furthermore, SiOC is also able to induce the Eu3+ → Eu2+ reduction, providing a simple method to obtain high concentrations of the most optically efficient Eu species (Eu2+). Figure 6
Fig. 6 Room temperature PL spectra for Eu-doped SiOC films annealed at 900 °C in N2 (blue line), and in O2 ambient (magenta line, multiplied by a factor of 10 in the region 370-550 nm and by a factor of 400 in the region 550-750 nm). Eu concentration is 1.5 × 1020 cm−3. The inset compares the integrated PL intensity as a function of the annealing temperature of undoped and Eu-doped SiOC (for both processes in N2 and O2); the data referring to undoped SiOC annealed in N2 are multiplied by a factor of 4 to allow an easier comparison.
reports the room temperature PL spectra, obtained by exciting with the 325 nm line of a He-Cd laser, of Eu-doped SiOC samples having an Eu concentration of 1.5 × 1020 cm−3, treated at 900 °C in N2 or O2 ambient. The N2-treated sample (blue line) exhibits a very intense PL band, centered at about 440 nm, due to the 4f65d → 4f7 transitions of Eu2+ ions, massively formed owing to a reduction reaction involving the C atoms of the SiOC matrix [12

12. S. Boninelli, G. Bellocchi, G. Franzò, M. Miritello, and F. Iacona, “New strategies to improve the luminescence efficiency of Eu ions embedded in Si-based matrices,” J. Appl. Phys. 113(14), 143503 (2013). [CrossRef]

]. No PL lines associated to Eu3+ are detected. The PL spectrum of the sample treated in O2 ambient (magenta line, multiplied by a factor of 10 in the region 370-550 nm and by a factor of 400 in the region 550-750 nm) shows a band centered at about 420 nm, attributable to Eu2+ ions, and some weaker sharp peaks at longer wavelengths, typical of Eu3+ emission; the main Eu3+ peak is detected at 618 nm, which corresponds to the 5D07F2 transition. The other less intense peaks at about 575, 657, and 705 nm correspond to 5D07FJ transitions of Eu3+ ions in solid matrices, with J = 0, 3 and 5, respectively. As expected, the annealing in oxidizing ambient promotes the formation of Eu3+ ions and it is therefore unsuitable to provide a strong Eu2+ emission. The shift of about 20 nm between the Eu2+ peaks detected in SiOC films annealed in O2 or N2 ambient is due to the well known dependence of the wavelength of this emission on the Eu concentration [27

27. X. Song, R. Fu, S. Agathopoulos, H. He, X. Zhao, and S. Zhang, “Photoluminescence properties of Eu2+-activated CaSi2O2N2: Redshift and concentration quenching,” J. Appl. Phys. 106(3), 033103 (2009). [CrossRef]

].

Figure 7
Fig. 7 Comparison of the room temperature PLE spectra of Eu-doped SiOC annealed at 900 °C in N2 (obtained by integrating the PL spectra measured by exciting with wavelengths in the range 260-370 nm) and of an Eu2+ silicate (obtained by integrating the PL spectra measured by exciting with wavelengths in the range 260-475 nm). The two spectra are normalized.
reports the room temperature PLE spectrum of Eu-doped SiOC with an Eu concentration of 1.5 × 1020 cm−3 and annealed at 900 °C in N2, obtained by integrating the PL spectra measured by exciting in the 260-370 nm wavelength range.

From the comparison with the PLE spectrum of an Eu2+ silicate [16

16. G. Bellocchi, G. Franzò, F. Iacona, S. Boninelli, M. Miritello, T. Cesca, and F. Priolo, “Eu3+ reduction and efficient light emission in Eu2O3 films deposited on Si substrates,” Opt. Express 20(5), 5501–5507 (2012). [CrossRef] [PubMed]

], reported in the same figure, it is evident that the PL efficiency of Eu-doped SiOC is strongly enhanced for wavelengths ≤ 300 nm; indeed, its PLE curve is characterized a monotonic decrease by increasing the excitation wavelength, while the Eu2+ silicate exhibits a maximum at about 350 nm and it is remarkably less efficient for shorter excitation wavelengths, in agreement with literature data concerning very different Eu2+-containing systems [31

31. Q. Zhang, X. Liu, Y. Qiao, B. Qian, G. Dong, J. Ruan, Q. Zhou, J. Qiu, and D. Chen, “Reduction of Eu3+ to Eu2+ in Eu-doped high silica glass prepared in air atmosphere,” Opt. Mater. 32(3), 427–431 (2010). [CrossRef]

33

33. Y. Qiao, D. Chen, J. Ren, B. Wu, J. Qiu, and T. Akai, “Blue emission from Eu2+-doped high silica glass by near-infrared femtosecond laser irradiation,” J. Appl. Phys. 103(2), 023108 (2008). [CrossRef]

]. Since, as shown in Fig. 4, also the PLE spectrum of undoped SiOC monotonically decreases by increasing the excitation wavelength, it is possible to conclude that the SiOC matrix has an active role in the optical properties of Eu-doped SiOC. We can reasonably exclude that this role consists in the presence of a SiOC emission, since the spectral shape shown in Fig. 6 for an excitation wavelength of 325 nm does not appreciably change by changing the excitation wavelength, even by using the wavelengths which maximize a possible SiOC emission. We could therefore suppose the existence of an energy transfer mechanism, in which the very efficient absorption properties of SiOC in the short wavelength region are exploited to transfer the excitation energy to the Eu2+ ions, by enhancing their PL efficiency under excitation at short wavelength.

Further information about the nature of Eu2+ emission can be obtained by time-resolved PL measurements. Figure 8
Fig. 8 Room temperature PL time-decay curves of Eu-doped SiOC treated in N2 at 900 °C, measured at different emission wavelengths.
shows the time-decay curves of an Eu-doped SiOC sample with an Eu concentration of 1.5 × 1020 cm−3 and treated at 900 °C in N2, measured at different emission wavelengths lying within the broad PL peak shown in Fig. 6.

All of the curves are not single-exponential. The values of the decay-time τ, obtained by taking the time at which the PL signal is 1/e of the value at the laser shut-off, depend on the emission wavelength, since τ varies in the range 0.3-0.8 µs. Similarly to the interpretation given to the same phenomenon observed in Si nc [34

34. J. Linnros, N. Lalic, A. Galeckas, and V. Grivickas, “Analysis of the stretched exponential photoluminescence decay from nanometer-sized silicon crystals in SiO2,” J. Appl. Phys. 86(11), 6128–6134 (1999). [CrossRef]

], the dependence of the τ values of the Eu PL emission on the detection wavelength could be due to the mutual interactions among non-equivalent Eu2+ sites. These sites are characterized by a different local Eu concentration and, in agreement with literature [27

27. X. Song, R. Fu, S. Agathopoulos, H. He, X. Zhao, and S. Zhang, “Photoluminescence properties of Eu2+-activated CaSi2O2N2: Redshift and concentration quenching,” J. Appl. Phys. 106(3), 033103 (2009). [CrossRef]

], the PL peak is redshifted when the concentration is higher. Sites characterized by a faster decay lifetime show a radiative emission at shorter wavelengths and non-radiative decay channels that quench the PL emission through the interaction with sites emitting at longer wavelengths. On the other hand, sites characterized by very high Eu concentrations (emitting at longer wavelengths) can hardly transfer their energy to other Eu sites and therefore exhibit the longest decay lifetime values. Time resolved PL measurements therefore demonstrate that the Eu2+ band peaked at 440 nm shown in Fig. 6 can be actually considered the convolution of several contributions, corresponding to different Eu sites in the SiOC matrix.

4. Conclusions

Although the emission of SiOC is bright enough to be considered potentially interesting for applications in photonics (as the active medium in Si-based light emitting devices) or in lighting technology, this material has been found to be even more promising as a host matrix for optically active Eu ions. Indeed, Eu precipitation in SiOC is strongly reduced with respect to the more conventional SiO2 matrix (so greatly increasing the fraction of optically active Eu ions and therefore the optical efficiency of the system) and Eu3+ ions are efficiently reduced to Eu2+, whose very bright visible luminescence is currently attracting a great attention for LED fabrication. Accordingly, our data demonstrate that an increase of the luminescence intensity at 440 nm accounting for about a factor of 15 can be obtained in Eu-doped films in comparison with undoped SiOC. We have also found evidences of the occurrence of an energy transfer mechanism between the matrix and the Eu2+ ions which, by increasing the efficiency of photon absorption for exciting wavelengths shorter than 300 nm, further contribute to increase the optical efficiency of Eu-doped SiOC layers. These properties open the way to new promising perspectives for the application of Eu-doped materials in photonics and LED fabrication.

Acknowledgments

The authors wish to thank F. Priolo and S. Boninelli (MATIS IMM CNR) for fruitful discussions.

References and links

1.

L. Pavesi, L. Dal Negro, C. Mazzoleni, G. Franzò, and F. Priolo, “Optical gain in silicon nanocrystals,” Nature 408(6811), 440–444 (2000). [CrossRef] [PubMed]

2.

G. Franzò, V. Vinciguerra, and F. Priolo, “The excitation mechanism of rare-earth ions in silicon nanocrystals,” Appl. Phys., A Mater. Sci. Process. 69(1), 3–12 (1999). [CrossRef]

3.

M. Fujii, M. Yoshida, Y. Kanzawa, S. Hayashi, and K. Yamamoto, “1.54 µm photoluminescence of Er3+ doped into SiO2 films containing Si nanocrystals: Evidence for energy transfer from Si nanocrystals to Er3+,” Appl. Phys. Lett. 71(9), 1198–1200 (1997). [CrossRef]

4.

J. H. Shin, J. Lee, H.-S. Han, J.-H. Jhe, J. S. Chang, S.-Y. Seo, H. Lee, and N. Park, “Si nanocluster sensitization of Er-doped silica for optical amplet using top-pumping visible LEDs,” IEEE J. Sel. Top. Quantum Electron. 12(4), 783–796 (2006). [CrossRef]

5.

X. Ye, W. Zhuang, Y. Hu, T. He, X. Huang, C. Liao, S. Zhong, Z. Xu, H. Nie, and G. Deng, “Preparation, characterization, and optical properties of nano- and submicron-sized Y2O3:Eu3+ phosphors,” J. Appl. Phys. 105(6), 064302 (2009). [CrossRef]

6.

D. Li, X. Zhang, L. Jin, and D. Yang, “Structure and luminescence evolution of annealed europium-doped silicon oxides films,” Opt. Express 18(26), 27191–27196 (2010). [CrossRef] [PubMed]

7.

L. Rebohle, J. Lehmann, S. Prucnal, A. Kanjilal, A. Nazarov, I. Tyagulskii, W. Skorupa, and M. Helm, “Blue and red electroluminescence of Europium-implanted metal-oxide-semiconductor structures as a probe for the dynamics of microstructure,” Appl. Phys. Lett. 93(7), 071908 (2008). [CrossRef]

8.

L. Rebohle, J. Lehmann, S. Prucnal, A. Nazarov, I. Tyagulskii, S. Tyagulskii, A. Kanjilal, M. Voelskow, D. Grambole, W. Skorupa, and M. Helm, “Anomalous wear-out phenomena of europium-implanted light emitters based on a metal-oxide-semiconductor structure,” J. Appl. Phys. 106(12), 123103 (2009). [CrossRef]

9.

S. Prucnal, J. M. Sun, W. Skorupa, and M. Helm, “Switchable two-color electroluminescence based on a Si metal-oxide-semiconductor structure doped with Eu,” Appl. Phys. Lett. 90(18), 181121 (2007). [CrossRef]

10.

N. D. Afify and G. Mountjoy, “Molecular-dynamics modeling of Eu3+-ion clustering in SiO2 glass,” Phys. Rev. B 79(2), 024202 (2009). [CrossRef]

11.

J. Laegsgaard, “Theory of Al2O3 incorporation in SiO2,” Phys. Rev. B 65(17), 174104 (2002). [CrossRef]

12.

S. Boninelli, G. Bellocchi, G. Franzò, M. Miritello, and F. Iacona, “New strategies to improve the luminescence efficiency of Eu ions embedded in Si-based matrices,” J. Appl. Phys. 113(14), 143503 (2013). [CrossRef]

13.

J. Qi, T. Matsumoto, M. Tanaka, and Y. Masumoto, “Electroluminescence of europium silicate thin film on silicon,” Appl. Phys. Lett. 74(21), 3203–3205 (1999). [CrossRef]

14.

Y. C. Shin, D. H. Kong, W. C. Choi, and T. G. Kim, “Formation of europium-silicate thin films and their photoluminescence properties,” J. Korean Phys. Soc. 48, 1246–1249 (2006).

15.

Y. C. Shin, S. J. Leem, C. M. Kim, S. J. Kim, Y. M. Sung, C. K. Hahn, J. H. Baek, and T. G. Kim, “Deposition of europium oxide on Si and its optical properties depending on thermal annealing conditions,” J. Electroceram. 23(2-4), 326–330 (2009). [CrossRef]

16.

G. Bellocchi, G. Franzò, F. Iacona, S. Boninelli, M. Miritello, T. Cesca, and F. Priolo, “Eu3+ reduction and efficient light emission in Eu2O3 films deposited on Si substrates,” Opt. Express 20(5), 5501–5507 (2012). [CrossRef] [PubMed]

17.

S.-Y. Seo, K.-S. Cho, and J. H. Shin, “Intense blue-white luminescence from carbon-doped silicon-rich silicon oxide,” Appl. Phys. Lett. 84(5), 717–719 (2004). [CrossRef]

18.

S. Gallis, V. Nikas, H. Suhag, M. Huang, and A. E. Kaloyeros, “White light emission from amorphous silicon oxycarbide (a-SiCxOy) thin films: Role of composition and postdeposition annealing,” Appl. Phys. Lett. 97(8), 081905 (2010). [CrossRef]

19.

Y. P. Guo, J. C. Zheng, A. T. S. Wee, C. H. A. Huan, K. Li, J. S. Pan, Z. C. Feng, and S. J. Chua, “Photoluminescence studies of SiC nanocrystals embedded in a SiO2 matrix,” Chem. Phys. Lett. 339(5-6), 319–322 (2001). [CrossRef]

20.

A. Perez-Rodriguez, O. Gonzalez-Varona, B. Garrido, P. Pellegrino, J. R. Morante, C. Bonafos, M. Carrada, and A. Claverie, “White luminescence from Si+ and C+ ion-implanted SiO2 films,” J. Appl. Phys. 94(1), 254–262 (2003). [CrossRef]

21.

Y. Ishikawa, A. V. Vasin, J. Salonen, S. Muto, V. S. Lysenko, A. N. Nazarov, N. Shibata, and V.-P. Lehto, “Color control of white photoluminescence from carbon-incorporated silicon oxide,” J. Appl. Phys. 104(8), 083522 (2008). [CrossRef]

22.

Y. Ding and H. Shirai, “White light emission from silicon oxycarbide films prepared by using atmospheric pressure microplasma jet,” J. Appl. Phys. 105(4), 043515 (2009). [CrossRef]

23.

A. V. Vasin, Y. Ishikawa, N. Shibata, J. Salonen, and V.-P. Lehto, “Strong white photoluminescence from carbon-incorporated silicon oxide fabricated by preferential oxidation of silicon in nano-structured Si:C layer,” Jpn. J. Appl. Phys. 46(19), L465–L467 (2007). [CrossRef]

24.

S. Gallis, M. Huang, and A. E. Kaloyeros, “Efficient energy transfer from silicon oxycarbide matrix to Er ions via indirect excitation mechanisms,” Appl. Phys. Lett. 90(16), 161914 (2007). [CrossRef]

25.

Y. Zhang, A. Quaranta, and G. D. Soraru, “Synthesis and luminescent properties of novel Eu2+-doped silicon oxycarbide glasses,” Opt. Mater. 24(4), 601–605 (2004). [CrossRef]

26.

G. Blasse and B. C. Grabmaier, Luminescent Materials (Springer Verlag, 1994).

27.

X. Song, R. Fu, S. Agathopoulos, H. He, X. Zhao, and S. Zhang, “Photoluminescence properties of Eu2+-activated CaSi2O2N2: Redshift and concentration quenching,” J. Appl. Phys. 106(3), 033103 (2009). [CrossRef]

28.

C. M. Brewer, D. R. Bujalski, V. E. Parent, K. Su, and G. A. Zank, “Insights into the oxidation chemistry of SiOC ceramics derived from silsesquioxanes,” J. Sol-Gel Sci. Technol. 14(1), 49–68 (1999). [CrossRef]

29.

T. Rajagopalan, X. Wang, B. Lahlouh, C. Ramkumar, P. Dutta, and S. Gangopadhyaya, “Low temperature deposition of nanocrystalline silicon carbide films by plasma enhanced chemical vapor deposition and their structural and optical characterization,” J. Appl. Phys. 94(8), 5252–5260 (2003). [CrossRef]

30.

J. Y. Kim, M. S. Hwang, Y.-H. Kim, H. J. Kim, and Y. Lee, “Origin of low dielectric constant of carbon-incorporated silicon oxide film deposited by plasma enhanced chemical vapor deposition,” J. Appl. Phys. 90(5), 2469–2473 (2001). [CrossRef]

31.

Q. Zhang, X. Liu, Y. Qiao, B. Qian, G. Dong, J. Ruan, Q. Zhou, J. Qiu, and D. Chen, “Reduction of Eu3+ to Eu2+ in Eu-doped high silica glass prepared in air atmosphere,” Opt. Mater. 32(3), 427–431 (2010). [CrossRef]

32.

Y. Kishimoto, X. Zhang, T. Hayakawa, and M. Nogami, “Blue light emission from Eu2+ ions in sol-gel-derived Al2O3-SiO2 glasses,” J. Lumin. 129(9), 1055–1059 (2009). [CrossRef]

33.

Y. Qiao, D. Chen, J. Ren, B. Wu, J. Qiu, and T. Akai, “Blue emission from Eu2+-doped high silica glass by near-infrared femtosecond laser irradiation,” J. Appl. Phys. 103(2), 023108 (2008). [CrossRef]

34.

J. Linnros, N. Lalic, A. Galeckas, and V. Grivickas, “Analysis of the stretched exponential photoluminescence decay from nanometer-sized silicon crystals in SiO2,” J. Appl. Phys. 86(11), 6128–6134 (1999). [CrossRef]

OCIS Codes
(160.4670) Materials : Optical materials
(160.5690) Materials : Rare-earth-doped materials
(260.3800) Physical optics : Luminescence

ToC Category:
Materials

History
Original Manuscript: May 16, 2013
Revised Manuscript: June 12, 2013
Manuscript Accepted: June 12, 2013
Published: August 22, 2013

Citation
Gabriele Bellocchi, Fabio Iacona, Maria Miritello, Tiziana Cesca, and Giorgia Franzò, "SiOC thin films: an efficient light source and an ideal host matrix for Eu2+ ions," Opt. Express 21, 20280-20290 (2013)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-21-17-20280


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. L. Pavesi, L. Dal Negro, C. Mazzoleni, G. Franzò, and F. Priolo, “Optical gain in silicon nanocrystals,” Nature408(6811), 440–444 (2000). [CrossRef] [PubMed]
  2. G. Franzò, V. Vinciguerra, and F. Priolo, “The excitation mechanism of rare-earth ions in silicon nanocrystals,” Appl. Phys., A Mater. Sci. Process.69(1), 3–12 (1999). [CrossRef]
  3. M. Fujii, M. Yoshida, Y. Kanzawa, S. Hayashi, and K. Yamamoto, “1.54 µm photoluminescence of Er3+ doped into SiO2 films containing Si nanocrystals: Evidence for energy transfer from Si nanocrystals to Er3+,” Appl. Phys. Lett.71(9), 1198–1200 (1997). [CrossRef]
  4. J. H. Shin, J. Lee, H.-S. Han, J.-H. Jhe, J. S. Chang, S.-Y. Seo, H. Lee, and N. Park, “Si nanocluster sensitization of Er-doped silica for optical amplet using top-pumping visible LEDs,” IEEE J. Sel. Top. Quantum Electron.12(4), 783–796 (2006). [CrossRef]
  5. X. Ye, W. Zhuang, Y. Hu, T. He, X. Huang, C. Liao, S. Zhong, Z. Xu, H. Nie, and G. Deng, “Preparation, characterization, and optical properties of nano- and submicron-sized Y2O3:Eu3+ phosphors,” J. Appl. Phys.105(6), 064302 (2009). [CrossRef]
  6. D. Li, X. Zhang, L. Jin, and D. Yang, “Structure and luminescence evolution of annealed europium-doped silicon oxides films,” Opt. Express18(26), 27191–27196 (2010). [CrossRef] [PubMed]
  7. L. Rebohle, J. Lehmann, S. Prucnal, A. Kanjilal, A. Nazarov, I. Tyagulskii, W. Skorupa, and M. Helm, “Blue and red electroluminescence of Europium-implanted metal-oxide-semiconductor structures as a probe for the dynamics of microstructure,” Appl. Phys. Lett.93(7), 071908 (2008). [CrossRef]
  8. L. Rebohle, J. Lehmann, S. Prucnal, A. Nazarov, I. Tyagulskii, S. Tyagulskii, A. Kanjilal, M. Voelskow, D. Grambole, W. Skorupa, and M. Helm, “Anomalous wear-out phenomena of europium-implanted light emitters based on a metal-oxide-semiconductor structure,” J. Appl. Phys.106(12), 123103 (2009). [CrossRef]
  9. S. Prucnal, J. M. Sun, W. Skorupa, and M. Helm, “Switchable two-color electroluminescence based on a Si metal-oxide-semiconductor structure doped with Eu,” Appl. Phys. Lett.90(18), 181121 (2007). [CrossRef]
  10. N. D. Afify and G. Mountjoy, “Molecular-dynamics modeling of Eu3+-ion clustering in SiO2 glass,” Phys. Rev. B79(2), 024202 (2009). [CrossRef]
  11. J. Laegsgaard, “Theory of Al2O3 incorporation in SiO2,” Phys. Rev. B65(17), 174104 (2002). [CrossRef]
  12. S. Boninelli, G. Bellocchi, G. Franzò, M. Miritello, and F. Iacona, “New strategies to improve the luminescence efficiency of Eu ions embedded in Si-based matrices,” J. Appl. Phys.113(14), 143503 (2013). [CrossRef]
  13. J. Qi, T. Matsumoto, M. Tanaka, and Y. Masumoto, “Electroluminescence of europium silicate thin film on silicon,” Appl. Phys. Lett.74(21), 3203–3205 (1999). [CrossRef]
  14. Y. C. Shin, D. H. Kong, W. C. Choi, and T. G. Kim, “Formation of europium-silicate thin films and their photoluminescence properties,” J. Korean Phys. Soc.48, 1246–1249 (2006).
  15. Y. C. Shin, S. J. Leem, C. M. Kim, S. J. Kim, Y. M. Sung, C. K. Hahn, J. H. Baek, and T. G. Kim, “Deposition of europium oxide on Si and its optical properties depending on thermal annealing conditions,” J. Electroceram.23(2-4), 326–330 (2009). [CrossRef]
  16. G. Bellocchi, G. Franzò, F. Iacona, S. Boninelli, M. Miritello, T. Cesca, and F. Priolo, “Eu3+ reduction and efficient light emission in Eu2O3 films deposited on Si substrates,” Opt. Express20(5), 5501–5507 (2012). [CrossRef] [PubMed]
  17. S.-Y. Seo, K.-S. Cho, and J. H. Shin, “Intense blue-white luminescence from carbon-doped silicon-rich silicon oxide,” Appl. Phys. Lett.84(5), 717–719 (2004). [CrossRef]
  18. S. Gallis, V. Nikas, H. Suhag, M. Huang, and A. E. Kaloyeros, “White light emission from amorphous silicon oxycarbide (a-SiCxOy) thin films: Role of composition and postdeposition annealing,” Appl. Phys. Lett.97(8), 081905 (2010). [CrossRef]
  19. Y. P. Guo, J. C. Zheng, A. T. S. Wee, C. H. A. Huan, K. Li, J. S. Pan, Z. C. Feng, and S. J. Chua, “Photoluminescence studies of SiC nanocrystals embedded in a SiO2 matrix,” Chem. Phys. Lett.339(5-6), 319–322 (2001). [CrossRef]
  20. A. Perez-Rodriguez, O. Gonzalez-Varona, B. Garrido, P. Pellegrino, J. R. Morante, C. Bonafos, M. Carrada, and A. Claverie, “White luminescence from Si+ and C+ ion-implanted SiO2 films,” J. Appl. Phys.94(1), 254–262 (2003). [CrossRef]
  21. Y. Ishikawa, A. V. Vasin, J. Salonen, S. Muto, V. S. Lysenko, A. N. Nazarov, N. Shibata, and V.-P. Lehto, “Color control of white photoluminescence from carbon-incorporated silicon oxide,” J. Appl. Phys.104(8), 083522 (2008). [CrossRef]
  22. Y. Ding and H. Shirai, “White light emission from silicon oxycarbide films prepared by using atmospheric pressure microplasma jet,” J. Appl. Phys.105(4), 043515 (2009). [CrossRef]
  23. A. V. Vasin, Y. Ishikawa, N. Shibata, J. Salonen, and V.-P. Lehto, “Strong white photoluminescence from carbon-incorporated silicon oxide fabricated by preferential oxidation of silicon in nano-structured Si:C layer,” Jpn. J. Appl. Phys.46(19), L465–L467 (2007). [CrossRef]
  24. S. Gallis, M. Huang, and A. E. Kaloyeros, “Efficient energy transfer from silicon oxycarbide matrix to Er ions via indirect excitation mechanisms,” Appl. Phys. Lett.90(16), 161914 (2007). [CrossRef]
  25. Y. Zhang, A. Quaranta, and G. D. Soraru, “Synthesis and luminescent properties of novel Eu2+-doped silicon oxycarbide glasses,” Opt. Mater.24(4), 601–605 (2004). [CrossRef]
  26. G. Blasse and B. C. Grabmaier, Luminescent Materials (Springer Verlag, 1994).
  27. X. Song, R. Fu, S. Agathopoulos, H. He, X. Zhao, and S. Zhang, “Photoluminescence properties of Eu2+-activated CaSi2O2N2: Redshift and concentration quenching,” J. Appl. Phys.106(3), 033103 (2009). [CrossRef]
  28. C. M. Brewer, D. R. Bujalski, V. E. Parent, K. Su, and G. A. Zank, “Insights into the oxidation chemistry of SiOC ceramics derived from silsesquioxanes,” J. Sol-Gel Sci. Technol.14(1), 49–68 (1999). [CrossRef]
  29. T. Rajagopalan, X. Wang, B. Lahlouh, C. Ramkumar, P. Dutta, and S. Gangopadhyaya, “Low temperature deposition of nanocrystalline silicon carbide films by plasma enhanced chemical vapor deposition and their structural and optical characterization,” J. Appl. Phys.94(8), 5252–5260 (2003). [CrossRef]
  30. J. Y. Kim, M. S. Hwang, Y.-H. Kim, H. J. Kim, and Y. Lee, “Origin of low dielectric constant of carbon-incorporated silicon oxide film deposited by plasma enhanced chemical vapor deposition,” J. Appl. Phys.90(5), 2469–2473 (2001). [CrossRef]
  31. Q. Zhang, X. Liu, Y. Qiao, B. Qian, G. Dong, J. Ruan, Q. Zhou, J. Qiu, and D. Chen, “Reduction of Eu3+ to Eu2+ in Eu-doped high silica glass prepared in air atmosphere,” Opt. Mater.32(3), 427–431 (2010). [CrossRef]
  32. Y. Kishimoto, X. Zhang, T. Hayakawa, and M. Nogami, “Blue light emission from Eu2+ ions in sol-gel-derived Al2O3-SiO2 glasses,” J. Lumin.129(9), 1055–1059 (2009). [CrossRef]
  33. Y. Qiao, D. Chen, J. Ren, B. Wu, J. Qiu, and T. Akai, “Blue emission from Eu2+-doped high silica glass by near-infrared femtosecond laser irradiation,” J. Appl. Phys.103(2), 023108 (2008). [CrossRef]
  34. J. Linnros, N. Lalic, A. Galeckas, and V. Grivickas, “Analysis of the stretched exponential photoluminescence decay from nanometer-sized silicon crystals in SiO2,” J. Appl. Phys.86(11), 6128–6134 (1999). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited