Persistent luminescence in MSi2O2N2:Eu phosphors

Jonas Botterman, Koen Van den Eeckhout, Adrie J. J. Bos, Pieter Dorenbos, and Philippe F. Smet  »View Author Affiliations


Optical Materials Express, Vol. 2, Issue 3, pp. 341-349 (2012)
http://dx.doi.org/10.1364/OME.2.000341


View Full Text Article

Acrobat PDF (1187 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

In this work we study the persistent luminescence properties of europium-doped alkaline earth silicon oxynitrides (CaSi2O2N2, SrSi2O2N2 and BaSi2O2N2). All compounds show afterglow emission, with an emission spectrum which is similar to the steady state photoluminescence. The afterglow decay time for BaSi2O2N2:Eu and SrSi2O2N2:Eu is about 50 and 100 minutes respectively, while for CaSi2O2N2:Eu the afterglow intensity is very low. Although the persistent luminescence can be induced by ultraviolet light (250-300 nm) in all three phosphors, only for BaSi2O2N2:Eu low energy radiation (350-500 nm) allows filling of the traps responsible for the afterglow.

© 2012 OSA

1. Introduction

Persistent luminescent materials are able to emit light for a long time after the excitation has ended (typically minutes to hours). This remarkable ‘afterglow’ of persistent luminescent materials allows for a wide range of applications from commercial products including watch dials, luminous paints and glow-in-the-dark gadgets to emergency signage and safety illumination in public places and medical imaging applications. Currently, europium doped materials are among the most efficient and most studied persistent phosphors. Other rare-earth elements are often added to enhance the persistence lifetime. An overview of reported europium based persistent luminescent materials (and suggested mechanisms) is given by Van den Eeckhout et al. [1

1. K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials 3(4), 2536–2566 (2010). [CrossRef]

]. SrAl2O4:Eu,Dy is an efficient persistent luminescent material with an afterglow duration exceeding 30 h. The report on this green emitting phosphor in 1996 by Matsuzawa et al. [2

2. T. Matsuzawa, Y. Aoki, N. Takeuchi, and Y. Murayama, “New long phosphorescent phosphor with high brightness, SrAl2O4:Eu2+,Dy3+,” J. Electrochem. Soc. 143(8), 2670–2673 (1996). [CrossRef]

] marked the start for intensive scientific research on persistent luminescence.

Europium doped oxynitrides (MSi2O2N2:Eu with M = Ba, Sr, Ca) have recently been proposed as excellent conversion phosphor materials for white-light-emitting LED applications based on near ultraviolet (UV) or blue emitting InGaN LEDs. This is not only because of their strong absorption in the near UV to blue-light region of the light spectrum, but also for their high quantum efficiency and their good thermal and chemical stability compared to most oxide and sulfide phosphors [3

3. R. Mueller-Mach, G. Mueller, M. R. Krames, H. A. Höppe, F. Stadler, W. Schnick, T. Juestel, and P. Schmidt, “Highly efficient all-nitride phosphor-converted white light emitting diode,” Phys. Status Solidi A 202(9), 1727–1732 (2005). [CrossRef]

5

5. P. F. Smet, A. B. Parmentier, and D. Poelman, “Selecting conversion phosphors for white light-emitting diodes,” J. Electrochem. Soc. 158(6), R37–R54 (2011). [CrossRef]

]. BaSi2O2N2:Eu emits blue-green light and has an emission maximum around 494 nm and a full width at half-maximum (FWHM) for the emission band of 32 nm. SrSi2O2N2:Eu emits in the green region of the visible light spectrum. Its emission spectrum is broad (FWHM = 76 nm) with an emission maximum around 539 nm. CaSi2O2N2:Eu is a green-yellow emitting phosphor with an even broader emission band (FWHM = 106 nm) with a maximum around 560 nm. The photoluminescent properties of these oxynitrides were reported in detail by Bachmann et al. [6

6. V. Bachmann, C. Ronda, O. Oeckler, W. Schnick, and A. Meijerink, “Color point tuning for (Sr,Ca,Ba)Si2O2N2:Eu2+ for white light LEDs,” Chem. Mater. 21(2), 316–325 (2009). [CrossRef]

,7

7. V. Bachmann, T. Justel, A. Meijerink, C. Ronda, and P. J. Schmidt, “Luminescence properties of SrSi2O2N2 doped with divalent rare earth ions,” J. Lumin. 121(2), 441–449 (2006). [CrossRef]

].

2. Experimental

MSi2O2N2:Eu powders (with M = Ba, Sr, Ca) were synthesized using a high temperature solid state reaction. Stoichiometric amounts of starting materials MCO3 (99.95%, Alfa Aesar) and Si3N4 (α-phase, 99.5%, Alfa Aesar) were weighed and thoroughly mixed in a mortar. In order to dope with Eu, appropriate amounts of MCO3 were substituted by EuF3 (99.5%, Alfa Aesar). All powders were prepared with 2 mol% of Eu unless stated otherwise. The obtained mixtures were put in zirconia crucibles and fired at 1425 °C during 4 h in a horizontal tube furnace under a flowing atmosphere of forming gas (90% N2, 10% H2). Since the europium ions are incorporated on divalent lattice sites, and the reaction atmosphere is reducing, europium is dominantly incorporated into the host lattice as Eu2+. After cooling in a natural way, the powders were recuperated from the crucibles and grinded in a mortar.

The crystal structure of the prepared powders was checked by θ-2θ X-ray diffraction (XRD) measurements (Siemens D5000, CuKα radiation) and compared with literature data [11

11. J. A. Kechele, O. Oeckler, F. Stadler, and W. Schnick, “Structure elucidation of BaSi2O2N2 - A host lattice for rare-earth doped luminescent materials in phosphor-converted (pc)-LEDs,” Solid State Sci. 11(2), 537–543 (2009). [CrossRef]

13

13. H. A. Höppe, F. Stadler, O. Oeckler, and W. Schnick, “Ca[Si2O2N2] - A novel layer silicate,” Angew. Chem. Int. Ed. 43(41), 5540–5542 (2004). [CrossRef]

].

Photoluminescence (PL) excitation and emission spectra were recorded with a steady state fluorescence spectrometer (Edinburgh Instruments FS920). Luminescence decay measurements were performed using the Edinburgh spectrometer and a calibrated photometer (International Light Technologies ILT1700).

Thermoluminescence excitation spectra were obtained on the setup described in detail in [9

9. A. J. J. Bos, R. M. van Duijvenvoorde, E. van der Kolk, W. Drozdowski, and P. Dorenbos, “Thermoluminescence excitation spectroscopy: A versatile technique to study persistent luminescence phosphors,” J. Lumin. 131(7), 1465–1471 (2011). [CrossRef]

,10

10. P. F. Smet, K. Van den Eeckhout, A. J. J. Bos, E. van der Kolk, and P. Dorenbos, “Temperature and wavelength dependent trap filling in M2Si5N8:Eu (M = Ca, Sr, Ba) persistent phosphors,” J. Lumin. 132(3), 682–689 (2012). [CrossRef]

]. A fiber-coupled grating monochromator in combination with a xenon arc light source allows to direct monochromatic excitation light towards the sample. Thermoluminescence glow curves are then collected by a Risø thermoluminescence reader (TL/OSL-DA-15), equipped with a photomultiplier tube and suitable optical filters. The setup is fully automated and software controlled, which allows the reproducible collection of thermoluminescence glow curves for consecutive excitation wavelengths. Typically, a measurement time of 8 h was needed for the TL excitation contour plots shown in this work. All spectra were corrected for the wavelength-dependent optical output of the excitation source. TL excitation contour plots were collected with a heating rate of 5 K/s.

3. Results

3.1 Crystal structure

XRD spectra (Fig. 1
Fig. 1 x-ray diffraction patterns of MSi2O2N2 (colored traces) along with their reference patterns (black).
) of the BaSi2O2N2:Eu powders showed the structure of the BaSi2O2N2 host lattice [11

11. J. A. Kechele, O. Oeckler, F. Stadler, and W. Schnick, “Structure elucidation of BaSi2O2N2 - A host lattice for rare-earth doped luminescent materials in phosphor-converted (pc)-LEDs,” Solid State Sci. 11(2), 537–543 (2009). [CrossRef]

] with only minor traces of BaSi6ON8 [14

14. F. Stadler, R. Kraut, O. Oeckler, S. Schmid, and W. Schnick, “Synthesis, crystal structure and solid-state NMR spectroscopic investigation of the oxonitridosilicate BaSi6N8O,” ChemInform 36(43), 1773–1778 (2005). [CrossRef]

] and Ba3Si6O9N4 [15

15. F. Stadler and W. Schnick, “The new layer-silicates Ba3Si6O9N4 and Eu3Si6O9N4,” Z. Anorg. Allg. Chem. 632(6), 949–954 (2006). [CrossRef]

] in some samples. Substituting a small amount of Ba atoms by Eu atoms in the crystal lattice does not have a detectable influence on the XRD spectra and thus we assume that for low doping concentration the crystal structure is unaltered. Also for the synthesis of SrSi2O2N2:Eu and CaSi2O2N2:Eu we verified that under the used synthesis conditions the desired materials are obtained with only minor traces of impurities [12

12. O. Oeckler, F. Stadler, T. Rosenthal, and W. Schnick, “Real structure of SrSi2O2N2,” Solid State Sci. 9(2), 205–212 (2007). [CrossRef]

,13

13. H. A. Höppe, F. Stadler, O. Oeckler, and W. Schnick, “Ca[Si2O2N2] - A novel layer silicate,” Angew. Chem. Int. Ed. 43(41), 5540–5542 (2004). [CrossRef]

].

In BaSi2O2N2, there is only one Ba2+ site with a rather highly symmetric environment: the Ba2+ ions are coordinated by eight O atoms in a nearly cubic formation. This cuboid is additionally capped by two N atoms. In SrSi2O2N2 and CaSi2O2N2 there are four different M2+ cation sites in the lattice. For all sites the cations are coordinated by 6 O atoms, forming a distorted trigonal prism, and capped by one N atom [6

6. V. Bachmann, C. Ronda, O. Oeckler, W. Schnick, and A. Meijerink, “Color point tuning for (Sr,Ca,Ba)Si2O2N2:Eu2+ for white light LEDs,” Chem. Mater. 21(2), 316–325 (2009). [CrossRef]

,11

11. J. A. Kechele, O. Oeckler, F. Stadler, and W. Schnick, “Structure elucidation of BaSi2O2N2 - A host lattice for rare-earth doped luminescent materials in phosphor-converted (pc)-LEDs,” Solid State Sci. 11(2), 537–543 (2009). [CrossRef]

13

13. H. A. Höppe, F. Stadler, O. Oeckler, and W. Schnick, “Ca[Si2O2N2] - A novel layer silicate,” Angew. Chem. Int. Ed. 43(41), 5540–5542 (2004). [CrossRef]

]. Although the crystal structures of SrSi2O2N2 and CaSi2O2N2 are not isotypic, they show strong similarities.

3.2 Photoluminescence

3.3 Afterglow

After excitation with ultraviolet light, all MSi2O2N2:Eu oxynitrides show some form of persistent luminescence. Figure 3
Fig. 3 Decay at room temperature of the afterglow intensity of MSi2O2N2:Eu (with M = Ba, Sr, Ca) after 1 min excitation with a Xe arc lamp at 1000 lux.
shows the afterglow intensity as a function of time for the different materials after 1 min excitation with an unfiltered xenon arc lamp at 1000 lux, containing a significant fraction of ultraviolet light in its emission spectrum. For many persistent luminescent materials the decay curve follows a descending straight line in a log-log plot, implying that the afterglow can be modeled by a power law with negative scaling exponent. The decay curves of the MSi2O2N2:Eu oxynitrides deviate only slightly from this phenomenological law.

We define the afterglow duration as the time between the end of the excitation and the moment where the afterglow intensity drops below 0.32 mcd/m2. This is a threshold value often used in industrial standards and is about 100 times the sensitivity of the human eye [16

16. D. Poelman, N. Avci, and P. F. Smet, “Measured luminance and visual appearance of multi-color persistent phosphors,” Opt. Express 17(1), 358–364 (2009). [CrossRef] [PubMed]

]. CaSi2O2N2:Eu shows the shortest afterglow duration of about 400 s. The afterglow duration is longest SrSi2O2N2:Eu, around 6000 s. Although the afterglow of BaSi2O2N2:Eu starts with approximate the same intensity as that of SrSi2O2N2:Eu, the afterglow duration is only around 2800 s which is about half the afterglow duration of SrSi2O2N2:Eu.

For many persistent luminescent materials the afterglow intensity and duration can be improved by codoping the material with selected rare earth elements. In SrAl2O4:Eu,Dy for example, the afterglow is enhanced by almost two orders of magnitude compared to the afterglow of SrAl2O4:Eu [2

2. T. Matsuzawa, Y. Aoki, N. Takeuchi, and Y. Murayama, “New long phosphorescent phosphor with high brightness, SrAl2O4:Eu2+,Dy3+,” J. Electrochem. Soc. 143(8), 2670–2673 (1996). [CrossRef]

]. This enhancement is attributed to creation or modification of traps in the material by the dysprosium codopant. Also other rare earth elements such as neodymium, thulium, holmium or yttrium have been proven to be useful codopants to enhance the afterglow of certain compounds [1

1. K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials 3(4), 2536–2566 (2010). [CrossRef]

]. For BaSi2O2N2:Eu, different rare earth elements (Pr, Nd, Sm, Tb, Dy, Ho, Er and Tm) were tested as codopant but they hardly influenced the afterglow. This is not uncommon since several other persistent luminescent materials have been reported for which adding of rare earth element codopants has no or even a negative effect on the afterglow [17

17. K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Luminescent afterglow behavior in the M2Si5N8: Eu family (M = Ca, Sr, Ba),” Materials 4(6), 980–990 (2011). [CrossRef]

]. More research on the effect of codoping SrSi2O2N2:Eu and CaSi2O2N2:Eu with different rare earth elements needs to be performed.

When we measure the afterglow of the MSi2O2N2:Eu oxynitrides after excitation with monochromatic light of 280 nm and compare this with the afterglow after excitation with 425 nm, we observe a remarkable difference between BaSi2O2N2:Eu on the one hand and SrSi2O2N2:Eu and CaSi2O2N2:Eu on the other. Figure 4
Fig. 4 Decay of the afterglow intensity of MSi2O2N2:Eu (with M = Ba, Sr, Ca) after 30 s excitation with 280 nm UV radiation (left) and 425 nm violet light (right).
shows the afterglow for the three compounds after excitation with 280 nm (left) and 425 nm (right). In the former case, all of them show a similar afterglow intensity compared to the intensity after excitation with the unfiltered Xe arc lamp at 1000 lux (Fig. 3). However, when we excite the powders with 425 nm violet light, only the afterglow of BaSi2O2N2:Eu remains visible. The SrSi2O2N2:Eu compound shows an afterglow which is over hundred times weaker than the afterglow after 280 nm excitation and is below the 0.32 mcd/cm2 limit within seconds. For CaSi2O2N2:Eu the afterglow is negligible upon excitation with 425 nm light.

3.4 TL excitation

TL excitation spectroscopy was used to extend the information obtained by monitoring the afterglow after excitation at two different wavelengths. TL excitation contour plots for MSi2O2N2:Eu are shown in Fig. 5
Fig. 5 (top) Normalized TL excitation contour plots for MSi2O2N2:Eu. Heating rate was 5 °C/s. (bottom, left) TL glow curves and (bottom, right) trap filling spectra for MSi2O2N2:Eu, extracted from the TL excitation contour plots.
, which are obtained by recording consecutive TL glow curves upon excitation with monochromatic light.

For CaSi2O2N2:Eu and SrSi2O2N2:Eu filling of traps via excitation into the lower 5d states of Eu2+ is not possible, presumably due to a large energy separation between the lowest 5d excited state and the conduction band of the host material. Consequently, the use of these phosphors for wavelength conversion in LEDs is not hampered by undesired afterglow, as in general only near-UV or blue pumping LEDs are used.

4. Discussion

Based on the results shown in Fig. 3, it is clear that the MSi2O2N2:Eu compounds show a significant afterglow emission, with the Sr and Ba compounds obviously being more efficient in storing energy. Although the afterglow intensity is one to two orders of magnitude lower than the best currently available (strontium aluminate) based phosphors, there is still room for further optimization, with respect to composition and synthesis conditions.

By performing thermoluminescence excitation spectroscopy we obtained a better grasp on the trapping and release mechanisms in these compounds. For several established Eu2+-doped persistent phosphors, such as SrAl2O4:Eu,Dy and CaAl2O4:Eu,Nd, there are strong similarities between the shape of the trap filling spectra, as derived from the thermoluminescence excitation contour plots, and the excitation spectra for the steady state photoluminescence [9

9. A. J. J. Bos, R. M. van Duijvenvoorde, E. van der Kolk, W. Drozdowski, and P. Dorenbos, “Thermoluminescence excitation spectroscopy: A versatile technique to study persistent luminescence phosphors,” J. Lumin. 131(7), 1465–1471 (2011). [CrossRef]

]. This proved that for these compounds the first step in the trapping process occurs via the excitation into the 5d states of the europium ion, after which trapping can occur. For SrAl2O4:Eu,Dy it was recently shown that during the excitation and the filling of trap states, an ionization of europium to its trivalent state indeed occurs [18

18. K. Korthout, K. Van den Eeckhout, J. Botterman, S. Nikitenko, D. Poelman, and P. F. Smet, “Luminescence and x-ray absorption measurements of persistent SrAl2O4:Eu,Dy powders: Evidence for valence state changes,” Phys. Rev. B 84(8), 085140 (2011). [CrossRef]

].

For CaSi2O2N2:Eu and SrSi2O2N2:Eu, the relevant traps can only be filled by excitation with UV light (λ < 325 nm), while for BaSi2O2N2:Eu a low energy band occurs in the trap filling spectra, which coincides with the lower 5d excitation band(s) of the steady state luminescence. Similar to the recently reported case of M2Si5N8:Eu(,Tm) persistent phosphors [10

10. P. F. Smet, K. Van den Eeckhout, A. J. J. Bos, E. van der Kolk, and P. Dorenbos, “Temperature and wavelength dependent trap filling in M2Si5N8:Eu (M = Ca, Sr, Ba) persistent phosphors,” J. Lumin. 132(3), 682–689 (2012). [CrossRef]

], we assign this different behavior to the energy separation between the lower 5d excitation levels of Eu2+ and the bottom of the conduction band. Apparently, this energy barrier is too large for CaSi2O2N2:Eu and SrSi2O2N2:Eu to be overcome at room temperature. Hence excitation to the lower 5d levels is not leading to charge trapping.

The major hurdle to be taken is the relation between the thermal quenching behavior and the trap filling via the lower 5d excited state. One would expect that, presuming that the electron transfer from the excited europium ion to the relevant traps occurs via the conduction band, a low thermal barrier for trap filling is associated to a relatively low thermal quenching behavior. This was indeed observed for several efficient persistent phosphors [10

10. P. F. Smet, K. Van den Eeckhout, A. J. J. Bos, E. van der Kolk, and P. Dorenbos, “Temperature and wavelength dependent trap filling in M2Si5N8:Eu (M = Ca, Sr, Ba) persistent phosphors,” J. Lumin. 132(3), 682–689 (2012). [CrossRef]

]. However, for the MSi2O2N2:Eu phosphors this is clearly not the case. CaSi2O2N2:Eu shows a much lower thermal quenching temperature (T50% = 440K) compared to the Sr and Ba compounds (T50% = 600K) [6

6. V. Bachmann, C. Ronda, O. Oeckler, W. Schnick, and A. Meijerink, “Color point tuning for (Sr,Ca,Ba)Si2O2N2:Eu2+ for white light LEDs,” Chem. Mater. 21(2), 316–325 (2009). [CrossRef]

], while only the Ba-compound shows the possibility of trap-filling via the lowest excited 5d-state. Although this could imply a different trapping mechanism (i.e. not involving the conduction band levels), the situation is considerably blurred in the case of CaSi2O2N2:Eu and SrSi2O2N2:Eu due to the several available sites for the Eu ions and the energy transfer between them. Clearly, further energy level modeling is required to elucidate the trapping mechanism.

5. Conclusions

Europium doped oxynitrides MSi2O2N2:Eu (with M = Ba, Sr, Ca) were successfully synthesized using a solid state reaction at 1425 °C. All these oxynitrides are bright and efficient phosphor materials with a broad excitation spectrum and with emission maximum at 493 nm for M = Ba, 539 nm for M = Sr and 556 nm for M = Ca.

All MSi2O2N2:Eu show persistent luminescence upon excitation by UV radiation (λ < 325 nm). The afterglow duration is about 400 s, 2800 s and 6000 s for CaSi2O2N2:Eu, BaSi2O2N2:Eu and SrSi2O2N2:Eu respectively. Upon excitation with near UV and blue light (360 nm < λ <500 nm) only BaSi2O2N2:Eu shows persistent luminescence. TL excitation measurements confirm these findings. Codoping BaSi2O2N2:Eu with various rare earth ions does not increase the afterglow emission intensity.

Acknowledgments

Jonas Botterman and Koen Van den Eeckhout are Research Assistants for the BOF-UGent. Philippe F. Smet is indebted to the Fund for Scientific Research - Flanders (FWO-Vlaanderen) for a Mobility Grant to TU Delft.

References and links

1.

K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials 3(4), 2536–2566 (2010). [CrossRef]

2.

T. Matsuzawa, Y. Aoki, N. Takeuchi, and Y. Murayama, “New long phosphorescent phosphor with high brightness, SrAl2O4:Eu2+,Dy3+,” J. Electrochem. Soc. 143(8), 2670–2673 (1996). [CrossRef]

3.

R. Mueller-Mach, G. Mueller, M. R. Krames, H. A. Höppe, F. Stadler, W. Schnick, T. Juestel, and P. Schmidt, “Highly efficient all-nitride phosphor-converted white light emitting diode,” Phys. Status Solidi A 202(9), 1727–1732 (2005). [CrossRef]

4.

R. J. Xie, N. Hirosaki, K. Sakuma, and N. Kimura, “White light-emitting diodes (LEDs) using (oxy) nitride phosphors,” J. Phys. D Appl. Phys. 41(14), 144013 (2008). [CrossRef]

5.

P. F. Smet, A. B. Parmentier, and D. Poelman, “Selecting conversion phosphors for white light-emitting diodes,” J. Electrochem. Soc. 158(6), R37–R54 (2011). [CrossRef]

6.

V. Bachmann, C. Ronda, O. Oeckler, W. Schnick, and A. Meijerink, “Color point tuning for (Sr,Ca,Ba)Si2O2N2:Eu2+ for white light LEDs,” Chem. Mater. 21(2), 316–325 (2009). [CrossRef]

7.

V. Bachmann, T. Justel, A. Meijerink, C. Ronda, and P. J. Schmidt, “Luminescence properties of SrSi2O2N2 doped with divalent rare earth ions,” J. Lumin. 121(2), 441–449 (2006). [CrossRef]

8.

M. Y. Wang, X. Zhang, Z. D. Hao, X. G. Ren, Y. S. Luo, H. F. Zhao, X. J. Wang, and J. H. Zhang, “Long-lasting phosphorescence in BaSi2O2N2:Eu2+ and Ba2SiO4:Eu2+ phases for x-ray and cathode ray tubes,” J. Electrochem. Soc. 157(2), H178–H181 (2010). [CrossRef]

9.

A. J. J. Bos, R. M. van Duijvenvoorde, E. van der Kolk, W. Drozdowski, and P. Dorenbos, “Thermoluminescence excitation spectroscopy: A versatile technique to study persistent luminescence phosphors,” J. Lumin. 131(7), 1465–1471 (2011). [CrossRef]

10.

P. F. Smet, K. Van den Eeckhout, A. J. J. Bos, E. van der Kolk, and P. Dorenbos, “Temperature and wavelength dependent trap filling in M2Si5N8:Eu (M = Ca, Sr, Ba) persistent phosphors,” J. Lumin. 132(3), 682–689 (2012). [CrossRef]

11.

J. A. Kechele, O. Oeckler, F. Stadler, and W. Schnick, “Structure elucidation of BaSi2O2N2 - A host lattice for rare-earth doped luminescent materials in phosphor-converted (pc)-LEDs,” Solid State Sci. 11(2), 537–543 (2009). [CrossRef]

12.

O. Oeckler, F. Stadler, T. Rosenthal, and W. Schnick, “Real structure of SrSi2O2N2,” Solid State Sci. 9(2), 205–212 (2007). [CrossRef]

13.

H. A. Höppe, F. Stadler, O. Oeckler, and W. Schnick, “Ca[Si2O2N2] - A novel layer silicate,” Angew. Chem. Int. Ed. 43(41), 5540–5542 (2004). [CrossRef]

14.

F. Stadler, R. Kraut, O. Oeckler, S. Schmid, and W. Schnick, “Synthesis, crystal structure and solid-state NMR spectroscopic investigation of the oxonitridosilicate BaSi6N8O,” ChemInform 36(43), 1773–1778 (2005). [CrossRef]

15.

F. Stadler and W. Schnick, “The new layer-silicates Ba3Si6O9N4 and Eu3Si6O9N4,” Z. Anorg. Allg. Chem. 632(6), 949–954 (2006). [CrossRef]

16.

D. Poelman, N. Avci, and P. F. Smet, “Measured luminance and visual appearance of multi-color persistent phosphors,” Opt. Express 17(1), 358–364 (2009). [CrossRef] [PubMed]

17.

K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Luminescent afterglow behavior in the M2Si5N8: Eu family (M = Ca, Sr, Ba),” Materials 4(6), 980–990 (2011). [CrossRef]

18.

K. Korthout, K. Van den Eeckhout, J. Botterman, S. Nikitenko, D. Poelman, and P. F. Smet, “Luminescence and x-ray absorption measurements of persistent SrAl2O4:Eu,Dy powders: Evidence for valence state changes,” Phys. Rev. B 84(8), 085140 (2011). [CrossRef]

OCIS Codes
(160.2540) Materials : Fluorescent and luminescent materials
(160.2900) Materials : Optical storage materials
(160.5690) Materials : Rare-earth-doped materials
(170.6280) Medical optics and biotechnology : Spectroscopy, fluorescence and luminescence
(250.5230) Optoelectronics : Photoluminescence

ToC Category:
Fluorescent and Luminescent Materials

History
Original Manuscript: December 20, 2011
Revised Manuscript: February 23, 2012
Manuscript Accepted: February 23, 2012
Published: February 27, 2012

Virtual Issues
Persistent Phosphors (2012) Optical Materials Express

Citation
Jonas Botterman, Koen Van den Eeckhout, Adrie J. J. Bos, Pieter Dorenbos, and Philippe F. Smet, "Persistent luminescence in MSi2O2N2:Eu phosphors," Opt. Mater. Express 2, 341-349 (2012)
http://www.opticsinfobase.org/ome/abstract.cfm?URI=ome-2-3-341


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu2+-doped compounds: a review,” Materials3(4), 2536–2566 (2010). [CrossRef]
  2. T. Matsuzawa, Y. Aoki, N. Takeuchi, and Y. Murayama, “New long phosphorescent phosphor with high brightness, SrAl2O4:Eu2+,Dy3+,” J. Electrochem. Soc.143(8), 2670–2673 (1996). [CrossRef]
  3. R. Mueller-Mach, G. Mueller, M. R. Krames, H. A. Höppe, F. Stadler, W. Schnick, T. Juestel, and P. Schmidt, “Highly efficient all-nitride phosphor-converted white light emitting diode,” Phys. Status Solidi A202(9), 1727–1732 (2005). [CrossRef]
  4. R. J. Xie, N. Hirosaki, K. Sakuma, and N. Kimura, “White light-emitting diodes (LEDs) using (oxy) nitride phosphors,” J. Phys. D Appl. Phys.41(14), 144013 (2008). [CrossRef]
  5. P. F. Smet, A. B. Parmentier, and D. Poelman, “Selecting conversion phosphors for white light-emitting diodes,” J. Electrochem. Soc.158(6), R37–R54 (2011). [CrossRef]
  6. V. Bachmann, C. Ronda, O. Oeckler, W. Schnick, and A. Meijerink, “Color point tuning for (Sr,Ca,Ba)Si2O2N2:Eu2+ for white light LEDs,” Chem. Mater.21(2), 316–325 (2009). [CrossRef]
  7. V. Bachmann, T. Justel, A. Meijerink, C. Ronda, and P. J. Schmidt, “Luminescence properties of SrSi2O2N2 doped with divalent rare earth ions,” J. Lumin.121(2), 441–449 (2006). [CrossRef]
  8. M. Y. Wang, X. Zhang, Z. D. Hao, X. G. Ren, Y. S. Luo, H. F. Zhao, X. J. Wang, and J. H. Zhang, “Long-lasting phosphorescence in BaSi2O2N2:Eu2+ and Ba2SiO4:Eu2+ phases for x-ray and cathode ray tubes,” J. Electrochem. Soc.157(2), H178–H181 (2010). [CrossRef]
  9. A. J. J. Bos, R. M. van Duijvenvoorde, E. van der Kolk, W. Drozdowski, and P. Dorenbos, “Thermoluminescence excitation spectroscopy: A versatile technique to study persistent luminescence phosphors,” J. Lumin.131(7), 1465–1471 (2011). [CrossRef]
  10. P. F. Smet, K. Van den Eeckhout, A. J. J. Bos, E. van der Kolk, and P. Dorenbos, “Temperature and wavelength dependent trap filling in M2Si5N8:Eu (M = Ca, Sr, Ba) persistent phosphors,” J. Lumin.132(3), 682–689 (2012). [CrossRef]
  11. J. A. Kechele, O. Oeckler, F. Stadler, and W. Schnick, “Structure elucidation of BaSi2O2N2 - A host lattice for rare-earth doped luminescent materials in phosphor-converted (pc)-LEDs,” Solid State Sci.11(2), 537–543 (2009). [CrossRef]
  12. O. Oeckler, F. Stadler, T. Rosenthal, and W. Schnick, “Real structure of SrSi2O2N2,” Solid State Sci.9(2), 205–212 (2007). [CrossRef]
  13. H. A. Höppe, F. Stadler, O. Oeckler, and W. Schnick, “Ca[Si2O2N2] - A novel layer silicate,” Angew. Chem. Int. Ed.43(41), 5540–5542 (2004). [CrossRef]
  14. F. Stadler, R. Kraut, O. Oeckler, S. Schmid, and W. Schnick, “Synthesis, crystal structure and solid-state NMR spectroscopic investigation of the oxonitridosilicate BaSi6N8O,” ChemInform36(43), 1773–1778 (2005). [CrossRef]
  15. F. Stadler and W. Schnick, “The new layer-silicates Ba3Si6O9N4 and Eu3Si6O9N4,” Z. Anorg. Allg. Chem.632(6), 949–954 (2006). [CrossRef]
  16. D. Poelman, N. Avci, and P. F. Smet, “Measured luminance and visual appearance of multi-color persistent phosphors,” Opt. Express17(1), 358–364 (2009). [CrossRef] [PubMed]
  17. K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Luminescent afterglow behavior in the M2Si5N8: Eu family (M = Ca, Sr, Ba),” Materials4(6), 980–990 (2011). [CrossRef]
  18. K. Korthout, K. Van den Eeckhout, J. Botterman, S. Nikitenko, D. Poelman, and P. F. Smet, “Luminescence and x-ray absorption measurements of persistent SrAl2O4:Eu,Dy powders: Evidence for valence state changes,” Phys. Rev. B84(8), 085140 (2011). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.

Figures

Fig. 1 Fig. 2 Fig. 3
 
Fig. 4 Fig. 5
 

« Previous Article

OSA is a member of CrossRef.

CrossCheck Deposited