OSA's Digital Library

Optics Express

Optics Express

  • Editor: Andrew M. Weiner
  • Vol. 22, Iss. 16 — Aug. 11, 2014
  • pp: 19047–19054
« Show journal navigation

A nonreciprocal racetrack resonator based on vacuum-annealed magnetooptical cerium-substituted yttrium iron garnet

Taichi Goto, Mehmet C. Onbasli, Dong Hun Kim, Vivek Singh, M. Inoue, Lionel C. Kimerling, and C. A. Ross  »View Author Affiliations


Optics Express, Vol. 22, Issue 16, pp. 19047-19054 (2014)
http://dx.doi.org/10.1364/OE.22.019047


View Full Text Article

Acrobat PDF (8531 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

Vacuum annealed polycrystalline cerium substituted yttrium iron garnet (CeYIG) films deposited by radio frequency magnetron sputtering on non-garnet substrates were used in nonreciprocal racetrack resonators. CeYIG annealed at 800°C for 30 min provided a large Faraday rotation angle, close to the single crystal value. Crystallinity, magnetic properties, refractive indices and absorption coefficients were measured. The resonant transmission peak of the racetrack resonator covered with CeYIG was non-reciprocally shifted by applying an in-plane magnetic field.

© 2014 Optical Society of America

1. Introduction

Demands for non-reciprocal phase shifters or polarization rotators, e.g., isolators [1–4

1. L. Bi, J. Hu, P. Jiang, D. H. Kim, G. F. Dionne, L. C. Kimerling, and C. A. Ross, “On-chip optical isolation in monolithically integrated non-reciprocal optical resonators,” Nat. Photonics 5(12), 758–762 (2011). [CrossRef]

], circulators [5, 6

5. Q. Wang, Z. Ouyang, and Q. Liu, “Multiport photonic crystal circulators created by cascading magneto-optical cavities,” J. Opt. Soc. Am. B 28(4), 703–708 (2011). [CrossRef]

], or modulators [7, 8

7. T. Goto, R. Isogai, and M. Inoue, “Para-magneto- and electro-optic microcavities for blue wavelength modulation,” Opt. Express 21(17), 19648–19656 (2013). [CrossRef] [PubMed]

] are increasing with the rapid growth of integrated photonics [6, 9

6. K. Yayoi, K. Tobinaga, Y. Kaneko, A. V. Baryshev, and M. Inoue, “Optical waveguide circulators based on two-dimensional magnetophotonic crystals: Numerical simulation for structure simplification and experimental verification,” J. Appl. Phys. 109(7), 07B750 (2011). [CrossRef]

]. Magnetooptical (MO) garnets have been used to achieve nonreciprocal isolation with low optical losses from visible to near IR wavelengths, but their integration onto non-garnet substrates, e.g., Si, Si-on-insulator (SOI), or silica, is still challenging because of the mismatch of the thermal expansion and lattice constants between the films and substrates. In particular, cerium substituted yttrium iron garnet (CexY3-xFe5O12 or CeYIG) with 1 Ce per formula unit (Ce1Y2Fe5O12) or more has been difficult to fabricate on non-garnet substrates because of the formation of undesirable non-garnet phases [10, 11

10. M. Gomi, H. Furuyama, and M. Abe, “Strong magneto-optical enhancement in highly Ce-substituted iron garnet films prepared by sputtering,” J. Appl. Phys. 70(11), 7065 (1991). [CrossRef]

] even though a large Faraday rotation (FR) angle (–3300 deg/cm) and low absorption (–9.7 dB/cm) at a wavelength of λ = 1550 nm were demonstrated in single crystalline CeYIG on garnet substrates [12

12. T. Shintaku, A. Tate, and S. Mino, “Ce-substituted yttrium iron garnet films prepared on Gd3Sc2Ga3O12 garnet substrates by sputter epitaxy,” Appl. Phys. Lett. 71(12), 1640–1642 (1997). [CrossRef]

].

Recently, we demonstrated two methods to fabricate CeYIG on non-garnet substrates: two-step deposition using pulsed laser deposition (PLD) [13

13. T. Goto, M. C. Onbaşlı, and C. A. Ross, “Magneto-optical properties of cerium substituted yttrium iron garnet films with reduced thermal budget for monolithic photonic integrated circuits,” Opt. Express 20(27), 28507–28517 (2012). [CrossRef] [PubMed]

] and sputtering with thermal annealing in vacuum [14

14. T. Goto, Y. Eto, K. Kobayashi, Y. Haga, M. Inoue, and C. A. Ross, “Vacuum annealed cerium-substituted yttrium iron garnet films on non-garnet substrates for integrated optical circuits,” J. Appl. Phys. 113(17), 17A939 (2013). [CrossRef]

]. The two-step deposition uses a thin YIG buffer layer as a seed layer for epitaxial growth of polycrystalline CeYIG on non-garnet substrates [1

1. L. Bi, J. Hu, P. Jiang, D. H. Kim, G. F. Dionne, L. C. Kimerling, and C. A. Ross, “On-chip optical isolation in monolithically integrated non-reciprocal optical resonators,” Nat. Photonics 5(12), 758–762 (2011). [CrossRef]

], and was used in a demonstration of an integrated isolator based on a racetrack resonator. On the other hand, the CeYIG fabricated by sputtering on silicon with thermal annealing in vacuum showed larger FR (–3000 deg/cm) at λ = 1550 nm [14

14. T. Goto, Y. Eto, K. Kobayashi, Y. Haga, M. Inoue, and C. A. Ross, “Vacuum annealed cerium-substituted yttrium iron garnet films on non-garnet substrates for integrated optical circuits,” J. Appl. Phys. 113(17), 17A939 (2013). [CrossRef]

], but its nonreciprocal shift as a isolator has not been reported. In this paper, we optimized the fabrication condition of CeYIG on Si and SOI substrates. The structural characteristics, the FR, refractive index, extinction coefficient, and figure of merit (FOM) of polycrystalline CeYIG are shown as a function of annealing conditions. Finally, we demonstrate a non-reciprocal shift of transmissivity in a racetrack resonator using optimized CeYIG.

2. CeYIG preparation

The 170 nm thick films were deposited on double-side polished SOI substrates by radio frequency sputtering using the same conditions as [14

14. T. Goto, Y. Eto, K. Kobayashi, Y. Haga, M. Inoue, and C. A. Ross, “Vacuum annealed cerium-substituted yttrium iron garnet films on non-garnet substrates for integrated optical circuits,” J. Appl. Phys. 113(17), 17A939 (2013). [CrossRef]

], from a sintered Ce1Y2.5Fe5Ox target in 10 mTorr Ar at 0.3 nm/min onto substrates at room temperature. The base pressure was 1.0 × 10−7 Torr. A vacuum anneal was carried out at a pressure of 5 Pa as shown in [14

14. T. Goto, Y. Eto, K. Kobayashi, Y. Haga, M. Inoue, and C. A. Ross, “Vacuum annealed cerium-substituted yttrium iron garnet films on non-garnet substrates for integrated optical circuits,” J. Appl. Phys. 113(17), 17A939 (2013). [CrossRef]

]. The temperature and time of the thermal anneal was varied. Composition of the annealed films was measured by energy dispersive x-ray spectrometer (EDS) and normalized to the iron atomic fraction. Transmissivity was measured with a spectrophotometer, using specimens of CeYIG on Si substrates to suppress the oscillations in the transmission spectra generated by the SOI substrates. FR loops were measured by oscillating polarizer method [15

15. K. Sato, Hikari-to-jiki (Asakura-shoten, Tokyo, 2007).

] with a laser diode at a wavelength of λ = 1550 nm. Magnetic hysteresis loops were measured by vibrating sample magnetometry (VSM). Structural properties were characterized with atomic force microscopy (AFM) and x-ray diffraction (XRD) with CuKα radiation at 0.1541 nm wavelength. All measurements were carried out at ambient temperature (25°C).

3. CeYIG properties

Figure 1
Fig. 1 XRD patterns of the SOI substrate/CeYIG samples annealed (a) at various temperatures (600–1000°C) for 60 minutes and (b) at 800°C for various times (1–120 minutes). The thickness of the CeYIG was 170 nm. Black squares show the peaks of Y3Fe5O12, white squares show yttria, and white triangles show YFe2O4.
shows diffraction patterns for a set of CeYIG samples deposited on SOI substrates. The composition was Ce0.97 ± 0.011Y1.96 ± 0.083Fe5O12.2 ± 0.030 (the value after ± is the standard deviation). Pure garnet phase was obtained from the samples annealed at 700 and 800°C, Fig. 1(a). The films annealed at more than 900°C showed YFe2O4 and Y2O3 peaks which lead to large optical absorption. A garnet phase was not found in the samples annealed below 600°C. In Fig. 1(b), the annealing time was varied from 1 to 120 minutes at 800°C.

Figures 2(a)
Fig. 2 FR loops of the samples of Si substrate/CeYIG (170 nm) annealed (a) at various temperatures for 60 minutes and (b) at 800°C for various times. Insets show the saturation FR dependence on annealing temperature and time.
and 2(b) show the corresponding FR loops of the samples annealed at various conditions. The FR was measured through the film thickness which is the magnetic hard axis, so the FR did not saturate until the field reached 2–3 kOe. There is a clear dependence of the FR loop on both the temperature and time. Although the XRD results were similar after 700°C and 800°C annealing, the 800°C anneal produced a much higher FR.

The sample annealed at 800°C for 30 minutes showed the largest value in this study, around –3.0 × 103 deg/cm, which is 90% of the value reported for single crystal CeYIG [12

12. T. Shintaku, A. Tate, and S. Mino, “Ce-substituted yttrium iron garnet films prepared on Gd3Sc2Ga3O12 garnet substrates by sputter epitaxy,” Appl. Phys. Lett. 71(12), 1640–1642 (1997). [CrossRef]

]. It is not known why there is an optimum anneal time, but excessive annealing could produce unwanted phases or roughness of the film, or changes in stoichiometry [16

16. B. Stadler and A. Gopinath, “Magneto-optical garnet films made by reactive sputtering,” IEEE Trans. Magn. 36(6), 3957–3961 (2000). [CrossRef]

].

The influence of annealing on the magnetic properties was observed in the VSM hysteresis loops, Fig. 3
Fig. 3 (a) In-plane and (b) out-of-plane magnetic properties of the samples Si substrate/CeYIG (170 nm) annealed at 800°C for various minutes. Insets show the enlarged portions of these data, respectively around zero.
. The saturation magnetization Ms was ~118 emu cm−3, similar to single crystal values [17

17. S. Mino, A. Tate, T. Uno, T. Shintaku, and A. Shibukawa, “Properties of Ce-substituted yttrium iron garnet film containing indium prepared by RF-sputtering,” Jpn. J. Appl. Phys. 32(Part 2, No. 7B), L994–L996 (1993). [CrossRef]

]. The dominant magnetic anisotropy in these films is the shape anisotropy and the hard-axis (out-of-plane) saturation field Hs, obtained from extrapolating the out-of-plane loops to saturation, was close to the calculated shape anisotropy field of 4πMs = 1.48 kOe. For the 800°C, 30 min sample the coercivity Hc for in-plane and out-of-plane loops was 45 and 102 Oe respectively. The remnant magnetization Mr for in-plane and out-of-plane loops was 75 and 6.3 emu cm−3 respectively.

Figure 4(a)
Fig. 4 Transmission spectra of (a) Si/CeYIG on 0.38 mm thick Si substrate, and (b) silica/CeYIG and 0.7 mm thick silica substrate.
shows the transmission spectra of CeYIG on Si substrate annealed at 800°C for various times. The transmissivity was increased because of the anti-reflection effect of introducing the lower refractive index garnet on the higher refractive index Si substrates. This is not the case for the silica substrates. To obtain the refractive index and absorption, the transmissivity of CeYIG on a silica substrate was measured, Fig. 4(b). The silica substrate is highly transmissive, enabling the optical index to be found from the fringes. The simulation software (SCOUT) [14

14. T. Goto, Y. Eto, K. Kobayashi, Y. Haga, M. Inoue, and C. A. Ross, “Vacuum annealed cerium-substituted yttrium iron garnet films on non-garnet substrates for integrated optical circuits,” J. Appl. Phys. 113(17), 17A939 (2013). [CrossRef]

], based on the Fresnel equation, was used to derive the refractive index and extinction coefficient of CeYIG annealed at 800°C for 30 min, Fig. 5
Fig. 5 (a) Refractive index and (b) extinction coefficient of Si/CeYIG annealed at 800°C for 30 minutes. The error bars are determined by the thickness deviation of the CeYIG.
.

4. Racetrack resonator preparation

An optical isolator based on a racetrack resonator with optimized CeYIG as cladding was fabricated by electron beam lithography (EBL). In this design one straight side of the racetrack is clad with MO material which is magnetized perpendicular to the track to produce a nonreciprocal phase shift in the circulating light. The device structure was based on Ref [1

1. L. Bi, J. Hu, P. Jiang, D. H. Kim, G. F. Dionne, L. C. Kimerling, and C. A. Ross, “On-chip optical isolation in monolithically integrated non-reciprocal optical resonators,” Nat. Photonics 5(12), 758–762 (2011). [CrossRef]

], and also its process was similar, but several steps were improved, e.g., the SiO2 cladding layer was formed by chemical vapor deposition (CVD) and etched by reactive ion etching (RIE) in CHF3 gas instead of by a wet processes, which improved the control over the deposition and etching rate.

Figure 7
Fig. 7 Process for formation of optical isolator with CeYIG cladding annealed in vacuum.
shows the process flow. The 80 nm thick negative-contrast hydrogen silsesquioxane (HSQ) resist (Dow Corning, XR-1541, 6%) was spin coated on SOI wafers (Soitec) for 1 minute at 5000 rpm, Fig. 7(a). The SOI substrates were composed of 0.5 mm thick Si/3 μm thick SiO2/250 nm thick Si. The coated substrates were exposed by electron beam lithography (Elionix, ELS-F125) with acceleration voltage of 125 kV, current of 10 nA, aperture of 120 μm, 6 × 104 pixels in a 600 × 600 μm2 area, at a dose time of 0.20 μsec, Fig. 7(b). The exposed width of the waveguide was 450 nm. The curvature radius of the racetrack was 45 μm. The length of the straight line portion of the racetrack was 200 μm. After development with tetra-methyl-ammonium hydroxide (TMAH, MF-CD-36) at 25°C with sonication for 3 minutes and a rinse with deionized water, Fig. 7(c), the uncovered Si area was etched by RIE (PlasmaTherm SLR) in 10 mTorr HBr gas pressure, Figs. 7(d) and 7(e). The base pressure was 1.0 × 10−5 Torr, forward power was 200 W, and the etching rate was 1.0 nm/sec. A 1 μm thick SiO2 was deposited onto the sample by plasma-enhanced CVD (PlasmaTherm) with a deposition rate of 28.9 nm/min, Fig. 7(f). The substrate temperature was 250°C, base pressure was 10 mTorr, and working pressure was 500 mTorr. The introduced gasses were 150 sccm 5% SiH4 in He and 600 sccm N2O. The input power was 25 W.

The quality of the racetrack resonator without MO cladding was evaluated by a transmission measurement performed on a Newport Auto Align workstation using an optical vector analyzer (LUNA Technologies OVA-5000) with a built-in tunable laser. The laser light was coupled into and out of the devices with tapered lens-tip fibers to improve coupling efficiency. The transmitted light was analyzed with an optical vector analyzer (LUNA Technologies). The sample was placed onto a thermostat stage kept at 25°C to decrease the effects of the temperature-dependent index of silicon. Figure 8
Fig. 8 Transmission spectra of the waveguide without CeYIG cladding at a temperature of 25°C. Solid and dashed lines show the TM and TE mode, respectively.
shows the transmission spectra of the Si racetrack resonator. The TE mode undergoes greater attenuation than the TM mode because it is more sensitive to sidewall roughness, even though the cross-sectional dimensions of the waveguide suggest it should propagate the TE mode better, according to Lumerical MODE simulations. The Q factor was 3.4 × 104 and free spectral range (FSR) was 0.82 nm. Although the FSR was comparable to the reported values (0.90 nm) in [1

1. L. Bi, J. Hu, P. Jiang, D. H. Kim, G. F. Dionne, L. C. Kimerling, and C. A. Ross, “On-chip optical isolation in monolithically integrated non-reciprocal optical resonators,” Nat. Photonics 5(12), 758–762 (2011). [CrossRef]

], the Q factor was one order smaller than the value 1.3 × 105 in [1

1. L. Bi, J. Hu, P. Jiang, D. H. Kim, G. F. Dionne, L. C. Kimerling, and C. A. Ross, “On-chip optical isolation in monolithically integrated non-reciprocal optical resonators,” Nat. Photonics 5(12), 758–762 (2011). [CrossRef]

].

To deposit CeYIG only in a 20 × 200 μm region on the racetrack, a window in the SiO2 cladding layer was etched using a positive resist. The 1 μm thick positive resist (ZEP520A) was spin coated for 1 minute at 5000 rpm followed by baking at 180°C for 3 minutes on a hot plate. The resist was exposed by EBL under the conditions described above except the current was 2 nA, aperture 120 μm, and dose time 0.2 μsec, Fig. 7(g). To form the window at the appropriate part of the racetrack, two cross-shaped alignment marks were formed on first 3 μm thick SiO2 layer at the edge of the SOI substrate, and covered with polyimide tapes during the SiO2 deposition and the ZEP coating so they would be visible. The pattern was developed with o-xylene (ZED-WN) for 1 minute at room temperature (RT) without sonication followed by rinsing with IPA for 1 minute at RT and N2 blowing. The SiO2 was etched by RIE in 200 mTorr (20 sccm) CHF3 gas with a substrate temperature of 200°C, base pressure of 1 μTorr, and input power of 100 W, Fig. 7(h). The etching rate for the resist and SiO2 were both ~21 nm/min. The top image of the sample is shown in Fig. 7(i). The presence of residual SiO2 (from the HSQ) beside the waveguide was confirmed by comparing the profiles in Figs. 7(e) and 7(j). 80 nm thick CeYIG was deposited on this sample and annealed with the above conditions, Figs. 7(k) and 7(l). A cross sectional image of the waveguide covered with MO material was obtained by focused ion beam (FIB) cutting and scanning electron microscope (SEM), Fig. 7(l). Only the CeYIG on the top of the waveguide was in direct contact with the waveguide because the side of the Si waveguide was covered with residual SiO2 and was decoupled from the MO layer. Cracks in the CeYIG were not observed on the Si waveguide, but grain growth was observed and might lead to optical losses. This result suggests that it will be useful to optimize the fabrication conditions of the CeYIG in the geometry used in the actual device.

5. Nonreciprocal shift measurement

6. Conclusion

Acknowledgment

TG acknowledges the Japan Society for the Promotion of Science (JSPS) Postdoctoral Fellowships for Research Abroad, Grant-in-Aid for Young Scientists (A) No. 26706009, and Challenging Exploratory Research No. 26600043. CR acknowledges support of the NSF and FAME, a SRC STARnet Center supported by DARPA and MARCO. This work made use of the shared experimental facilities of the Center for Materials Science and Engineering (CMSE), award NSF DMR0819762. We thank Mr. Yu Eto, Mr. Keiichi Kobayashi, Mr. Naoto Sagara, Mr. Ryosuke Isogai, Mr. Masahiko Watanabe, Dr. Lei Bi and Dr. Gerald F. Dionne for experimental support and discussions.

References and links

1.

L. Bi, J. Hu, P. Jiang, D. H. Kim, G. F. Dionne, L. C. Kimerling, and C. A. Ross, “On-chip optical isolation in monolithically integrated non-reciprocal optical resonators,” Nat. Photonics 5(12), 758–762 (2011). [CrossRef]

2.

S. Ghosh, S. Keyvaninia, Y. Shirato, T. Mizumoto, G. Roelkens, and R. Baets, “Optical isolator for TE polarized light realized by adhesive bonding of Ce:YIG on Silicon-on-Insulator waveguide circuits,” IEEE Photon. J. 5(3), 6601108 (2013). [CrossRef]

3.

S. Ghosh, S. Keyvavinia, W. Van Roy, T. Mizumoto, G. Roelkens, and R. Baets, “Ce:YIG/Silicon-on-Insulator waveguide optical isolator realized by adhesive bonding,” Opt. Express 20(2), 1839–1848 (2012). [CrossRef] [PubMed]

4.

P. Pintus, T. Ming-Chun, and J. E. Bowers, “Design of magneto-optical ring isolator on SOI based on the finite-element method,” IEEE Photon. Technol. Lett. 23(22), 1670–1672 (2011). [CrossRef]

5.

Q. Wang, Z. Ouyang, and Q. Liu, “Multiport photonic crystal circulators created by cascading magneto-optical cavities,” J. Opt. Soc. Am. B 28(4), 703–708 (2011). [CrossRef]

6.

K. Yayoi, K. Tobinaga, Y. Kaneko, A. V. Baryshev, and M. Inoue, “Optical waveguide circulators based on two-dimensional magnetophotonic crystals: Numerical simulation for structure simplification and experimental verification,” J. Appl. Phys. 109(7), 07B750 (2011). [CrossRef]

7.

T. Goto, R. Isogai, and M. Inoue, “Para-magneto- and electro-optic microcavities for blue wavelength modulation,” Opt. Express 21(17), 19648–19656 (2013). [CrossRef] [PubMed]

8.

J. W. Pritchard, M. Mina, and R. J. Weber, “Improved switching for magneto-optic fiber-based technologies,” IEEE Trans. Magn. 48(11), 3772–3775 (2012). [CrossRef]

9.

Y. Arakawa, T. Nakamura, Y. Urino, and T. Fujita, “Silicon photonics for next generation system integration platform,” IEEE Commun. Mag. 51(3), 72–77 (2013). [CrossRef]

10.

M. Gomi, H. Furuyama, and M. Abe, “Strong magneto-optical enhancement in highly Ce-substituted iron garnet films prepared by sputtering,” J. Appl. Phys. 70(11), 7065 (1991). [CrossRef]

11.

B. Stadler, K. Vaccaro, P. Yip, J. Lorenzo, L. Yi-Qun, and M. Cherif, “Integration of magneto-optical garnet films by metal-organic chemical vapor deposition,” IEEE Trans. Magn. 38(3), 1564–1567 (2002). [CrossRef]

12.

T. Shintaku, A. Tate, and S. Mino, “Ce-substituted yttrium iron garnet films prepared on Gd3Sc2Ga3O12 garnet substrates by sputter epitaxy,” Appl. Phys. Lett. 71(12), 1640–1642 (1997). [CrossRef]

13.

T. Goto, M. C. Onbaşlı, and C. A. Ross, “Magneto-optical properties of cerium substituted yttrium iron garnet films with reduced thermal budget for monolithic photonic integrated circuits,” Opt. Express 20(27), 28507–28517 (2012). [CrossRef] [PubMed]

14.

T. Goto, Y. Eto, K. Kobayashi, Y. Haga, M. Inoue, and C. A. Ross, “Vacuum annealed cerium-substituted yttrium iron garnet films on non-garnet substrates for integrated optical circuits,” J. Appl. Phys. 113(17), 17A939 (2013). [CrossRef]

15.

K. Sato, Hikari-to-jiki (Asakura-shoten, Tokyo, 2007).

16.

B. Stadler and A. Gopinath, “Magneto-optical garnet films made by reactive sputtering,” IEEE Trans. Magn. 36(6), 3957–3961 (2000). [CrossRef]

17.

S. Mino, A. Tate, T. Uno, T. Shintaku, and A. Shibukawa, “Properties of Ce-substituted yttrium iron garnet film containing indium prepared by RF-sputtering,” Jpn. J. Appl. Phys. 32(Part 2, No. 7B), L994–L996 (1993). [CrossRef]

OCIS Codes
(160.3820) Materials : Magneto-optical materials
(230.3240) Optical devices : Isolators

ToC Category:
Integrated Optics

History
Original Manuscript: June 23, 2014
Revised Manuscript: July 21, 2014
Manuscript Accepted: July 22, 2014
Published: July 29, 2014

Citation
Taichi Goto, Mehmet C. Onbasli, Dong Hun Kim, Vivek Singh, M. Inoue, Lionel C. Kimerling, and C. A. Ross, "A nonreciprocal racetrack resonator based on vacuum-annealed magnetooptical cerium-substituted yttrium iron garnet," Opt. Express 22, 19047-19054 (2014)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-22-16-19047


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. L. Bi, J. Hu, P. Jiang, D. H. Kim, G. F. Dionne, L. C. Kimerling, and C. A. Ross, “On-chip optical isolation in monolithically integrated non-reciprocal optical resonators,” Nat. Photonics5(12), 758–762 (2011). [CrossRef]
  2. S. Ghosh, S. Keyvaninia, Y. Shirato, T. Mizumoto, G. Roelkens, and R. Baets, “Optical isolator for TE polarized light realized by adhesive bonding of Ce:YIG on Silicon-on-Insulator waveguide circuits,” IEEE Photon. J.5(3), 6601108 (2013). [CrossRef]
  3. S. Ghosh, S. Keyvavinia, W. Van Roy, T. Mizumoto, G. Roelkens, and R. Baets, “Ce:YIG/Silicon-on-Insulator waveguide optical isolator realized by adhesive bonding,” Opt. Express20(2), 1839–1848 (2012). [CrossRef] [PubMed]
  4. P. Pintus, T. Ming-Chun, and J. E. Bowers, “Design of magneto-optical ring isolator on SOI based on the finite-element method,” IEEE Photon. Technol. Lett.23(22), 1670–1672 (2011). [CrossRef]
  5. Q. Wang, Z. Ouyang, and Q. Liu, “Multiport photonic crystal circulators created by cascading magneto-optical cavities,” J. Opt. Soc. Am. B28(4), 703–708 (2011). [CrossRef]
  6. K. Yayoi, K. Tobinaga, Y. Kaneko, A. V. Baryshev, and M. Inoue, “Optical waveguide circulators based on two-dimensional magnetophotonic crystals: Numerical simulation for structure simplification and experimental verification,” J. Appl. Phys.109(7), 07B750 (2011). [CrossRef]
  7. T. Goto, R. Isogai, and M. Inoue, “Para-magneto- and electro-optic microcavities for blue wavelength modulation,” Opt. Express21(17), 19648–19656 (2013). [CrossRef] [PubMed]
  8. J. W. Pritchard, M. Mina, and R. J. Weber, “Improved switching for magneto-optic fiber-based technologies,” IEEE Trans. Magn.48(11), 3772–3775 (2012). [CrossRef]
  9. Y. Arakawa, T. Nakamura, Y. Urino, and T. Fujita, “Silicon photonics for next generation system integration platform,” IEEE Commun. Mag.51(3), 72–77 (2013). [CrossRef]
  10. M. Gomi, H. Furuyama, and M. Abe, “Strong magneto-optical enhancement in highly Ce-substituted iron garnet films prepared by sputtering,” J. Appl. Phys.70(11), 7065 (1991). [CrossRef]
  11. B. Stadler, K. Vaccaro, P. Yip, J. Lorenzo, L. Yi-Qun, and M. Cherif, “Integration of magneto-optical garnet films by metal-organic chemical vapor deposition,” IEEE Trans. Magn.38(3), 1564–1567 (2002). [CrossRef]
  12. T. Shintaku, A. Tate, and S. Mino, “Ce-substituted yttrium iron garnet films prepared on Gd3Sc2Ga3O12 garnet substrates by sputter epitaxy,” Appl. Phys. Lett.71(12), 1640–1642 (1997). [CrossRef]
  13. T. Goto, M. C. Onbaşlı, and C. A. Ross, “Magneto-optical properties of cerium substituted yttrium iron garnet films with reduced thermal budget for monolithic photonic integrated circuits,” Opt. Express20(27), 28507–28517 (2012). [CrossRef] [PubMed]
  14. T. Goto, Y. Eto, K. Kobayashi, Y. Haga, M. Inoue, and C. A. Ross, “Vacuum annealed cerium-substituted yttrium iron garnet films on non-garnet substrates for integrated optical circuits,” J. Appl. Phys.113(17), 17A939 (2013). [CrossRef]
  15. K. Sato, Hikari-to-jiki (Asakura-shoten, Tokyo, 2007).
  16. B. Stadler and A. Gopinath, “Magneto-optical garnet films made by reactive sputtering,” IEEE Trans. Magn.36(6), 3957–3961 (2000). [CrossRef]
  17. S. Mino, A. Tate, T. Uno, T. Shintaku, and A. Shibukawa, “Properties of Ce-substituted yttrium iron garnet film containing indium prepared by RF-sputtering,” Jpn. J. Appl. Phys.32(Part 2, No. 7B), L994–L996 (1993). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited