Femtosecond pulse generation from a topological insulator mode-locked fiber laser

Hao Liu, Xu-Wu Zheng, Meng Liu, Nian Zhao, Ai-Ping Luo, Zhi-Chao Luo, Wen-Cheng Xu, Han Zhang, Chu-Jun Zhao, and Shuang-Chun Wen  »View Author Affiliations


Optics Express, Vol. 22, Issue 6, pp. 6868-6873 (2014)
http://dx.doi.org/10.1364/OE.22.006868


View Full Text Article

Acrobat PDF (1569 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

We reported on the generation of femtosecond pulse in a fiber ring laser by using a polyvinyl alcohol (PVA)-based topological insulator (TI), Bi2Se3 saturable absorber (SA). The PVA-TI composite has a low saturable optical intensity of 12 MW/cm2 and a modulation depth of ~3.9%. By incorporating the fabricated PVA-TISA into a fiber laser, mode-locking operation could be achieved at a low pump threshold of 25 mW. After an optimization of the cavity parameters, optical pulse with ~660 fs centered at 1557.5 nm wavelength had been generated. The experimental results demonstrate that the PVA could be an excellent host material for fabricating high-performance TISA, and also indicate that the filmy PVA-TISA is indeed a good candidate for ultrafast saturable absorption device.

© 2014 Optical Society of America

1. Introduction

Ultrashort pulses have received much attention due to the great significance in a variety of applications, such as optical communications, spectroscopy, biomedicine, and material processing [1

1. L. E. Nelson, D. J. Jones, K. Tamura, H. A. Haus, and E. P. Ippen, “Ultrashort-pulse fiber ring lasers,” Appl. Phys. B 65(2), 277–294 (1997). [CrossRef]

3

3. M. E. Fermann and I. Hartl, “Ultrafast fibre lasers,” Nat. Photonics 7(11), 868–874 (2013). [CrossRef]

]. As a simple and economic ultrashort pulse source, passively mode-locked fiber lasers have been extensively investigated in the past decade. To date, several passively mode-locked techniques, such as nonlinear polarization rotation (NPR) [4

4. F. Ö. Ilday, J. R. Buckley, W. G. Clark, and F. W. Wise, “Self-similar evolution of parabolic pulses in a laser,” Phys. Rev. Lett. 92(21), 213902 (2004). [CrossRef] [PubMed]

,5

5. D. Y. Tang and L. M. Zhao, “Generation of 47-fs pulses directly from an erbium-doped fiber laser,” Opt. Lett. 32(1), 41–43 (2007). [CrossRef] [PubMed]

], nonlinear amplifying loop mirror (NALM) [6

6. D. A. Chestnut and J. R. Taylor, “Wavelength-versatile subpicosecond pulsed lasers using Raman gain in figure-of-eight fiber geometries,” Opt. Lett. 30(22), 2982–2984 (2005). [CrossRef] [PubMed]

8

8. Z. C. Luo, Q. Y. Ning, H. L. Mo, H. Cui, J. Liu, L. J. Wu, A. P. Luo, and W. C. Xu, “Vector dissipative soliton resonance in a fiber laser,” Opt. Express 21(8), 10199–10204 (2013). [CrossRef] [PubMed]

], and real saturable absorber (SA) [9

9. O. Okhotnikov, A. Grudinin, and M. Pessa, “Ultra-fast fibre laser systems based on SESAM technology: new horizons and applications,” New J. Phys. 6, 177 (2004). [CrossRef]

16

16. Z. Q. Luo, Y. Z. Huang, J. Z. Wang, H. H. Cheng, Z. P. Cai, and C. C. Ye, “Multiwavelength dissipative-soliton generation in Yb-Fiber laser using graphene-deposited fiber-taper,” IEEE Photonics Technol. Lett. 24(17), 1539–1542 (2012). [CrossRef]

], were employed to achieve ultrashort pulses in fiber lasers. Among them, inserting a high performance material based SA into the laser cavity was allowing successful mode-locking to be achieved with free cavity designs compared with other two techniques. Therefore, several types of SAs had been demonstrated to achieve the passive mode-locking operation of fiber lasers. In recent years many researches had focused their attention on nanomaterial based SAs, which function as the rising candidates for ultrafast lasers due to their distinguished advantages in ultrafast recovery time, controllable modulation depth, and easy fabrication [11

11. S. Yamashita, “A tutorial on nonlinear photonic applications of carbon nanotube and graphene,” J. Lightwave Technol. 30(4), 427–447 (2012). [CrossRef]

16

16. Z. Q. Luo, Y. Z. Huang, J. Z. Wang, H. H. Cheng, Z. P. Cai, and C. C. Ye, “Multiwavelength dissipative-soliton generation in Yb-Fiber laser using graphene-deposited fiber-taper,” IEEE Photonics Technol. Lett. 24(17), 1539–1542 (2012). [CrossRef]

]. In particular, graphene, a type of Dirac nanomaterials, had been successfully demonstrated as a medium that allows for high performance ultrafast fiber lasers [13

13. H. Zhang, Q. L. Bao, D. Y. Tang, L. M. Zhao, and K. Loh, “Large energy soliton erbium-doped fiber laser with a graphene-polymer composite mode locker,” Appl. Phys. Lett. 95(14), 141103 (2009). [CrossRef]

16

16. Z. Q. Luo, Y. Z. Huang, J. Z. Wang, H. H. Cheng, Z. P. Cai, and C. C. Ye, “Multiwavelength dissipative-soliton generation in Yb-Fiber laser using graphene-deposited fiber-taper,” IEEE Photonics Technol. Lett. 24(17), 1539–1542 (2012). [CrossRef]

].

Recently, topological insulator (TI), another type of Dirac nanoscale materials, was also proposed to as SA device to obtain ultrashort pulses in fiber lasers. F. Bernard et al. have firstly presented the saturable absorption behavior of TIs around 1550 nm [17

17. F. Bernard, H. Zhang, S. P. Gorza, and P. Emplit, “Towards mode-locked fiber laser using topological insulators,” in Nonlinear Photonics, OSA Technical Digest (online) (Optical Society of America, 2012), paper NTh1A.5.

]. In the following, by inserting the TIs-based SA into the laser cavity, Zhao et al. further demonstrated the mode-locked picosecond pulses in fiber laser [18

18. C. J. Zhao, H. Zhang, X. Qi, Y. Chen, Z. T. Wang, S. C. Wen, and D. Y. Tang, “Ultra-short pulse generation by a topological insulator based saturable absorber,” Appl. Phys. Lett. 101(21), 211106 (2012). [CrossRef]

,19

19. C. J. Zhao, Y. H. Zou, Y. Chen, Z. T. Wang, S. B. Lu, H. Zhang, S. C. Wen, and D. Y. Tang, “Wavelength-tunable picosecond soliton fiber laser with Topological Insulator: Bi2Se3 as a mode locker,” Opt. Express 20(25), 27888–27895 (2012). [CrossRef] [PubMed]

]. Very recently, it was also shown that the TIs possess the saturable absorption around 1060 nm wavelength range, indicating that the TI is a material with broadband saturable absorption [20

20. H. Yu, H. Zhang, T. Wang, C. J. Zhao, B. Wang, S. C. Wen, H. J. Zhang, and J. Wang, “Topological insulator as an optical modulator for pulsed solid-state lasers,” Laser Photonics Rev. 7(6), L77–L83 (2013). [CrossRef]

,21

21. Z. Q. Luo, Y. Z. Huang, J. Weng, H. H. Cheng, Z. Q. Lin, B. Xu, Z. P. Cai, and H. Y. Xu, “1.06μm Q-switched ytterbium-doped fiber laser using few-layer topological insulator Bi2Se3 as a saturable absorber,” Opt. Express 21(24), 29516–29522 (2013). [CrossRef] [PubMed]

]. In addition, taking advantage of the large nonlinear refractive index of TI [22

22. S. B. Lu, C. J. Zhao, Y. H. Zou, S. Q. Chen, Y. Chen, Y. Li, H. Zhang, S. C. Wen, and D. Y. Tang, “Third order nonlinear optical property of Bi₂Se₃,” Opt. Express 21(2), 2072–2082 (2013). [CrossRef] [PubMed]

], we had obtained high repetition rate pulse with a microfiber-based TISA, demonstrating that the TIs could operate as both the high nonlinear photonic device and the SA in the laser system [23

23. Z. C. Luo, M. Liu, H. Liu, X. W. Zheng, A. P. Luo, C. J. Zhao, H. Zhang, S. C. Wen, and W. C. Xu, “2 GHz passively harmonic mode-locked fiber laser by a microfiber-based Topological Insulator saturable absorber,” Opt. Lett. 38(24), 5212–5215 (2013). [CrossRef] [PubMed]

]. However, all the mode-locked fiber lasers based on TISA delivered the pulse-trains with the durations of a few picoseconds while the femtosecond pulse have not yet been achieved. The limited pulse duration (picosecond regime) observed in previously reported TI mode-locked fiber lasers could be caused by the large anomalous cavity dispersion. Moreover, the TISAs reported before were fabricated by spraying TI on a quartz plate [18

18. C. J. Zhao, H. Zhang, X. Qi, Y. Chen, Z. T. Wang, S. C. Wen, and D. Y. Tang, “Ultra-short pulse generation by a topological insulator based saturable absorber,” Appl. Phys. Lett. 101(21), 211106 (2012). [CrossRef]

20

20. H. Yu, H. Zhang, T. Wang, C. J. Zhao, B. Wang, S. C. Wen, H. J. Zhang, and J. Wang, “Topological insulator as an optical modulator for pulsed solid-state lasers,” Laser Photonics Rev. 7(6), L77–L83 (2013). [CrossRef]

], and depositing it onto the fiber end facet [21

21. Z. Q. Luo, Y. Z. Huang, J. Weng, H. H. Cheng, Z. Q. Lin, B. Xu, Z. P. Cai, and H. Y. Xu, “1.06μm Q-switched ytterbium-doped fiber laser using few-layer topological insulator Bi2Se3 as a saturable absorber,” Opt. Express 21(24), 29516–29522 (2013). [CrossRef] [PubMed]

,24

24. J. Sotor, G. Sobon, W. Macherzynski, P. Paletko, K. Grodecki, and K. M. Abramski, “Mode-locking in Er-doped fiber laser based on mechanically exfoliated Sb2Te3 saturable absorber,” Opt. Mater. Express 4(1), 1–6 (2014). [CrossRef]

] or microfiber [23

23. Z. C. Luo, M. Liu, H. Liu, X. W. Zheng, A. P. Luo, C. J. Zhao, H. Zhang, S. C. Wen, and W. C. Xu, “2 GHz passively harmonic mode-locked fiber laser by a microfiber-based Topological Insulator saturable absorber,” Opt. Lett. 38(24), 5212–5215 (2013). [CrossRef] [PubMed]

]. In fact, for the purpose of flexibility, cost-effective and controllability, a filmy TISA composited by polyvinyl alcohol (PVA) or polymethyl methacrylate (PMMA) would be more favorable. As we know, the pulse characteristics, such as duration and stability, could be affected by the fabrication method of the nanomaterial-based SA and the cavity dispersion [13

13. H. Zhang, Q. L. Bao, D. Y. Tang, L. M. Zhao, and K. Loh, “Large energy soliton erbium-doped fiber laser with a graphene-polymer composite mode locker,” Appl. Phys. Lett. 95(14), 141103 (2009). [CrossRef]

16

16. Z. Q. Luo, Y. Z. Huang, J. Z. Wang, H. H. Cheng, Z. P. Cai, and C. C. Ye, “Multiwavelength dissipative-soliton generation in Yb-Fiber laser using graphene-deposited fiber-taper,” IEEE Photonics Technol. Lett. 24(17), 1539–1542 (2012). [CrossRef]

]. Therefore, a question would arise as to whether the femtosecond pulse could be achieved by inserting a filmy TISA into a fiber laser.

In this work, we reported on the generation of femtosecond pulse from an anomalous-dispersion fiber ring laser by using a filmy TISA composited by the PVA. The measured Raman spectrum of the PVA-TISA shows that the TI: Bi2Se3 nano-sheets could maintain their structure when embedding into the PVA. The modulation depth and the saturable intensity are 3.9% and 12 MW/cm2, respectively. By inserting the PVA-TISA into a fiber laser, ~660 fs output pulse centered at 1557.5 nm wavelength could be obtained. These results suggest that the TISA could be indeed a good candidate of ultrafast saturable absorption device, and also demonstrate that the PVA could be the excellent host for fabricating high-performance TISA.

2. Fabrication and characteristics of the PVA-TISA

The TI: Bi2Se3 nanosheets could be synthesized by various methods such as chemical vapor transport, mechanical exfoliations by Scotch tape or peeling by an atomic force microscope tip, molecular beam epitaxial growth etc . Here, the polyol method was utilized to synthesize Bi2Se3 nanosheets [25

25. Y. Chen, C. J. Zhao, H. H. Huang, S. Q. Chen, P. H. Tang, Z. T. Wang, S. B. Lu, H. Zhang, S. C. Wen, and D. Y. Tang, “Self-assembled topological insulator: Bi2Se3 membrane as a passive Q-switcher in an Erbium-doped fiber laser,” J. Lightwave Technol. 31(17), 2857–2863 (2013). [CrossRef]

,26

26. J. Zhang, Z. P. Peng, A. Soni, Y. Y. Zhao, Y. Xiong, B. Peng, J. B. Wang, M. S. Dresselhaus, and Q. H. Xiong, “Raman spectroscopy of few-quintuple layer topological insulator Bi2Se3 nanoplatelets,” Nano Lett. 11(6), 2407–2414 (2011). [CrossRef] [PubMed]

]. The TI nanosheets for the SA fabrication are the same as those reported in Ref [22

22. S. B. Lu, C. J. Zhao, Y. H. Zou, S. Q. Chen, Y. Chen, Y. Li, H. Zhang, S. C. Wen, and D. Y. Tang, “Third order nonlinear optical property of Bi₂Se₃,” Opt. Express 21(2), 2072–2082 (2013). [CrossRef] [PubMed]

]. The dispersion enriched TI solution is prepared by ultra-sonicating Bi2Se3 nanosheets for 1 hour in acetone solution, as shown in Fig. 1(a).
Fig. 1 (a) Image of Bi2Se3 acetone solution; (b) Image of TI-PVA film; (c) Image of the fabricated fiber-compatible PVA-TISA.
The concentration of TI/acetone solution is ~0.1 mg/ml. Then 1 mL TI/acetone solution is mixed with 5 mL aqueous solution of polyvinyl alcohol (PVA) and ultrasonicated for 30 minutes. The mixture is then evaporated at room temperature on a slide glass, resulting in the formation of a filmy PVA-TI composite, as presented in Fig. 1(b). Finally the prepared PVA-TI composite is placed between two fiber connectors to form a fiber-compatible SA, as shown in Fig. 1(c).

In order to check that whether the TI Bi2Se3 nano-sheets could maintain their structures or not after it has been embedded into PVA, we performed the Raman spectrum analysis on the samples. Figure 2(a) compares the Raman spectra of the filmy PVA-TISA (blue curve) and pure PVA film (black curve) in the range of 0-1250 cm−1 using the 514 nm excitation line at room temperature by a Renishaw inVia micro-Raman system (Renishaw Inc., New Mills, UK).
Fig. 2 (a) Raman spectra of TI-PVA, inset: zoom-in view of the Raman peaks of Bi2Se3; (b) Measured nonlinear saturable absorption curve and corresponding fitting curve.
The spectrum of the TI-PVA composite, which shows the Raman peaks of both TI Bi2Se3 and PVA, can be seen as a superposition of PVA (black curve) and TI (red curve). Three typical Raman peaks of Bi2Se3 (Inset: Zoom-in view of the Raman peaks of Bi2Se3) centered at ~70 cm−1,~130 cm−1 and ~173 cm−1, were found in the Raman spectra of TI-PVA, which are correlated with the out-plane vibrational mode A1g1, in-plane vibrational mode Eg2 and the out-plane vibrational mode A1g2of Se-Bi-Se-Bi-Se lattice vibration, respectively [26

26. J. Zhang, Z. P. Peng, A. Soni, Y. Y. Zhao, Y. Xiong, B. Peng, J. B. Wang, M. S. Dresselhaus, and Q. H. Xiong, “Raman spectroscopy of few-quintuple layer topological insulator Bi2Se3 nanoplatelets,” Nano Lett. 11(6), 2407–2414 (2011). [CrossRef] [PubMed]

,27

27. K. M. F. Shahil, M. Z. Hossain, V. Goyal, and A. A. Balandin, “Micro-Raman spectroscopy of mechanically exfoliated few-quintuple layers of Bi2Te3, Bi2Se3, and Sb2Te3 materials,” J. Appl. Phys. 111(5), 054305 (2012). [CrossRef]

]. Therefore, one can conclude that Bi2Se3 nanosheets could still keep their structures even though they are embedded into PVA matrix, also indicating that the optical property of TI does not encounter significant change.

For further investigating nonlinear optical characteristics of the fabricated PVA-TISA, the nonlinear absorption of TISA was measured by the power-dependent transmission technique. The experimental setup is the same as that in Ref [23

23. Z. C. Luo, M. Liu, H. Liu, X. W. Zheng, A. P. Luo, C. J. Zhao, H. Zhang, S. C. Wen, and W. C. Xu, “2 GHz passively harmonic mode-locked fiber laser by a microfiber-based Topological Insulator saturable absorber,” Opt. Lett. 38(24), 5212–5215 (2013). [CrossRef] [PubMed]

]. In the setup of saturable absorption measurement, it should be noted that the pulse duration of the pump source broadens slightly from 502 fs to 513 fs after amplification. Figure 2(b) provides the saturable absorption data of PVA-TISA and the corresponding fitting curve as a function of peak intensity. As can be seen here, the modulation depth is ~3.9% and the non-saturable loss is ~67.5%. Note that the non-saturable loss is a bit large in this experiment. However, it was expected that the non-saturable loss could be improved by further optimizing the quality of the PVA-TISA film such as the thickness of film and the uniformity of TI within the composites. It should be also noted that the saturable intensity of the fabricated PVA-TISA is about two orders of magnitude less than the reported one (0.49 GW/cm2) by depositing the TI onto a onto a thick quartz plate [19

19. C. J. Zhao, Y. H. Zou, Y. Chen, Z. T. Wang, S. B. Lu, H. Zhang, S. C. Wen, and D. Y. Tang, “Wavelength-tunable picosecond soliton fiber laser with Topological Insulator: Bi2Se3 as a mode locker,” Opt. Express 20(25), 27888–27895 (2012). [CrossRef] [PubMed]

] and also smaller than the one (53 MW/cm2) deposited onto fiber end facet [21

21. Z. Q. Luo, Y. Z. Huang, J. Weng, H. H. Cheng, Z. Q. Lin, B. Xu, Z. P. Cai, and H. Y. Xu, “1.06μm Q-switched ytterbium-doped fiber laser using few-layer topological insulator Bi2Se3 as a saturable absorber,” Opt. Express 21(24), 29516–29522 (2013). [CrossRef] [PubMed]

]. With such a low saturable intensity, it would be predicted that the threshold of mode-locking using the as-prepared PVA-TISA can be significantly reduced.

3. Laser performance

To check the laser performance by using the prepared PVA-TISA, the PVA-TISA was inserted into a fiber ring laser cavity. Figure 3 shows the schematic of the proposed fiber laser.
Fig. 3 Schematic of mode-locked fiber laser with a PVA-TISA.
A 4 m EDF was used as the gain medium fiber. The group velocity dispersion (GVD) parameter of the EDF, which was calculated through the Kelly sidebands, was ~-15 ps/nm/km. The 976 nm pump light was coupled into the gain fiber by a wavelength division multiplexer (WDM). The polarization state of circulating light in the laser cavity could be controlled by adjusting a pair of polarization controllers (PCs). A polarization insensitive isolator (PI-ISO) was used to force the unidirectional operation of the laser cavity and a 10/90 coupler was used to output the laser emission. An optical spectrum analyzer (Anritsu MS9710C) and an oscilloscope (LeCroy Wave Runner 104MXi, 1 GHz) with a photodetector (New Focus P818-BB-35F, 12.5GHz) were used to study the laser spectrum and output pulse train, respectively. In addition, the pulse duration was measured with a commercial autocorrelator (FR-103XL).

Continuous wave operation started at a pump power of about 10 mW and the self-started mode-locking occurred at about 25 mW. For better performance of the fiber laser, the pump power was further increased to 90 mW. Figure 4(a) shows the typical spectrum of the mode-locked pulses at 90 mW.
Fig. 4 Mode-locked operation. (a) Mode locked spectrum; (b) Corresponding pulse-train; (c) Corresponding autocorrelation trace; Inset: autocorrelation trace with full range scan.
Here, the central wavelength and the 3 dB spectral bandwidth are 1557.5 nm and 4.3 nm, respectively. The evident Kelly sidebands on the spectrum indicate that the mode locked laser is operating in the soliton regime. Here, a cw peak centered at 1554.4 nm was shown on the mode-locked spectrum. It should be noted that the passive mode-locking state of the fiber laser could be also observed when the positions of the TISA placed onto fiber ferrule was moved. The corresponding pulse-train is presented in Fig. 4(b). The repetition rate is 12.5 MHz, which was determined by the 16.4 m cavity length. In this case, the average output power is 1.8 mW. Therefore, the pulse energy is 0.144 nJ. Then a commercial autocorrelator was employed to measure the pulse width. The measured result in Fig. 4(c) indicates that the fiber laser delivers a pulse-train with duration of 660 fs if the Sech2 intensity profile was assumed. Thus, the time-bandwidth product is about 0.351, which was slightly higher than 0.315, indicating that the mode-locked pulses are slightly chirped. Moreover, as can be seen in Fig. 4(c), there is small pedestal shown on the autocorrelation trace. It could be attributed to the imperfect alignments of the autocorrelator.

To verify whether the mode locking operation was stable, the RF spectrum (Advantest R3131A) of the mode-locked pulse was measured, as presented in Fig. 5(a).
Fig. 5 Stability of femtosecond pulses. (a) RF spectrum; (b) RF spectrum in 2 GHz span; (c) Long term optical spectra measured at a 2-h interval.
The fundamental peak locates at the fundamental repetition rate of 12.5 MHz with a signal-to-noise ratio of over 55 dB, indicating that the stable pulse operation was obtained in this case. The RF spectrum up to 2 GHz was shown in Fig. 5(b). The wideband RF spectrum is free of spectral modulation, suggesting that the fiber laser operates well in the cw mode-locking state. To further investigate the stability, we recorded the optical spectra of the mode-locked laser every 2-hour, as shown in Fig. 5(c). It should be noted that the central spectral peak locations, spectral bandwidth, spectral strength remained reasonably stable over the time period.

In the experiment, ~660 fs pulse could be obtained by employing the prepared PVA-TISA. It should be noted that, apart from the quality of the SA, the pulse duration could be also affected by the cavity dispersion. To investigate the influence of cavity dispersion on the pulse duration, a segment of 9.9 m long SMF was inserted into the laser cavity to increase the cavity dispersion to ~-0.4 ps2. The fiber laser was still mode locked with the same piece of PVA-TISA. In this case, only the picosecond pulse could be achieved despite of the variation of PC settings and pump power level. The results are shown in Fig. 6.
Fig. 6 Mode-locked operation when the cavity dispersion is increased to be ~-0.4 ps2. (a) Mode-locked spectrum; (b) Corresponding pulse-train; (c) Autocorrelation trace.
Here, the 3 dB bandwidth of mode-locked spectrum is 2 nm, as shown in Fig. 6(a). The pulse train is presented in Fig. 6(b), whose repetition rate is 7.78 MHz. The measured autocorrelation trace in Fig. 6(c) shows that the pulse duration is 1.45 ps. The comparative experiments demonstrated that the femtosecond pulse generation from our fiber laser could be attributed to the combination effect of PVA-TISA and cavity dispersion.

4. Conclusion

In summary, we have demonstrated a femtosecond pulse fiber laser mode-locked by a filmy TISA. The filmy TISA, which is composited by the PVA, shows a modulation depth of ~3.9% and a low saturable optical intensity of 12 MW/cm2. With the prepared PVA-TISA, the fiber laser delivers stable pulse-train with ~660 fs duration at the fundamental repetition rate of 12.5 MHz. Based on the experimental observations, it was expected that the PVA could be an excellent host material for fabricating high-performance TISA. The obtained results suggest that the PVA-TISA could be employed as a simple, low-cost ultrafast saturable absorption device for the applications such as mode-locked fiber lasers.

Acknowledgments

We would like to thank Yong-Fang Dong (South China Normal University) for help in measuring the Raman spectra. This work was supported in part by the National Natural Science Foundation of China (Grant No. 11074078, 61378036, 61307058, 11304101), and the PhD Start-up Fund of Natural Science Foundation of Guangdong Province, China (Grant No. S2013040016320).

References and links

1.

L. E. Nelson, D. J. Jones, K. Tamura, H. A. Haus, and E. P. Ippen, “Ultrashort-pulse fiber ring lasers,” Appl. Phys. B 65(2), 277–294 (1997). [CrossRef]

2.

U. Keller, “Recent developments in compact ultrafast lasers,” Nature 424(6950), 831–838 (2003). [CrossRef] [PubMed]

3.

M. E. Fermann and I. Hartl, “Ultrafast fibre lasers,” Nat. Photonics 7(11), 868–874 (2013). [CrossRef]

4.

F. Ö. Ilday, J. R. Buckley, W. G. Clark, and F. W. Wise, “Self-similar evolution of parabolic pulses in a laser,” Phys. Rev. Lett. 92(21), 213902 (2004). [CrossRef] [PubMed]

5.

D. Y. Tang and L. M. Zhao, “Generation of 47-fs pulses directly from an erbium-doped fiber laser,” Opt. Lett. 32(1), 41–43 (2007). [CrossRef] [PubMed]

6.

D. A. Chestnut and J. R. Taylor, “Wavelength-versatile subpicosecond pulsed lasers using Raman gain in figure-of-eight fiber geometries,” Opt. Lett. 30(22), 2982–2984 (2005). [CrossRef] [PubMed]

7.

J. W. Nicholson and M. Andrejco, “A polarization maintaining, dispersion managed, femtosecond figure-eight fiber laser,” Opt. Express 14(18), 8160–8167 (2006). [CrossRef] [PubMed]

8.

Z. C. Luo, Q. Y. Ning, H. L. Mo, H. Cui, J. Liu, L. J. Wu, A. P. Luo, and W. C. Xu, “Vector dissipative soliton resonance in a fiber laser,” Opt. Express 21(8), 10199–10204 (2013). [CrossRef] [PubMed]

9.

O. Okhotnikov, A. Grudinin, and M. Pessa, “Ultra-fast fibre laser systems based on SESAM technology: new horizons and applications,” New J. Phys. 6, 177 (2004). [CrossRef]

10.

A. Chong, W. H. Renninger, and F. W. Wise, “Environmentally stable all-normal-dispersion femtosecond fiber laser,” Opt. Lett. 33(10), 1071–1073 (2008). [CrossRef] [PubMed]

11.

S. Yamashita, “A tutorial on nonlinear photonic applications of carbon nanotube and graphene,” J. Lightwave Technol. 30(4), 427–447 (2012). [CrossRef]

12.

Y. D. Cui and X. M. Liu, “Graphene and nanotube mode-locked fiber laser emitting dissipative and conventional solitons,” Opt. Express 21(16), 18969–18974 (2013). [CrossRef] [PubMed]

13.

H. Zhang, Q. L. Bao, D. Y. Tang, L. M. Zhao, and K. Loh, “Large energy soliton erbium-doped fiber laser with a graphene-polymer composite mode locker,” Appl. Phys. Lett. 95(14), 141103 (2009). [CrossRef]

14.

Q. L. Bao, H. Zhang, J. X. Yang, S. Wang, D. Y. Tang, R. Jose, S. Ramakrishna, C. T. Lim, and K. P. Loh, “Graphene-polymer nanofiber membrane for ultrafast photonics,” Adv. Funct. Mater. 20(5), 782–791 (2010). [CrossRef]

15.

Z. Sun, T. Hasan, F. Torrisi, D. Popa, G. Privitera, F. Wang, F. Bonaccorso, D. M. Basko, and A. C. Ferrari, “Graphene mode-locked ultrafast laser,” ACS Nano 4(2), 803–810 (2010). [CrossRef] [PubMed]

16.

Z. Q. Luo, Y. Z. Huang, J. Z. Wang, H. H. Cheng, Z. P. Cai, and C. C. Ye, “Multiwavelength dissipative-soliton generation in Yb-Fiber laser using graphene-deposited fiber-taper,” IEEE Photonics Technol. Lett. 24(17), 1539–1542 (2012). [CrossRef]

17.

F. Bernard, H. Zhang, S. P. Gorza, and P. Emplit, “Towards mode-locked fiber laser using topological insulators,” in Nonlinear Photonics, OSA Technical Digest (online) (Optical Society of America, 2012), paper NTh1A.5.

18.

C. J. Zhao, H. Zhang, X. Qi, Y. Chen, Z. T. Wang, S. C. Wen, and D. Y. Tang, “Ultra-short pulse generation by a topological insulator based saturable absorber,” Appl. Phys. Lett. 101(21), 211106 (2012). [CrossRef]

19.

C. J. Zhao, Y. H. Zou, Y. Chen, Z. T. Wang, S. B. Lu, H. Zhang, S. C. Wen, and D. Y. Tang, “Wavelength-tunable picosecond soliton fiber laser with Topological Insulator: Bi2Se3 as a mode locker,” Opt. Express 20(25), 27888–27895 (2012). [CrossRef] [PubMed]

20.

H. Yu, H. Zhang, T. Wang, C. J. Zhao, B. Wang, S. C. Wen, H. J. Zhang, and J. Wang, “Topological insulator as an optical modulator for pulsed solid-state lasers,” Laser Photonics Rev. 7(6), L77–L83 (2013). [CrossRef]

21.

Z. Q. Luo, Y. Z. Huang, J. Weng, H. H. Cheng, Z. Q. Lin, B. Xu, Z. P. Cai, and H. Y. Xu, “1.06μm Q-switched ytterbium-doped fiber laser using few-layer topological insulator Bi2Se3 as a saturable absorber,” Opt. Express 21(24), 29516–29522 (2013). [CrossRef] [PubMed]

22.

S. B. Lu, C. J. Zhao, Y. H. Zou, S. Q. Chen, Y. Chen, Y. Li, H. Zhang, S. C. Wen, and D. Y. Tang, “Third order nonlinear optical property of Bi₂Se₃,” Opt. Express 21(2), 2072–2082 (2013). [CrossRef] [PubMed]

23.

Z. C. Luo, M. Liu, H. Liu, X. W. Zheng, A. P. Luo, C. J. Zhao, H. Zhang, S. C. Wen, and W. C. Xu, “2 GHz passively harmonic mode-locked fiber laser by a microfiber-based Topological Insulator saturable absorber,” Opt. Lett. 38(24), 5212–5215 (2013). [CrossRef] [PubMed]

24.

J. Sotor, G. Sobon, W. Macherzynski, P. Paletko, K. Grodecki, and K. M. Abramski, “Mode-locking in Er-doped fiber laser based on mechanically exfoliated Sb2Te3 saturable absorber,” Opt. Mater. Express 4(1), 1–6 (2014). [CrossRef]

25.

Y. Chen, C. J. Zhao, H. H. Huang, S. Q. Chen, P. H. Tang, Z. T. Wang, S. B. Lu, H. Zhang, S. C. Wen, and D. Y. Tang, “Self-assembled topological insulator: Bi2Se3 membrane as a passive Q-switcher in an Erbium-doped fiber laser,” J. Lightwave Technol. 31(17), 2857–2863 (2013). [CrossRef]

26.

J. Zhang, Z. P. Peng, A. Soni, Y. Y. Zhao, Y. Xiong, B. Peng, J. B. Wang, M. S. Dresselhaus, and Q. H. Xiong, “Raman spectroscopy of few-quintuple layer topological insulator Bi2Se3 nanoplatelets,” Nano Lett. 11(6), 2407–2414 (2011). [CrossRef] [PubMed]

27.

K. M. F. Shahil, M. Z. Hossain, V. Goyal, and A. A. Balandin, “Micro-Raman spectroscopy of mechanically exfoliated few-quintuple layers of Bi2Te3, Bi2Se3, and Sb2Te3 materials,” J. Appl. Phys. 111(5), 054305 (2012). [CrossRef]

OCIS Codes
(140.3510) Lasers and laser optics : Lasers, fiber
(140.4050) Lasers and laser optics : Mode-locked lasers
(160.4330) Materials : Nonlinear optical materials
(250.5530) Optoelectronics : Pulse propagation and temporal solitons

ToC Category:
Ultrafast Optics

History
Original Manuscript: January 28, 2014
Revised Manuscript: March 9, 2014
Manuscript Accepted: March 9, 2014
Published: March 17, 2014

Citation
Hao Liu, Xu-Wu Zheng, Meng Liu, Nian Zhao, Ai-Ping Luo, Zhi-Chao Luo, Wen-Cheng Xu, Han Zhang, Chu-Jun Zhao, and Shuang-Chun Wen, "Femtosecond pulse generation from a topological insulator mode-locked fiber laser," Opt. Express 22, 6868-6873 (2014)
http://www.opticsinfobase.org/oe/abstract.cfm?URI=oe-22-6-6868


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. L. E. Nelson, D. J. Jones, K. Tamura, H. A. Haus, E. P. Ippen, “Ultrashort-pulse fiber ring lasers,” Appl. Phys. B 65(2), 277–294 (1997). [CrossRef]
  2. U. Keller, “Recent developments in compact ultrafast lasers,” Nature 424(6950), 831–838 (2003). [CrossRef] [PubMed]
  3. M. E. Fermann, I. Hartl, “Ultrafast fibre lasers,” Nat. Photonics 7(11), 868–874 (2013). [CrossRef]
  4. F. Ö. Ilday, J. R. Buckley, W. G. Clark, F. W. Wise, “Self-similar evolution of parabolic pulses in a laser,” Phys. Rev. Lett. 92(21), 213902 (2004). [CrossRef] [PubMed]
  5. D. Y. Tang, L. M. Zhao, “Generation of 47-fs pulses directly from an erbium-doped fiber laser,” Opt. Lett. 32(1), 41–43 (2007). [CrossRef] [PubMed]
  6. D. A. Chestnut, J. R. Taylor, “Wavelength-versatile subpicosecond pulsed lasers using Raman gain in figure-of-eight fiber geometries,” Opt. Lett. 30(22), 2982–2984 (2005). [CrossRef] [PubMed]
  7. J. W. Nicholson, M. Andrejco, “A polarization maintaining, dispersion managed, femtosecond figure-eight fiber laser,” Opt. Express 14(18), 8160–8167 (2006). [CrossRef] [PubMed]
  8. Z. C. Luo, Q. Y. Ning, H. L. Mo, H. Cui, J. Liu, L. J. Wu, A. P. Luo, W. C. Xu, “Vector dissipative soliton resonance in a fiber laser,” Opt. Express 21(8), 10199–10204 (2013). [CrossRef] [PubMed]
  9. O. Okhotnikov, A. Grudinin, M. Pessa, “Ultra-fast fibre laser systems based on SESAM technology: new horizons and applications,” New J. Phys. 6, 177 (2004). [CrossRef]
  10. A. Chong, W. H. Renninger, F. W. Wise, “Environmentally stable all-normal-dispersion femtosecond fiber laser,” Opt. Lett. 33(10), 1071–1073 (2008). [CrossRef] [PubMed]
  11. S. Yamashita, “A tutorial on nonlinear photonic applications of carbon nanotube and graphene,” J. Lightwave Technol. 30(4), 427–447 (2012). [CrossRef]
  12. Y. D. Cui, X. M. Liu, “Graphene and nanotube mode-locked fiber laser emitting dissipative and conventional solitons,” Opt. Express 21(16), 18969–18974 (2013). [CrossRef] [PubMed]
  13. H. Zhang, Q. L. Bao, D. Y. Tang, L. M. Zhao, K. Loh, “Large energy soliton erbium-doped fiber laser with a graphene-polymer composite mode locker,” Appl. Phys. Lett. 95(14), 141103 (2009). [CrossRef]
  14. Q. L. Bao, H. Zhang, J. X. Yang, S. Wang, D. Y. Tang, R. Jose, S. Ramakrishna, C. T. Lim, K. P. Loh, “Graphene-polymer nanofiber membrane for ultrafast photonics,” Adv. Funct. Mater. 20(5), 782–791 (2010). [CrossRef]
  15. Z. Sun, T. Hasan, F. Torrisi, D. Popa, G. Privitera, F. Wang, F. Bonaccorso, D. M. Basko, A. C. Ferrari, “Graphene mode-locked ultrafast laser,” ACS Nano 4(2), 803–810 (2010). [CrossRef] [PubMed]
  16. Z. Q. Luo, Y. Z. Huang, J. Z. Wang, H. H. Cheng, Z. P. Cai, C. C. Ye, “Multiwavelength dissipative-soliton generation in Yb-Fiber laser using graphene-deposited fiber-taper,” IEEE Photonics Technol. Lett. 24(17), 1539–1542 (2012). [CrossRef]
  17. F. Bernard, H. Zhang, S. P. Gorza, and P. Emplit, “Towards mode-locked fiber laser using topological insulators,” in Nonlinear Photonics, OSA Technical Digest (online) (Optical Society of America, 2012), paper NTh1A.5.
  18. C. J. Zhao, H. Zhang, X. Qi, Y. Chen, Z. T. Wang, S. C. Wen, D. Y. Tang, “Ultra-short pulse generation by a topological insulator based saturable absorber,” Appl. Phys. Lett. 101(21), 211106 (2012). [CrossRef]
  19. C. J. Zhao, Y. H. Zou, Y. Chen, Z. T. Wang, S. B. Lu, H. Zhang, S. C. Wen, D. Y. Tang, “Wavelength-tunable picosecond soliton fiber laser with Topological Insulator: Bi2Se3 as a mode locker,” Opt. Express 20(25), 27888–27895 (2012). [CrossRef] [PubMed]
  20. H. Yu, H. Zhang, T. Wang, C. J. Zhao, B. Wang, S. C. Wen, H. J. Zhang, J. Wang, “Topological insulator as an optical modulator for pulsed solid-state lasers,” Laser Photonics Rev. 7(6), L77–L83 (2013). [CrossRef]
  21. Z. Q. Luo, Y. Z. Huang, J. Weng, H. H. Cheng, Z. Q. Lin, B. Xu, Z. P. Cai, H. Y. Xu, “1.06μm Q-switched ytterbium-doped fiber laser using few-layer topological insulator Bi2Se3 as a saturable absorber,” Opt. Express 21(24), 29516–29522 (2013). [CrossRef] [PubMed]
  22. S. B. Lu, C. J. Zhao, Y. H. Zou, S. Q. Chen, Y. Chen, Y. Li, H. Zhang, S. C. Wen, D. Y. Tang, “Third order nonlinear optical property of Bi₂Se₃,” Opt. Express 21(2), 2072–2082 (2013). [CrossRef] [PubMed]
  23. Z. C. Luo, M. Liu, H. Liu, X. W. Zheng, A. P. Luo, C. J. Zhao, H. Zhang, S. C. Wen, W. C. Xu, “2 GHz passively harmonic mode-locked fiber laser by a microfiber-based Topological Insulator saturable absorber,” Opt. Lett. 38(24), 5212–5215 (2013). [CrossRef] [PubMed]
  24. J. Sotor, G. Sobon, W. Macherzynski, P. Paletko, K. Grodecki, K. M. Abramski, “Mode-locking in Er-doped fiber laser based on mechanically exfoliated Sb2Te3 saturable absorber,” Opt. Mater. Express 4(1), 1–6 (2014). [CrossRef]
  25. Y. Chen, C. J. Zhao, H. H. Huang, S. Q. Chen, P. H. Tang, Z. T. Wang, S. B. Lu, H. Zhang, S. C. Wen, D. Y. Tang, “Self-assembled topological insulator: Bi2Se3 membrane as a passive Q-switcher in an Erbium-doped fiber laser,” J. Lightwave Technol. 31(17), 2857–2863 (2013). [CrossRef]
  26. J. Zhang, Z. P. Peng, A. Soni, Y. Y. Zhao, Y. Xiong, B. Peng, J. B. Wang, M. S. Dresselhaus, Q. H. Xiong, “Raman spectroscopy of few-quintuple layer topological insulator Bi2Se3 nanoplatelets,” Nano Lett. 11(6), 2407–2414 (2011). [CrossRef] [PubMed]
  27. K. M. F. Shahil, M. Z. Hossain, V. Goyal, A. A. Balandin, “Micro-Raman spectroscopy of mechanically exfoliated few-quintuple layers of Bi2Te3, Bi2Se3, and Sb2Te3 materials,” J. Appl. Phys. 111(5), 054305 (2012). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited