Nanoparticle-tuned structural color from polymer opals

Otto L. J. Pursiainen, Jeremy J. Baumberg, Holger Winkler, Benjamin Viel, Peter Spahn, and Tilmann Ruhl  »View Author Affiliations


Optics Express, Vol. 15, Issue 15, pp. 9553-9561 (2007)
http://dx.doi.org/10.1364/OE.15.009553


View Full Text Article

Acrobat PDF (573 KB)





Browse Journals / Lookup Meetings

Browse by Journal and Year


   


Lookup Conference Papers

Close Browse Journals / Lookup Meetings

Article Tools

Share
Citations

Abstract

The production of high-quality low-defect single-domain flexible polymer opals which possess fundamental photonic bandgaps tuneable across the visible and near-infrared regions is demonstrated in an industrially-scalable process. Incorporating sub-50nm nanoparticles into the interstices of the fcc lattice dramatically changes the perceived color without affecting the lattice quality. Contrary to iridescence based on Bragg diffraction, color generation arises through spectrally-resonant scattering inside the 3D photonic crystal. Viewing angles widen beyond 40° removing the strong dependence of the perceived color on the position of light sources, greatly enhancing the color appearance. This opens up a range of decorative, sensing, security and photonic applications, and suggests an origin for structural colors in Nature.

© 2007 Optical Society of America

1. Introduction

Structural color in nature arises mostly from optical interference of multiple light paths reflected inside periodically-textured materials. Natural opals consisting of stacked silica spheres acquire their characteristic iridescence due to Bragg interference from the lattice planes [1

1. R. K. Iler, “Formation of precious opal,” Nature 207, 472–473 (1965). [CrossRef]

6

6. P. Vukusic and J. R. Sambles, “Photonic structures in biology,” Nature 424, 852–855 (2003). [CrossRef] [PubMed]

]. Similarly butterfly wings can change their color with viewing angle due to the grating-like fine structure on their surfaces [6

6. P. Vukusic and J. R. Sambles, “Photonic structures in biology,” Nature 424, 852–855 (2003). [CrossRef] [PubMed]

9

9. P. Vukusic and I. Hooper, “Directionally controlled fluorescence emission in butterflies,” Science 18, 1151 (2005). [CrossRef]

].

Photonic crystals have attracted great interest since initial proposals suggested the inhibition of light emission in periodic structures [10

10. E. Yablonovitch, “Inhibited spontaneous emission in solid-state physics and electronics,” Phys. Rev. Lett. 58, 2059–2062 (1987). [CrossRef] [PubMed]

11

11. S. John, “Strong localization of photons in certain disordered dielectric superlattices,” Phys. Rev. Lett. 58, 2486–2489 (1987). [CrossRef] [PubMed]

]. Formation of complete photonic band gaps requires large refractive index contrast between the different components. Recently, there has been great interest in fabricating artificial opals or inverse opal structures [12

12. J. E. G. J. Wijnhoven and W. L. Vos, “Preparation of photonic crystals made of air spheres in titania,” Science 281, 802–804 (1998). [CrossRef]

16

16. A. A. Zakhidov, R. H. Baughman, Z. Iqbal, C. Cui, I. Khayrullin, S. O. Dantas, J. Marti, and V. G. Ralchenko, “Carbon structures with three-dimensional periodicity at optical wavelengths,” Science 282, 897–901 (1998). [CrossRef] [PubMed]

] as their structural color can replace toxic and carcinogenic dyes. However, the problem with these structures is their poor lattice quality due to cracks and poly-crystallinity, and their rigidity, which limits practical structural color applications.

Our ability to compression mould these flexible films, and to create emissive quantum-dot-doped polymer opals, anticipates their use in a range of decorative, sensing, security and photonic applications. Our results also suggest a re-examination of structural color in nature which we believe may exploit the same phenomena.

2. Opal fabrication

Our fabrication technique exploits polymer nano-sphere interactions in the viscous melt when lateral shear forces are applied, either by transverse pressure, or through extrusion [20

20. T. Ruhl, P. Spahn, and G. P. Hellmann, “Artificial opals prepared by melt compression,” Polymer 44, 7625–7634 (2003). [CrossRef]

]. These sub-micron particle precursors have a core-shell architecture consisting of a hard crosslinked polystyrene (PS) sphere coated with a thin polymethyl-methacrylate (PMMA) inter-layer which anchors the outer shell composed of soft polyethylacrylate (PEA). During shear flow [Fig. 1(a)], these core particles self-assemble into an fcc-lattice with the soft PEA shell filling the interstitial voids [20

20. T. Ruhl, P. Spahn, and G. P. Hellmann, “Artificial opals prepared by melt compression,” Polymer 44, 7625–7634 (2003). [CrossRef]

]. The fundamental optical response arising from the Bragg reflections (or incomplete photonic bandgaps) can be directly tuned across the visible and near-infrared spectral regions by varying the precursor nano-sphere size (around 200–350nm), and hence the resulting lattice parameter. The thickness of these thin opals can be straightforwardly varied between 100–300 µm. One of the most attractive features is the flexibility and the malleability of these structures, with color highlights produced by the bending or stretching modification of the (111) plane spacing [21

21. O. L. J. Pursiainen, J. J. Baumberg, H. Winkler, B. Viel, and T. Ruhl, “Compact strain-sensitive flexible photonic crystals for sensors,” Appl. Phys. Lett. 87, 101902–101904 (2005). [CrossRef]

].

Fig. 1. (a). Compression shear-assembly of polymer opal. (b-c) Optical images under natural lighting of 10cm diameter polymer opal films, which are (b) undoped (S3) and (c) doped (S4) with 0.05% by weight carbon nanoparticles.

Critical for the work here, is the ability to introduce additional sub-50nm nanoparticle dopants into the interstices of the photonic crystal lattice without disrupting the lattice quality. This is achieved by introducing the nanoparticle dopants into the precursor mix resulting in their homogeneous distribution within the interstitial PEA voids. A detailed description of the manufacturing can be found in Ref. [20

20. T. Ruhl, P. Spahn, and G. P. Hellmann, “Artificial opals prepared by melt compression,” Polymer 44, 7625–7634 (2003). [CrossRef]

]. The nanoparticle dopant we concentrate on in the present paper is carbon, however we have also successfully incorporated gold and hematite nanoparticles as well as CdSe colloidal quantum dots to produce emissive films. Results here are taken on 15cm-diameter polymer opal sheets produced by polymer melt compression, which we have shown previously are representative of the process, and can be well controlled. Samples studied in this work vary in precursor sphere size and different carbon black nanoparticle concentration (Table 1).

The key result we concentrate on here is that by introducing only 0.05% (by weight) of carbon nanoparticles into the lattice structure, the visual appearance of the elastomeric opals changes quite remarkably from milky white to intense green [Figs. 1(b)–1(c)]. These pictures are taken under natural lighting conditions and show the weak and highly-orientation-dependent Bragg diffraction gives way to a new color mechanism which is relatively insensitive to viewing angle. Detailed measurements of the angular optical response below strongly indicate that this effect is due to resonant scattering inside the photonically-structured environment and is critically dependent on the use of low-, not high-, refractive-index-contrast photonic crystals.

Table 1. Structural and doping parameters for several polymer opal films used in this work.

table-icon
View This Table

We confirm that the introduction of the nanoparticle doping at such low concentrations does not affect the structural quality of the opaline films, using a number of techniques. A large number of cross-sections examined by transmission electron microscopy (TEM) in every case show excellent lattice ordering in the hundreds of layers that light penetrates from the top of the films. Both with and without doping, this lattice uniformity is preserved [Figs. 2(a)–2(b)], with up to 30% loading of each interstice in the lattice with a carbon nanoparticle. Note that shear in the TEM images is produced in the microtoming of the relatively soft films. This excellent surface-ordering quality can also be verified from the six-fold surface diffraction pattern observed across the entire sample [Fig. 2(b) inset], taken with a 244nm UV laser normally incident on sample S2 with the diffracted UV light observed on a fluorescent white card. The penetration of UV light is on the order of a few hundred nanometers in these polymers (due to UV absorption in the polymer mix) and hence only surface ordering can be probed. Further confirmation of the single domain nature of the opal fabrication is seen [Fig. 2(c)] when comparing the Bragg diffraction from the poly-crystals of typical high-quality sedimented opal (left) with that from the mono-domain composing the opaline film (right, note that the gradation in color is because the flexible opal is intentionally bent).

These structural colors can be readily incorporated into applications, for instance in compression moulding onto an automobile model [Fig. 2(d)] producing highlighted color changes on the edges. We have produced >100m lengths of such extruded polymer opals showing the capability for industrial scalability.

Fig. 2. (a).–(b). TEM images of the (111) lattice plane of sample S4, where the polymer in (b) has been stained with ruthenium tetroxide for better contrast of the polystyrene/polyacrylate system. Inset of (b): surface diffraction pattern of sample S2 under normal incidence UV illumination. (c) Digital images of a sedimented and a polymer opal S1. (d) Miniature automobile with moulded polymer opal.

3. Experimental setups

The angle dependence of the Bragg-reflection and scattering was studied in two different setups. In the goniometer setup [Fig. 3(a)] the sample was mounted on a rotation stage and excited by an unpolarised super-continuum light source (emitted by a holey fiber pumped with 1064nm Nd-YAG microchip laser pulses) focused to a 500µm spot. On the detection arm are two lenses (L1 to collimate reflected/scattered light and L2 to refocus it on a multimode fiber) and in between is a variable-diameter iris. In the experiments reported here we fix the detection angle at the mirror reflection angle (θr=θi), but vary the iris aperture to record the strictly reflected (R) light (collection angle Δθr=3° equal to the input laser collimation) or the wide-angle-scattered (S) contribution (iris fully open, collection angle Δθs=30°). The light was then focussed into a multimode fiber (200 µm core) which was coupled to an Ocean Optics USB2000 spectrometer. We separately confirmed that the phenomena presented here are not significantly dependent on input and output polarization.

To map a wider angular scattering cone we use a hyperspectral imaging setup [Fig. 3(b)]. Here the incident light from the super-continuum source is first spectrally filtered (tunable center wavelength 400–700nm with a 7-nm bandwidth) using a CRI Varispec filter, and the incident light is p-polarised. For fixed incident angle, at each incident wavelength we record the resulting reflection/scattering (R/S) emission on a semi-transparent hemi-spherical white screen centered at the sample focus, using a zoom lens and CCD-camera which are aligned along the axis of the specular reflection angle. The spectral response is calibrated by replacing the sample with an aluminum mirror and recording the directly reflected spectrally-filtered laser [which appears as a small spot in the center of the images - see white spot in center of Fig. 4(b)]. Knowledge of the imaging geometry enables us to extract from the images obtained for each sample the angular widths of the different scattering cones at each wavelength [Figs. 4(c), 5(d), 6(d)]. The experiment is repeated at different angles of incidence to identify scattering that depends on the direction of incoming light (ie. identifying scattering with some memory of incident k orientation). For illustrative purposes, the full scattering is recorded on a white screen in Fig. 4(b) using a color digital camera in the geometry depicted in Fig. 4(a).

Fig. 3. Experimental setups used for (a,b) angle-dependent reflectivity and scattering measurements, (c) coherent backscattering mean free path measurements.

In order to quantify the effect of nanoparticle doping, the scattering mean free paths (lmfp) are measured using a standard coherent back-scattering (CBS) technique [22

22. G. Labeyrie, C. A. Muller, D. S. Wiersma, C. Miniatura, and R. Kaiser, “Observation of coherent backscattering of light by cold atoms,” J. Opt. B: Quantum Semiclass. Opt. 2, 672–685 (2000). [CrossRef]

]. Here [Fig. 3(c)], the light from an Ar+ laser at 514.5nm is beam expanded six-fold (BE) to 10mm diameter, vertically polarized (P1) and incident on a beamsplitter (BS). While the reflected component of the beam is carefully beam-dumped (D), the transmitted beam passes through a λ/4 waveplate to change its polarization state into right-circular (σ+) before being incident on the sample. Since the multiply-scattered light does not flip its polarization [22

22. G. Labeyrie, C. A. Muller, D. S. Wiersma, C. Miniatura, and R. Kaiser, “Observation of coherent backscattering of light by cold atoms,” J. Opt. B: Quantum Semiclass. Opt. 2, 672–685 (2000). [CrossRef]

], after direct backscatter (θCBS=-θi) the emerging light is converted back into vertical polarization (by the λ/4) and reflected off the BS into the CCD camera. With the polarizer P2 set vertically, only multiply-scattered contributions are transmitted while singly-scattered photons which emerge with left-circular (σ-) polarization are subsequently rejected by P2. The 150mm focusing lens (L) converts different back-scatter angles into spatial position in the image, which is calibrated from the geometry. The mean free paths were then calculated from the (~mrad) angular width of the coherent back-scattering peak using Ref. [22

22. G. Labeyrie, C. A. Muller, D. S. Wiersma, C. Miniatura, and R. Kaiser, “Observation of coherent backscattering of light by cold atoms,” J. Opt. B: Quantum Semiclass. Opt. 2, 672–685 (2000). [CrossRef]

].

4. Results and discussion

The peculiar optical properties of these polymer opals arise from chromatically-redirected scattering. To first demonstrate this we use a simple imaging geometry [Fig. 4(a)] in which light from a white light laser continuum source is incident at an angle of 40° on sample S1 and the resulting scattered light emerging from the opal around the reflection angle is recorded using a digital camera [Fig. 4(b)]. The chromatic scattering shows different colors emerging in different directions surrounding the central white reflected laser spot (R). By spectrally filtering the incident laser as described in Fig. 3(a), we image the evolution of the scattering cone across the photonic bandgap, centered here at 580nm [Fig. 4(c)]. The superimposed white dashed lines intersect in the specular reflected direction (reflected spot divergence ~3°), and strong scattering is seen over 30° away from this specular reflection angle.

Fig. 4. (a). Scattering geometry employed. (b). Optical image of the front surface scattering of the polymer opal S1 revealing the structural color content, light incident and reflected at 40°. (c) Scattering cone of S1 for three different color components at, and on the red and blue sides of the bandgap at 580nm for 40° incidence. Specular reflected spot at intersection of lines.

To demonstrate the influence of Bragg scattering within the photonic crystal, the full reflection of light including the scattering component is measured as a function of the size of the sphere precursor used to make the opal samples [Fig. 5(a)]. A strong peak is observed, which tunes proportional to sphere separation according to the standard Bragg equation for (111) planes parallel to the front surface. The relationship between reflection and scattering is then extracted from angle-dependent spectra in which either the full scattering intensity (R+S), or only the reflected contribution in the central spot (R), is measured [Fig. 5(b)]. In this experimental configuration [Fig. 3(a)] the light emerging from the sample is collected within an angular cone whose width is controllable, and focused into a multimode fiber connected to a spectrometer. The full scattering intensity (red line, 30° collection angular width) peaks at the expected Bragg spectral position for this angle of incidence. However when only the reflected spot is collected (3° cone angle, black line), a deep dip is observed [23

23. Using conventional spectro-photometers thus yields erroneous measurements as some significant fraction of S is also collected.

]. By subtracting these two, the scattered contribution is identified (blue line) which exhibits a strong resonant peak. Comparing the contrast on- and off-resonance, for reflection this ratio is <0.2 (the residual measured on resonance is also probably scatter — see below) while for scattering this ratio is >15. Counter to the conventional picture for photonic crystals of enhanced reflectivity at the Bragg resonance, we observe almost no light reflected in this Bragg condition. Simultaneously we observe strongly-enhanced scattering maximized near the same spectral position. Light entering the sample at the band gap wavelength is almost all redistributed into a wide scattering cone around the reflection direction.

To confirm that this scattering is dependent on the Bragg resonance, extraction of R and S is carried out for different angles of incidence [Fig. 5(c)]. Both the scattering peak and the reflection dip tune exactly in accordance with the (111)-plane Bragg resonance expected for the periodicity of this sample [Fig. 5(c) inset shows theoretical line with experimental points].

Fig. 5. (a). Evolution of the (111) bandgap for different sphere sizes at 5° incidence. (b) Scattering (S) and reflection (R) spectra for 40° incident angle. (c) Extracted R,S at different angles of incidence from 20° to 60° (in 10° steps), inset: fit to Bragg law. (d) Scattering with angle in the plane of incidence [horizontal cross-sections of Fig. 4(c)] around the specular reflected direction (at 40°) for selected colors around the bandgap. Inset: On-resonant scattering cross-section in orthogonal plane. (b-d) are taken for sample S1.

Angular cross-sections of the scattering cones [Fig. 5(d)] resolve the reflection and scattering components for different wavelengths around the bandgap (at 580nm for sample S1). The scattering cone passes across the specular reflection direction (which is the narrow peak shaded yellow) and is maximized at the Bragg condition [cf. Fig. 4(b)] while off-resonant wavelengths are scattered into directions depending on their spectral detuning from the band gap wavelength. Note these directions also change if the angle of incidence is changed, and are thus not fixed by the Bragg condition for escaping light. The width of the scattering cone reaches a maximum of 40° at the band gap. On the Bragg condition, the scattering falls off exponentially with angle [best seen in the orthogonal cross-section of the scattering cone taken perpendicularly to the incident plane, Fig. 5(d) inset] with no component of the specular reflection remaining (no angularly sharp component is observed). Fourier transforming this scattering dependence provides an estimate of the real-space scattering distribution, which has a long Lorentzian tail that implies that defects spatially localize light over length scales of many sphere periods.

The key to understanding these intriguing structural color properties are three important length scales: the typical penetration depth of resonant light inside the structure, known as the Bragg length, LB; the scattering mean free path of photons between scattering events, lmfp; and the absorption length of light, lα. The Bragg length is controlled by the strength of reflection at each interface inside the material: the polymer opal has low refractive index contrast (Δn/n=0.06) leading to LB~7µm while in high contrast TiO2 inverse opals (Δn/n=1.18) LB~1µm. On the other hand the scattering mean free path is controlled by scattering inside the imperfect structure, while the absorption length is almost 100 times this scattering length and easily measured from the non-resonant transmission through the sample [Fig. 6(a)].

Two different regimes are possible, shown schematically in Fig. 6. In an inverse opal [Fig. 6(b)], LBlmfp, prohibiting backward scattering out of the crystal through two mechanisms. Firstly, resonant photons mostly reflect off the uppermost layers of the structure before scattering, while secondly when a non-resonant photon scatters internally into a resonant direction it is likely to be re-reflected into the structure. However, in these polymer opals [Fig. 6(c)] the opposite regime arises, LB ~lmfp, which implies that all scattering events take place within the resonant photonic environment. We measure separately using coherent backscattering [Fig. 3(c)] that lmfp~27µm off-resonance in the undoped material [see Fig. 6(a)], which decreases strongly on resonance. We note that the scattering mean free path is many times longer than the separation between doped nanoparticles, which have an estimated cross section of <5% due to their small size. Scattered photons are thus likely to escape the structure, while the enhanced optical density of states (ODoS) inside the photonic crystal resonantly enhances and redirects the scattering for particular wavelengths [Fig. 6(c)]. This process is highly sensitive to the size and location of the scatterers in the interstitial sites [29

29. C. Hermann and O. Hess, “Modified spontaneous-emission rate in an inverted-opal structure with complete photonic bandgap,” J. Opt. Soc. Am. B 19, 3013–3018 (2002). [CrossRef]

]. While the conventional ODoS integrates over 3D angles (as needed to calculate the radiative lifetime of an embedded emitter), the resonant scattering here is explicitly angle dependent and a different measure is required, the Mutual Density of States (MDOS) described in [30

30. R. C. McPhedran, L. C. Botten, J. McOrist, A. A. Asatryan, C. M. de Sterke, and N. A. Nicorovici, “Density of states functions for photonic crystals,” Phys. Rev. E 69, 16609–16624 (2004). [CrossRef]

]. We surmise that essentially the scattering cross-section of defects inside such a low-contrast structure becomes large and anisotropic due to coupling with standing waves produced by multiple reflection. However, we note a full theoretical model has yet to be developed for this situation to describe the scattering enhancement from the angle-dependent local density of states - no current theoretical models incorporate 3D scattering and absorption within a photonic crystal environment. The scattering mean free path can be experimentally controlled by the level of doping [see Fig. 6(a)] and our current efforts include the characterization of the scattering induced by different nanoparticles. We note that since the sample thickness greatly exceeds l mfp, different effects are observed in transmission [21

21. O. L. J. Pursiainen, J. J. Baumberg, H. Winkler, B. Viel, and T. Ruhl, “Compact strain-sensitive flexible photonic crystals for sensors,” Appl. Phys. Lett. 87, 101902–101904 (2005). [CrossRef]

]. Disorder effects in opals and colloidal crystals have recently become of increasing interest [31

31. A. V. Baryshev, V. A. Kosobukin, K. B. Samusev, D. E. Usvyat, and M. F. Limonov, “Light diffraction from opal-based photonic crystals with growth-induced disorder: Experiment and theory,” Phys. Rev. E 73, 205118 (2006).

, 32

32. S. A. Asher, J. M. Weissman, A. Tikhonov, R. D. Coalson, and R. Kesavamoorthy, “Diffraction in crystalline colloidal-array photonic crystals,” Phys. Rev. B 69, 066619 (2004). [CrossRef]

] but have not observed the intense and angularly-broad scattering cones obtained here. Most work has been so far devoted to higher order bandgaps for which multiple scattering can become more important. Contrary to current efforts in obtaining complete bandgaps with high index contrast components, the previously unreported scattering-based structural color here requires low index contrast photonic crystals.

Finally, we show how doping the polymer opal with absorbing nanoparticles has such a dramatic effect on the scattering-based apparent color [Fig. 1(b–c)]. Angular scattering cross-sections for wavelengths around the resonant Bragg condition are measured for two opals with identical structures (samples S3 and S4, bandgap at 570nm for 30° incidence) differing only in their nanoparticle doping levels [Figs. 6(d)–6(e)]. Again we confirm by TEM that such low loadings of small (<50nm) nanoparticle produces no obvious distortion of the periodic lattice [see Figs. 2(a)–2(b)]. Without absorbing nanoparticles (thin lines) the scattering is mostly diffuse, hence such samples (like most opals) look milky white with a faint color tinge strongly dependent on their orientation compared to light sources. With the absorbing nanoparticles selectively embedded in the interstices (thick lines), the resonant scattering increases and fills a much larger solid angle (note the overall diffuse light scattered from film also decreases). Examining the energy of light scattered into different directions [Fig. 6(e) shaded] shows that even 0.05% carbon nanoparticles loading increases the resonant scattering by a factor of 300%, while the scattering cone width doubles. Hence these films appear strongly colored, virtually independent of illumination sources. Scattering inside such polymer opals can arise from Rayleigh scattering off the nanoparticle dopants or Mie scattering from lattice imperfections, and further experiments examining the anisotropy and polarization dependence (both weak) should help elucidate this.

Fig. 6. (a). Effect of carbon loading on the scattering mean free path (lmfp) and the absorption length (lα), measured for samples S3–6. (b)–(c) Structural color formation schematically shown for (111) planes with black points representing scattering events (not nanoparticles). In an inverse opal (b), light incident at the Bragg angle (green) is directly reflected, while off-resonant light (red) that is scattered into this angle inside the structure cannot escape. In a polymer opal (c), all colors penetrate, and Bragg angle light is resonantly scattered. (d) Scattering cross-sections with angle for carbon nanoparticle doped (thick lines) and un-doped (thin lines) polymer opals at, and either side of, the bandgap at 570nm (samples S3 & S4). (e) Scattered optical energy emerging in a 1° annulus around each angle for doped & undoped opals. Reflection (R) and scattering (S) domains indicated, resonant Bragg scattering shaded.

4. Conclusion

Acknowledgments

This work was supported by EPSRC grant EP/C511786/1. OLJP acknowledges support of Merck KGaA and Helsingin Sanomat Centennial Foundation.

References and links

1.

R. K. Iler, “Formation of precious opal,” Nature 207, 472–473 (1965). [CrossRef]

2.

P. J. Darragh, A. J. Gaskin, B. C. Terrell, and J. V. Sanders, “Origin of precious opal,” Nature 209, 13–16 (1966). [CrossRef]

3.

J. V. Sanders and M. J. Murray, “Ordered arrangements of spheres of two different sizes in opal,” Nature 275, 201–203 (1978). [CrossRef]

4.

A. van Blaaderen, “Opals in a new light,” Science 282, 887–888 (1998).

5.

D. W. Oxtoby, “Crystallization: Diversity suppresses growth,” Nature 413, 694–695 (2001). [CrossRef] [PubMed]

6.

P. Vukusic and J. R. Sambles, “Photonic structures in biology,” Nature 424, 852–855 (2003). [CrossRef] [PubMed]

7.

H. Ghiradella, D. Aneshansley, T. Eisner, R. E. Silberglied, and H. E. Hinton, “Ultraviolet reflection of a male butterfly: Interference color caused by thin-layer elaboration of wing scales,” Science 178, 1214–1217 (1972). [CrossRef] [PubMed]

8.

A. Jenkins, “Photonics: Wingèd light,” Nature 438, 436 (2005). [CrossRef] [PubMed]

9.

P. Vukusic and I. Hooper, “Directionally controlled fluorescence emission in butterflies,” Science 18, 1151 (2005). [CrossRef]

10.

E. Yablonovitch, “Inhibited spontaneous emission in solid-state physics and electronics,” Phys. Rev. Lett. 58, 2059–2062 (1987). [CrossRef] [PubMed]

11.

S. John, “Strong localization of photons in certain disordered dielectric superlattices,” Phys. Rev. Lett. 58, 2486–2489 (1987). [CrossRef] [PubMed]

12.

J. E. G. J. Wijnhoven and W. L. Vos, “Preparation of photonic crystals made of air spheres in titania,” Science 281, 802–804 (1998). [CrossRef]

13.

R. de la Rue, “Photonic crystals: Microassembly in 3D,” Nature Mater. 2, 74–76 (2003). [CrossRef]

14.

P. V. Braun and P. Wiltzius, “Electrochemically grown photonic crystals,” Nature 402, 603–604 (1999). [CrossRef]

15.

G. Subramania, K. Constant, R. Biswas, M. M. Sigalas, and K. -M. Ho, “Inverse face-centered cubic thin film photonic crystals,” Adv. Mater. 13, 443–446 (2001). [CrossRef]

16.

A. A. Zakhidov, R. H. Baughman, Z. Iqbal, C. Cui, I. Khayrullin, S. O. Dantas, J. Marti, and V. G. Ralchenko, “Carbon structures with three-dimensional periodicity at optical wavelengths,” Science 282, 897–901 (1998). [CrossRef] [PubMed]

17.

J. H. Holtz and S. A. Asher, “Polymerized colloidal crystal hydrogel films as intelligent chemical sensing materials,” Nature 389, 829–832 (1997). [CrossRef]

18.

A. C. Arsenault, T. J. Clark, G. von Freymann, L. Cademartiri, R. Sapienza, J. Bertolotti, E. Vekris, S. Wong, V. Kitaev, I. Manners, R. Z. Wang, S. John, D. Wiersma, G. A. Ozin, J. M. Jethmalani, and W. T. Ford, “Diffraction of visible light by ordered monodisperse silica-poly(methyl acrylate) composite films,” Chem. Mater. , 8, 2138–2146 (1996). [CrossRef]

19.

S. H. Foulger, P. Jiang, A. Lattam, D. W. Smith, J. Ballato, D. E. Dausch, S. Grego, and B. R. Stoner, “Photonic crystal composites with reversible high-frequency stop band shifts,” Adv. Mater. 15, 685–689 (2003). [CrossRef]

20.

T. Ruhl, P. Spahn, and G. P. Hellmann, “Artificial opals prepared by melt compression,” Polymer 44, 7625–7634 (2003). [CrossRef]

21.

O. L. J. Pursiainen, J. J. Baumberg, H. Winkler, B. Viel, and T. Ruhl, “Compact strain-sensitive flexible photonic crystals for sensors,” Appl. Phys. Lett. 87, 101902–101904 (2005). [CrossRef]

22.

G. Labeyrie, C. A. Muller, D. S. Wiersma, C. Miniatura, and R. Kaiser, “Observation of coherent backscattering of light by cold atoms,” J. Opt. B: Quantum Semiclass. Opt. 2, 672–685 (2000). [CrossRef]

23.

Using conventional spectro-photometers thus yields erroneous measurements as some significant fraction of S is also collected.

24.

V. N. Astratov, A. M. Adawi, S. Fricker, M. S. Skolnick, D. M. Whittaker, and P. N. Pusey “Interplay of order and disorder in the optical properties of opal photonic crystals,” Phys. Rev. B 66, 165215–165227 (2002). [CrossRef]

25.

T. Ruhl and G. P. Hellmann, “Colloidal crystals in latex films: rubbery opals,” Macromol. Chem. Phys. 202, 3502–3505 (2001). [CrossRef]

26.

Yu. A. Vlasov, M. A. Kaliteevski, and V. V. Nikolaev, “Different regimes of light localization in a disordered photonic crystal,” Phys. Rev. B 60, 1555–1562 (1999). [CrossRef]

27.

R. Rengarajan, D. Mittleman, C. Rich, and V. Colvin, “Effect of disorder on the optical properties of colloidal crystals,” Phys. Rev. E 71, 016615–016625 (2005). [CrossRef]

28.

A. F. Koenderink and W. L. Vos, “Optical properties of real photonic crystals: anomalous diffuse transmission,” J. Opt. Soc. Am. B 22, 1075–1084 (2005). [CrossRef]

29.

C. Hermann and O. Hess, “Modified spontaneous-emission rate in an inverted-opal structure with complete photonic bandgap,” J. Opt. Soc. Am. B 19, 3013–3018 (2002). [CrossRef]

30.

R. C. McPhedran, L. C. Botten, J. McOrist, A. A. Asatryan, C. M. de Sterke, and N. A. Nicorovici, “Density of states functions for photonic crystals,” Phys. Rev. E 69, 16609–16624 (2004). [CrossRef]

31.

A. V. Baryshev, V. A. Kosobukin, K. B. Samusev, D. E. Usvyat, and M. F. Limonov, “Light diffraction from opal-based photonic crystals with growth-induced disorder: Experiment and theory,” Phys. Rev. E 73, 205118 (2006).

32.

S. A. Asher, J. M. Weissman, A. Tikhonov, R. D. Coalson, and R. Kesavamoorthy, “Diffraction in crystalline colloidal-array photonic crystals,” Phys. Rev. B 69, 066619 (2004). [CrossRef]

OCIS Codes
(160.4760) Materials : Optical properties
(160.5470) Materials : Polymers
(290.5850) Scattering : Scattering, particles
(330.1690) Vision, color, and visual optics : Color

ToC Category:
Metamaterials

History
Original Manuscript: May 1, 2007
Revised Manuscript: July 4, 2007
Manuscript Accepted: July 9, 2007
Published: July 17, 2007

Virtual Issues
Vol. 2, Iss. 8 Virtual Journal for Biomedical Optics

Citation
Otto L. Pursiainen, Jeremy J. Baumberg, Holger Winkler, Benjamin Viel, Peter Spahn, and Tilmann Ruhl, "Nanoparticle-tuned structural color from polymer opals," Opt. Express 15, 9553-9561 (2007)
http://www.opticsinfobase.org/vjbo/abstract.cfm?URI=oe-15-15-9553


Sort:  Author  |  Year  |  Journal  |  Reset  

References

  1. R. K. Iler, "Formation of precious opal," Nature 207, 472-473 (1965). [CrossRef]
  2. P. J. Darragh, A. J. Gaskin, B. C. Terrell, and J. V. Sanders, "Origin of precious opal," Nature 209, 13-16 (1966). [CrossRef]
  3. J. V. Sanders and M. J. Murray, "Ordered arrangements of spheres of two different sizes in opal," Nature 275, 201-203 (1978). [CrossRef]
  4. A. van Blaaderen, "Opals in a new light," Science 282, 887-888 (1998).
  5. D. W. Oxtoby, "Crystallization: Diversity suppresses growth," Nature 413, 694-695 (2001). [CrossRef] [PubMed]
  6. P. Vukusic and J. R. Sambles, "Photonic structures in biology," Nature 424, 852-855 (2003). [CrossRef] [PubMed]
  7. H. Ghiradella, D. Aneshansley, T. Eisner, R. E. Silberglied, and H. E. Hinton, "Ultraviolet reflection of a male butterfly: Interference color caused by thin-layer elaboration of wing scales," Science 178, 1214-1217 (1972). [CrossRef] [PubMed]
  8. A. Jenkins, "Photonics: Wingèd light," Nature 438, 436 (2005). [CrossRef] [PubMed]
  9. P. Vukusic and I. Hooper, "Directionally controlled fluorescence emission in butterflies," Science 18, 1151 (2005). [CrossRef]
  10. E. Yablonovitch, "Inhibited spontaneous emission in solid-state physics and electronics," Phys. Rev. Lett. 58, 2059-2062 (1987). [CrossRef] [PubMed]
  11. S. John, "Strong localization of photons in certain disordered dielectric superlattices," Phys. Rev. Lett. 58, 2486-2489 (1987). [CrossRef] [PubMed]
  12. J. E. G. J. Wijnhoven and W. L. Vos, "Preparation of photonic crystals made of air spheres in titania," Science 281, 802-804 (1998). [CrossRef]
  13. R. de la Rue, "Photonic crystals: Microassembly in 3D," Nature Mater. 2, 74-76 (2003). [CrossRef]
  14. P. V. Braun and P. Wiltzius, "Electrochemically grown photonic crystals," Nature 402, 603-604 (1999). [CrossRef]
  15. G. Subramania, K. Constant, R. Biswas, M. M. Sigalas, and K. -M. Ho, "Inverse face-centered cubic thin film photonic crystals," Adv. Mater. 13, 443-446 (2001). [CrossRef]
  16. A. A. Zakhidov, R. H. Baughman, Z. Iqbal, C. Cui, I. Khayrullin, S. O. Dantas, J. Marti, and V. G. Ralchenko, "Carbon structures with three-dimensional periodicity at optical wavelengths," Science 282, 897-901 (1998). [CrossRef] [PubMed]
  17. J. H. Holtz and S. A. Asher, "Polymerized colloidal crystal hydrogel films as intelligent chemical sensing materials," Nature 389, 829-832 (1997). [CrossRef]
  18. A. C. Arsenault, T. J. Clark, G. von Freymann, L. Cademartiri, R. Sapienza, J. Bertolotti, E. Vekris, S. Wong, V. Kitaev, I. Manners, R. Z. Wang, S. John, D. Wiersma, G. A. Ozin, J. M. Jethmalani, and W. T. Ford, "Diffraction of visible light by ordered monodisperse silica-poly(methyl acrylate) composite films," Chem. Mater.  8, 2138-2146 (1996). [CrossRef]
  19. S. H. Foulger, P. Jiang, A. Lattam, D. W. SmithJr., J. Ballato, D. E. Dausch, S. Grego, and B. R. Stoner, "Photonic crystal composites with reversible high-frequency stop band shifts," Adv. Mater. 15, 685-689 (2003). [CrossRef]
  20. T. Ruhl, P. Spahn, and G. P. Hellmann, "Artificial opals prepared by melt compression," Polymer 44, 7625-7634 (2003). [CrossRef]
  21. O. L. J. Pursiainen, J. J. Baumberg, H. Winkler, B. Viel, and T. Ruhl, "Compact strain-sensitive flexible photonic crystals for sensors," Appl. Phys. Lett. 87, 101902-101904 (2005). [CrossRef]
  22. G. Labeyrie, C. A. Muller, D. S. Wiersma, C. Miniatura, and R. Kaiser, "Observation of coherent backscattering of light by cold atoms," J. Opt. B: Quantum Semiclassical Opt. 2, 672-685 (2000). [CrossRef]
  23. Using conventional spectro-photometers thus yields erroneous measurements as some significant fraction of S is also collected.
  24. V. N. Astratov, A. M. Adawi, S. Fricker, M. S. Skolnick, D. M. Whittaker, and P. N. Pusey "Interplay of order and disorder in the optical properties of opal photonic crystals," Phys. Rev. B 66, 165215-165227 (2002). [CrossRef]
  25. T. Ruhl and G. P. Hellmann, "Colloidal crystals in latex films: rubbery opals," Macromol. Chem. Phys. 202, 3502-3505 (2001). [CrossRef]
  26. Yu. A. Vlasov, M. A. Kaliteevski, and V. V. Nikolaev, "Different regimes of light localization in a disordered photonic crystal," Phys. Rev. B 60, 1555-1562 (1999). [CrossRef]
  27. R. Rengarajan, D. Mittleman, C. Rich, and V. Colvin, "Effect of disorder on the optical properties of colloidal crystals," Phys. Rev. E 71, 016615-016625 (2005). [CrossRef]
  28. A. F. Koenderink and W. L. Vos, "Optical properties of real photonic crystals: anomalous diffuse transmission," J. Opt. Soc. Am. B 22, 1075-1084 (2005). [CrossRef]
  29. C. Hermann and O. Hess, "Modified spontaneous-emission rate in an inverted-opal structure with complete photonic bandgap," J. Opt. Soc. Am. B 19, 3013-3018 (2002). [CrossRef]
  30. R. C. McPhedran, L. C. Botten, J. McOrist, A. A. Asatryan, C. M. de Sterke, and N. A. Nicorovici, "Density of states functions for photonic crystals," Phys. Rev. E 69, 16609-16624 (2004). [CrossRef]
  31. A. V. Baryshev, V. A. Kosobukin, K. B. Samusev, D. E. Usvyat, and M. F. Limonov, "Light diffraction from opal-based photonic crystals with growth-induced disorder: Experiment and theory," Phys. Rev. E 73, 205118 (2006).
  32. S. A. Asher, J. M. Weissman, A. Tikhonov, R. D. Coalson, and R. Kesavamoorthy, "Diffraction in crystalline colloidal-array photonic crystals," Phys. Rev. B 69, 066619 (2004). [CrossRef]

Cited By

Alert me when this paper is cited

OSA is able to provide readers links to articles that cite this paper by participating in CrossRef's Cited-By Linking service. CrossRef includes content from more than 3000 publishers and societies. In addition to listing OSA journal articles that cite this paper, citing articles from other participating publishers will also be listed.


« Previous Article  |  Next Article »

OSA is a member of CrossRef.

CrossCheck Deposited