Waveguide-integrated microdisk light-emitting diode and photodetector based on Ge quantum dots

Xuejun Xu, Takuya Maruizumi, and Yasuhiro Shiraki  »View Author Affiliations


Optics Express, Vol. 22, Issue 4, pp. 3902-3910 (2014)
http://dx.doi.org/10.1364/OE.22.003902


View Full Text Article

Acrobat PDF (1539 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

Microdisk integrated with a bus waveguide is fabricated on silicon-on-insulator substrate containing Ge self-assembled quantum dots as active medium. The device is demonstrated to be operated as both light-emitting diode and photodetector. At forward bias, carriers are injected into the microdisk and light emission at 1.45–1.6 μm is extracted through the waveguide via microdisk-waveguide coupling. Sharp resonant peaks with Q-factor as high as 1350 are obtained in the electroluminescence spectra, corresponding to whispering gallery modes of the microdisk. At reverse bias, the device functions as a resonant cavity enhanced photodetector with wavelength-selective photo-response. The photo-current at resonant wavelength of 1533.65 nm is 50 times larger than that at non-resonant wavelength. The dark current density of the photodetector is as low as 0.29 mA/cm2 up to −10 V bias and the peak responsivity is 5.645 mA/W.

© 2014 Optical Society of America

1. Introduction

Due to its indirect band gap property, silicon (Si) is thought to be a less efficient material for active photonic devices such as light sources and photodetectors. This has been the last obstacle for complementary metal-oxide-semiconductor (CMOS) monolithic Si-based photonic integrated circuits [1

1. R. Soref, “The past, present, and future of silicon photonics,” IEEE J. Sel. Top. Quantum Electron. 12, 1678–1687 (2006). [CrossRef]

, 2

2. M. Haurylau, G. Chen, H. Chen, J. Zhang, N. A. Nelson, D. H. Albonesi, E. G. Friedman, and P. M. Fauchet, “On-chip optical interconnect roadmap: challenges and critical directions,” IEEE J. Sel. Top. Quantum Electron. 12, 1699–1705 (2006). [CrossRef]

]. Recently, germanium (Ge), which is also a group-IV semiconductor, has attracted great attention as an optical material due to its light emission and absorption wavelength in the telecommunication band and CMOS process compatibility with Si. Although Ge is also with indirect band gap, its light emission efficiency can be enhanced by material engineering. By applying tensile strain and n-type doping on Ge, the small difference between its direct and indirect conduction band valleys can be reduced and it is potential to convert Ge into a quasi-direct band gap material [3

3. J. Liu, X. Sun, D. Pan, X. Wang, L. C. Kimerling, T. L. Koch, and J. Michel, “Tensile-strained, n-type Ge as a gain medium for monolithic laser integration on Si,” Opt. Express 15, 11272–11277 (2007). [CrossRef] [PubMed]

]. Direct gap photoluminescence (PL) [4

4. X. Sun, J. Liu, L. C. Kimerling, and J. Michel, “Direct gap photoluminescence of n-type tensile-strained Ge-on-Si,” Appl. Phys. Lett. 95, 011911 (2009). [CrossRef]

], electroluminescence (EL) [5

5. X. Sun, J. Liu, L. C. Kimerling, and J. Michel, “Room-temperature direct bandgap electroluminesence from Ge-on-Si light-emitting diodes,” Opt. Lett. 34, 1198–1200 (2009). [CrossRef] [PubMed]

, 6

6. S.-L. Cheng, J. Lu, G. Shambat, H.-Y. Yu, K. Saraswat, J. Vuckovic, and Y. Nishi, “Room temperature 1.6 μm electroluminescence from Ge light emitting diode on Si substrate,” Opt. Express 17, 10019–10024 (2009). [CrossRef] [PubMed]

], optical gain [7

7. J. Liu, X. Sun, L. C. Kimerling, and J. Michel, “Direct-gap optical gain of Ge on Si at room temperature,” Opt. Lett. 34, 1738–1740 (2009). [CrossRef] [PubMed]

], as well as pulsed lasing actions from Ge [8

8. J. Liu, X. Sun, R. Camacho-Aguilera, L. C. Kimerling, and J. Michel, “Ge-on-Si laser operating at room temperature,” Opt. Lett. 35, 679–681 (2010). [CrossRef] [PubMed]

, 9

9. R. E. Camacho-Aguilera, Y. Cai, N. Patel, J. T. Bessette, M. Romagnoli, L. C. Kimerling, and J. Michel, “An electrically pumped germanium laser,” Opt. Express 20, 11316–11320 (2012). [CrossRef] [PubMed]

] have been demonstrated through these methods.

Another efficient way is to use SiGe nanostructures, in which carriers can be locally confined [10

10. R. Apetz, L. Vescan, A. Hartmann, C. Dieker, and H. Luth, “Photoluminescence and electroluminescence of SiGe dots fabricated by island growth,” Appl. Phys. Lett. 66, 445–447 (1995). [CrossRef]

, 11

11. H. Sunamura, N. Usami, Y. Shiraki, and S. Fukatsu, “Island formation during growth of Ge on Si (100): A study using photoluminescence spectroscopy,” Appl. Phys. Lett. 66, 3024–3026 (1995). [CrossRef]

]. Self-assembled Ge quantum dots (QDs) can be easily grown on Si without defects through Stranski-Krastanov mode. Ge QDs have been demonstrated to emit light in the infrared at room-temperature [12

12. W.-H. Chang, A. T. Chou, W. Y. Chen, H. S. Chang, T. M. Hsu, Z. Pei, P. S. Chen, S. W. Lee, L. S. Lai, S. C. Lu, and M.-J. Tsai, “Room-temperature electroluminescence at 1.3 and 1.5 μm from Ge/Si self-assembled quantum dots,” Appl. Phys. Lett. 83, 2958–2960 (2003). [CrossRef]

]. By embedding them into optical microcavities, the spontaneous emission rate can be significantly enhanced due to the Purcell effect [13

13. E. Purcell, “Spontaneous emission probabilities at radio frequencies,” Phys. Rev. 69, 681 (1946).

, 14

14. J. Gerard, B. Sermage, B. Gayral, B. Legrand, E. Costard, and V. Thierry-Mieg, “Enhanced spontaneous emission by quantum boxes in a monolithic optical microcavity,” Phys. Rev. Lett. 81, 1110–1113 (1998). [CrossRef]

]. Strong PL and EL with sharp resonant peaks from photonic crystal cavities and microdisks with Ge QDs have been demonstrated recently [15

15. J. Xia, Y. Ikegami, Y. Shiraki, N. Usami, and Y. Nakata, “Strong resonant luminescence from Ge quantum dots in photonic crystal microcavity at room temperature,” Appl. Phys. Lett. 89, 201102 (2006). [CrossRef]

19

19. X. Xu, T. Tsuboi, T. Chiba, N. Usami, T. Maruizumi, and Y. Shiraki, “Silicon-based current-injected light emitting diodes with Ge self-assembled quantum dots embedded in photonic crystal nanocavities,” Opt. Express 20, 14714–14721 (2012). [CrossRef] [PubMed]

]. However, light emission in all of these devices was extracted from the top surface via free-space optics. In order for monolithic integration with other photonic devices, extracting the light emission from a coupled waveguide on chip is desirable [20

20. S. Koseki, B. Zhang, K. De Greve, and Y. Yamamoto, “Monolithic integration of quantum dot containing microdisk microcavities coupled to air-suspended waveguides,” Appl. Phys. Lett. 94, 051110 (2009). [CrossRef]

].

On the other hand, Ge is also an excellent platform for optical detection in the telecommunication band. Photodetectors based on bulk Ge films grown on Si have been realized with large responsivity and high speed [21

21. T. Yin, R. Cohen, M. M. Morse, G. Sarid, Y. Chetrit, D. Rubin, and M. J. Paniccia, “31 Ghz Ge n–i–p waveguide photodetectors on Silicon-on-Insulator substrate,” Opt. Express 15, 13965–13971 (2007). [CrossRef] [PubMed]

, 22

22. C. T. DeRose, D. C. Trotter, W. A. Zortman, A. L. Starbuck, M. Fisher, M. R. Watts, and P. S. Davids, “Ultra compact 45 GHz CMOS compatible Germanium waveguide photodiode with low dark current,” Opt. Express 19, 24897–24904 (2011). [CrossRef]

]. However, the dark currents of these devices are usually rather high due to the limited crystal quality of Ge. High quality Ge QDs are attractive materials for photodetectors with low dark current, but the absorption efficiency is rather low due to very small absorption volume [23

23. M. Elkurdi, P. Boucaud, S. Sauvage, O. Kermarrec, Y. Campidelli, D. Bensahel, G. Saint-Girons, and I. Sagnes, “Near-infrared waveguide photodetector with Ge/Si self-assembled quantum dots,” Appl. Phys. Lett. 80, 509–511 (2002). [CrossRef]

, 24

24. S. Tong, J. Liu, J. Wan, and K. L. Wang, “Normal-incidence Ge quantum-dot photodetectors at 1.5 μm based on Si substrate,” Appl. Phys. Lett. 80, 1189–1191 (2002). [CrossRef]

]. Optical microcavities are also efficient tools to enhance the absorption since light can be trapped in the cavities for a long time for efficient absorption [25

25. M. S. Unlu and S. Strite, “Resonant cavity enhanced photonic devices,” J. Appl. Phys. 78, 607–639 (1995). [CrossRef]

, 26

26. O. I. Dosunmu, D. D. Cannon, M. K. Emsley, L. C. Kimerling, and M. S. Unlu, “High-speed resonant cavity enhanced Ge photodetectors on reflecting Si substrates for 1550-nm operation,” IEEE Photon. Technol. Lett. 17, 175–177 (2005). [CrossRef]

]. Ge QDs resonant-cavity-enhanced photodetectors with enhanced absorption has been demonstrated with high reflectivity top and bottom dielectric stacking mirrors [27

27. C. Li, R. Mao, Y. Zuo, L. Zhao, W. Shi, L. Luo, B. Cheng, J. Yu, and Q. Wang, “1.55 μm Ge islands resonant-cavity-enhanced detector with high-reflectivity bottom mirror,” Appl. Phys. Lett. 85, 2697–2699 (2004). [CrossRef]

]. However, the responsivity is still very low due to the small absorption length limited by epitaxy growth. By using a waveguide configuration, the absorption length can be easily controlled via lithography and the responsivity is expected to be significantly increased [28

28. H. Chen, X. Luo, and A. W. Poon, “Cavity-enhanced photocurrent generation by 1.55 μm wavelengths linear absorption in a pin diode embedded silicon microring resonator,” Appl. Phys. Lett. 95, 171111 (2009). [CrossRef]

, 29

29. J. Doylend, P. Jessop, and A. Knights, “Silicon photonic resonator-enhanced defect-mediated photodiode for sub-bandgap detection,” Opt. Express 18, 14671–14678 (2010). [CrossRef] [PubMed]

].

In this paper, we report the fabrication and characterization of waveguide-coupled microdisk with Ge QDs. Microdisk is preferred since radiation from the cavity modes is mainly along in-plane directions and is easily coupled with the bus waveguides. A vertical PIN diode is integrated with the microdisk serving as electrical structure. Light-emitting diode (LED) and photodetector are demonstrated on the same device at forward and reverse biases, respectively.

2. Device structure and fabrication

Figure 1(a) shows the three-dimensional schematic diagram of the waveguide-integrated microdisk and Fig. 1(b) shows the cross-section view along the center of the microdisk. The bus waveguide is located adjacently to the microdisk so that light emission can be coupled out from the microdisk, or input light can be launched into the microdisk from the waveguide. A vertical PIN diode is fabricated on the the microdisk, with P+ doped region on the surrounding slab and N+ doped region on the top of the microdisk, to inject carriers into or extract carriers from the microdisk.

Fig. 1 (a) Three-dimensional schematic diagram of the waveguide-integrated microdisk. (b) Cross-section view of the device along the center of the microdisk. (c) SEM image of a fabricated device.

The device was fabricated as the following procedures: Three layers of Ge QDs were firstly grown on silicon-on-insulator (SOI) substrate with 160-nm-thick top Si layer and 2-μm-thick buried-oxide (BOX) layer by solid-source molecular beam epitaxy. The layer stack includes a 40-nm-thick Si buffer, three-layers of Ge QDs separated by two 20-nm-thick Si spacers, and a 200-nm-thick Si cap. The nominal Ge layer thickness is 10 mono-layers (about 1.4 nm). All the layers were grown at a nominal temperature of 700 °C. Atomic force microscope measurement of the test sample with only one layer of Ge QDs grown with the same condition shows that the typical base diameter of the dots is around 80–95 nm, the height is around 9.0–9.7 nm, and the overall dot density is around 9.5×109 cm−2. The total thickness of Si/Ge layers is about 470 nm. The as-grown samples show intense PL peak around 1.5 μm at room-temperature. The band gap energy corresponding to this peak wavelength is much larger than the indirect band gap of Ge, indicating that there is considerable Si/Ge intermixing under this high growth temperature. However, it’s difficult to determine the exact Ge composition due to the very thin Ge layers and few layer numbers. After material growth, selective ion implantations of As was performed to make the N+ doping region. Microdisk and bus waveguide patterns were then defined by electron-beam lithography (EBL) and dry etching. A thin slab of about 120-nm-thick was left for electrical path. Shallow-etched grating couplers on the input and output ports of the waveguide were also fabricated by EBL and dry etching, with a different etching depth. The grating couplers are used to convert the light propagated along the waveguide upward for easy measurement [30

30. D. Taillaert, W. Bogaerts, P. Bienstman, T. F. Krauss, P. Van Daele, I. Moerman, S. Verstuyft, K. De Mesel, and R. Baets, “An out-of-plane grating coupler for efficient butt-coupling between compact planar waveguides and single-mode fibers,” IEEE J. Quantum Electron. 38, 949–955 (2002). [CrossRef]

]. P+ doping region was then formed by selective ion implantation of BF2. The samples were then experienced a rapid thermal anneal at 750 °C for 10 seconds for dopant activation. After that, SiO2 film was deposited by plasma-enhanced chemical vapor deposition and VIA contact holes were fabricated by EBL and a combination of dry and wet etching of SiO2. At last, AlSi was thermally evaporated and lifted-off to form the electrodes. The scanning electron microscope (SEM) image of a typical fabricated device is shown in Fig. 1(c), with disk radius of 4 μm, bus waveguide width of 550 nm and gap width of 150 nm.

3. Experimental results and discussion

The current-voltage (I–V) curve of the fabricated device characterized by a semiconductor parameter analyzer is shown in Fig. 2. A typical diode characteristic is obtained with very low reverse current, which is a strong sign of excellent crystal quality of the Ge QDs. With these active layers in the device, carriers will be injected and radiative recombination will occur under forward bias. On the other hand, if there is light input, it will be absorbed by the Ge QDs and photo-current will be generated under reverse bias.

Fig. 2 I–V curve of the fabricated device.

3.1. Operation as light-emitting diode

Fig. 3 (a) EL spectra of the device detected from the grating coupler under different injected currents. The EL intensity was offset by 40 for clear view. (b) Lorentz fitting of the strongest peak near 1.53 μm in the EL spectrum under 2 mA injected current.

In order to confirm the coupling between microdisk and bus waveguide, optical transmission through the bus waveguide was also measured. Light from a tunable laser was launched into the waveguide through a single-mode fiber and grating coupler. The output light was extracted by the other grating coupler and directed into a powermeter. Figure 4(a) shows the comparison of the optical transmission and EL spectra under the same injected current of 2 mA. The non-flat background in the transmission spectrum is due to the non-uniform coupling efficiency of the grating couplers. Several resonant dips can be also seen in the spectrum, with the deeper and narrower ones corresponding to the stronger peaks in the EL spectrum and the shallower and broader ones corresponding to the weaker peaks. The peak positions in transmission and EL spectra agree very well, except that there is a 2–3 nm blue-shift of EL peaks compared with transmission dips. We have confirmed by launching the tunable laser directly into the EL measurement system that this difference was due to the different wavelength standard used in two measurement apparatuses. Provided that the grating coupler has a minimum coupling loss of 7.4 dB and the light emission is equally coupled to the two directions of the waveguide, the EL intensity in the waveguide is at least 10 times of those shown in Fig. 3(a). By fitting the resonant dips in the transmission spectrum, we obtained that the coupling efficiency at resonant wavelength of 1533 nm is about 36%. It can be further increased by decreasing the gaps between microdisk and bus waveguide, with the expense of reduction of the resonant Q-factor.

Fig. 4 (a) Comparison of optical transmission and EL spectra under 2 mA injected current. (b) Comparison of simulated resonant wavelengths of WGMs and experimental resonant wavelengths extracted from transmission spectrum without current injection. (c) and (d) are calculated electrical field intensity distributions for the TE0,46 and TE1,41 WGMs of the microdisk. The intensity plotted here is log10(|E|2/max{|E|2} + 10−2) so that one can easily see the leakage towards outside.

3.2. Operation as photodetector

The photo-response of the device was measured in a similar configuration with transmission measurement, except that the PIN diode was reversely biased and the photo-current was measured by a source-meter. Figure 5 shows the photo-current spectrum of the device with input laser power of 1 mW and bias of −10 V. As a comparison, the transmission spectrum is also shown. Sharp resonant peaks are again clearly observed in the current spectrum. The peak wavelengths agree well with those of resonances in the transmission spectrum, indicating that enhanced absorption occurs at resonances. At the peak wavelength of 1533.65 nm, the photo-current is enhanced by a factor > 50 compared with background current (off-resonance). This large wavelength selectivity makes the device very attractive for wavelength-division multiplexing optical receiver.

Fig. 5 Comparison of optical transmission and photo-current spectra at input laser power of 1 mW and bias of −10 V.

The I–V curves of the photodetector at the resonant wavelength of 1533.65 nm are shown in Fig. 6(a). In the case of no laser input, the dark current of the photodetector is as low as 0.15 nA even when the bias is up to −10 V. This corresponds to a dark current density of 0.29 mA/cm2, which is several orders lower than those of photodetectors based on bulk Ge film grown on Si [21

21. T. Yin, R. Cohen, M. M. Morse, G. Sarid, Y. Chetrit, D. Rubin, and M. J. Paniccia, “31 Ghz Ge n–i–p waveguide photodetectors on Silicon-on-Insulator substrate,” Opt. Express 15, 13965–13971 (2007). [CrossRef] [PubMed]

,22

22. C. T. DeRose, D. C. Trotter, W. A. Zortman, A. L. Starbuck, M. Fisher, M. R. Watts, and P. S. Davids, “Ultra compact 45 GHz CMOS compatible Germanium waveguide photodiode with low dark current,” Opt. Express 19, 24897–24904 (2011). [CrossRef]

]. The photo-current can be obviously seen when there is laser input. Figure 6(b) shows the photo-current at 1533.65 nm with different input laser power. The horizontal axis indicates the coupled optical power into microdisk, in which the coupling loss of grating couplers and propagation loss of the waveguide before and after the microdisk has been eliminated from the total input power. At low input power, the current increases linearly, but the slope decreases at high input power. This is because the resonant wavelength slightly red-shifts at high input power due to thermal-optic effect. The wavelength at which the photo-current was measured was no longer the resonant wavelength. The red-shift was confirmed by comparing the transmission spectra at different input laser power.

Fig. 6 (a) I–V curves of the photodetector at resonant wavelength of 1533.65 with and without laser input. (b) Photo-current at 1533.65 nm with different input laser power.

4. Conclusion

Acknowledgments

This work was partly supported by the MEXT-Supported Program for the Strategic Research Foundation at Private Universities (2009–2013), the Strategic Information and Communications R&D Promotion Programme (SCOPE) from MIC, Japan, and the Exchange Research Grant from Marubun Research Promotion Foundation.

References and links

1.

R. Soref, “The past, present, and future of silicon photonics,” IEEE J. Sel. Top. Quantum Electron. 12, 1678–1687 (2006). [CrossRef]

2.

M. Haurylau, G. Chen, H. Chen, J. Zhang, N. A. Nelson, D. H. Albonesi, E. G. Friedman, and P. M. Fauchet, “On-chip optical interconnect roadmap: challenges and critical directions,” IEEE J. Sel. Top. Quantum Electron. 12, 1699–1705 (2006). [CrossRef]

3.

J. Liu, X. Sun, D. Pan, X. Wang, L. C. Kimerling, T. L. Koch, and J. Michel, “Tensile-strained, n-type Ge as a gain medium for monolithic laser integration on Si,” Opt. Express 15, 11272–11277 (2007). [CrossRef] [PubMed]

4.

X. Sun, J. Liu, L. C. Kimerling, and J. Michel, “Direct gap photoluminescence of n-type tensile-strained Ge-on-Si,” Appl. Phys. Lett. 95, 011911 (2009). [CrossRef]

5.

X. Sun, J. Liu, L. C. Kimerling, and J. Michel, “Room-temperature direct bandgap electroluminesence from Ge-on-Si light-emitting diodes,” Opt. Lett. 34, 1198–1200 (2009). [CrossRef] [PubMed]

6.

S.-L. Cheng, J. Lu, G. Shambat, H.-Y. Yu, K. Saraswat, J. Vuckovic, and Y. Nishi, “Room temperature 1.6 μm electroluminescence from Ge light emitting diode on Si substrate,” Opt. Express 17, 10019–10024 (2009). [CrossRef] [PubMed]

7.

J. Liu, X. Sun, L. C. Kimerling, and J. Michel, “Direct-gap optical gain of Ge on Si at room temperature,” Opt. Lett. 34, 1738–1740 (2009). [CrossRef] [PubMed]

8.

J. Liu, X. Sun, R. Camacho-Aguilera, L. C. Kimerling, and J. Michel, “Ge-on-Si laser operating at room temperature,” Opt. Lett. 35, 679–681 (2010). [CrossRef] [PubMed]

9.

R. E. Camacho-Aguilera, Y. Cai, N. Patel, J. T. Bessette, M. Romagnoli, L. C. Kimerling, and J. Michel, “An electrically pumped germanium laser,” Opt. Express 20, 11316–11320 (2012). [CrossRef] [PubMed]

10.

R. Apetz, L. Vescan, A. Hartmann, C. Dieker, and H. Luth, “Photoluminescence and electroluminescence of SiGe dots fabricated by island growth,” Appl. Phys. Lett. 66, 445–447 (1995). [CrossRef]

11.

H. Sunamura, N. Usami, Y. Shiraki, and S. Fukatsu, “Island formation during growth of Ge on Si (100): A study using photoluminescence spectroscopy,” Appl. Phys. Lett. 66, 3024–3026 (1995). [CrossRef]

12.

W.-H. Chang, A. T. Chou, W. Y. Chen, H. S. Chang, T. M. Hsu, Z. Pei, P. S. Chen, S. W. Lee, L. S. Lai, S. C. Lu, and M.-J. Tsai, “Room-temperature electroluminescence at 1.3 and 1.5 μm from Ge/Si self-assembled quantum dots,” Appl. Phys. Lett. 83, 2958–2960 (2003). [CrossRef]

13.

E. Purcell, “Spontaneous emission probabilities at radio frequencies,” Phys. Rev. 69, 681 (1946).

14.

J. Gerard, B. Sermage, B. Gayral, B. Legrand, E. Costard, and V. Thierry-Mieg, “Enhanced spontaneous emission by quantum boxes in a monolithic optical microcavity,” Phys. Rev. Lett. 81, 1110–1113 (1998). [CrossRef]

15.

J. Xia, Y. Ikegami, Y. Shiraki, N. Usami, and Y. Nakata, “Strong resonant luminescence from Ge quantum dots in photonic crystal microcavity at room temperature,” Appl. Phys. Lett. 89, 201102 (2006). [CrossRef]

16.

M. El Kurdi, X. Checoury, S. David, T. Ngo, N. Zerounian, P. Boucaud, O. Kermarrec, Y. Campidelli, and D. Bensahel, “Quality factor of Si-based photonic crystal L3 nanocavities probed with an internal source,” Opt. Express 16, 8780–8791 (2008). [CrossRef] [PubMed]

17.

X. Xu, S. Narusawa, T. Chiba, T. Tsuboi, J. Xia, N. Usami, T. Maruizumi, and Y. Shiraki, “Silicon-based light emitting devices based on Ge self-assembled quantum dots embedded in optical cavities,” IEEE J. Sel. Top. Quantum Electron. 18, 1830–1838 (2012). [CrossRef]

18.

J. Xia, Y. Takeda, N. Usami, T. Maruizumi, and Y. Shiraki, “Room-temperature electroluminescence from Si microdisks with Ge quantum dots,” Opt. Express 18, 13945–13950 (2010). [CrossRef] [PubMed]

19.

X. Xu, T. Tsuboi, T. Chiba, N. Usami, T. Maruizumi, and Y. Shiraki, “Silicon-based current-injected light emitting diodes with Ge self-assembled quantum dots embedded in photonic crystal nanocavities,” Opt. Express 20, 14714–14721 (2012). [CrossRef] [PubMed]

20.

S. Koseki, B. Zhang, K. De Greve, and Y. Yamamoto, “Monolithic integration of quantum dot containing microdisk microcavities coupled to air-suspended waveguides,” Appl. Phys. Lett. 94, 051110 (2009). [CrossRef]

21.

T. Yin, R. Cohen, M. M. Morse, G. Sarid, Y. Chetrit, D. Rubin, and M. J. Paniccia, “31 Ghz Ge n–i–p waveguide photodetectors on Silicon-on-Insulator substrate,” Opt. Express 15, 13965–13971 (2007). [CrossRef] [PubMed]

22.

C. T. DeRose, D. C. Trotter, W. A. Zortman, A. L. Starbuck, M. Fisher, M. R. Watts, and P. S. Davids, “Ultra compact 45 GHz CMOS compatible Germanium waveguide photodiode with low dark current,” Opt. Express 19, 24897–24904 (2011). [CrossRef]

23.

M. Elkurdi, P. Boucaud, S. Sauvage, O. Kermarrec, Y. Campidelli, D. Bensahel, G. Saint-Girons, and I. Sagnes, “Near-infrared waveguide photodetector with Ge/Si self-assembled quantum dots,” Appl. Phys. Lett. 80, 509–511 (2002). [CrossRef]

24.

S. Tong, J. Liu, J. Wan, and K. L. Wang, “Normal-incidence Ge quantum-dot photodetectors at 1.5 μm based on Si substrate,” Appl. Phys. Lett. 80, 1189–1191 (2002). [CrossRef]

25.

M. S. Unlu and S. Strite, “Resonant cavity enhanced photonic devices,” J. Appl. Phys. 78, 607–639 (1995). [CrossRef]

26.

O. I. Dosunmu, D. D. Cannon, M. K. Emsley, L. C. Kimerling, and M. S. Unlu, “High-speed resonant cavity enhanced Ge photodetectors on reflecting Si substrates for 1550-nm operation,” IEEE Photon. Technol. Lett. 17, 175–177 (2005). [CrossRef]

27.

C. Li, R. Mao, Y. Zuo, L. Zhao, W. Shi, L. Luo, B. Cheng, J. Yu, and Q. Wang, “1.55 μm Ge islands resonant-cavity-enhanced detector with high-reflectivity bottom mirror,” Appl. Phys. Lett. 85, 2697–2699 (2004). [CrossRef]

28.

H. Chen, X. Luo, and A. W. Poon, “Cavity-enhanced photocurrent generation by 1.55 μm wavelengths linear absorption in a pin diode embedded silicon microring resonator,” Appl. Phys. Lett. 95, 171111 (2009). [CrossRef]

29.

J. Doylend, P. Jessop, and A. Knights, “Silicon photonic resonator-enhanced defect-mediated photodiode for sub-bandgap detection,” Opt. Express 18, 14671–14678 (2010). [CrossRef] [PubMed]

30.

D. Taillaert, W. Bogaerts, P. Bienstman, T. F. Krauss, P. Van Daele, I. Moerman, S. Verstuyft, K. De Mesel, and R. Baets, “An out-of-plane grating coupler for efficient butt-coupling between compact planar waveguides and single-mode fibers,” IEEE J. Quantum Electron. 38, 949–955 (2002). [CrossRef]

31.

M. Oxborrow, “Ex-house 2d finite-element simulation of the whispering-gallery modes of arbitrarily shaped axisymmetric electromagnetic resonators,” arXiv preprint quant-ph/0607156 (2006).

OCIS Codes
(130.3120) Integrated optics : Integrated optics devices
(230.3670) Optical devices : Light-emitting diodes
(230.5160) Optical devices : Photodetectors
(230.5590) Optical devices : Quantum-well, -wire and -dot devices
(140.3948) Lasers and laser optics : Microcavity devices

ToC Category:
Integrated Optics

History
Original Manuscript: November 8, 2013
Revised Manuscript: January 20, 2014
Manuscript Accepted: February 3, 2014
Published: February 12, 2014

Citation
Xuejun Xu, Takuya Maruizumi, and Yasuhiro Shiraki, "Waveguide-integrated microdisk light-emitting diode and photodetector based on Ge quantum dots," Opt. Express 22, 3902-3910 (2014)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-22-4-3902


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. R. Soref, “The past, present, and future of silicon photonics,” IEEE J. Sel. Top. Quantum Electron. 12, 1678–1687 (2006). [CrossRef]
  2. M. Haurylau, G. Chen, H. Chen, J. Zhang, N. A. Nelson, D. H. Albonesi, E. G. Friedman, P. M. Fauchet, “On-chip optical interconnect roadmap: challenges and critical directions,” IEEE J. Sel. Top. Quantum Electron. 12, 1699–1705 (2006). [CrossRef]
  3. J. Liu, X. Sun, D. Pan, X. Wang, L. C. Kimerling, T. L. Koch, J. Michel, “Tensile-strained, n-type Ge as a gain medium for monolithic laser integration on Si,” Opt. Express 15, 11272–11277 (2007). [CrossRef] [PubMed]
  4. X. Sun, J. Liu, L. C. Kimerling, J. Michel, “Direct gap photoluminescence of n-type tensile-strained Ge-on-Si,” Appl. Phys. Lett. 95, 011911 (2009). [CrossRef]
  5. X. Sun, J. Liu, L. C. Kimerling, J. Michel, “Room-temperature direct bandgap electroluminesence from Ge-on-Si light-emitting diodes,” Opt. Lett. 34, 1198–1200 (2009). [CrossRef] [PubMed]
  6. S.-L. Cheng, J. Lu, G. Shambat, H.-Y. Yu, K. Saraswat, J. Vuckovic, Y. Nishi, “Room temperature 1.6 μm electroluminescence from Ge light emitting diode on Si substrate,” Opt. Express 17, 10019–10024 (2009). [CrossRef] [PubMed]
  7. J. Liu, X. Sun, L. C. Kimerling, J. Michel, “Direct-gap optical gain of Ge on Si at room temperature,” Opt. Lett. 34, 1738–1740 (2009). [CrossRef] [PubMed]
  8. J. Liu, X. Sun, R. Camacho-Aguilera, L. C. Kimerling, J. Michel, “Ge-on-Si laser operating at room temperature,” Opt. Lett. 35, 679–681 (2010). [CrossRef] [PubMed]
  9. R. E. Camacho-Aguilera, Y. Cai, N. Patel, J. T. Bessette, M. Romagnoli, L. C. Kimerling, J. Michel, “An electrically pumped germanium laser,” Opt. Express 20, 11316–11320 (2012). [CrossRef] [PubMed]
  10. R. Apetz, L. Vescan, A. Hartmann, C. Dieker, H. Luth, “Photoluminescence and electroluminescence of SiGe dots fabricated by island growth,” Appl. Phys. Lett. 66, 445–447 (1995). [CrossRef]
  11. H. Sunamura, N. Usami, Y. Shiraki, S. Fukatsu, “Island formation during growth of Ge on Si (100): A study using photoluminescence spectroscopy,” Appl. Phys. Lett. 66, 3024–3026 (1995). [CrossRef]
  12. W.-H. Chang, A. T. Chou, W. Y. Chen, H. S. Chang, T. M. Hsu, Z. Pei, P. S. Chen, S. W. Lee, L. S. Lai, S. C. Lu, M.-J. Tsai, “Room-temperature electroluminescence at 1.3 and 1.5 μm from Ge/Si self-assembled quantum dots,” Appl. Phys. Lett. 83, 2958–2960 (2003). [CrossRef]
  13. E. Purcell, “Spontaneous emission probabilities at radio frequencies,” Phys. Rev. 69, 681 (1946).
  14. J. Gerard, B. Sermage, B. Gayral, B. Legrand, E. Costard, V. Thierry-Mieg, “Enhanced spontaneous emission by quantum boxes in a monolithic optical microcavity,” Phys. Rev. Lett. 81, 1110–1113 (1998). [CrossRef]
  15. J. Xia, Y. Ikegami, Y. Shiraki, N. Usami, Y. Nakata, “Strong resonant luminescence from Ge quantum dots in photonic crystal microcavity at room temperature,” Appl. Phys. Lett. 89, 201102 (2006). [CrossRef]
  16. M. El Kurdi, X. Checoury, S. David, T. Ngo, N. Zerounian, P. Boucaud, O. Kermarrec, Y. Campidelli, D. Bensahel, “Quality factor of Si-based photonic crystal L3 nanocavities probed with an internal source,” Opt. Express 16, 8780–8791 (2008). [CrossRef] [PubMed]
  17. X. Xu, S. Narusawa, T. Chiba, T. Tsuboi, J. Xia, N. Usami, T. Maruizumi, Y. Shiraki, “Silicon-based light emitting devices based on Ge self-assembled quantum dots embedded in optical cavities,” IEEE J. Sel. Top. Quantum Electron. 18, 1830–1838 (2012). [CrossRef]
  18. J. Xia, Y. Takeda, N. Usami, T. Maruizumi, Y. Shiraki, “Room-temperature electroluminescence from Si microdisks with Ge quantum dots,” Opt. Express 18, 13945–13950 (2010). [CrossRef] [PubMed]
  19. X. Xu, T. Tsuboi, T. Chiba, N. Usami, T. Maruizumi, Y. Shiraki, “Silicon-based current-injected light emitting diodes with Ge self-assembled quantum dots embedded in photonic crystal nanocavities,” Opt. Express 20, 14714–14721 (2012). [CrossRef] [PubMed]
  20. S. Koseki, B. Zhang, K. De Greve, Y. Yamamoto, “Monolithic integration of quantum dot containing microdisk microcavities coupled to air-suspended waveguides,” Appl. Phys. Lett. 94, 051110 (2009). [CrossRef]
  21. T. Yin, R. Cohen, M. M. Morse, G. Sarid, Y. Chetrit, D. Rubin, M. J. Paniccia, “31 Ghz Ge n–i–p waveguide photodetectors on Silicon-on-Insulator substrate,” Opt. Express 15, 13965–13971 (2007). [CrossRef] [PubMed]
  22. C. T. DeRose, D. C. Trotter, W. A. Zortman, A. L. Starbuck, M. Fisher, M. R. Watts, P. S. Davids, “Ultra compact 45 GHz CMOS compatible Germanium waveguide photodiode with low dark current,” Opt. Express 19, 24897–24904 (2011). [CrossRef]
  23. M. Elkurdi, P. Boucaud, S. Sauvage, O. Kermarrec, Y. Campidelli, D. Bensahel, G. Saint-Girons, I. Sagnes, “Near-infrared waveguide photodetector with Ge/Si self-assembled quantum dots,” Appl. Phys. Lett. 80, 509–511 (2002). [CrossRef]
  24. S. Tong, J. Liu, J. Wan, K. L. Wang, “Normal-incidence Ge quantum-dot photodetectors at 1.5 μm based on Si substrate,” Appl. Phys. Lett. 80, 1189–1191 (2002). [CrossRef]
  25. M. S. Unlu, S. Strite, “Resonant cavity enhanced photonic devices,” J. Appl. Phys. 78, 607–639 (1995). [CrossRef]
  26. O. I. Dosunmu, D. D. Cannon, M. K. Emsley, L. C. Kimerling, M. S. Unlu, “High-speed resonant cavity enhanced Ge photodetectors on reflecting Si substrates for 1550-nm operation,” IEEE Photon. Technol. Lett. 17, 175–177 (2005). [CrossRef]
  27. C. Li, R. Mao, Y. Zuo, L. Zhao, W. Shi, L. Luo, B. Cheng, J. Yu, Q. Wang, “1.55 μm Ge islands resonant-cavity-enhanced detector with high-reflectivity bottom mirror,” Appl. Phys. Lett. 85, 2697–2699 (2004). [CrossRef]
  28. H. Chen, X. Luo, A. W. Poon, “Cavity-enhanced photocurrent generation by 1.55 μm wavelengths linear absorption in a pin diode embedded silicon microring resonator,” Appl. Phys. Lett. 95, 171111 (2009). [CrossRef]
  29. J. Doylend, P. Jessop, A. Knights, “Silicon photonic resonator-enhanced defect-mediated photodiode for sub-bandgap detection,” Opt. Express 18, 14671–14678 (2010). [CrossRef] [PubMed]
  30. D. Taillaert, W. Bogaerts, P. Bienstman, T. F. Krauss, P. Van Daele, I. Moerman, S. Verstuyft, K. De Mesel, R. Baets, “An out-of-plane grating coupler for efficient butt-coupling between compact planar waveguides and single-mode fibers,” IEEE J. Quantum Electron. 38, 949–955 (2002). [CrossRef]
  31. M. Oxborrow, “Ex-house 2d finite-element simulation of the whispering-gallery modes of arbitrarily shaped axisymmetric electromagnetic resonators,” arXiv preprint quant-ph/0607156 (2006).

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited