Substrate and aspect-ratio effects in resonant nanoaperture arrays

A. Roberts and L. Lin  »View Author Affiliations


Optical Materials Express, Vol. 1, Issue 3, pp. 480-488 (2011)
http://dx.doi.org/10.1364/OME.1.000480


View Full Text Article

Acrobat PDF (1590 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

Here we discuss the influence of a substrate on transmission through subwavelength holes in metallic films. In particular, we show that in the case of transmission maxima associated with localized resonances of the apertures, that the wavelength at which this maximum occurs are strongly influenced by the presence of a substrate and the aspect ratio of the structure. Furthermore, we show that removing a shallow region of the substrate immediately below the apertures leads to blue-shifting of the resonance and increased transmission compared to that in the presence of a homogeneous substrate.

© 2011 OSA

1. Introduction

Considerable interest in the transmission of light through subwavelength apertures in metallic films has persisted since unexpectedly high transmission was first seen in periodic arrangements of apertures [1

1. T. W. Ebbesen, H. J. Lezec, H. F. Ghaemi, T. Thio, and P. A. Wolff, “Extraordinary optical transmission through sub-wavelength hole arrays,” Nature 391(6668), 667–669 (1998). [CrossRef]

]. Applications utilizing this phenomenon have been demonstrated and envisaged in optical sensing [2

2. A. G. Brolo, R. Gordon, B. Leathem, and K. L. Kavanagh, “Surface plasmon sensor based on the enhanced light transmission through arrays of nanoholes in gold films,” Langmuir 20(12), 4813–4815 (2004). [CrossRef] [PubMed]

] novel compact filters [3

3. D. Van Labeke, D. Gérard, B. Guizal, F. I. Baida, and L. Li, “An angle-independent Frequency Selective Surface in the optical range,” Opt. Express 14(25), 11945–11951 (2006). [CrossRef] [PubMed]

] and in wavefront control devices [4

4. X. M. Goh, L. Lin, and A. Roberts, “Plasmonic lenses for wavefront control applications using two-dimensional nanometric cross-shaped aperture arrays,” J. Opt. Soc. Am. B 28(3), 547–553 (2011). [CrossRef]

6

6. L. Verslegers, P. B. Catrysse, Z. Yu, J. S. White, E. S. Barnard, M. L. Brongersma, and S. Fan, “Planar lenses based on nanoscale slit arrays in a metallic film,” Nano Lett. 9(1), 235–238 (2009). [CrossRef] [PubMed]

]. A large number of issues associated with these structures have been investigated: the arrangement of the apertures, the geometry of the holes and the nature of the illumination as well as the optical properties of the metal, the super- and substrate and the material within the apertures. Substrates are commonly used to lend robustness to a thin metallic film and provide support for isolated metallic elements. Furthermore, understanding the response of plasmonic systems to variations in the dielectric environment is central to the development of novel sensing applications [2

2. A. G. Brolo, R. Gordon, B. Leathem, and K. L. Kavanagh, “Surface plasmon sensor based on the enhanced light transmission through arrays of nanoholes in gold films,” Langmuir 20(12), 4813–4815 (2004). [CrossRef] [PubMed]

]. It is well-known that in the case of apertures in metallic films [2

2. A. G. Brolo, R. Gordon, B. Leathem, and K. L. Kavanagh, “Surface plasmon sensor based on the enhanced light transmission through arrays of nanoholes in gold films,” Langmuir 20(12), 4813–4815 (2004). [CrossRef] [PubMed]

,7

7. J. H. Kang, J.-H. Choe, D. S. Kim, and Q.-H. Park, “Substrate effect on aperture resonances in a thin metal film,” Opt. Express 17(18), 15652–15658 (2009). [CrossRef] [PubMed]

10

10. K. L. Shuford, S. K. Gray, M. A. Ratner, and G. C. Schatz, “Substrate effects on surface plasmons in single nanoholes,” Chem. Phys. Lett. 435(1-3), 123–126 (2007). [CrossRef]

] as well as metallic nanoparticles [11

11. K. C. Vernon, A. M. Funston, C. Novo, D. E. Gómez, P. Mulvaney, and T. J. Davis, “Influence of particle-substrate interaction on localized plasmon resonances,” Nano Lett. 10(6), 2080–2086 (2010). [CrossRef] [PubMed]

,12

12. S. Zhang, K. Bao, N. J. Halas, H. Xu, and P. Nordlander, “Substrate-induced Fano resonances of a plasmonic nanocube: a route to increased-sensitivity localized surface plasmon resonance sensors revealed,” Nano Lett. 11(4), 1657–1663 (2011). [CrossRef] [PubMed]

] that the presence and optical properties of a substrate can significantly modify the transmission from that in its absence. In the case of high transmission through structures where the dominant mechanism underlying high transmission relies on surface wave excitation [2

2. A. G. Brolo, R. Gordon, B. Leathem, and K. L. Kavanagh, “Surface plasmon sensor based on the enhanced light transmission through arrays of nanoholes in gold films,” Langmuir 20(12), 4813–4815 (2004). [CrossRef] [PubMed]

,8

8. A. Krishnan, T. Thio, T. J. Kim, H. J. Lezec, T. Ebbesen, P. A. Wolff, J. Pendry, L. Martin-Moreno, and F. J. Garcia-Vidal, “Evanescently coupled resonance in surface plasmon enhanced transmission,” Opt. Commun. 200(1-6), 1–7 (2001). [CrossRef]

,9

9. Y. Pang, C. Genet, and T. Ebbesen, “Optical transmission through subwavelength slit apertures in metallic films,” Opt. Commun. 280(1), 10–15 (2007). [CrossRef]

] the peak wavelength is red-shifted. This is apparent in the dispersion relation for the excitation of surface plasmon polaritons (SPPs) at a metal-dielectric interface. The case of high transmission emerging from the excitation of localized resonances within the apertures, however, is less clear [13

13. F. I. Baida, “Enhanced transmission through subwavelength metallic coaxial apertures by excitation of the TEM mode,” Appl. Phys. B 89(2-3), 145–149 (2007). [CrossRef]

21

21. A. Roberts, “Beam transmission through hole arrays,” Opt. Express 18(3), 2528–2533 (2010). [CrossRef] [PubMed]

] since fields that occur at resonance are tightly confined within the aperture and do not extend substantially into the substrate.

Here we investigate transmission through arrays of annular (or coaxial) apertures in metallic films (Fig. 1
Fig. 1 Schematic showing metal films periodically perforated with coaxial apertures: (a) Schematic showing the geometry of an aperture of outer radius a and inner radius b (b) Schematic showing a metallic film of thickness h perforated with a square array of apertures with periodicity d sitting on a dielectric substrate, and (c) a structure similar to that shown in (b) where the apertures extend into the substrate a distance t.
). In particular, we look at the role played by the refractive index and structure of the substrate and the thickness of the metal layer. The investigation of arrays of apertures with the distinct resonances seen in these structures has the potential to provide insight not only into the mechanisms underpinning changes in transmission in these particular structures introduced by a substrate, but may also inform the design of novel sensors and metamaterials. Furthermore, we show that selective removal of a thin layer of the substrate immediately below the apertures leads to a blue-shifting of the resonance compared with that in the presence of a homogeneous substrate.

2. Substrate effects in frequency selective surfaces, aperture arrays and metamaterials

Localized resonances within apertures in metal films (also known as Localized Surface Plasmon (LSP) resonances) are cavity Fabry-Perot resonances where the cavity is defined by the aperture walls and the upper and lower boundaries of the metal film. The location of each resonance is influenced by phase shifts at the ends of the cavity [22

22. D. Li and R. Gordon, “Electromagnetic transmission resonances for a single annular aperture in a metal plate,” Phys. Rev. A 82(4), 041801 (2010). [CrossRef]

]. By modifying the refractive index of the superstrate, the substrate or the material filling the apertures, this phase is modified leading to a shift in the resonant frequency and corresponding free-space wavelength. This phenomenon can also be considered as arising from changes in the capacitance of the structure [23

23. R. Ulrich, “Far-infrared properties of metallic mesh and its complementary structure,” Infrared Phys. 7(1), 37–55 (1967). [CrossRef]

]. Arrays of apertures with slot [7

7. J. H. Kang, J.-H. Choe, D. S. Kim, and Q.-H. Park, “Substrate effect on aperture resonances in a thin metal film,” Opt. Express 17(18), 15652–15658 (2009). [CrossRef] [PubMed]

,24

24. F. J. García-Vidal, L. Martin-Moreno, E. Moreno, L. K. S. Kumar, and R. Gordon, “Transmission of light through a single rectangular hole in a real metal,” Phys. Rev. B 74(15), 153411 (2006). [CrossRef]

], cross-shaped [20

20. L. Lin, L. B. Hande, and A. Roberts, “Resonant nanometric cross-shaped apertures: Single apertures versus periodic arrays,” Appl. Phys. Lett. 95(20), 201116 (2009). [CrossRef]

,25

25. K. D. Möller, J. B. Warren, J. B. Heaney, and C. Kotecki, “Cross-shaped bandpass filters for the near- and mid-infrared wavelength regions,” Appl. Opt. 35(31), 6210–6215 (1996). [CrossRef] [PubMed]

] or annular [13

13. F. I. Baida, “Enhanced transmission through subwavelength metallic coaxial apertures by excitation of the TEM mode,” Appl. Phys. B 89(2-3), 145–149 (2007). [CrossRef]

19

19. S. M. Orbons and A. Roberts, “Resonance and extraordinary transmission in annular aperture arrays,” Opt. Express 14(26), 12623–12628 (2006). [CrossRef] [PubMed]

] geometries with small gaps possess relatively high capacitances and distinct aperture resonances can be designed to be well-separated from any surface wave resonant excitations. When a dielectric substrate is introduced, the capacitance is increased producing a red-shift in the resonance.

The topic of the influence of a dielectric substrate on transmission through lossless inductive and capacitive grids [23

23. R. Ulrich, “Far-infrared properties of metallic mesh and its complementary structure,” Infrared Phys. 7(1), 37–55 (1967). [CrossRef]

], originally developed as frequency-selective surfaces, has been extensively investigated [26

26. R. C. Compton, L. B. Whitbourn, and R. C. McPhedran, “Strip gratings at a dielectric interface and applicaton of Babinet’s principle,” Appl. Opt. 23(18), 3236–3242 (1984). [CrossRef] [PubMed]

,27

27. L. B. Whitbourn and R. C. Compton, “Equivalent-circuit formulas for metal grid reflectors at a dielectric boundary,” Appl. Opt. 24(2), 217–220 (1985). [CrossRef] [PubMed]

]. By invoking a monomodal approximation and other arguments, the performance of inductive and capacitive grids can be described using an equivalent circuit model where, in the case of lossless media, the grid can be ascribed an effective capacitance, C0, and inductance, L0. It has been shown [26

26. R. C. Compton, L. B. Whitbourn, and R. C. McPhedran, “Strip gratings at a dielectric interface and applicaton of Babinet’s principle,” Appl. Opt. 23(18), 3236–3242 (1984). [CrossRef] [PubMed]

] that in the presence of a semi-infinit substrate with refractive index, n, the capacitance of an infinitesimally thin, perfectly conducting capacitive grid is given by:
Csub=C0(1+n22),
(1)
where C0 is the capacitance in the absence of the substrate. These leads to a shift in the resonant free-space wavelength, λres:
λres=λ01+n22,
(2)
where λ0 is the resonant wavelength when the mesh is surrounded by vacuum.

Resonances of metamaterials, have also been shown to be extremely sensitive to the presence of a substrate or dielectric overlayer [28

28. S. Y. Chiam, R. Singh, W. Zhang, and A. A. Bettiol, “Controlling metamaterial resonances via dielectric and aspect ratio effects,” Appl. Phys. Lett. 97(19), 191906 (2010). [CrossRef]

,29

29. J. F. O’Hara, R. Singh, I. Brener, E. Smirnova, J. Han, A. J. Taylor, and W. Zhang, “Thin-film sensing with planar terahertz metamaterials: sensitivity and limitations,” Opt. Express 16(3), 1786–1795 (2008). [CrossRef] [PubMed]

] and the thickness of the metal [28

28. S. Y. Chiam, R. Singh, W. Zhang, and A. A. Bettiol, “Controlling metamaterial resonances via dielectric and aspect ratio effects,” Appl. Phys. Lett. 97(19), 191906 (2010). [CrossRef]

,29

29. J. F. O’Hara, R. Singh, I. Brener, E. Smirnova, J. Han, A. J. Taylor, and W. Zhang, “Thin-film sensing with planar terahertz metamaterials: sensitivity and limitations,” Opt. Express 16(3), 1786–1795 (2008). [CrossRef] [PubMed]

]. In particular, it has been shown [28

28. S. Y. Chiam, R. Singh, W. Zhang, and A. A. Bettiol, “Controlling metamaterial resonances via dielectric and aspect ratio effects,” Appl. Phys. Lett. 97(19), 191906 (2010). [CrossRef]

,29

29. J. F. O’Hara, R. Singh, I. Brener, E. Smirnova, J. Han, A. J. Taylor, and W. Zhang, “Thin-film sensing with planar terahertz metamaterials: sensitivity and limitations,” Opt. Express 16(3), 1786–1795 (2008). [CrossRef] [PubMed]

] that increasing the thickness of a metamaterial leads to a shift in the resonant frequency and that this is accompanied by a decrease in sensitivity to the presence of a substrate [28

28. S. Y. Chiam, R. Singh, W. Zhang, and A. A. Bettiol, “Controlling metamaterial resonances via dielectric and aspect ratio effects,” Appl. Phys. Lett. 97(19), 191906 (2010). [CrossRef]

]. As in the case of frequency-selective surfaces, these effects can similarly be attributed to changes in the capacitance of the structure. The loss of sensitivity to the substrate would, therefore, be anticipated since by increasing the thickness of the structure, the contribution to its total capacitance by the substrate would be reduced.

3. Simulations and discussion

3.1. PEC - rigorous modal method

In Fig. 3
Fig. 3 The location of the maximum in transmission associated with the longest wavelength localized aperture resonance (a) as a function of substrate refractive index for two structures with films of thickness h = 0.10d and h = 0.40d and (b) as a function of film thickness for structures on substrates of refractive index n = 1 and n = 1.52. The periodicity of the array is d, the outer radius of the rings, a = 1.45d and the inner radius, b = 0.40d.The dashed line in (b) shows the cutoff wavelength for the TE11 coaxial waveguide mode.
, the position of λres for the geometries shown in Fig. 2 is plotted. In Fig. 3(a) the dependence on substrate index is shown for both thicknesses shown in Figs. 2(a) and 2(b) as well as that for h = 0.001d. The expected dependence given by Eq. (2) (i.e. that for h = 0) is also shown as a dashed line. It is apparent that the resonant wavelength increases monotonically with increasing substrate index and that its dependence on n approaches that given by Eq. (2) as h → 0. As discussed earlier in the context of metamaterials, the origins of this red-shift lie in the increased capacitance of the structure which leads to a decrease in the resonant frequency of the equivalent circuit and, hence, a red-shifting of the wavelength. As the thickness of the metal film increases, however, the sensitivity of λres to the substrate index decreases. This is expected since as the metal becomes thicker, the relative contribution to the total capacitance from the ends of the cavity would decrease.

Figure 3(b) shows that in the absence of the substrate (n = 1), the location of the maximum transmission shifts to longer wavelengths as the thickness, h, of the metal film increases, whereas if n = 1.52, the location shifts to shorter wavelengths. For very thick films, the resonance is expected to approach the cutoff wavelength of the TE11 coaxial waveguide mode (shown as a dashed line in the figure) which, for the parameters considered here, is 2.66d. In the case of films supported by a substrate, the resonant wavelength shifts to shorter wavelengths and approaches that of the free-standing film.

It is clear that the dependence of the resonant wavelength on the refractive index of the substrate and the thickness are consistent with those seen in [28

28. S. Y. Chiam, R. Singh, W. Zhang, and A. A. Bettiol, “Controlling metamaterial resonances via dielectric and aspect ratio effects,” Appl. Phys. Lett. 97(19), 191906 (2010). [CrossRef]

] for THz metamaterials and with analytic results for thin screens.

3.2. Silver films – finite element method

In order to accommodate the optical properties of a real metal in the visible and near-infrared regions of the electromagnetic spectrum, the transmission properties of the device were modeled using the Finite Element Method (FEM) implemented in COMSOL Multiphysics 4.1a. Floquet boundary conditions were used to simulate the periodicity of the array and perfectly matched layers (PML) were used at the upper and lower surfaces. Optical properties of Ag were taken from [30

30. P. B. Johnson and R. W. Christy, “Optical constants of the noble metals,” Phys. Rev. B 6(12), 4370–4379 (1972). [CrossRef]

] and the refractive index of the substrate (when included) was taken to be 1.52, to correspond to that of BK7 glass. The transmitted power was calculated by integrating the z-component of the Poynting flux over a plane below the metal film and above the PML. This was normalized to the same value calculated in the absence of the metal film and any substrate.

Consider now an array of apertures in a metallic film located on a substrate where the region in the substrate immediately below the apertures has been selectively removed to a depth of t (Fig. 1(c)). It is possible to produce this structure using focused ion beam (FIB) milling, for example, since the material could be removed during the same process through which the metal film is processed. It is anticipated that this structure would possess a lower capacitance and, hence, shorter resonant wavelength than that of a structure with a homogeneous substrate. Given that many applications of plasmonic devices lie in the visible or near-infrared, the ability to blue-tune the structure while maintaining the mechanical benefits of a substrate using a simple process compatible with other fabrication techniques is highly desirable. In particular, there are resonant structures of interest which are not self-supporting, for example the arrays of coaxial apertures investigated here, where the ability to maintain a substrate while decreasing the resonant wavelength is extremely useful.

The transmission spectra for different values of t in a substrate of index 1.52 for a structure in a Ag film of thickness 150 nm are shown in Fig. 6(a)
Fig. 6 Transmission through arrays of coaxial apertures in silver films of thickness 150 nm. The outer and inner radii of the apertures are 125 nm and 75 nm respectively. The films are supported by a substrate with refractive index of 1.52 where the substrate has been milled to different depths. Figure (a) shows the transmission spectra, while (b) shows the location of the transmission maximum for different milling depths, t. The horizontal black dashed line in (b) shows the value of the resonant wavelength of the corresponding free-standing film, while the blue dashed curve is an exponential fit to the data drawn to guide the eye.
, while the location of the transmission maximum in each case is shown in Fig. 6(b). It can be seen that the location of the resonance is extremely sensitive to the removal of even a small amount of the substrate and saturates once the depth of the structure in the substrate reaches approximately 50 nm. At this depth, the fields, protruding only a short distance below the structure, do not interact significantly with the substrate.

This is illustrated in Fig. 7
Fig. 7 The magnitude of the electric field at resonance around the metal film. The magnitude of the electric field, |E|, near a free-standing perforated Ag film at λ = 818 nm with parameters given in Fig. 5: (a) a transverse slice z = 0 through the centre of the Ag, (b) a meridional slice at y = 0, (c) |E| through the structure milled to a depth of 20 nm at λ = 841 nm and (d) shows |E| along the dotted line shown in (b) at a radius of (a + b)/2 as a function of distance below the lower surface of the Ag film in the absence (at 818 nm) and presence (at 879 nm) of a substrate and at 841 nm when the substrate has been milled to a depth of 20 nm.
where the magnitude of the electric field around these nanostructures at resonance is shown. The transverse field pattern is shown in Fig. 7(a), while the fields in meridional planes through the free-standing structure and the milled structure are shown in Figs. 7(b) and 7(c) respectively. The strong localization of the fields within the aperture and their limited extent into the region below the metal film are apparent. In Fig. 7(d), a plot of |E| at a distance (a + b)/2 from the centre of the aperture is plotted as a function of distance below the lower surface of the film. The plot line is indicated by the cross in Fig. 7(a) and the dashed line in Fig. 7(b). |E| is plotted for this structure in the presence and absence of the substrate and when the substrate has been modified. It is apparent that the field in each case decreases rapidly with distance from the lower surface of the metal with a characteristic 1/e distance of approximately 30-35 nm in each case. It is, therefore, not surprising that the resonant wavelength is extremely sensitive to milling depth. Overall, a shift in resonant wavelength of approximately 50 nm can be achieved by tailoring the substrate in this way. Furthermore, the structuring of the substrate improves the impedance match between the array and the substrate leading to higher transmission than that seen in the presence of a unpatterned semi-infinite substrate. It should also be pointed out that the corresponding shift in the location of the Rayleigh-Wood anomaly near 650 nm shifts by only approximately 15 nm as the substrate is modified.

4. Conclusion

We have shown that, in general, transmission through arrays of apertures where the dominant mechanism facilitating high transmission is the excitation of localized aperture resonances that both the substrate refractive index and the thickness of the metal film significantly influences the location and magnitude of the transmission maximum. The sensitivity of the transmission to the refractive index decreases as the film increases in thickness.

We have also shown that the influence of the substrate can be substantially moderated by selective removal of the substrate so that there is a coaxial gap in the substrate immediately below the film. The location of the resonant wavelength is sensitive to the removal of even small amounts of the substrate below the apertures. It is expected that since the resonances are a property of the apertures, rather than their arrangement, that the conclusions drawn here would also be true of an isolated aperture, or a random arrangement of apertures [18

18. S. M. Orbons, M. I. Haftel, C. Schlockermann, D. Freeman, M. Milicevic, T. J. Davis, B. Luther-Davies, D. N. Jamieson, and A. Roberts, “Dual resonance mechanisms facilitating enhanced optical transmission in coaxial waveguide arrays,” Opt. Lett. 33(8), 821–823 (2008). [CrossRef] [PubMed]

,33

33. J. Bravo-Abad, A. I. Fernández-Domínguez, F. J. García-Vidal, and L. Martín-Moreno, “Theory of extraordinary transmission of light through quasiperiodic arrays of subwavelength holes,” Phys. Rev. Lett. 99(20), 203905 (2007). [CrossRef] [PubMed]

]. In the examples presented here, the geometry of the apertures was specifically chosen so that the localized aperture resonance occurs at a wavelength longer than any strong Rayleigh-Wood or other surface wave excitations. If the apertures were smaller, or their geometries tuned to produce resonances at shorter wavelengths, the phenomena discussed here would still exist, but may be masked by order-dependent excitations. The research lays the foundation for the development of new three-dimensional plasmonic structures and metamaterials and suggests new strategies for tuning the electromagnetic response of these devices. It also has consequences for new strategies for sensing based on localized aperture resonances.

Acknowledgments

This research was supported under the Australian Research Council's Discovery Projects funding scheme (project number DP0878268). The authors would like to acknowledge useful conversations with Dr Tim Davis.

References and links

1.

T. W. Ebbesen, H. J. Lezec, H. F. Ghaemi, T. Thio, and P. A. Wolff, “Extraordinary optical transmission through sub-wavelength hole arrays,” Nature 391(6668), 667–669 (1998). [CrossRef]

2.

A. G. Brolo, R. Gordon, B. Leathem, and K. L. Kavanagh, “Surface plasmon sensor based on the enhanced light transmission through arrays of nanoholes in gold films,” Langmuir 20(12), 4813–4815 (2004). [CrossRef] [PubMed]

3.

D. Van Labeke, D. Gérard, B. Guizal, F. I. Baida, and L. Li, “An angle-independent Frequency Selective Surface in the optical range,” Opt. Express 14(25), 11945–11951 (2006). [CrossRef] [PubMed]

4.

X. M. Goh, L. Lin, and A. Roberts, “Plasmonic lenses for wavefront control applications using two-dimensional nanometric cross-shaped aperture arrays,” J. Opt. Soc. Am. B 28(3), 547–553 (2011). [CrossRef]

5.

L. Lin, X. M. Goh, L. P. McGuinness, and A. Roberts, “Plasmonic lenses formed by two-dimensional nanometric cross-shaped aperture arrays for Fresnel-region focusing,” Nano Lett. 10(5), 1936–1940 (2010). [CrossRef] [PubMed]

6.

L. Verslegers, P. B. Catrysse, Z. Yu, J. S. White, E. S. Barnard, M. L. Brongersma, and S. Fan, “Planar lenses based on nanoscale slit arrays in a metallic film,” Nano Lett. 9(1), 235–238 (2009). [CrossRef] [PubMed]

7.

J. H. Kang, J.-H. Choe, D. S. Kim, and Q.-H. Park, “Substrate effect on aperture resonances in a thin metal film,” Opt. Express 17(18), 15652–15658 (2009). [CrossRef] [PubMed]

8.

A. Krishnan, T. Thio, T. J. Kim, H. J. Lezec, T. Ebbesen, P. A. Wolff, J. Pendry, L. Martin-Moreno, and F. J. Garcia-Vidal, “Evanescently coupled resonance in surface plasmon enhanced transmission,” Opt. Commun. 200(1-6), 1–7 (2001). [CrossRef]

9.

Y. Pang, C. Genet, and T. Ebbesen, “Optical transmission through subwavelength slit apertures in metallic films,” Opt. Commun. 280(1), 10–15 (2007). [CrossRef]

10.

K. L. Shuford, S. K. Gray, M. A. Ratner, and G. C. Schatz, “Substrate effects on surface plasmons in single nanoholes,” Chem. Phys. Lett. 435(1-3), 123–126 (2007). [CrossRef]

11.

K. C. Vernon, A. M. Funston, C. Novo, D. E. Gómez, P. Mulvaney, and T. J. Davis, “Influence of particle-substrate interaction on localized plasmon resonances,” Nano Lett. 10(6), 2080–2086 (2010). [CrossRef] [PubMed]

12.

S. Zhang, K. Bao, N. J. Halas, H. Xu, and P. Nordlander, “Substrate-induced Fano resonances of a plasmonic nanocube: a route to increased-sensitivity localized surface plasmon resonance sensors revealed,” Nano Lett. 11(4), 1657–1663 (2011). [CrossRef] [PubMed]

13.

F. I. Baida, “Enhanced transmission through subwavelength metallic coaxial apertures by excitation of the TEM mode,” Appl. Phys. B 89(2-3), 145–149 (2007). [CrossRef]

14.

F. I. Baida and D. Van Labeke, “Light transmission by subwavelength annular aperture arrays in metallic films,” Opt. Commun. 209(1-3), 17–22 (2002). [CrossRef]

15.

F. I. Baida, D. Van Labeke, G. Granet, A. Moreau, and A. Belkhir, “Origin of the super-enhanced light transmission through a 2-D metallic annular aperture array: a study of photonic bands,” Appl. Phys. B 79(1), 1–8 (2004). [CrossRef]

16.

M. I. Haftel, C. Schlockermann, and G. Blumberg, “Role of cylindrical surface plasmons in enhanced transmission,” Appl. Phys. Lett. 88(19), 193104 (2006). [CrossRef]

17.

M. I. Haftel, C. Schlockermann, and G. Blumberg, “Enhanced transmission with coaxial nanoapertures: Role of cylindrical surface plasmons,” Phys. Rev. B 74(23), 235405 (2006). [CrossRef]

18.

S. M. Orbons, M. I. Haftel, C. Schlockermann, D. Freeman, M. Milicevic, T. J. Davis, B. Luther-Davies, D. N. Jamieson, and A. Roberts, “Dual resonance mechanisms facilitating enhanced optical transmission in coaxial waveguide arrays,” Opt. Lett. 33(8), 821–823 (2008). [CrossRef] [PubMed]

19.

S. M. Orbons and A. Roberts, “Resonance and extraordinary transmission in annular aperture arrays,” Opt. Express 14(26), 12623–12628 (2006). [CrossRef] [PubMed]

20.

L. Lin, L. B. Hande, and A. Roberts, “Resonant nanometric cross-shaped apertures: Single apertures versus periodic arrays,” Appl. Phys. Lett. 95(20), 201116 (2009). [CrossRef]

21.

A. Roberts, “Beam transmission through hole arrays,” Opt. Express 18(3), 2528–2533 (2010). [CrossRef] [PubMed]

22.

D. Li and R. Gordon, “Electromagnetic transmission resonances for a single annular aperture in a metal plate,” Phys. Rev. A 82(4), 041801 (2010). [CrossRef]

23.

R. Ulrich, “Far-infrared properties of metallic mesh and its complementary structure,” Infrared Phys. 7(1), 37–55 (1967). [CrossRef]

24.

F. J. García-Vidal, L. Martin-Moreno, E. Moreno, L. K. S. Kumar, and R. Gordon, “Transmission of light through a single rectangular hole in a real metal,” Phys. Rev. B 74(15), 153411 (2006). [CrossRef]

25.

K. D. Möller, J. B. Warren, J. B. Heaney, and C. Kotecki, “Cross-shaped bandpass filters for the near- and mid-infrared wavelength regions,” Appl. Opt. 35(31), 6210–6215 (1996). [CrossRef] [PubMed]

26.

R. C. Compton, L. B. Whitbourn, and R. C. McPhedran, “Strip gratings at a dielectric interface and applicaton of Babinet’s principle,” Appl. Opt. 23(18), 3236–3242 (1984). [CrossRef] [PubMed]

27.

L. B. Whitbourn and R. C. Compton, “Equivalent-circuit formulas for metal grid reflectors at a dielectric boundary,” Appl. Opt. 24(2), 217–220 (1985). [CrossRef] [PubMed]

28.

S. Y. Chiam, R. Singh, W. Zhang, and A. A. Bettiol, “Controlling metamaterial resonances via dielectric and aspect ratio effects,” Appl. Phys. Lett. 97(19), 191906 (2010). [CrossRef]

29.

J. F. O’Hara, R. Singh, I. Brener, E. Smirnova, J. Han, A. J. Taylor, and W. Zhang, “Thin-film sensing with planar terahertz metamaterials: sensitivity and limitations,” Opt. Express 16(3), 1786–1795 (2008). [CrossRef] [PubMed]

30.

P. B. Johnson and R. W. Christy, “Optical constants of the noble metals,” Phys. Rev. B 6(12), 4370–4379 (1972). [CrossRef]

31.

A. Roberts and R. C. McPhedran, “Bandpass grids with annular apertures,” IEEE Trans. Antenn. Propag. 36(5), 607–611 (1988). [CrossRef]

32.

M. J. Lockyear, A. P. Hibbins, J. R. Sambles, and C. R. Lawrence, “Enhanced microwave transmission through a single subwavelength aperture surrounded by concentric grooves,” J. Opt. A, Pure Appl. Opt. 7(2), S152–S158 (2005). [CrossRef]

33.

J. Bravo-Abad, A. I. Fernández-Domínguez, F. J. García-Vidal, and L. Martín-Moreno, “Theory of extraordinary transmission of light through quasiperiodic arrays of subwavelength holes,” Phys. Rev. Lett. 99(20), 203905 (2007). [CrossRef] [PubMed]

OCIS Codes
(050.1220) Diffraction and gratings : Apertures
(160.3918) Materials : Metamaterials
(160.4236) Materials : Nanomaterials
(250.5403) Optoelectronics : Plasmonics
(050.6624) Diffraction and gratings : Subwavelength structures

ToC Category:
Metamaterials

History
Original Manuscript: May 10, 2011
Revised Manuscript: June 23, 2011
Manuscript Accepted: June 23, 2011
Published: June 29, 2011

Citation
A. Roberts and L. Lin, "Substrate and aspect-ratio effects in resonant nanoaperture arrays," Opt. Mater. Express 1, 480-488 (2011)
http://www.opticsinfobase.org/ome/abstract.cfm?URI=ome-1-3-480


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. T. W. Ebbesen, H. J. Lezec, H. F. Ghaemi, T. Thio, and P. A. Wolff, “Extraordinary optical transmission through sub-wavelength hole arrays,” Nature 391(6668), 667–669 (1998). [CrossRef]
  2. A. G. Brolo, R. Gordon, B. Leathem, and K. L. Kavanagh, “Surface plasmon sensor based on the enhanced light transmission through arrays of nanoholes in gold films,” Langmuir 20(12), 4813–4815 (2004). [CrossRef] [PubMed]
  3. D. Van Labeke, D. Gérard, B. Guizal, F. I. Baida, and L. Li, “An angle-independent Frequency Selective Surface in the optical range,” Opt. Express 14(25), 11945–11951 (2006). [CrossRef] [PubMed]
  4. X. M. Goh, L. Lin, and A. Roberts, “Plasmonic lenses for wavefront control applications using two-dimensional nanometric cross-shaped aperture arrays,” J. Opt. Soc. Am. B 28(3), 547–553 (2011). [CrossRef]
  5. L. Lin, X. M. Goh, L. P. McGuinness, and A. Roberts, “Plasmonic lenses formed by two-dimensional nanometric cross-shaped aperture arrays for Fresnel-region focusing,” Nano Lett. 10(5), 1936–1940 (2010). [CrossRef] [PubMed]
  6. L. Verslegers, P. B. Catrysse, Z. Yu, J. S. White, E. S. Barnard, M. L. Brongersma, and S. Fan, “Planar lenses based on nanoscale slit arrays in a metallic film,” Nano Lett. 9(1), 235–238 (2009). [CrossRef] [PubMed]
  7. J. H. Kang, J.-H. Choe, D. S. Kim, and Q.-H. Park, “Substrate effect on aperture resonances in a thin metal film,” Opt. Express 17(18), 15652–15658 (2009). [CrossRef] [PubMed]
  8. A. Krishnan, T. Thio, T. J. Kim, H. J. Lezec, T. Ebbesen, P. A. Wolff, J. Pendry, L. Martin-Moreno, and F. J. Garcia-Vidal, “Evanescently coupled resonance in surface plasmon enhanced transmission,” Opt. Commun. 200(1-6), 1–7 (2001). [CrossRef]
  9. Y. Pang, C. Genet, and T. Ebbesen, “Optical transmission through subwavelength slit apertures in metallic films,” Opt. Commun. 280(1), 10–15 (2007). [CrossRef]
  10. K. L. Shuford, S. K. Gray, M. A. Ratner, and G. C. Schatz, “Substrate effects on surface plasmons in single nanoholes,” Chem. Phys. Lett. 435(1-3), 123–126 (2007). [CrossRef]
  11. K. C. Vernon, A. M. Funston, C. Novo, D. E. Gómez, P. Mulvaney, and T. J. Davis, “Influence of particle-substrate interaction on localized plasmon resonances,” Nano Lett. 10(6), 2080–2086 (2010). [CrossRef] [PubMed]
  12. S. Zhang, K. Bao, N. J. Halas, H. Xu, and P. Nordlander, “Substrate-induced Fano resonances of a plasmonic nanocube: a route to increased-sensitivity localized surface plasmon resonance sensors revealed,” Nano Lett. 11(4), 1657–1663 (2011). [CrossRef] [PubMed]
  13. F. I. Baida, “Enhanced transmission through subwavelength metallic coaxial apertures by excitation of the TEM mode,” Appl. Phys. B 89(2-3), 145–149 (2007). [CrossRef]
  14. F. I. Baida and D. Van Labeke, “Light transmission by subwavelength annular aperture arrays in metallic films,” Opt. Commun. 209(1-3), 17–22 (2002). [CrossRef]
  15. F. I. Baida, D. Van Labeke, G. Granet, A. Moreau, and A. Belkhir, “Origin of the super-enhanced light transmission through a 2-D metallic annular aperture array: a study of photonic bands,” Appl. Phys. B 79(1), 1–8 (2004). [CrossRef]
  16. M. I. Haftel, C. Schlockermann, and G. Blumberg, “Role of cylindrical surface plasmons in enhanced transmission,” Appl. Phys. Lett. 88(19), 193104 (2006). [CrossRef]
  17. M. I. Haftel, C. Schlockermann, and G. Blumberg, “Enhanced transmission with coaxial nanoapertures: Role of cylindrical surface plasmons,” Phys. Rev. B 74(23), 235405 (2006). [CrossRef]
  18. S. M. Orbons, M. I. Haftel, C. Schlockermann, D. Freeman, M. Milicevic, T. J. Davis, B. Luther-Davies, D. N. Jamieson, and A. Roberts, “Dual resonance mechanisms facilitating enhanced optical transmission in coaxial waveguide arrays,” Opt. Lett. 33(8), 821–823 (2008). [CrossRef] [PubMed]
  19. S. M. Orbons and A. Roberts, “Resonance and extraordinary transmission in annular aperture arrays,” Opt. Express 14(26), 12623–12628 (2006). [CrossRef] [PubMed]
  20. L. Lin, L. B. Hande, and A. Roberts, “Resonant nanometric cross-shaped apertures: Single apertures versus periodic arrays,” Appl. Phys. Lett. 95(20), 201116 (2009). [CrossRef]
  21. A. Roberts, “Beam transmission through hole arrays,” Opt. Express 18(3), 2528–2533 (2010). [CrossRef] [PubMed]
  22. D. Li and R. Gordon, “Electromagnetic transmission resonances for a single annular aperture in a metal plate,” Phys. Rev. A 82(4), 041801 (2010). [CrossRef]
  23. R. Ulrich, “Far-infrared properties of metallic mesh and its complementary structure,” Infrared Phys. 7(1), 37–55 (1967). [CrossRef]
  24. F. J. García-Vidal, L. Martin-Moreno, E. Moreno, L. K. S. Kumar, and R. Gordon, “Transmission of light through a single rectangular hole in a real metal,” Phys. Rev. B 74(15), 153411 (2006). [CrossRef]
  25. K. D. Möller, J. B. Warren, J. B. Heaney, and C. Kotecki, “Cross-shaped bandpass filters for the near- and mid-infrared wavelength regions,” Appl. Opt. 35(31), 6210–6215 (1996). [CrossRef] [PubMed]
  26. R. C. Compton, L. B. Whitbourn, and R. C. McPhedran, “Strip gratings at a dielectric interface and applicaton of Babinet’s principle,” Appl. Opt. 23(18), 3236–3242 (1984). [CrossRef] [PubMed]
  27. L. B. Whitbourn and R. C. Compton, “Equivalent-circuit formulas for metal grid reflectors at a dielectric boundary,” Appl. Opt. 24(2), 217–220 (1985). [CrossRef] [PubMed]
  28. S. Y. Chiam, R. Singh, W. Zhang, and A. A. Bettiol, “Controlling metamaterial resonances via dielectric and aspect ratio effects,” Appl. Phys. Lett. 97(19), 191906 (2010). [CrossRef]
  29. J. F. O’Hara, R. Singh, I. Brener, E. Smirnova, J. Han, A. J. Taylor, and W. Zhang, “Thin-film sensing with planar terahertz metamaterials: sensitivity and limitations,” Opt. Express 16(3), 1786–1795 (2008). [CrossRef] [PubMed]
  30. P. B. Johnson and R. W. Christy, “Optical constants of the noble metals,” Phys. Rev. B 6(12), 4370–4379 (1972). [CrossRef]
  31. A. Roberts and R. C. McPhedran, “Bandpass grids with annular apertures,” IEEE Trans. Antenn. Propag. 36(5), 607–611 (1988). [CrossRef]
  32. M. J. Lockyear, A. P. Hibbins, J. R. Sambles, and C. R. Lawrence, “Enhanced microwave transmission through a single subwavelength aperture surrounded by concentric grooves,” J. Opt. A, Pure Appl. Opt. 7(2), S152–S158 (2005). [CrossRef]
  33. J. Bravo-Abad, A. I. Fernández-Domínguez, F. J. García-Vidal, and L. Martín-Moreno, “Theory of extraordinary transmission of light through quasiperiodic arrays of subwavelength holes,” Phys. Rev. Lett. 99(20), 203905 (2007). [CrossRef] [PubMed]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited